Records |
Author |
Ulu Okudur, F.; D'Haen, J.; Vranken, T.; De Sloovere, D.; Verheijen, M.; Karakulina, O.M.; Abakumov, A.M.; Hadermann, J.; Van Bael, M.K.; Hardy, A. |
Title |
Ti surface doping of LiNi0.5Mn1.5O4−δpositive electrodes for lithium ion batteries |
Type |
A1 Journal article |
Year |
2018 |
Publication |
RSC advances |
Abbreviated Journal |
Rsc Adv |
Volume |
8 |
Issue |
13 |
Pages |
7287-7300 |
Keywords |
A1 Journal article; Electron microscopy for materials research (EMAT) |
Abstract |
The particle surface of LiNi0.5Mn1.5O4−δ (LNMO), a Li-ion battery cathode material, has been modified by Ti cation doping through a hydrolysis–condensation reaction followed by annealing in oxygen. The effect of different annealing temperatures (500–850 °C) on the Ti distribution and electrochemical performance of the surface modified LNMO was investigated. Ti cations diffuse from the preformed amorphous ‘TiOx’ layer into the LNMO surface during annealing at 500 °C. This results in a 2–4 nm thick Ti-rich spinel surface having lower Mn and Ni content compared to the core of the LNMO particles, which was observed with scanning transmission electron microscopy coupled with compositional EDX mapping. An increase in the annealing temperature promotes the formation of a Ti bulk doped LiNi(0.5−w)Mn(1.5+w)−tTitO4 phase and Ti-rich LiNi0.5Mn1.5−yTiyO4 segregates above 750 °C. Fourier-transform infrared spectrometry indicates increasing Ni–Mn ordering with annealing temperature, for both bare and surface modified LNMO. Ti surface modified LNMO annealed at 500 °C shows a superior cyclic stability, coulombic efficiency and rate performance compared to bare LNMO annealed at 500 °C when cycled at 3.4–4.9 V vs. Li/Li+. The improvements are probably due to suppressed Ni and Mn dissolution with Ti surface doping. |
Address |
|
Corporate Author |
|
Thesis |
|
Publisher |
|
Place of Publication |
|
Editor |
|
Language |
|
Wos |
000425508900064 |
Publication Date |
2018-02-13 |
Series Editor |
|
Series Title |
|
Abbreviated Series Title |
|
Series Volume |
|
Series Issue |
|
Edition |
|
ISSN |
2046-2069 |
ISBN |
|
Additional Links |
UA library record; WoS full record; WoS citing articles |
Impact Factor |
3.108 |
Times cited |
9 |
Open Access |
OpenAccess |
Notes |
This research is supported by the Research Foundation Flanders (FWO Vlaanderen, grant number G040116N). This project receives the support of the European Union, the European Regional Development Fund ERDF, Flanders Innovation & Entrepreneurship and the Province of Limburg (project 936). Greet Cuyvers and Gilles Bonneux (UHasselt) are acknowledged for the ICP-AES sample preparation and measurements. Vera Meynen and Karen Leyssens (Antwerp University, Belgium) are acknowledged for the BET measurements. Special thanks to Bart Ruttens (UHasselt) for XRD measurements and discussions on the refinements. |
Approved |
Most recent IF: 3.108 |
Call Number ![sorted by Call Number field, descending order (down)](img/sort_desc.gif) |
EMAT @ emat @c:irua:149513 |
Serial |
4905 |
Permanent link to this record |
|
|
|
Author |
Niu, H.; Pitcher, M.J.; Corkett, A.J.; Ling, S.; Mandal, P.; Zanella, M.; Dawson, K.; Stamenov, P.; Batuk, D.; Abakumov, A.M.; Bull, C.L.; Smith, R.I.; Murray, C.A.; Day, S.J.; Slater, B.; Cora, F.; Claridge, J.B.; Rosseinsky, M.J. |
Title |
Room Temperature Magnetically Ordered Polar Corundum GaFeO3 Displaying Magnetoelectric Coupling |
Type |
A1 Journal article |
Year |
2017 |
Publication |
Journal of the American Chemical Society |
Abbreviated Journal |
J Am Chem Soc |
Volume |
139 |
Issue |
4 |
Pages |
1520-1531 |
Keywords |
A1 Journal article; Electron microscopy for materials research (EMAT) |
Abstract |
The polar corundum structure type offers a route to new room temperature multiferroic materials, as the partial LiNbO3-type cation ordering that breaks inversion symmetry may be combined with long-range magnetic ordering of high spin d(5) cations above room temperature in the AFeO(3) system. We report the synthesis of a polar corundum GaFeO3 by a high-pressure, high-temperature route and demonstrate that its polarity arises from partial LiNbO3 -type cation ordering by complementary use of neutron, X-ray, and electron diffraction methods. In situ neutron diffraction shows that the polar corundum forms directly from AlFeO3-type GaFeO3 under the synthesis conditions. The A(3+)/Fe3+ cations are shown to be more ordered in polar corundum GaFeO3 than in isostructural ScFeO3. This is explained by DFT calculations which indicate that the extent of ordering is dependent on the configurational entropy available to each system at the very different synthesis temperatures required to form their corundum structures. Polar corundum GaFeO3 exhibits weak ferromagnetism at room temperature that arises from its Fe2O3-like magnetic ordering, which persists to a temperature of 408 K. We demonstrate that the polarity and magnetization are coupled in this system with a measured linear magnetoelectric coupling coefficient of 0.057 ps/m. Such coupling is a prerequisite for potential applications of polar corundum materials in multiferroic/magnetoelectric devices. |
Address |
|
Corporate Author |
|
Thesis |
|
Publisher |
|
Place of Publication |
|
Editor |
|
Language |
|
Wos |
000393355600034 |
Publication Date |
2016-12-25 |
Series Editor |
|
Series Title |
|
Abbreviated Series Title |
|
Series Volume |
|
Series Issue |
|
Edition |
|
ISSN |
0002-7863 |
ISBN |
|
Additional Links |
UA library record; WoS full record; WoS citing articles |
Impact Factor |
13.858 |
Times cited |
12 |
Open Access |
OpenAccess |
Notes |
This work was funded by the EPSRC under EP/N004884. We thank the STFC for provision of beam time at ISIS and Diamond Light Source. We thank the Materials Chemistry Consortium (EPSRC, EP/L000202) for access to computer time on the ARCHER UK National Supercomputing Service (http://www.archer.ac.uk). A.M.A. is grateful to the Russian Science Foundation (Grant 14-13-00680) for financial support. MJ.R is a Royal Society Research Professor. We wish to thank Dr. Ming Li (University of Nottingham, UK) for helpful discussion and advice. Original data is available at the University of Liverpool's DataCat repository at DOI: 10.17638/datacat.liverpool.ac.uk/235. The supporting crystallographic information file may also be obtained from FIZ Karlsruhe, 76344 Eggenstein-Leopoldshafen, Germany (e-mail: crysdata@fiz-karlsruhe.de), on quoting the deposition number CSD-432419. |
Approved |
Most recent IF: 13.858 |
Call Number ![sorted by Call Number field, descending order (down)](img/sort_desc.gif) |
EMAT @ emat @c:irua:147507 |
Serial |
4777 |
Permanent link to this record |
|
|
|
Author |
Vishwakarma, M.; Karakulina, O.M.; Abakumov, A.M.; Hadermann, J.; Mehta, B.R. |
Title |
Nanoscale Characterization of Growth of Secondary Phases in Off-Stoichiometric CZTS Thin Films |
Type |
A1 Journal article |
Year |
2018 |
Publication |
Journal of nanoscience and nanotechnology |
Abbreviated Journal |
J Nanosci Nanotechno |
Volume |
18 |
Issue |
3 |
Pages |
1688-1695 |
Keywords |
A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT) |
Abstract |
The presence of secondary phases is one of the main issues that hinder the growth of pure kesterite Cu2ZnSnS4 (CZTS) based thin films with suitable electronic and junction properties for efficient solar cell devices. In this work, CZTS thin films with varied Zn and Sn content have been prepared by RF-power controlled co-sputtering deposition using Cu, ZnS and SnS targets and a subsequent sulphurization step. Detailed TEM investigations show that the film shows a layered structure with the majority of the top layer being the kesterite phase. Depending on the initial thin film composition, either about ~1 μm Cu-rich and Zn-poor kesterite or stoichiometric CZTS is formed as top layer. X-ray diffraction, Raman spectroscopy and transmission electron microscopy reveal the presence of Cu2−x S, ZnS and SnO2 minor secondary phases in the form of nanoinclusions or nanoparticles or intermediate layers. |
