Abstract: Zeolitic growth is often absent or occurs in separate phases when synthetic strategies based on the combination of zeolite templates and mesopore templating agents are applied. In this work, zeolitic growth and mesopore formation have been investigated at different temperatures by applying a one-pot templating approach, based on a TS-1 zeolite synthesis whereby part of the microtemplate (tetrapropylammonium hydroxide, TPAOH) is replaced by a mesotemplate (hexadecyltrimethylammonium bromide, CTMABr). Moreover, the synthesis duration and the molar ratio of the microtemplate/mesotemplate have also been studied. The different syntheses clearly show the inherent competitive mechanism between zeolitic growth and mesopore formation. These insights have led to the conclusion that by following a one-pot templating strategy with standard, nonexotic commercial templates, i.e. CTMABr and TPAOH, it is not possible to develop a true hierarchical mesoporous zeolite, meaning a mesoporous siliceous material with highly crystalline zeolitic walls. The resultant materials are instead combined zeolitic/mesoporous composite structures with, however, highly tuneable and controllable porosity characteristics.

Abstract: The chromium-based metal organic framework MIL-101(Cr) served as a host for the in situ synthesis of Fe3O4 nano particles. This hybrid nanomaterial was tested as an adsorbent for arsenite and arsenate species in groundwater and surface water and showed excellent affinity towards As-III and As-V species. The adsorption capacities of 121.5 and 80.0 mg g(-1) for arsenite and arsenate species, respectively, are unprecedented. The presence of Ca2+, Mg2+, and phosphate ions and natural organic matter does not affect the removal efficiency or the selectivity. The structural integrity of the hybrid nanomaterial was maintained during the adsorption process and even after desorption through phosphate elution. Additionally, no significant leaching of Cr or Fe species was observed.

Abstract: Co-containing fluoride-phosphates are of interest in sense of delivering high electrode potentials and attractive specific energy values as positive electrode materials for rechargeable batteries. In this paper we report on a new Co-based fluoride-phosphate, LiNaCoPO4F, with a layered structure (2D), which was Rietveld-refined based on X-ray powder diffraction data [P2(1)/c, a = 6.83881(4) angstrom, b = 11.23323(5) angstrom, c = 5.07654(2) angstrom, beta = 90.3517(5) degrees, V = 389.982(3) angstrom(3)] and validated by electron diffraction and high-resolution scanning transmission electron microscopy. The differential scanning calorimetry measurements revealed that 2D-LiNaCoPO4F forms in a narrow temperature range of 520-530 degrees C and irreversibly converts to the known 3D-LiNaCoPO4F modification (Pnma) above 530 degrees C. The non-carbon-coated 2D-LiNaCoPO4F shows reversible electrochemical activity in Li-ion cell in the potential range of 3.0-4.9 V vs. Li/Li+ with an average potential of approximate to 4.5 V and in Na-ion cell in the range of 3.0-4.5 V vs. Na/Na+ exhibiting a plateau profile centered around 4.2 V, in agreement with the calculated potentials by density functional theory. The energy barriers for both Li+ and Na+ migration in 2D-LiNaCoPO4F amount to 0.15 eV along the [001] direction rendering 2D-LiNaCoPO4F as a viable electrode material for high-power Li- and Na-ion rechargeable batteries. The discovery and stabilization of the 2D-LiNaCoPO4F polymorph indicates that temperature influence on the synthesis of A(2)MPO(4)F fluoride-phosphates needs more careful examination with perspective to unveil new structures.

Abstract: The ordering for 11/20 alloys has been studied by high-resolution electron microscopy (HREM). The distribution of the intensity maxima in the HREM image have been statistically examined, which provides a profound basis for the image interpretation. Processing of the HREM images allows ''dark-field'' images to be obtained, exhibiting a two-dimensional distribution of those columns which contain the most information in order to interpret the short-range order correlations. Pair correlations and higher cluster correlations between projected columns can be visualised, providing unique information about the ordering as retrieved from an experimental result without any other assumption. The method has been applied to Au4Cr and to Au4Mn to interpret the quenched short-range order state and the transition to long-range order.

