“Monitoring galvanic replacement through three-dimensional morphological and chemical mapping”. Goris B, Polavarapu L, Bals S, Van Tendeloo G, Liz-Marzán LM, Nano letters 14, 3220 (2014). http://doi.org/10.1021/nl500593j
Abstract: Galvanic replacement reactions on metal nanoparticles are often used for the preparation of hollow nanostructures with tunable porosity and chemical composition, leading to tailored optical and catalytic properties. However, the precise interplay between the three-dimensional (3D) morphology and chemical composition of nanostructures during galvanic replacement is not always well understood as the 3D chemical imaging of nanoscale materials is still challenging. It is especially far from straightforward to obtain detailed information from the inside of hollow nanostructures using electron microscopy techniques such as SEM or TEM. We demonstrate here that a combination of state-of-the-art EDX mapping with electron tomography results in the unambiguous determination of both morphology transformation and elemental composition of nanostructures in 3D, during galvanic replacement of Ag nanocubes. This work provides direct and unambiguous experimental evidence toward understanding the galvanic replacement reaction. In addition, the powerful approach presented here can be applied to a wide range of nanoscale transformation processes, which will undoubtedly guide the development of novel nanostructures.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 12.712
Times cited: 120
DOI: 10.1021/nl500593j
|
|
|
“Morphological transformations and fusion of PbSe nanocrystals studied using atomistic simulations”. Schapotschnikow P, van Huis MA, Zandbergen HW, Vanmaekelbergh D, Vlugt TJH, Nano letters 10, 3966 (2010). http://doi.org/10.1021/nl101793b
Abstract: Molecular dynamics simulations are performed on capped and uncapped PbSe nanocrystals, employing newly developed classical interaction potentials. Here, we show that two uncapped nanocrystals fuse efficiently via direct surface attachment, even if they are initially misaligned. In sharp contrast to the general belief, interparticle dipole interactions do not play a significant role in this oriented attachment process. Furthermore, it is shown that presumably polar, capped PbSe{111} facets are never fully Pb- or Se-terminated.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 12.712
Times cited: 59
DOI: 10.1021/nl101793b
|
|
|
“Networks of quantum nanorings : programmable spintronic devices”. Földi P, Kálmán O, Benedict MG, Peeters FM, Nano letters 8, 2556 (2008). http://doi.org/10.1021/nl801858a
Abstract: An array of quantum rings with local (ring by ring) modulation of the spin orbit interaction (SOI) can lead to novel effects in spin state transformation of electrons. It is shown that already small (3 x 3, 5 x 5) networks are remarkably versatile from this point of view: Working in a given network geometry, the input current can be directed to any of the output ports, simply by changing the SOI strengths by external gate voltages. Additionally, the same network with different SOI strengths can be completely analogous to the Stern-Gerlach device, exhibiting spatial-spin entanglement.
Keywords: A1 Journal article; Engineering sciences. Technology; Condensed Matter Theory (CMT)
Impact Factor: 12.712
Times cited: 76
DOI: 10.1021/nl801858a
|
|
|
“Phase selection enabled formation of abrupt axial heterojunctions in branched oxide nanowires”. Gao J, Lebedev OI, Turner S, Li YF, Lu YH, Feng YP, Boullay P, Prellier W, Van Tendeloo G, Wu T, Nano letters 12, 275 (2012). http://doi.org/10.1021/nl2035089
Abstract: Rational synthesis of nanowires via the vaporliquidsolid (VLS) mechanism with compositional and structural controls is vitally important for fabricating functional nanodevices from bottom up. Here, we show that branched indium tin oxide nanowires can be in situ seeded in vapor transport growth using tailored AuCu alloys as catalyst. Furthermore, we demonstrate that VLS synthesis gives unprecedented freedom to navigate the ternary InSnO phase diagram, and a rare and bulk-unstable cubic phase can be selectively stabilized in nanowires. The stabilized cubic fluorite phase possesses an unusual almost equimolar concentration of In and Sn, forming a defect-free epitaxial interface with the conventional bixbyite phase of tin-doped indium oxide that is the most employed transparent conducting oxide. This rational methodology of selecting phases and making abrupt axial heterojunctions in nanowires presents advantages over the conventional synthesis routes, promising novel composition-modulated nanomaterials.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 12.712
Times cited: 25
DOI: 10.1021/nl2035089
|
|
|
“Phonon band structure of Si nanowires: a stability analysis”. Peelaers H, Partoens B, Peeters FM, Nano letters 9, 107 (2009). http://doi.org/10.1021/nl802613p
Abstract: We present full ab initio calculations of the phonon band structure of thin Si nanowires oriented along the [110] direction. Using these phonon dispersion relations, we investigate the structural stability of these wires. We found that all studied wires were stable also when doped with either B or P, if the unit cell was taken sufficiently large along the wire axis. The evolution of the phonon dispersion relations and of the sound velocities with respect to the wire diameters is discussed. Softening is observed for acoustic modes and hardening for optical phonon modes with increasing wire diameters.