Address |
|
Corporate Author |
|
Thesis |
|
Publisher |
|
Place of Publication |
|
Editor |
|
Language |
|
Wos |
000426033400022 |
Publication Date |
2018-03-01 |
Series Editor |
|
Series Title |
|
Abbreviated Series Title |
|
Series Volume |
|
Series Issue |
|
Edition |
|
ISSN |
1533-4880 |
ISBN |
|
Additional Links |
UA library record; WoS full record; WoS citing articles |
Impact Factor |
1.483 |
Times cited |
|
Open Access |
Not_Open_Access |
Notes |
Manoj Vishwakarma acknowl- edges IIT Delhi for MHRD fellowship. Professor B. R. Mehta acknowledges the support of the Schlumberger chair professorship. Manoj Vishwakarma, Joke Hadermann and Olesia M. karakulina acknowledge support provided by InsoL-DST. Manoj Vishwakarma acknowledges sup- port provided by CSIR funded projects and the support of DST-FIST Raman facility. References |
Approved |
Most recent IF: 1.483 |
Call Number ![sorted by Call Number field, descending order (down)](img/sort_desc.gif) |
EMAT @ emat @c:irua:147505 |
Serial |
4775 |
Permanent link to this record |
|
|
|
Author |
Pearce, P.E.; Perez, A.J.; Rousse, G.; Saubanère, M.; Batuk, D.; Foix, D.; McCalla, E.; Abakumov, A.M.; Van Tendeloo, G.; Doublet, M.-L.; Tarascon, J.-M. |
Title |
Evidence for anionic redox activity in a tridimensional-ordered Li-rich positive electrode β-Li2IrO3 |
Type |
A1 Journal article |
Year |
2017 |
Publication |
Nature materials |
Abbreviated Journal |
Nat Mater |
Volume |
16 |
Issue |
5 |
Pages |
580-586 |
Keywords |
A1 Journal article; Electron microscopy for materials research (EMAT) |
Abstract |
Lithium-ion battery cathode materials have relied on cationic redox reactions until the recent discovery of anionic redox activity in Li-rich layered compounds which enables capacities as high as 300 mAh g(-1). In the quest for new high-capacity electrodes with anionic redox, a still unanswered question was remaining regarding the importance of the structural dimensionality. The present manuscript provides an answer. We herein report on a beta-Li2IrO3 phase which, in spite of having the Ir arranged in a tridimensional (3D) framework instead of the typical two-dimensional (2D) layers seen in other Li-rich oxides, can reversibly exchange 2.5 e(-) per Ir, the highest value ever reported for any insertion reaction involving d-metals. We show that such a large activity results from joint reversible cationic (Mn+) and anionic (O-2)(n-) redox processes, the latter being visualized via complementary transmission electron microscopy and neutron diffraction experiments, and confirmed by density functional theory calculations. Moreover, beta-Li2IrO3 presents a good cycling behaviour while showing neither cationic migration nor shearing of atomic layers as seen in 2D-layered Li-rich materials. Remarkably, the anionic redox process occurs jointly with the oxidation of Ir4+ at potentials as low as 3.4 V versus Li+/Li-0, as equivalently observed in the layered alpha-Li2IrO3 polymorph. Theoretical calculations elucidate the electrochemical similarities and differences of the 3D versus 2D polymorphs in terms of structural, electronic and mechanical descriptors. Our findings free the structural dimensionality constraint and broaden the possibilities in designing high-energy-density electrodes for the next generation of Li-ion batteries. |
Address |
|
Corporate Author |
|
Thesis |
|
Publisher |
|
Place of Publication |
|
Editor |
|
Language |
|
Wos |
000400004200018 |
Publication Date |
2017-02-27 |
Series Editor |
|
Series Title |
|
Abbreviated Series Title |
|
Series Volume |
|
Series Issue |
|
Edition |
|
ISSN |
1476-1122 |
ISBN |
|
Additional Links |
UA library record; WoS full record; WoS citing articles |
Impact Factor |
39.737 |
Times cited |
|
Open Access |
Not_Open_Access |
Notes |
The authors thank Q. Jacquet for fruitful discussions and V. Pomjakushin for his valuable help in neutron diffraction experiments. This work is based on experiments performed at the Swiss Spallation Neutron Source SINQ, Paul Scherrer Institute, Villigen, Switzerland. Use of the 11-BM mail service of the APS at Argonne National Laboratory was supported by the US Department of Energy under contract No. DE-AC02-06CH11357 and is greatly acknowledged. J.-M.T. acknowledges funding from the European Research Council (ERC) (FP/2014)/ERC Grant-Project 670116-ARPEMA. E.M. acknowledges financial support from the Fonds de Recherche du Quebec-Nature et Technologies. |
Approved |
Most recent IF: 39.737 |
Call Number ![sorted by Call Number field, descending order (down)](img/sort_desc.gif) |
EMAT @ emat @c:irua:147502 |
Serial |
4773 |
Permanent link to this record |
|
|
|
Author |
Morozov, V.A.; Batuk, D.; Batuk, M.; Basovich, O.M.; Khaikina, E.G.; Deyneko, D.V.; Lazoryak, B.I.; Leonidov, I.I.; Abakumov, A.M.; Hadermann, J. |
Title |
Luminescence Property Upgrading via the Structure and Cation Changing in AgxEu(2–x)/3WO4and AgxGd(2–x)/3–0.3Eu0.3WO4 |
Type |
A1 Journal article |
Year |
2017 |
Publication |
Chemistry of materials |
Abbreviated Journal |
Chem Mater |
Volume |
29 |
Issue |
20 |
Pages |
8811-8823 |
Keywords |
A1 Journal article; Electron microscopy for materials research (EMAT) |
Abstract |
The creation and ordering of A-cation vacancies and the effect of cation substitutions in the scheelite-type framework are investigated as a factor for controlling the scheelite-type structure and luminescence properties. AgxEu3+(2−x)/3□(1−2x)/3WO4 and AgxGd(2−x)/3−0.3Eu3+0.3□(1−2x)/3WO4 (x = 0.5−0) scheelite-type phases were synthesized by a solid state method, and their structures were investigated using a combination of transmission electron microscopy techniques and powder synchrotron X-ray diffraction. Transmission electron microscopy also revealed the (3 + 1)D incommensurately modulated character of AgxEu3+(2−x)/3□(1−2x)/3WO4 (x = 0.286, 0.2) phases. The crystal structures of the scheelite-based AgxEu3+(2−x)/3□(1−2x)/3WO4 (x = 0.5, 0.286, 0.2) red phosphors have been refined from high resolution synchrotron powder X-ray diffraction data. The luminescence properties of all phases under near-ultraviolet (n-UV) light have been investigated. The excitation spectra of AgxEu3+(2−x)/3□(1−2x)/3WO4 (x = 0.5, 0.286,0.2) phosphors show the strongest absorption at 395 nm, which matches well with the commercially available n-UV-emitting GaN-based LED chip. The excitation spectra of the Eu2/3□1/3WO4 and Gd0.367Eu0.30□1/3WO4 phases exhibit the highest contribution of the charge transfer band at 250 nm and thus the most efficient energy transfer mechanism between the host and the luminescent ion as compared to direct excitation. The emission spectra of all samples indicate an intense red emission due to the 5D0 → 7F2 transition of Eu3+. Concentration dependence of the 5D0 → 7F2 emission for AgxEu(2−x)/3□(1−2x)/3WO4 samples differs from the same dependence for the earlier studied NaxEu3+(2−x)/3□(1−2x)/3MoO4 (0 ≤ x ≤ 0.5) phases. The intensity of the 5D0 → 7F2 emission is reduced almost 7 times with decreasing x from 0.5 to 0, but it practically does not change in the range from x = 0.286 to x = 0.200. The emission spectra of Gd-containing samples show a completely different trend as compared to only Eu-containing samples. The Eu3+ emission under excitation of Eu3+(5L6) level (λex = 395 nm) increases more than 2.5 times with the increasing Gd3+ concentration from 0.2 (x = 0.5) to 0.3 (x = 0.2) in the AgxGd(2−x)/3−0.3Eu3+0.3□(1−2x)/3WO4, after which it remains almost constant for higher Gd3+ concentrations. |
Address |
|
Corporate Author |
|
Thesis |
|
Publisher |
|
Place of Publication |
|
Editor |
|
Language |
|
Wos |
000413884900028 |
Publication Date |
2017-10-24 |
Series Editor |
|
Series Title |
|
Abbreviated Series Title |
|
Series Volume |