Abstract: In this paper a particularly simple but efficient method is presented by which samples of alkali-doped C-60 materials or other air-sensitive materials can be prepared and transferred into a transmission electron microscope for direct observations and investigations. Flexible, transparent glove bags are used which are filled to a slight overpressure with dry nitrogen. Under this protective atmosphere, the air-sensitive sample is mounted in the specimen holder and inserted in the vacuum of the electron microscope. Rb6C60 which is prepared and transferred into the microscope in this way has been investigated by transmission electron microscopy (TEM). The results confirm the bcc structure and especially the location of the rubidium atoms.

Abstract: The evolution of the use of the 1250 keV high-voltage electron microscope in Antwerp is sketched by illustrating a non-exhaustive set of examples in various fields. One of the main present fields of application gets some more attention, i.e. the defect studies as produced by processing steps in microelectronic devices: (i) strain-induced dislocations at the edges of various device isolation interlayers, (ii) morphologies resulting from high-energy ion implantation creating buried layers for silicon on insulator (SOI) and other implantation technologies.

Abstract: The study of shock metamorphism of olivine might help to constrain impact events in the history of meteorites. Although shock features in olivine are well known, so far, there are processes that are not yet completely understood. In shock veins, olivine clasts with a complex structure, with a ringwoodite rim and a dense network of lamellae of unidentified nature in the core, have been reported in the literature. A highly shocked (S5-6), L6 meteorite, Asuka 09584, which was recently collected in Antarctica by a Belgian-Japanese joint expedition, contains this type of shocked olivine clasts and has been, therefore, selected for detailed investigations of these features by transmission electron microscopy (TEM). Petrographic, geochemical, and crystallographic studies showed that the rim of these shocked clasts consists of an aggregate of nanocrystals of ringwoodite, with lower Mg/Fe ratio than the unshocked olivine. The clast's core consists of an aggregate of iso-oriented grains of olivine and wadsleyite, with higher Mg/Fe ratio than the unshocked olivine. This aggregate is crosscut by veinlets of nanocrystals of olivine, with extremely low Mg/Fe ratio. The formation of the ringwoodite rim is likely due to solid-state, diffusion-controlled, transformation from olivine under high-temperature conditions. The aggregate of iso-oriented olivine and wadsleyite crystals is interpreted to have formed also by a solid-state process, likely by coherent intracrystalline nucleation. Following the compression, shock release is believed to have caused opening of cracks and fractures in olivine and formation of olivine melt, which has lately crystallized under postshock equilibrium pressure conditions as olivine.

Abstract: Shallow trench isolation (STI) is a promising technology for the isolation structures of the new generation of ULSI devices with dimensions below 0.18 mum. The various processing steps cause stress fields in STI structures, which can lead to defect formation in the silicon substrate. In their turn, stress fields affect the electrical parameters and the reliability of devices. Convergent beam electron diffraction (CBED) is used in this study to examine the influence of a wet and a dry pre-gate oxidation on the stress distribution around STI structures. The measurements are performed on STI structures with different width and spacing. CBED analysis is compared with bright-field TEM images. Defects are observed in high-strain areas of small isolated structures. (C) 2001 Elsevier Science Ltd. All rights reserved.

Abstract: We report the high temperature electronic transport properties of SrFeO3 − ä epitaxial thin films obtained by pulsed laser deposition on NdGaO3(110) substrates. The films show total conductivity higher than the bulk material and apparent activation energy of about 0.12 eV in O2, lower than reported values for SrFeO3 − ä films. The conductivity dependence with oxygen partial pressure shows a power dependence with an exponent close to + 1/4, in agreement with expected point defect equilibrium. For a given oxygen partial pressure, the temperature coefficient of resistance (TCR) shows a low positive value of about 1.52.5 10− 3 K− 1, which is still suitable for resistive oxygen sensing applications. The transport properties of the films are discussed in view of their particular microstructure.