Keywords: A1 Journal article; Condensed Matter Theory (CMT)
Impact Factor: 12.712
Times cited: 51
DOI: 10.1021/nl802613p
|
|
|
“Quantitative three-dimensional reconstruction of catalyst particles for bamboo-like carbon nanotubes”. Bals S, Batenburg J, Verbeeck J, Sijbers J, Van Tendeloo G, Nano letters 7, 3669 (2007). http://doi.org/10.1021/nl071899m
Abstract: The three-dimensional (3D) structure and chemical composition of bamboo-like carbon nanotubes including the catalyst particles that are. used during their growth are studied by discrete electron tomography in combination with energy-filtered transmission electron microscopy. It is found that cavities are present in the catalyst particles. Furthermore, only a small percentage of the catalyst particles consist of pure Cu, since a large volume fraction of the particles is oxidized to CU(2)0. These volume fractions are determined quantitatively from 3D reconstructions obtained by discrete tomography.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT); Vision lab
Impact Factor: 12.712
Times cited: 78
DOI: 10.1021/nl071899m
|
|
|
“Real-time atomic scale imaging of nanostructural evolution in aluminum alloys”. Malladi SK, Xu Q, van Huis MA, Tichelaar FD, Batenburg KJ, Yucelen E, Dubiel B, Czyrska-Filemonowicz A, Zandbergen HW, Nano Letters 14, 384 (2014). http://doi.org/10.1021/nl404565j
Abstract: We present a new approach to study the three-dimensional compositional and structural evolution of metal alloys during heat treatments such as commonly used for improving overall material properties. It relies on in situ heating in a high-resolution scanning transmission electron microscope (STEM). The approach is demonstrated using a commercial Al alloy AA2024 at 100-240 degrees C, showing in unparalleled detail where and how precipitates nucleate, grow,or dissolve. The observed size evolution of individual precipitates enables a separation between nucleation and growth phenomena, necessary for the development of refined growth models. We conclude that the in situ heating STEM approach opens a route to a much faster determination of the interplay between local compositions, heat treatments, microstructure, and mechanical properties of new alloys.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT); Vision lab
Impact Factor: 12.712
Times cited: 12
DOI: 10.1021/nl404565j
|
|
|
“Rings of double-walled carbon nanotube bundles”. Colomer J-F, Henrard L, Flahaut E, Van Tendeloo G, Lucas AA, Lambin P, Nano letters 3, 685 (2003). http://doi.org/10.1021/nl034159w
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 12.712
Times cited: 59
DOI: 10.1021/nl034159w
|
|
|
“Steric hindrance induces crosslike self-assembly of gold nanodumbbells”. Grzelczak M, Sánchez-Iglesias A, Heidari Mezerji H, Bals S, Pérez-Juste J, Liz-Marzán LM, Nano letters 12, 4380 (2012). http://doi.org/10.1021/nl3021957
Abstract: In the formation of colloidal molecules, directional interactions are crucial for controlling the spatial distribution of the building blocks. Anisotropic nanoparticles facilitate directional clustering via steric constraints imposed by each specific shape, thereby restricting assembly along certain directions. We show in this Letter that the combination of patchiness (attraction) and shape (steric hindrance) allows assembling gold nanodumbbell building blocks into crosslike dimers with well-controlled interparticle distance and relative orientation. Steric hindrance between interacting dumbbell-like particles opens up a new synthetic approach toward low-symmetry plasmonic clusters, which may significantly contribute to understand complex plasmonic phenomena.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 12.712
Times cited: 85
DOI: 10.1021/nl3021957
|
|
|
“Three-dimensional atomic imaging of colloidal core-shell nanocrystals”. Bals S, Casavola M, van Huis MA, Van Aert S, Batenburg KJ, Van Tendeloo G, Vanmaekelbergh D, Nano letters 11, 3420 (2011). http://doi.org/10.1021/nl201826e
Abstract: Colloidal coreshell semiconductor nanocrystals form an important class of optoelectronic materials, in which the exciton wave functions can be tailored by the atomic configuration of the core, the interfacial layers, and the shell. Here, we provide a trustful 3D characterization at the atomic scale of a free-standing PbSe(core)CdSe(shell) nanocrystal by combining electron microscopy and discrete tomography. Our results yield unique insights for understanding the process of cation exchange, which is widely employed in the synthesis of coreshell nanocrystals. The study that we present is generally applicable to the broad range of colloidal heteronanocrystals that currently emerge as a new class of materials with technological importance.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT); Vision lab