|
Series Issue |
|
Edition |
|
ISSN |
0897-4756 |
ISBN |
|
Additional Links |
UA library record; WoS full record; WoS citing articles |
Impact Factor |
9.466 |
Times cited |
7 |
Open Access |
Not_Open_Access |
Notes |
This research was supported by FWO (project G039211N), Flanders Research Foundation. V.A.M. is grateful for financial support of the Russian Foundation for Basic Research (Grant 15-03-07741). E.G.K. and O.M.B. are grateful for financial support of the Russian Foundation for Basic Research (Grants 13-03-01020 and 16-03-00510). D.V.D. is grateful for financial support of the Russian Foundation for Basic Research (Grant 16-33-00197) and the Foundation of the President of the Russian Federation (Grant MK-7926.2016.5.). We are grateful to the ESRF for granting the beamtime. Experimental support of Andy Fitch at the ID31 beamline of ESRF is kindly acknowledged. |
Approved |
Most recent IF: 9.466 |
Call Number ![sorted by Call Number field, descending order (down)](img/sort_desc.gif) |
EMAT @ emat @c:irua:147241 |
Serial |
4768 |
Permanent link to this record |
|
|
|
Author |
Charkin, D.O.; Plokhikh, I.V.; Kazakov, S.M.; Kalmykov, S.N.; Akinfiev, V.S.; Gorbachev, A.V.; Batuk, M.; Abakumov, A.M.; Teterin, Y.A.; Maslakov, K.I.; Teterin, A.Y.; Ivanov, K.E. |
Title |
Synthesis and structural characterization of a novel Sillén – Aurivillius bismuth oxyhalide, PbBi3VO7.5Cl, and its derivatives |
Type |
A1 Journal article |
Year |
2018 |
Publication |
Solid state sciences |
Abbreviated Journal |
Solid State Sci |
Volume |
75 |
Issue |
|
Pages |
27-33 |
Keywords |
A1 Journal article; Electron microscopy for materials research (EMAT) |
Abstract |
A new Sillen – Aurivillius family of layered bismuth oxyhalides has been designed and successfully constructed on the basis of PbBiO2X(X = halogen) synthetic perites and g-form of Bi2VO5.5 solid elec- trolyte. This demonstrates, for the first time, the ability of the latter to serve as a building block in construction of mixed-layer structures. The parent compound PbBi3VO7.5-dCl (d = 0.05) has been investigated by powder XRD, TEM, XPS methods and magnetic susceptibility measurements. An unexpected but important condition for the formation of the mixed-layer structure is partial (ca. 5%) reduction of VV into VIV which probably suppresses competitive formation of apatite-like Pb – Bi vanadates. This reduction also stabilizes the g polymorphic form of Bi2VO5.5 not only in the intergrowth structure, but in Bi2V1-xMxO5.5-y (M – Nb, Sb) solid solutions. |
Address |
|
Corporate Author |
|
Thesis |
|
Publisher |
|
Place of Publication |
|
Editor |
|
Language |
|
Wos |
000418566200005 |
Publication Date |
2017-11-21 |
Series Editor |
|
Series Title |
|
Abbreviated Series Title |
|
Series Volume |
|
Series Issue |
|
Edition |
|
ISSN |
1293-2558 |
ISBN |
|
Additional Links |
UA library record; WoS full record; WoS citing articles |
Impact Factor |
1.811 |
Times cited |
1 |
Open Access |
Not_Open_Access |
Notes |
The work was partially supported by M.V. Lomonosov Moscow State University Program of Development and Russian Science Foundation under Grant No.14-13-00738. We also thank Dr. K.V. Zakharov (MSU) for the magnetic measurements of the PbBi3- VO7.5Cl sample. |
Approved |
Most recent IF: 1.811 |
Call Number ![sorted by Call Number field, descending order (down)](img/sort_desc.gif) |
EMAT @ emat @c:irua:147239 |
Serial |
4769 |
Permanent link to this record |
|
|
|
Author |
Tsirlin, A.A.; Rousochatzakis, I.; Filimonov, D.; Batuk, D.; Frontzek, M.; Abakumov, A.M. |
Title |
Spin-reorientation transitions in the Cairo pentagonal magnet Bi4Fe5O13F |
Type |
A1 Journal article |
Year |
2017 |
Publication |
Physical review B |
Abbreviated Journal |
Phys Rev B |
Volume |
96 |
Issue |
9 |
Pages |
094420 |
Keywords |
A1 Journal article; Electron microscopy for materials research (EMAT) |
Abstract |
We show that interlayer spins play a dual role in the Cairo pentagonal magnet Bi4Fe5O13F, on one hand mediating the three-dimensional magnetic order, and on the other driving spin-reorientation transitions both within and between the planes. The corresponding sequence of magnetic orders unraveled by neutron diffraction and Mossbauer spectroscopy features two orthogonal magnetic structures described by opposite local vector chiralities, and an intermediate, partly disordered phase with nearly collinear spins. A similar collinear phase has been predicted theoretically to be stabilized by quantum fluctuations, but Bi4Fe5O13F is very far from the relevant parameter regime. While the observed in-plane reorientation cannot be explained by any standard frustration mechanism, our ab initio band-structure calculations reveal strong single-ion anisotropy of the interlayer Fe3+ spins that turns out to be instrumental in controlling the local vector chirality and the associated interlayer order. |
Address |
|
Corporate Author |
|
Thesis |
|
Publisher |
|
Place of Publication |
|
Editor |
|
Language |
|
Wos |
000411161700002 |
Publication Date |
2017-09-19 |
Series Editor |
|
Series Title |
|
Abbreviated Series Title |
|
Series Volume |
|
Series Issue |
|
Edition |
|
ISSN |
2469-9950 |
ISBN |
|
Additional Links |
UA library record; WoS full record; WoS citing articles |
Impact Factor |
3.836 |
Times cited |
7 |
Open Access |
OpenAccess |
Notes |
We are grateful to J.-M. Perez-Mato and Dmitry Khalyavin for valuable discussions on the magnetic structures and symmetries. D.F. and A.A. are grateful to the Russian Science Foundation (Grant No. 14-13-00680) for support. A.T. was supported by the Federal Ministry for Education and Research through the Sofja Kovalevskaya Award of the Alexander von Humboldt Foundation. This work is based on experiments performed at the Swiss spallation neutron source SINQ, Paul Scherrer Institut, Villigen, Switzerland. |
Approved |
Most recent IF: 3.836 |
Call Number ![sorted by Call Number field, descending order (down)](img/sort_desc.gif) |
EMAT @ emat @c:irua:146748 |
Serial |
4774 |
Permanent link to this record |
|
|
|
Author |
Rumyantseva, M.N.; Vladimirova, S.A.; Vorobyeva, N.A.; Giebelhaus, I.; Mathur, S.; Chizhov, A.S.; Khmelevsky, N.O.; Aksenenko, A.Y.; Kozlovsky, V.F.; Karakulina, O.M.; Hadermann, J.; Abakumov, A.M.; Gaskov, A.M. |
Title |
p -CoO x / n -SnO 2 nanostructures: New highly selective materials for H 2 S detection |
Type |
A1 Journal article |
Year |
2017 |
Publication |
Sensors and actuators : B : chemical |
Abbreviated Journal |
Sensor Actuat B-Chem |
Volume |
|
Issue |
|
Pages |
|
Keywords |
A1 Journal article; Electron microscopy for materials research (EMAT) |
Abstract |
Nanostructures p-CoOx/n-SnO2 based on tin oxide nanowires have been prepared by two step CVD technique and characterized in detail by XRD, XRF, XPS, HAADF-STEM imaging and EDX-STEM mapping. Depending on the temperature of decomposition of cobalt complex during the second step of CVD synthesis of nanostructures cobalt oxide forms a coating and/or isolated nanoparticles on SnO2 nanowire surface. It was found that cobalt presents in +2 and +3 oxidation states. The measurements of gas sensor properties have been carried out during exposure to CO (14 ppm), NH3 (21 ppm), and H2S (2 ppm) in dry air. The opposite trends were observed in the effect of cobalt oxide on the SnO2 gas sensitivity when detecting CO or NH3 in comparison to H2S. The decrease of sensor signal toward CO and NH3 was attributed to high catalytic activity of Co3O4 in oxidation of these gases. Contrary, the significant increase of sensor signal in the presence of H2S was attributed to the formation of metallic cobalt sulfide and removal of the barrier between p-CoOx and n-SnO2. This effect provides an excellent selectivity of p-CoOx/n-SnO2 nanostructures in H2S detection. |
Address |
|
Corporate Author |
|
Thesis |
|
Publisher |
|
Place of Publication |
|
Editor |
|
Language |
|
Wos |
000414151800068 |