Impact Factor: 12.712
Times cited: 121
DOI: 10.1021/nl201826e
|
|
|
“Three-dimensional elemental mapping at the atomic scale in bimetallic nanocrystals”. Goris B, de Backer A, Van Aert S, Gómez-Graña S, Liz-Marzán LM, Van Tendeloo G, Bals S, Nano letters 13, 4236 (2013). http://doi.org/10.1021/nl401945b
Abstract: A thorough understanding of the three-dimensional (3D) atomic structure and composition of coreshell nanostructures is indispensable to obtain a deeper insight on their physical behavior. Such 3D information can be reconstructed from two-dimensional (2D) projection images using electron tomography. Recently, different electron tomography techniques have enabled the 3D characterization of a variety of nanostructures down to the atomic level. However, these methods have all focused on the investigation of nanomaterials containing only one type of chemical element. Here, we combine statistical parameter estimation theory with compressive sensing based tomography to determine the positions and atom type of each atom in heteronanostructures. The approach is applied here to investigate the interface in coreshell Au@Ag nanorods but it is of great interest in the investigation of a broad range of nanostructures.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 12.712
Times cited: 90
DOI: 10.1021/nl401945b
|
|
|
“Topological surface state enhanced photothermoelectric effect in Bi2Se3 nanoribbons”. Yan Y, Liao ZM, Ke X, Van Tendeloo G, Wang Q, Sun D, Yao W, Zhou S, Zhang L, Wu HC, Yu DP;, Nano letters 14, 4389 (2014). http://doi.org/10.1021/nl501276e
Abstract: The photothermoelectric effect in topological insulator Bi2Se3 nanoribbons is studied. The topological surface states are excited to be spin-polarized by circularly polarized light. Because the direction of the electron spin is locked to its momentum for the spin-helical surface states, the photothermoelectric effect is significantly enhanced as the oriented motions of the polarized spins are accelerated by the temperature gradient. The results are explained based on the microscopic mechanisms of a photon induced spin transition from the surface Dirac cone to the bulk conduction band. The as-reported enhanced photothermoelectric effect is expected to have potential applications in a spin-polarized power source.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 12.712
Times cited: 51
DOI: 10.1021/nl501276e
|
|
|
“Tunable quantum dots in bilayer graphene”. Milton Pereira J, Vasilopoulos P, Peeters FM, Nano letters 7, 946 (2007). http://doi.org/10.1021/nl062967s
Keywords: A1 Journal article; Condensed Matter Theory (CMT)
Impact Factor: 12.712
Times cited: 167
DOI: 10.1021/nl062967s
|
|
|
“Tuning the optical, magnetic, and electrical properties of ReSe2 by nanoscale strain engineering”. Yang S, Wang C, Sahin H, Chen H, Li Y, Li SS, Suslu A, Peeters FM, Liu Q, Li J, Tongay S;, Nano letters 15, 1660 (2015). http://doi.org/10.1021/nl504276u
Abstract: Creating materials with ultimate control over their physical properties is vital for a wide range of applications. From a traditional materials design perspective, this task often requires precise control over the atomic composition and structure. However, owing to their mechanical properties, low-dimensional layered materials can actually withstand a significant amount of strain and thus sustain elastic deformations before fracture. This, in return, presents a unique technique for tuning their physical properties by strain engineering. Here, we find that local strain induced on ReSe2, a new member of the transition metal dichalcogenides family, greatly changes its magnetic, optical, and electrical properties. Local strain induced by generation of wrinkle (1) modulates the optical gap as evidenced by red-shifted photoluminescence peak, (2) enhances light emission, (3) induces magnetism, and (4) modulates the electrical properties. The results not only allow us to create materials with vastly different properties at the nanoscale, but also enable a wide range of applications based on 2D materials, including strain sensors, stretchable electrodes, flexible field-effect transistors, artificial-muscle actuators, solar cells, and other spintronic, electromechanical, piezoelectric, photonic devices.
Keywords: A1 Journal article; Engineering sciences. Technology; Condensed Matter Theory (CMT)
Impact Factor: 12.712
Times cited: 314
DOI: 10.1021/nl504276u
|
|
|
“Controlled Living Nanowire Growth: Precise Control over the Morphology and Optical Properties of AgAuAg Bimetallic Nanowires”. Mayer M, Scarabelli L, March K, Altantzis T, Tebbe M, Kociak M, Bals S, Garcia de Abajo FJ, Fery A, Liz-Marzan LM, Nano letters 15, 5427 (2015). http://doi.org/10.1021/acs.nanolett.5b01833
Abstract: Inspired by the concept of living polymerization reaction, we are able to produce silver-gold-silver nanowires with a precise control over their total length and plasmonic properties by establishing a constant silver deposition rate on the tips of penta-twinned gold nanorods used as seed cores. Consequently, the length of the wires increases linearly in time. Starting with approximately 210 nm x 32 nm gold cores, we produce nanowire lengths up to several microns in a highly controlled manner, with a small self-limited increase in thickness of approximately 4 nm, corresponding to aspect ratios above 100, whereas the low polydispersity of the product allows us to detect up to nine distinguishable plasmonic resonances in a single colloidal solution. We analyze the spatial distribution and the nature of the plasmons by electron energy loss spectroscopy and obtain excellent agreement between measurements and electromagnetic simulations, clearly demonstrating that the presence of the gold core plays a marginal role, except for relatively short wires or high-energy modes.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 12.712
Times cited: 117
DOI: 10.1021/acs.nanolett.5b01833
|
|
|
“Femtosecond Laser-Controlled Tip-to-Tip Assembly and Welding of Gold Nanorods”. Gonzalez-Rubio G, Gonzalez-Izquierdo J, Banares L, Tardajos G, Rivera A, Altantzis T, Bals S, Pena-Rodriguez O, Guerrero-Martinez A, Liz-Marzan LM, Nano letters 15, 8282 (2015). http://doi.org/10.1021/acs.nanolett.5b03844
Abstract: Directed assembly of gold nanorods through the use of dithiolated molecular linkers is one of the most efficient methodologies for the morphologically controlled tip-to-tip assembly of this type of anisotropic nanocrystals. However, in a direct analogy to molecular polymerization synthesis, this process is characterized by difficulties in chain-growth control over nanoparticle oligomers. In particular, it is nearly impossible to favor the formation of one type of oligomer, making the methodology hard to use for actual applications in nanoplasmonics. We propose here a light-controlled synthetic procedure that allows obtaining selected plasmonic oligomers in high yield and with reaction times in the scale of minutes by irradiation with low fluence near-infrared (NIR) femtosecond laser pulses. Selective inhibition of the formation of gold nanorod n-mers (trimers) with a longitudinal localized surface plasmon in resonance with a 800 nm Ti:sapphire laser, allowed efficient trapping of the (n – 1)-mers (dimers) by hot spot mediated photothermal decomposition of the interparticle molecular linkers. Laser irradiation at higher energies produced near-field enhancement at the interparticle gaps, which is large enough to melt gold nanorod tips, offering a new pathway toward tip-to-tip welding of gold nanorod oligomers with a plasmonic response at the NIR. Thorough optical and electron microscopy characterization indicates that plasmonic oligomers can be selectively trapped and welded, which has been analyzed in terms of a model that predicts with reasonable accuracy the relative concentrations of the main plasmonic species.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 12.712
Times cited: 101
DOI: 10.1021/acs.nanolett.5b03844
|
|
|
“Single Particle Deformation and Analysis of Silica-Coated Gold Nanorods before and after Femtosecond Laser Pulse Excitation”. Albrecht W, Deng T-S, Goris B, van Huis MA, Bals S, van Blaaderen A, Nano letters 16, 1818 (2016). http://doi.org/10.1021/acs.nanolett.5b04851
Abstract: We performed single particle deformation experiments on silica-coated gold nanorods under femtosecond (fs) illumination. Changes in the particle shape were analyzed by electron microscopy and associated changes in the plasmon resonance by electron energy loss spectroscopy. Silica-coated rods were found to be more stable compared to uncoated rods but could still be deformed via an intermediate bullet-like shape for silica shell thicknesses of 14 nm. Changes in the size ratio of the rods after fs-illumination resulted in blue-shifting of the longitudinal plasmon resonances. Two-dimensional spatial mapping of the plasmon resonances revealed that the flat side of the bullet-like particles showed a less pronounced longitudinal plasmonic electric field enhancement. These findings were confirmed by finite-difference time-domain (FDTD) simulations. Furthermore, at higher laser fluences size reduction of the particles was found as well as for particles that were not completely deformed yet.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 12.712
Times cited: 55
DOI: 10.1021/acs.nanolett.5b04851
|
|
|
“Bending Gold Nanorods with Light”. Babynina A, Fedoruk M, Kuhler P, Meledin A, Doblinger M, Lohmueller T, Nano letters 16, 6485 (2016). http://doi.org/10.1021/acs.nanolett.6b03029