Publication Date |
2017-08-17 |
Series Editor |
|
Series Title |
|
Abbreviated Series Title |
|
Series Volume |
|
Series Issue |
|
Edition |
|
ISSN |
0925-4005 |
ISBN |
|
Additional Links |
UA library record; WoS full record; WoS citing articles |
Impact Factor |
5.401 |
Times cited |
13 |
Open Access |
Not_Open_Access: Available from 10.10.2019
|
Notes |
ERA-Net.Plus, 096 FONSENS ; |
Approved |
Most recent IF: 5.401 |
Call Number ![sorted by Call Number field, descending order (down)](img/sort_desc.gif) |
EMAT @ emat @c:irua:145926 |
Serial |
4710 |
Permanent link to this record |
|
|
|
Author |
Batuk, D.; Batuk, M.; Morozov, V.A.; Meert, K.W.; Smet, P.F.; Poelman, D.; Abakumov, A.M.; Hadermann, J. |
Title |
Effect of cation vacancies on the crystal structure and luminescent properties of Ca(0.85-1.5x)Gd(x)Eu(0.1)_(0.05+0.5x)WO(4) (0<x<0.567) scheelite-based red phosphors |
Type |
A1 Journal article |
Year |
2017 |
Publication |
Journal of alloys and compounds |
Abbreviated Journal |
J Alloy Compd |
Volume |
706 |
Issue |
706 |
Pages |
358-369 |
Keywords |
A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT) |
Abstract |
The Ca0.85-1.5xGdxEu0.1_0.05-0.5xWO4 (0 < x < 0.567) series of cation-deficient scheelites is investigated to unveil the influence of the cation vacancies on the crystal structure and luminescent properties. The concentration of the vacancies is varied by the heterovalent substitution of Gd3+ for Ca2+, keeping the concentration of the Eu3+ luminescent centers constant in all compounds of the series. The crystal structure of the materials is studied using a combination of transmission electron microscopy and synchrotron X-ray powder diffraction. At low vacancy concentration (x = 0.1, 0.2), cations and cation vacancies are randomly distributed in the structure, and the materials preserve the I41/a symmetry of the parent scheelite structure [x = 0.1: a = 5.25151(1) Å, c = 11.39479(2) Å; x = 0.2: a = 5.25042(1) Å, c = 11.41335(2) Å]. At higher concentration, the cation-vacancy ordering gives rise to incommensurately modulated structures. The x = 0.3 structure has a (3 + 2)D tetragonal symmetry [superspace group I41/a(a,b,0)00(-b,a,0)00, a = 5.24700(1) Å, c = 11.45514(3) Å, q1 = 0.51637(14)a* + 0.80761(13)b*, q2 = -0.80761a* + 0.51637b*]. At x = 0.4, the scheelite basic cell undergoes a monoclinic distortion with the formation of the (3 + 1)D structure [superspace group I2/b(a,b,0)00, a = 5.23757(1) Å, b = 5.25035(1) Å, c = 11.45750(2) Å, g = 90.5120(2) o, q = 0.54206(8)a* + 0.79330(8)b*]. In both structures, the antiphase Ca and (Gd,Eu) occupancy modulations indicate that the ordering between the A cations and vacancies also induces partial Ca/(Gd,Eu) cation ordering. Further increase of the Gd3þ content up to x = 0.567 leads to the formation of a monoclinic phase (space group C2/c) with the Eu2/3WO4-type structure. Despite the difference in the cation-vacancy ordering patterns, all materials in the series demonstrate very similar quantum efficiency and luminescence decay lifetimes. However, the difference in the local coordination environment of the A cation species noticeably affects the line width and the multiplet splitting of the 4f6-4f6 transitions. |
Address |
|
Corporate Author |
|
Thesis |
|
Publisher |
|
Place of Publication |
|
Editor |
|
Language |
|
Wos |
000397997300045 |
Publication Date |
2017-02-16 |
Series Editor |
|
Series Title |
|
Abbreviated Series Title |
|
Series Volume |
|
Series Issue |
|
Edition |
|
ISSN |
0925-8388 |
ISBN |
|
Additional Links |
UA library record; WoS full record; WoS citing articles |
Impact Factor |
3.133 |
Times cited |
2 |
Open Access |
OpenAccess |
Notes |
This research was supported by FWO (Flanders Research Foundation, project G039211N). V.A.M. is grateful for financial support of the Russian Foundation for Basic Research (Grant 15-03-07741).We are grateful to the ESRF for granting the beamtime at the ID22 beamline and to Andy Fitch for the support during the experiment. |
Approved |
Most recent IF: 3.133 |
Call Number ![sorted by Call Number field, descending order (down)](img/sort_desc.gif) |
EMAT @ emat @ c:irua:142367 |
Serial |
4581 |
Permanent link to this record |
|
|
|
Author |
Mikhailova, D.; Karakulina, O.M.; Batuk, D.; Hadermann, J.; Abakumov, A.M.; Herklotz, M.; Tsirlin, A.A.; Oswald, S.; Giebeler, L.; Schmidt, M.; Eckert, J.; Knapp, M.; Ehrenberg, H. |
Title |
Layered-to-Tunnel Structure Transformation and Oxygen Redox Chemistry in LiRhO2upon Li Extraction and Insertion |
Type |
A1 Journal article |
Year |
2016 |
Publication |
Inorganic chemistry |
Abbreviated Journal |
Inorg Chem |
Volume |
55 |
Issue |
55 |
Pages |
7079-7089 |
Keywords |
A1 Journal article; Electron microscopy for materials research (EMAT) |
Abstract |
Layered Li(M,Li)O2 (where M is a transition metal) ordered rock-salt-type structures are used in advanced metal-ion batteries as one of the best hosts for the reversible intercalation of Li ions. Besides the conventional redox reaction involving oxidation/reduction of the M cation upon Li extraction/insertion, creating oxygen-located holes because of the partial oxygen oxidation increases capacity while maintaining the oxidized oxygen species in the lattice through high covalency of the M–O bonding. Typical degradation mechanism of the Li(M,Li)O2 electrodes involves partially irreversible M cation migration toward the Li positions, resulting in gradual capacity/voltage fade. Here, using LiRhO2 as a model system (isostructural and isoelectronic to LiCoO2), for the first time, we demonstrate an intimate coupling between the oxygen redox and M cation migration. A formation of the oxidized oxygen species upon electrochemical Li extraction coincides with transformation of the layered Li1–xRhO2 structure into the γ-MnO2-type rutile–ramsdellite intergrowth LiyRh3O6 structure with rutile-like [1 × 1] channels along with bigger ramsdellite-like [2 × 1] tunnels through massive and concerted Rh migration toward the empty positions in the Li layers. The oxidized oxygen dimers with the O–O distances as short as 2.26 Å are stabilized in this structure via the local Rh–O configuration reminiscent to that in the μ-peroxo-μ-hydroxo Rh complexes. The LiyRh3O6 structure is remarkably stable upon electrochemical cycling illustrating that proper structural implementation of the oxidized oxygen species can open a pathway toward deliberate employment of the anion redox chemistry in high-capacity/high-voltage positive electrodes for metal-ion batteries. Upon chemical or electrochemical oxidation, layered LiRhO2 shows a unique structural transformation that involves both cation migration and oxidation of oxygen resulting in a stable tunnel-like rutile−ramsdellite intergrowth LiyRh3O6 structure. This structure demonstrates excellent performance with the steady and reversible capacity of ∼200 mAh/g. The stability of LiyRh3O6 is rooted in the accommodation of partially oxidized oxygen species through the formation of short O−O distances that are compatible with the connectivity of RhO6 octahedra. |
Address |
|
Corporate Author |
|
Thesis |
|
Publisher |
|
Place of Publication |
|
Editor |
|
Language |
|
Wos |
000380181400035 |
Publication Date |
2016-07-18 |
Series Editor |
|
Series Title |
|
Abbreviated Series Title |
|
Series Volume |
|
Series Issue |
|
Edition |
|
ISSN |
0020-1669 |
ISBN |
|
Additional Links |
UA library record; WoS full record; WoS citing articles |
Impact Factor |
4.857 |
Times cited |
12 |
Open Access |
|
Notes |
Bundesministerium fur Bildung und Forschung, 03SF0477B ; Fonds Wetenschappelijk Onderzoek, G040116N ; |
Approved |
Most recent IF: 4.857 |
Call Number ![sorted by Call Number field, descending order (down)](img/sort_desc.gif) |
EMAT @ emat @ c:irua:140848 |
Serial |
4424 |
Permanent link to this record |
|
|
|
Author |
Karakulina, O.M.; Khasanova, N.R.; Drozhzhin, O.A.; Tsirlin, A.A.; Hadermann, J.; Antipov, E.V.; Abakumov, A.M. |
Title |
Antisite Disorder and Bond Valence Compensation in Li2FePO4F Cathode for Li-Ion Batteries |
Type |
A1 Journal article |
Year |
2016 |
Publication |
Chemistry Of Materials |
Abbreviated Journal |
Chem Mater |
Volume |
28 |
Issue |
28 |
Pages |
7578-7581 |
Keywords |
A1 Journal article; Electron microscopy for materials research (EMAT) |
Abstract |
|
Address |
|
Corporate Author |
|
Thesis |
|
Publisher |
|
Place of Publication |
|
Editor |
|
Language |
|
Wos |
000387518500004 |
Publication Date |
2016-11-08 |
Series Editor |
|
Series Title |
|
Abbreviated Series Title |
|
Series Volume |
|
Series Issue |
|
Edition |
|
ISSN |
0897-4756 |
ISBN |
|
Additional Links |
UA library record; WoS full record; WoS citing articles |
Impact Factor |
9.466 |
Times cited |
10 |
Open Access |
|
Notes |
Russian Science Foundation, 16-19-00190 ; Fonds Wetenschappelijk Onderzoek, G040116N ; |
Approved |
Most recent IF: 9.466 |
Call Number ![sorted by Call Number field, descending order (down)](img/sort_desc.gif) |
EMAT @ emat @ c:irua:139170 c:irua:138599 |
Serial |
4320 |
Permanent link to this record |
|
|
|
Author |
Chizhov, A.S.; Rumyantseva, M.N.; Vasiliev, R.B.; Filatova, D.G.; Drozdov, K.A.; Krylov, I.V.; Marchevsky, A.V.; Karakulina, O.M.; Abakumov, A.M.; Gaskov, A.M. |
Title |
Visible light activation of room temperature NO2 gas sensors based on ZnO, SnO2 and In2O3 sensitized with CdSe quantum dots |
Type |
A1 Journal article |
Year |
2016 |
Publication |
Thin solid films : an international journal on the science and technology of thin and thick films |
Abbreviated Journal |
Thin Solid Films |
Volume |
618 |
Issue |
618 |
Pages |
253-262 |
Keywords |
A1 Journal article; Electron microscopy for materials research (EMAT) |
Abstract |
This work reports the analysis of visible light activation of room temperature NO2 gas sensitivity of metal oxide semiconductors (MOS): blank and CdSe quantum dots (QDs) sensitized nanocrystallinematrixes ZnO, SnO2 and In2O3. Nanocrystalline metal oxides (MOx) ZnO, SnO2, In2O3 were synthesized by the precipitation method. Colloidal CdSe QDs were obtained by high temperature colloidal synthesis. Sensitization was effectuated by direct adsorption of CdSe QDs stabilized with oleic acid on MOx surface. The role of illumination consists in generation of electrons, which can be transferred into MOx conduction band, and holes that can recombine with the electrons previously trapped by the chemisorbed acceptor species and thus activate desorption of analyte molecules. Under green light illumination for blank SnO2 and In2O3 matrixes the indirect consequential mechanism for the generation of holes is proposed. Anothermechanismis realized in the presence of CdSe QDs. In this case the electron-hole pair is generated in the CdSe quantum dot. Sensor measurements demonstrated that synthesizedmaterials can be used for NO2 detection under visible (green) light illumination at room temperature without any thermal heating. |
Address |
|
Corporate Author |
|
Thesis |
|
Publisher |
|
Place of Publication |
|
Editor |
|
Language |
|
Wos |
000389164400005 |
Publication Date |
2016-09-18 |
Series Editor |
|
Series Title |
|
Abbreviated Series Title |
|
Series Volume |
|
Series Issue |
|
Edition |
|
ISSN |
0040-6090 |
ISBN |
|
Additional Links |
UA library record; WoS full record; WoS citing articles |
Impact Factor |
1.879 |
Times cited |
19 |
Open Access |
|
Notes |
The work was financially supported by Russian Foundation for Basic Research grant no. 15-03-03026. |
Approved |
Most recent IF: 1.879 |
Call Number ![sorted by Call Number field, descending order (down)](img/sort_desc.gif) |
EMAT @ emat @ c:irua:138598 |
Serial |
4321 |
Permanent link to this record |
|
|
|
Author |
Kolchina, L. M.; Lyskov, N.V.; Kuznetsov, A.N.; Kazakov, S.M.; Galin, M.Z.; Meledin, A.; Abakumov, A.M.; Bredikhin, S.I.; Mazo, G.N.; Antipov, E.V. |
Title |
Evaluation of Ce-doped Pr2CuO4for potential application as a cathode material for solid oxide fuel cells |
Type |
A1 Journal article |
Year |
2016 |
Publication |
RSC advances |
Abbreviated Journal |
Rsc Adv |
Volume |
6 |
Issue |
6 |
Pages |
101029-101037 |
Keywords |
A1 Journal article; Electron microscopy for materials research (EMAT) |
Abstract |
Pr2−xCexCuO4 (x = 0.05; 0.1; 0.15) samples were synthesized and systematically characterized towards application as a cathode material for solid oxide fuel cells (SOFCs). High-temperature electrical conductivity, thermal expansion, and electrocatalytic activity in the oxygen reduction reaction (ORR) were examined. The electrical conductivity of Pr2−xCexCuO4 oxides demonstrates semiconducting behavior up to 900 °C. Small Ce-doping (2.5 at%) allows an increase in electrical conductivity from 100 to 130 S cm−1 in air at 500–800 °C. DFT calculations revealed that the density of states directly below the Fermi level, comprised mainly of Cu 3d and O 2p states, is significantly affected by atoms in rare earth positions, which might give an indication of a correlation between calculated electronic structures and measured conducting properties. Ce-doping in Pr2−xCexCuO4 slightly increases TEC from 11.9 × 10−6 K−1 for x = 0 to 14.2 × 10−6 K−1 for x = 0.15. Substitution of 2.5% of Pr atoms in Pr2CuO4 by Ce is effective to enhance the electrochemical performance of the material as a SOFC cathode in the ORR (ASR of Pr1.95Ce0.05CuO4 electrode applied on Ce0.9Gd0.1O1.95 electrolyte is 0.39 Ω cm2 at 750 °C in air). The peak power density achieved for the electrolyte-supported fuel cell with the Pr1.95Ce0.05CuO4 cathode is 150 mW cm−2 at 800 °C |
Address |
|
Corporate Author |
|
Thesis |
|
Publisher |
|
Place of Publication |
|
Editor |
|
Language |
|
Wos |
000387427700044 |
Publication Date |
2016-10-19 |
Series Editor |
|
Series Title |
|
Abbreviated Series Title |
|
Series Volume |
|
Series Issue |
|
Edition |
|
ISSN |
2046-2069 |
ISBN |
|
Additional Links |
UA library record; WoS full record; WoS citing articles |
Impact Factor |
3.108 |
Times cited |
7 |
Open Access |
|
Notes |
his work was partially supported by Russian Foundation for Basic Research (grant no. 153820247), Skolkovo Institute of Science and Technology (Center of electrochemical energy), and MSUdevelopment Program up to 2020. K.L.M. is grateful to Haldor Topsøe A/S for the financial support. |
Approved |
Most recent IF: 3.108 |
Call Number ![sorted by Call Number field, descending order (down)](img/sort_desc.gif) |
EMAT @ emat @ c:irua:136441 |
Serial |
4296 |
Permanent link to this record |
|
|
|
Author |
Perez, A.J.; Batuk, D.; Saubanère, M.; Rousse, G.; Foix, D.; Mc Calla, E.; J. Berg, E.; Dugas, R.; van den Bos, K. H. W.; Doublet, M.-L.; Gonbeau, D.; Abakumov, A.M.; Van Tendeloo, G.; Tarascon, J.-M. |
Title |
Strong oxygen participation in the redox governing the structural and electrochemical properties of Na-rich layered oxide Na2IrO3 |
Type |
A1 Journal article |
Year |
2016 |
Publication |
Chemistry of materials |
Abbreviated Journal |
Chem Mater |
Volume |
28 |
Issue |
28 |
Pages |
8278-8288 |
Keywords |
A1 Journal article; Electron microscopy for materials research (EMAT) |
Abstract |
The recent revival of the Na-ion battery concept has prompted intense activities in the search for new Na-based layered oxide positive electrodes. The largest capacity to date was obtained for a Na-deficient layered oxide that relies on cationic redox processes only. To go beyond this limit, we decided to chemically manipulate these Na-based layered compounds in a way to trigger the participation of the anionic network. We herein report the electrochemical properties of a Na-rich phase Na2IrO3, which can reversibly cycle 1.5 Na+ per formula unit while not suffering from oxygen release nor cationic migrations. Such large capacities, as deduced by complementary XPS, X-ray/neutron diffraction and transmission electron microscopy measurements, arise from cumulative cationic and anionic redox processes occurring simultaneously at potentials as low as 3.0 V. The inability to remove more than 1.5 Na+ is rooted in the formation of an O1-type phase having highly stabilized Na sites as confirmed by DFT calculations, which could rationalize as well the competing metal/oxygen redox processes in Na2IrO3. This work will help to define the most fertile directions in the search for novel high energy Na-rich materials based on more sustainable elements than Ir. |