Abstract: V-shaped gold nanoantennas are the functional components of plasmonic metasurfaces, which are capable of manipulating light in unprecedented ways. Designing a metasurface requires the custom arrangement of individual antennas with controlled shape and orientation. Here, we show how highly crystalline gold nanorods in solution can be bend, one-by one, into a V-shaped geometry and printed to the surface of a solid support through a combination of plasmonic heating and optical force. Significantly, we demonstrate that both the bending angle and the orientation of each rod-antenna can be adjusted independent from each other by tuning the laser intensity and polarization. This approach is applicable for the patterning of V-shaped plasmonic antennas on almost any substrate, which holds great potential for the fabrication of ultrathin optical components and devices.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 12.712
Times cited: 24
DOI: 10.1021/acs.nanolett.6b03029
|
|
|
“Accelerated removal of Fe-antisite defects while nanosizing hydrothermal LiFePO4 with Ca2+”. Paolella A, Turner S, Bertoni G, Hovington P, Flacau R, Boyer C, Feng Z, Colombo M, Marras S, Prato M, Manna L, Guerfi A, Demopoulos GP, Armand M, Zaghib K;, Nano letters 16, 2692 (2016). http://doi.org/10.1021/acs.nanolett.6b00334
Abstract: Based on neutron powder diffraction (NPD) and high angle annular dark field scanning transmission electron microscopy (HAADF-STEM), we show that calcium ions help eliminate the Fe-antisite defects by controlling the nucleation and evolution of the LiFePO4 particles during their hydrothermal synthesis. This Ca-regulated formation of LiFePO4 particles has an overwhelming impact on the removal of their iron antisite defects during the subsequent carbon coating step since (i) almost all the Fe-antisite defects aggregate at the surface of the LiFePO4 crystal when the crystals are small enough and (ii) the concomitant increase of the surface area, which further exposes the Fe-antisite defects. Our results not only justify a low-cost, efficient and reliable hydrothermal synthesis method for LiFePO4 but also provide a promising alternative viewpoint on the mechanism controlling the nanosizing of LiFePO4, which leads to improved electrochemical performances.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 12.712
Times cited: 30
DOI: 10.1021/acs.nanolett.6b00334
|
|
|
“Magnetic drug targeting : preclinical in vivo studies, mathematical modeling, and extrapolation to humans”. Al-Jamal KT, Bai J, Wang JTW, Protti A, Southern P, Bogart L, Heidari H, Li X, Cakebread A, Asker D, Al-Jamal WT, Shah A, Bals S, Sosabowski J, Pankhurst QA;, Nano letters 16, 5652 (2016). http://doi.org/10.1021/ACS.NANOLETT.6B02261
Abstract: A sound theoretical rationale for the design of a magnetic nanocarrier capable of magnetic capture in vivo after intravenous administration could help elucidate the parameters necessary for in vivo magnetic tumor targeting. In this work, we utilized our long-circulating polymeric magnetic nano carriers, encapsulating increasing amounts of superparamagnetic iron oxide nanoparticles (SPIONs) in a biocompatible oil carrier, to study the effects of SPION loading and of applied magnetic field strength on magnetic tumor targeting in CT26 tumor-bearing mice. Under controlled conditions, the in vivo magnetic targeting was quantified and found to be directly proportional to SPION loading and magnetic field strength. Highest SPION loading, however, resulted in a reduced blood circulation time and a plateauing of the magnetic targeting. Mathematical modeling was undertaken to compute the in vivo magnetic, viscoelastic, convective, and diffusive forces acting on the nanocapsules (NCs) in accordance with the Nacev-Shapiro construct, and this was then used to extrapolate to the expected behavior in humans. The model predicted that in the latter case, the NCs and magnetic forces applied here would have been sufficient to achieve successful targeting in humans. Lastly, an in vivo murine tumor growth delay study was performed using docetaxel (DTX)-encapsulated NCs. Magnetic targeting was found to offer enhanced therapeutic efficacy, and improve mice survival compared to passive targeting at drug doses of ca. 5-8 mg, of DTX/kg. This is,, to our knowledge, the first study that truly bridges the gap between preclinical experiments and clinical translation in the field of magnetic drug targeting.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 12.712
Times cited: 128
DOI: 10.1021/ACS.NANOLETT.6B02261
|
|
|
“Field mapping with nanometer-scale resolution for the next generation of electronic devices”. Cooper D, de la Peña F, Béché, A, Rouvière J-L, Servanton G, Pantel R, Morin P, Nano letters 11, 4585 (2011). http://doi.org/10.1021/NL201813W
Abstract: In order to improve the performance of todays nanoscaled semiconductor devices, characterization techniques that can provide information about the position and activity of dopant atoms and the strain fields are essential. Here we demonstrate that by using a modern transmission electron microscope it is possible to apply multiple techniques to advanced materials systems in order to provide information about the structure, fields, and composition with nanometer-scale resolution. Off-axis electron holography has been used to map the active dopant potentials in state-of-the-art semiconductor devices with 1 nm resolution. These dopant maps have been compared to electron energy loss spectroscopy maps that show the positions of the dopant atoms. The strain fields in the devices have been measured by both dark field electron holography and nanobeam electron diffraction.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 12.712
Times cited: 12
DOI: 10.1021/NL201813W
|
|
|
“Designing diameter-modulated heterostructure nanowires of PbTe/Te by controlled dewetting”. Kumar A, Kundu S, Samantaray D, Kundu P, Zanaga D, Bals S, Ravishankar N, Nano letters 17, 7226 (2017). http://doi.org/10.1021/ACS.NANOLETT.7B02442