Address |
|
Corporate Author |
|
Thesis |
|
Publisher |
|
Place of Publication |
|
Editor |
|
Language |
|
Wos |
000388914500021 |
Publication Date |
2016-10-17 |
Series Editor |
|
Series Title |
|
Abbreviated Series Title |
|
Series Volume |
|
Series Issue |
|
Edition |
|
ISSN |
0897-4756 |
ISBN |
|
Additional Links |
UA library record; WoS full record; WoS citing articles |
Impact Factor |
9.466 |
Times cited |
45 |
Open Access |
|
Notes |
The authors thank Montse Casas-Cabanas and Marine Reynaud for discussions about the FAULTS program, Sandra Van Aert for her great help in guiding us towards the use of the statistical parameter estimation method for establishing the O-O histogram, and Thomas Hansen and Vladimir Pomjakushin for their precious help in neutron diffraction experiments. This work is based on experiments performed at the Swiss spallation neutron source SINQ, Paul Scherrer Institute, Villigen, Switzerland, and at Institut Laue Langevin, Grenoble, France. Use of the 11-BM mail service of the APS at Argonne National Laboratory was supported by the U.S. department of Energy under contract No. DE-AC02-06CH11357 and is greatly acknowledged. |
Approved |
Most recent IF: 9.466 |
Call Number ![sorted by Call Number field, descending order (down)](img/sort_desc.gif) |
EMAT @ emat @ c:irua:135994 |
Serial |
4287 |
Permanent link to this record |
|
|
|
Author |
Gonnissen, J.; Batuk, D.; Nataf, G.F.; Jones, L.; Abakumov, A.M.; Van Aert, S.; Schryvers, D.; Salje, E.K.H. |
Title |
Direct Observation of Ferroelectric Domain Walls in LiNbO3: Wall-Meanders, Kinks, and Local Electric Charges |
Type |
A1 Journal article |
Year |
2016 |
Publication |
Advanced functional materials |
Abbreviated Journal |
Adv Funct Mater |
Volume |
26 |
Issue |
26 |
Pages |
7599-7604 |
Keywords |
A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT) |
Abstract |
Direct observations of the ferroelectric domain boundaries in LiNbO3 are performed using high-resolution high-angle annular dark field scanning transmission electron microscopy imaging, revealing a very narrow width of the domain wall between the 180° domains. The domain walls demonstrate local side-way meandering, which results in inclinations even when the overall wall orientation follows the ferroelectric polarization. These local meanders contain kinks with “head-to-head” and “tail-to-tail” dipolar configurations and are therefore locally charged. The charged meanders are confined to a few cation layers along the polarization direction and are separated by longer stretches of straight domain walls. |
Address |
|
Corporate Author |
|
Thesis |
|
Publisher |
|
Place of Publication |
|
Editor |
|
Language |
|
Wos |
000388166700006 |
Publication Date |
2016-09-16 |
Series Editor |
|
Series Title |
|
Abbreviated Series Title |
|
Series Volume |
|
Series Issue |
|
Edition |
|
ISSN |
1616-301X |
ISBN |
|
Additional Links |
UA library record; WoS full record; WoS citing articles |
Impact Factor |
12.124 |
Times cited |
23 |
Open Access |
|
Notes |
J.G. acknowledges the support from the Research Foundation Flanders (FWO, Belgium) through various project fundings (G.0368.15N, G.0369.15N, and G.0374.13N), as well as the financial support from the European Union Seventh Framework Program (FP7/2007–2013) under Grant agreement no. 312483 (ESTEEM2). The authors thank J. Hadermann for useful suggestions on the interpretation of the HAADFSTEM images. E.K.H.S. thanks the EPSRC (EP/K009702/1) and the Leverhulme Trust (EM-2016-004) for support. G.F.N. thanks the National Research Fund, Luxembourg (FNR/P12/4853155/Kreisel) for support.; esteem2_jra2 |
Approved |
Most recent IF: 12.124 |
Call Number ![sorted by Call Number field, descending order (down)](img/sort_desc.gif) |
c:irua:135336 c:irua:135336 |
Serial |
4129 |
Permanent link to this record |
|
|
|
Author |
Altantzis, T.; Coutino-Gonzalez, E.; Baekelant, W.; Martinez, G.T.; Abakumov, A.M.; Van Tendeloo, G.; Roeffaers, M.B.J.; Bals, S.; Hofkens, J. |
Title |
Direct Observation of Luminescent Silver Clusters Confined in Faujasite Zeolites |
Type |
A1 Journal article |
Year |
2016 |
Publication |
ACS nano |
Abbreviated Journal |
Acs Nano |
Volume |
10 |
Issue |
10 |
Pages |
7604-7611 |
Keywords |
A1 Journal article; Electron microscopy for materials research (EMAT) |
Abstract |
One of the ultimate goals in the study of metal clusters is the correlation between the atomic-scale organization and their physicochemical properties. However, direct observation of the atomic organization of such minuscule metal clusters is heavily hindered by radiation damage imposed by the different characterization techniques. We present direct evidence of the structural arrangement, at an atomic level, of luminescent silver species stabilized in faujasite (FAU) zeolites using aberration-corrected scanning transmission electron microscopy. Two different silver clusters were identified in Ag-FAU zeolites, a trinuclear silver species associated with green emission and a tetranuclear silver species related to yellow emission. By combining direct imaging with complementary information obtained from X-ray powder diffraction and Rietveld analysis, we were able to elucidate the main differences at an atomic scale between luminescent (heat-treated) and nonluminescent (cation-exchanged) Ag-FAU zeolites. It is expected that such insights will trigger the directed synthesis of functional metal nanocluster-zeolite composites with tailored luminescent properties. |
Address |
RIES, Hokkaido University , N20W10, Kita-Ward Sapporo 001-0020, Japan |
Corporate Author |
|
Thesis |
|
Publisher |
|
Place of Publication |
|
Editor |
|
Language |
English |
Wos |
000381959100043 |
Publication Date |
2016-07-08 |
Series Editor |
|
Series Title |
|
Abbreviated Series Title |
|
Series Volume |
|
Series Issue |
|
Edition |
|
ISSN |
1936-0851 |
ISBN |
|
Additional Links |
UA library record; WoS full record; WoS citing articles |
Impact Factor |
13.942 |
Times cited |
57 |
Open Access |
OpenAccess |
Notes |
The authors gratefully acknowledge financial support from the Belgian Federal government (Belspo through the IAP-VI/27 and IAP-VII/05 programs), the European Union’s Seventh Framework Programme (FP7/2007-2013 under grant agreement no. 310651 SACS and no. 312483-ESTEEM2), the Flemish government in the form of long-term structural funding “Methusalem” grant METH/15/04 CASAS2, the Hercules foundation (HER/11/14), the “Strategisch Initiatief Materialen” SoPPoM program, and the Fund for Scientific Research Flanders (FWO) grants G.0349.12 and G.0B39.15. S.B. acknowledges funding from ERC Starting Grant COLOURATOMS (335078). The authors thank Prof. S. Van Aert for helpful discussions, Dr. T. De Baerdemaeker for XRD measurements, Mr. B. Dieu for the preparation of graphical material, and UOP Antwerp for the kind donation of zeolite samples.; esteem2jra4; ECASSara; (ROMEO:white; preprint:; postprint:restricted 12 months embargo; pdfversion:cannot); |
Approved |
Most recent IF: 13.942 |
Call Number ![sorted by Call Number field, descending order (down)](img/sort_desc.gif) |
c:irua:134576 c:irua:134576 |
Serial |
4102 |
Permanent link to this record |
|
|
|
Author |
Ovsyannikov, S.V.; Bykov, M.; Bykova, E.; Kozlenko, D.P.; Tsirlin, A.A.; Karkin, A.E.; Shchennikov, V.V.; Kichanov, S.E.; Gou, H.; Abakumov, A.M.; Egoavil, R.; Verbeeck, J.; McCammon, C.; Dyadkin, V.; Chernyshov, D.; van Smaalen, S.; Dubrovinsky, L.S. |