Abstract: <script type='text/javascript'>document.write(unpmarked('Heterostructures consisting of semiconductors with controlled morphology and interfaces find applications in many fields. A range of axial, radial, and diameter-modulated nanostructures have been synthesized primarily using vapor phase methods. Here, we present a simple wet chemical routine to synthesize heterostructures of PbTe/Te using Te nanowires as templates. A morphology evolution study for the formation of these heterostructures has been performed. On the basis of these control experiments, a pathway for the formation of these nanostructures is proposed. Reduction of a Pb precursor to Pb on Te nanowire templates followed by interdiffusion of Pb/Te leads to the formation of a thin shell of PbTe on the Te wires. Controlled dewetting of the thin shell leads to the formation of cube-shaped PbTe that is periodically arranged on the Te wires. Using control experiments, we show that different reactions parameters like rate of addition of the reducing agent, concentration of Pb precursor and thickness of initial Te nanowire play a critical role in controlling the spacing between the PbTe cubes on the Te wires. Using simple surface energy arguments, we propose a mechanism for the formation of the hybrid. The principles presented are general and can be exploited for the synthesis of other nanoscale heterostructures.'));
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 12.712
Times cited: 11
DOI: 10.1021/ACS.NANOLETT.7B02442
|
|
|
“Nonlinear light mixing by graphene plasmons”. Kundys D, Van Duppen B, Marshall OP, Rodriguez F, Torre I, Tomadin A, Polini M, Grigorenko AN, Nano letters 18, 282 (2018). http://doi.org/10.1021/ACS.NANOLETT.7B04114
Abstract: <script type='text/javascript'>document.write(unpmarked('Graphene is known to possess strong optical nonlinearity which turned out to be suitable for creation of efficient saturable absorbers in mode locked fiber lasers. Nonlinear response of graphene can be further enhanced by the presence of graphene plasmons. Here, we report a novel nonlinear effect observed in nanostructured graphene which comes about due to excitation of graphene plasmons. We experimentally detect and theoretically explain enhanced mixing of near-infrared and mid-infrared light in arrays of graphene nanoribbons. Strong compression of light by graphene plasmons implies that the described effect of light mixing is nonlocal in nature and orders of magnitude larger than the conventional local graphene nonlinearity. Both second and third order nonlinear effects were observed in our experiments with the recalculated third-order nonlinearity coefficient reaching values of 4.5 x 10(-6) esu. The suggested effect could be used in variety of applications including nonlinear light modulators, light multiplexers, light logic, and sensing devices.'));
Keywords: A1 Journal article; Engineering sciences. Technology; Condensed Matter Theory (CMT)
Impact Factor: 12.712
Times cited: 12
DOI: 10.1021/ACS.NANOLETT.7B04114
|
|
|
“Asymmetric Modulation on Exchange Field in a Graphene/BiFeO3Heterostructure by External Magnetic Field”. Song H-D, Wu Y-F, Yang X, Ren Z, Ke X, Kurttepeli M, Tendeloo GV, Liu D, Wu H-C, Yan B, Wu X, Duan C-G, Han G, Liao Z-M, Yu D, Nano letters 18, 2435 (2018). http://doi.org/10.1021/acs.nanolett.7b05480
Abstract: Graphene, having all atoms on its surface, is favorable to extend the functions by introducing the spin–orbit coupling and magnetism through proximity effect. Here, we report the tunable interfacial exchange field produced by proximity coupling in graphene/BiFeO3 heterostructures. The exchange field has a notable dependence with external magnetic field, and it is much larger under negative magnetic field than that under positive magnetic field. For negative external magnetic field, interfacial exchange coupling gives rise to evident spin splitting for N ≠ 0 Landau levels and a quantum Hall metal state for N = 0 Landau level. Our findings suggest graphene/BiFeO3 heterostructures are promising for spintronics.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 12.712
Times cited: 9
DOI: 10.1021/acs.nanolett.7b05480
|
|
|
“Three-Dimensional Quantification of the Facet Evolution of Pt Nanoparticles in a Variable Gaseous Environment”. Altantzis T, Lobato I, De Backer A, Béché, A, Zhang Y, Basak S, Porcu M, Xu Q, Sánchez-Iglesias A, Liz-Marzán LM, Van Tendeloo G, Van Aert S, Bals S, Nano letters 19, 477 (2019). http://doi.org/10.1021/acs.nanolett.8b04303
Abstract: Pt nanoparticles play an essential role in a wide variety of catalytic reactions. The activity of the particles strongly depends on their three-dimensional (3D) structure and exposed facets, as well as on the reactive environment. High-resolution electron microscopy has often been used to characterize nanoparticle catalysts but unfortunately most observations so far have been either performed in vacuum and/or using conventional (2D) in situ microscopy. The latter however does not provide direct 3D morphological information. We have implemented a quantitative methodology to measure variations of the 3D atomic structure of nanoparticles under the flow of a selected gas. We were thereby able to quantify refaceting of Pt nanoparticles with atomic resolution during various oxidation−reduction cycles. In a H2 environment, a more faceted surface morphology of the particles was observed with {100} and {111} planes being dominant. On the other hand, in O2 the percentage of {100} and {111} facets decreased and a significant increase of higher order facets was found, resulting in a more rounded morphology. This methodology opens up new opportunities toward in situ characterization of catalytic nanoparticles because for the first time it enables one to directly measure 3D morphology variations at the atomic scale in a specific gaseous reaction environment.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 12.712