Title |
Charge-ordering transition in iron oxide Fe4O5 involving competing dimer and trimer formation |
Type |
A1 Journal article |
Year |
2016 |
Publication |
Nature chemistry |
Abbreviated Journal |
Nat Chem |
Volume |
8 |
Issue |
8 |
Pages |
501-508 |
Keywords |
A1 Journal article; Electron microscopy for materials research (EMAT) |
Abstract |
Phase transitions that occur in materials, driven, for instance, by changes in temperature or pressure, can dramatically change the materials' properties. Discovering new types of transitions and understanding their mechanisms is important not only from a fundamental perspective, but also for practical applications. Here we investigate a recently discovered Fe4O5 that adopts an orthorhombic CaFe3O5-type crystal structure that features linear chains of Fe ions. On cooling below approximately 150 K, Fe4O5 undergoes an unusual charge-ordering transition that involves competing dimeric and trimeric ordering within the chains of Fe ions. This transition is concurrent with a significant increase in electrical resistivity. Magnetic-susceptibility measurements and neutron diffraction establish the formation of a collinear antiferromagnetic order above room temperature and a spin canting at 85 K that gives rise to spontaneous magnetization. We discuss possible mechanisms of this transition and compare it with the trimeronic charge ordering observed in magnetite below the Verwey transition temperature. |
Address |
Bayerisches Geoinstitut, Universitat Bayreuth, Universitatsstrasse 30, D-95447, Bayreuth, Germany |
Corporate Author |
|
Thesis |
|
Publisher |
|
Place of Publication |
|
Editor |
|
Language |
English |
Wos |
000374534100019 |
Publication Date |
2016-04-04 |
Series Editor |
|
Series Title |
|
Abbreviated Series Title |
|
Series Volume |
|
Series Issue |
|
Edition |
|
ISSN |
1755-4330 |
ISBN |
|
Additional Links |
UA library record; WoS full record; WoS citing articles |
Impact Factor |
25.87 |
Times cited |
51 |
Open Access |
|
Notes |
S.V.O. acknowledges the financial support of the Deutsche Forschungsgemeinschaft (DFG) under project OV-110/1-3. A.E.K. and V.V.S. acknowledge the support of the Russian Foundation for Basic Research (Project 14–02–00622a). H.G. acknowledges the support from the Alexander von Humboldt (AvH) Foundation and the National Natural Science Foundation of China (No. 51201148). A.M.A., R.E. and J.V. acknowledge financial support from the European Commission (EC) under the Seventh Framework Programme (FP7) under a contract for an Integrated Infrastructure Initiative, Reference No. 312483- ESTEEM2. R.E. acknowledges support from the EC under FP7 Grant No. 246102 IFOX. A.M.A. acknowledges funding from the Russian Science Foundation (Grant No. 14-13- 00680). A.A.T. acknowledges funding and from the Federal Ministry for Education and Research through the Sofja Kovalevkaya Award of the AvH Foundation. Funding from the Fund for Scientific Research Flanders under FWO Project G.0044.13N is acknowledged. M.B. and S.v.S. acknowledge support from the DFG under Project Sm55/15-2. We acknowledge the European Synchrotron Radiation Facility for the provision of synchrotron radiation facilities.; esteem2jra2; esteem2jra3 |
Approved |
Most recent IF: 25.87 |
Call Number ![sorted by Call Number field, descending order (down)](img/sort_desc.gif) |
c:irua:133593 c:irua:133593UA @ admin @ c:irua:133593 |
Serial |
4068 |
Permanent link to this record |
|
|
|
Author |
Sathiya, M.; Abakumov, A.M.; Foix, D.; Rousse, G.; Ramesha, K.; Saubanère, M.; Doublet, M. .; Vezin, H.; Laisa, C.P.; Prakash, A.S.; Gonbeau, D.; Van Tendeloo, G.; Tarascon, J.M. |
Title |
Origin of voltage decay in high-capacity layered oxide electrodes |
Type |
A1 Journal article |
Year |
2015 |
Publication |
Nature materials |
Abbreviated Journal |
Nat Mater |
Volume |
14 |
Issue |
14 |
Pages |
230-238 |
Keywords |
A1 Journal article; Electron microscopy for materials research (EMAT) |
Abstract |
Although Li-rich layered oxides (Li1+xNiyCozMn1−x−y−zO2 > 250 mAh g−1) are attractive electrode materials providing energy densities more than 15% higher than todays commercial Li-ion cells, they suffer from voltage decay on cycling. To elucidate the origin of this phenomenon, we employ chemical substitution in structurally related Li2RuO3 compounds. Li-rich layered Li2Ru1−yTiyO3 phases with capacities of ~240 mAh g−1 exhibit the characteristic voltage decay on cycling. A combination of transmission electron microscopy and X-ray photoelectron spectroscopy studies reveals that the migration of cations between metal layers and Li layers is an intrinsic feature of the chargedischarge process that increases the trapping of metal ions in interstitial tetrahedral sites. A correlation between these trapped ions and the voltage decay is established by expanding the study to both Li2Ru1−ySnyO3 and Li2RuO3; the slowest decay occurs for the cations with the largest ionic radii. This effect is robust, and the finding provides insights into new chemistry to be explored for developing high-capacity layered electrodes that evade voltage decay. |
Address |
|
Corporate Author |
|
Thesis |
|
Publisher |
|
Place of Publication |
London |
Editor |
|
Language |
|
Wos |
000348600200024 |
Publication Date |
2014-12-01 |
Series Editor |
|
Series Title |
|
Abbreviated Series Title |
|
Series Volume |
|
Series Issue |
|
Edition |
|
ISSN |
1476-1122;1476-4660; |
ISBN |
|
Additional Links |
UA library record; WoS full record; WoS citing articles |
Impact Factor |
39.737 |
Times cited |
395 |
Open Access |
|
Notes |
246791 Countatoms; 312483 Esteem2; esteem2_ta |
Approved |
Most recent IF: 39.737; 2015 IF: 36.503 |
Call Number ![sorted by Call Number field, descending order (down)](img/sort_desc.gif) |
c:irua:132555 c:irua:132555 |
Serial |
2528 |
Permanent link to this record |
|
|
|
Author |
Paria Sena, R.; Babaryk, A.A.; Khainakov, S.; Garcia-Granda, S.; Slobodyanik, N.S.; Van Tendeloo, G.; Abakumov, A.M.; Hadermann, J. |
Title |
A pseudo-tetragonal tungsten bronze superstructure: a combined solution of the crystal structure of K6.4(Nb,Ta)36.3O94 with advanced transmission electron microscopy and neutron diffraction |
Type |
A1 Journal article |
Year |
2016 |
Publication |
Journal of the Chemical Society : Dalton transactions |
Abbreviated Journal |
Dalton T |
Volume |
45 |
Issue |
45 |
Pages |
973-979 |
Keywords |
A1 Journal article; Electron microscopy for materials research (EMAT) |
Abstract |
The crystal structure of the K6.4Nb28.2Ta8.1O94 pseudo-tetragonal tungsten bronze-type oxide was determined using a combination of X-ray powder diffraction, neutron diffraction and transmission electron microscopy techniques, including electron diffraction, high angle annular dark field scanning transmission electron microscopy (HAADF-STEM), annular bright field STEM (ABF-STEM) and energy-dispersive X-ray compositional mapping (STEM-EDX). The compound crystallizes in the space group Pbam with unit cell parameters a = 37.468(9) A, b = 12.493(3) A, c = 3.95333(15) A. The structure consists of corner sharing (Nb,Ta)O6 octahedra forming trigonal, tetragonal and pentagonal tunnels. All tetragonal tunnels are occupied by K(+) ions, while 1/3 of the pentagonal tunnels are preferentially occupied by Nb(5+)/Ta(5+) and 2/3 are occupied by K(+) in a regular pattern. A fractional substitution of K(+) in the pentagonal tunnels by Nb(5+)/Ta(5+) is suggested by the analysis of the HAADF-STEM images. In contrast to similar structures, such as K2Nb8O21, also parts of the trigonal tunnels are fractionally occupied by K(+) cations. |
Address |
Electron Microscopy for Materials Research (EMAT), University of Antwerp, Groenenborgerlaan 171, B-2020, Antwerp, Belgium. joke.hadermann@uantwerpen.be babaryk@univ.kiev.ua |
Corporate Author |
|
Thesis |
|
Publisher |
|