Times cited: 82
DOI: 10.1021/acs.nanolett.8b04303
|
|
|
“Fe2+Deficiencies, FeO Subdomains, and Structural Defects Favor Magnetic Hyperthermia Performance of Iron Oxide Nanocubes into Intracellular Environment”. Lak A, Cassani M, Mai BT, Winckelmans N, Cabrera D, Sadrollahi E, Marras S, Remmer H, Fiorito S, Cremades-Jimeno L, Litterst FJ, Ludwig F, Manna L, Teran FJ, Bals S, Pellegrino T, Nano letters 18, 6856 (2018). http://doi.org/10.1021/acs.nanolett.8b02722
Abstract: Herein, by studying a stepwise phase transformation of 23 nm FeO-Fe3O4 core-shell nanocubes into Fe3O4, we identify a composition at which the magnetic heating performance of the nanocubes is not affected by the medium viscosity and aggregation. Structural and magnetic characterizations reveal the transformation of the FeO-Fe3O4 nanocubes from having stoichiometric phase compositions into Fe2+ deficient Fe3O4 phases. The resultant nanocubes contain tiny compressed and randomly distributed FeO sub-domains as well as structural defects. This phase transformation causes a tenfold increase in the magnetic losses of the nanocubes, which remains exceptionally insensitive to the medium viscosity as well as aggregation unlike similarly sized single-phase magnetite nanocubes. We observe that the dominant relaxation mechanism switches from Néel in fresh core-shell nanocubes to Brownian in partially oxidized nanocubes and once again to Néel in completely treated nanocubes. The Fe2+ deficiencies and structural defects appear to reduce the magnetic energy barrier and anisotropy field, thereby driving the overall relaxation into Néel process. The magnetic losses of the particles remain unchanged through a progressive internalization/association to ovarian cancer cells. Moreover, the particles induce a significant cell death after being exposed to hyperthermia treatment. Here, we present the largest heating performance that has been reported to date for 23 nm iron oxide nanoparticles under cellular and intracellular conditions. Our findings clearly demonstrate the positive impacts of the Fe2+ deficiencies and structural defects in the Fe3O4 structure on the heating performance under cellular and intracellular conditions.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 12.712
Times cited: 51
DOI: 10.1021/acs.nanolett.8b02722
|
|
|
“In Situ Electron Diffraction Tomography Using a Liquid-Electrochemical Transmission Electron Microscopy Cell for Crystal Structure Determination of Cathode Materials for Li-Ion batteries”. Karakulina OM, Demortière A, Dachraoui W, Abakumov AM, Hadermann J, Nano letters 18, 6286 (2018). http://doi.org/10.1021/acs.nanolett.8b02436
Abstract: We demonstrate that changes in the unit cell structure of lithium battery cathode materials during electrochemical cycling in liquid electrolyte can be determined for particles of just a few hundred nanometers in size using in situ transmission electron microscopy (TEM). The atomic coordinates, site occupancies (including lithium occupancy), and cell parameters of the materials can all be reliably quantified. This was achieved using electron diffraction tomography (EDT) in a sealed electrochemical cell with conventional liquid electrolyte (LP30) and LiFePO4 crystals, which have a well-documented charged structure to use as reference. In situ EDT in a liquid environment cell provides a viable alternative to in situ X-ray and neutron diffraction experiments due to the more local character of TEM, allowing for single crystal diffraction data to be obtained from multiphased powder samples and from submicrometer- to nanometer-sized particles. EDT is the first in situ TEM technique to provide information at the unit cell level in the liquid environment of a commercial TEM electrochemical cell. Its application to a wide range of electrochemical experiments in liquid environment cells and diverse types of crystalline materials can be envisaged.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 12.712
Times cited: 12
DOI: 10.1021/acs.nanolett.8b02436
|
|
|
“Self-limiting growth of two-dimensional palladium between graphene oxide layers”. Su Y, Prestat E, Hu C, Puthiyapura VK, Neek-Amal M, Xiao H, Huang K, Kravets VG, Haigh SJ, Hardacre C, Peeters FM, Nair RR, Nano letters 19, 4678 (2019). http://doi.org/10.1021/ACS.NANOLETT.9B01733
Abstract: The ability of different materials to display self-limiting growth has recently attracted an enormous amount of attention because of the importance of nanoscale materials in applications for catalysis, energy conversion, (opto)-electronics, and so forth. Here, we show that the electrochemical deposition of palladium (Pd) between graphene oxide (GO) sheets result in the self-limiting growth of 5-nm-thick Pd nanosheets. The self-limiting growth is found to be a consequence of the strong interaction of Pd with the confining GO sheets, which results in the bulk growth of Pd being energetically unfavorable for larger thicknesses. Furthermore, we have successfully carried out liquid exfoliation of the resulting Pd-GO laminates to isolate Pd nanosheets and have demonstrated their high efficiency in continuous flow catalysis and electrocatalysis.
Keywords: A1 Journal article; Engineering sciences. Technology; Condensed Matter Theory (CMT)
Impact Factor: 12.712
Times cited: 17
DOI: 10.1021/ACS.NANOLETT.9B01733
|
|
|
“Two-dimensional covalent crystals by chemical conversion of thin van der Waals materials”. Sreepal V, Yagmurcukardes M, Vasu KS, Kelly DJ, Taylor SFR, Kravets VG, Kudrynskyi Z, Kovalyuk ZD, Patane A, Grigorenko AN, Haigh SJ, Hardacre C, Eaves L, Sahin H, Geim AK, Peeters FM, Nair RR, Nano letters 19, 6475 (2019). http://doi.org/10.1021/ACS.NANOLETT.9B02700
Abstract: Most of the studied two-dimensional (2D) materials have been obtained by exfoliation of van der Waals crystals. Recently, there has been growing interest in fabricating synthetic 2D crystals which have no layered bulk analogues. These efforts have been focused mainly on the surface growth of molecules in high vacuum. Here, we report an approach to making 2D crystals of covalent solids by chemical conversion of van der Waals layers. As an example, we used 2D indium selenide (InSe) obtained by exfoliation and converted it by direct fluorination into indium fluoride (InF3), which has a nonlayered, rhombohedral structure and therefore cannot possibly be obtained by exfoliation. The conversion of InSe into InF3 is found to be feasible for thicknesses down to three layers of InSe, and the obtained stable InF3 layers are doped with selenium. We study this new 2D material by optical, electron transport, and Raman measurements and show that it is a semiconductor with a direct bandgap of 2.2 eV, exhibiting high optical transparency across the visible and infrared spectral ranges. We also demonstrate the scalability of our approach by chemical conversion of large-area, thin InSe laminates obtained by liquid exfoliation, into InF3 films. The concept of chemical conversion of cleavable thin van der Waals crystals into covalently bonded noncleavable ones opens exciting prospects for synthesizing a wide variety of novel atomically thin covalent crystals.
Keywords: A1 Journal article; Engineering sciences. Technology; Condensed Matter Theory (CMT)
Impact Factor: 12.712
Times cited: 32
DOI: 10.1021/ACS.NANOLETT.9B02700
|
|
|
“Circular Dichroism Measurement of Single Metal Nanoparticles Using Photothermal Imaging”. Spaeth P, Adhikari S, Le L, Jollans T, Pud S, Albrecht W, Bauer T, Caldarola M, Kuipers L, Orrit M, Nano Letters 19, 8934 (2019). http://doi.org/10.1021/acs.nanolett.9b03853
Abstract: Circular dichroism (CD) spectroscopy is a powerful optical technique for the study of chiral materials and molecules. It gives access to an enantioselective signal based on the differential absorption of right and left circularly polarized light, usually obtained through polarization analysis of the light transmitted through a sample of interest. CD is routinely used to determine the secondary structure of proteins and their conformational state. However, CD signals are weak, limiting the use of this powerful technique to ensembles of many molecules. Here, we experimentally realize the concept of photothermal circular dichroism, a technique that combines the enantioselective signal from circular dichroism with the high sensitivity of photothermal microscopy, achieving a superior signal-to-noise ratio to detect chiral nano-objects. As a proof of principle, we studied the chiral response of single plasmonic nanostructures with CD in the visible range, demonstrating a signal-to-noise ratio better than 40 with only 30 ms integration time for these nanostructures. The high signal-to-noise ratio allows us to quantify the CD signal for individual nanoparticles. We show that we can distinguish relative absorption differences for right circularly and left circularly polarized light as small as gmin = 4 × 10–3 for a 30 ms integration time with our current experimental settings. The enhanced sensitivity of our technique extends CD studies to individual nano-objects and opens CD spectroscopy to numbers of molecules much lower than those in conventional experiments.
Keywords: A1 Journal article; Photothermal microscopy, chirality, circular dichroism, dissymmetry factor, linear dichroism, gold nanostructures; Electron Microscopy for Materials Science (EMAT) ;
Impact Factor: 12.712
DOI: 10.1021/acs.nanolett.9b03853
|
|