Place of Publication |
|
Editor |
|
Language |
English |
Wos |
000367614700018 |
Publication Date |
2015-11-23 |
Series Editor |
|
Series Title |
|
Abbreviated Series Title |
|
Series Volume |
|
Series Issue |
|
Edition |
|
ISSN |
1477-9226 |
ISBN |
|
Additional Links |
UA library record; WoS full record; WoS citing articles |
Impact Factor |
4.029 |
Times cited |
6 |
Open Access |
|
Notes |
We thank Dr E. Suard and Dr O. Fabello for assistance in collecting the neutron diffraction data. R.P.S. acknowledges funding from the European Research Council under the 7th Framework Program (FP7), ERC Grant No. 246791-COUNTATOMS. The titan microscope was partly funded by the Hercules fund from the Flemish Government. The authors acknowledge financial support from the European Union under the Seventh Framework Program under a contract for an Integrated Infrastructure Initiative. Reference No. 312483-ESTEEM2. AAB acknowledges the JSPDS ICDD Grant-in-Aid program (12-02).; esteem2jra1; esteem2jra2 |
Approved |
Most recent IF: 4.029 |
Call Number ![sorted by Call Number field, descending order (down)](img/sort_desc.gif) |
c:irua:130408 c:irua:130408 |
Serial |
3998 |
Permanent link to this record |
|
|
|
Author |
Juchtmans, R.; Béché, A.; Abakumov, A.; Batuk, M.; Verbeeck, J. |
Title |
Using electron vortex beams to determine chirality of crystals in transmission electron microscopy |
Type |
A1 Journal article |
Year |
2015 |
Publication |
Physical review : B : condensed matter and materials physics |
Abbreviated Journal |
Phys Rev B |
Volume |
91 |
Issue |
91 |
Pages |
094112 |
Keywords |
A1 Journal article; Electron microscopy for materials research (EMAT) |
Abstract |
We investigate electron vortex beams elastically scattered on chiral crystals. After deriving a general expression for the scattering amplitude of a vortex electron, we study its diffraction on point scatterers arranged on a helix. We derive a relation between the handedness of the helix and the topological charge of the electron vortex on one hand and the symmetry of the higher-order Laue zones in the diffraction pattern on the other for kinematically and dynamically scattered electrons. We then extend this to atoms arranged on a helix as found in crystals which belong to chiral space groups and propose a method to determine the handedness of such crystals by looking at the symmetry of the diffraction pattern. In contrast to alternative methods, our technique does not require multiple scattering, which makes it possible to also investigate extremely thin samples in which multiple scattering is suppressed. In order to verify the model, elastic scattering simulations are performed, and an experimental demonstration on Mn2Sb2O7 is given in which we find the sample to belong to the right-handed variant of its enantiomorphic pair. This demonstrates the usefulness of electron vortex beams to reveal the chirality of crystals in a transmission electron microscope and provides the required theoretical basis for further developments in this field. |
Address |
|
Corporate Author |
|
Thesis |
|
Publisher |
|
Place of Publication |
|
Editor |
|
Language |
|
Wos |
000352017000002 |
Publication Date |
2015-03-27 |
Series Editor |
|
Series Title |
|
Abbreviated Series Title |
|
Series Volume |
|
Series Issue |
|
Edition |
|
ISSN |
1098-0121;1550-235X; |
ISBN |
|
Additional Links |
UA library record; WoS full record; WoS citing articles |
Impact Factor |
3.836 |
Times cited |
54 |
Open Access |
|
Notes |
Fwo; 312483 Esteem2; 278510 Vortex; esteem2jra1; esteem2jra2 ECASJO_; |
Approved |
Most recent IF: 3.836; 2015 IF: 3.736 |
Call Number ![sorted by Call Number field, descending order (down)](img/sort_desc.gif) |
c:irua:125512 c:irua:125512 |
Serial |
3825 |
Permanent link to this record |
|
|
|
Author |
Ramachandran, D.; Egoavil, R.; Crabbe, A.; Hauffman, T.; Abakumov, A.; Verbeeck, J.; Vandendael, I.; Terryn, H.; Schryvers, D. |
Title |
TEM and AES investigations of the natural surface nano-oxide layer of an AISI 316L stainless steel microfibre |
Type |
A1 Journal article |
Year |
2016 |
Publication |
Journal of microscopy |
Abbreviated Journal |
J Microsc-Oxford |
Volume |
264 |
Issue |
264 |
Pages |
207-214 |
Keywords |
A1 Journal article; Electron microscopy for materials research (EMAT) |
Abstract |
The chemical composition, nanostructure and electronic structure of nanosized oxide scales naturally formed on the surface of AISI 316L stainless steel microfibres used for strengthening of composite materials have been characterised using a combination of scanning and transmission electron microscopy with energy-dispersive X-ray, electron energy loss and Auger spectroscopy. The analysis reveals the presence of three sublayers within the total surface oxide scale of 5.0-6.7 nm thick: an outer oxide layer rich in a mixture of FeO.Fe2 O3 , an intermediate layer rich in Cr2 O3 with a mixture of FeO.Fe2 O3 and an inner oxide layer rich in nickel. |
Address |
Electron Microscopy for Materials Science, University of Antwerp, Antwerp, Belgium |
Corporate Author |
|
Thesis |
|
Publisher |
|
Place of Publication |
|
Editor |
|
Language |
English |
Wos |
000385944300009 |
Publication Date |
2016-06-17 |
Series Editor |
|
Series Title |
|
Abbreviated Series Title |
|
Series Volume |
|
Series Issue |
|
Edition |
|
ISSN |
0022-2720 |
ISBN |
|
Additional Links |
UA library record; WoS full record; WoS citing articles |
Impact Factor |
1.692 |
Times cited |
12 |
Open Access |
|
Notes |
This work was supported by SIM vzw, Technologiepark 935, BE-9052 Zwijnaarde, Belgium, within the InterPoCo project of the H-INT-S horizontal program. The authors are also thankful to Stijn Van den Broeck for help in FIB sample preparation, to Hamed Heidari for useful comments and to the N.V. Bekaert S.A. company for providing the microfibres. RE acknowledges funding by the European Union Council under the 7th Framework Program (FP7) grant nr NMP3-LA-2010-246102 IFOX. |
Approved |
Most recent IF: 1.692 |
Call Number ![sorted by Call Number field, descending order (down)](img/sort_desc.gif) |
c:irua:134087 |
Serial |
4096 |
Permanent link to this record |
|
|
|
Author |
Fedotov, S.S.; Kuzovchikov, S.M.; Khasanova, N.R.; Drozhzhin, O.A.; Filimonov, D.S.; Karakulina, O.M.; Hadermann, J.; Abakumov, A.M.; Antipov, E.V. |
Title |
Synthesis, structure and electrochemical properties of LiNaCo0.5Fe0.5PO4F fluoride-phosphate |
Type |
A1 Journal article |
Year |
2016 |
Publication |
Journal of solid state chemistry |
Abbreviated Journal |
J Solid State Chem |
Volume |
242 |
Issue |
242 |
Pages |
70-77 |
Keywords |
A1 Journal article; Electron microscopy for materials research (EMAT) |
Abstract |
LiNaCo 0.5 Fe 0.5 PO 4 F fluoride-phosphate was synthesized via conventional solid-state and novel freeze-drying routes. The crystal structure was refined based on neutron powder diffraction (NPD) data and validated by electron diffraction (ED) and high-resolution transmission electron microscopy (HRTEM). The alkali ions are ordered in LiNaCo 0.5 Fe 0.5 PO 4 F and the transition metals jointly occupy the same crystallographic sites. The oxidation state and oxygen coordination environment of the Fe atoms were verified by 57 Fe Mössbauer spectroscopy. Electrochemical tests of the LiNaCo 0.5 Fe 0.5 PO 4 F cathode material demonstrated a reversible activity of the Fe 3+ /Fe 2+ redox couple at the electrode potential near 3.4 V and minor activity of the Co 3+ /Co 2+ redox couple over 5 V vs Li/Li + . The material exhibits a good capacity retention in the 2.4÷4.6 V vs Li/Li + potential range with the delivered discharge capacity of more than 82% (theo.) regarding Fe 3+ /Fe 2+ . |
Address |
|
Corporate Author |
|
Thesis |
|
Publisher |
|
Place of Publication |
|
Editor |
|
Language |
|
Wos |
000383304900010 |
Publication Date |
2016-02-27 |
Series Editor |
|
Series Title |
|
Abbreviated Series Title |
|
Series Volume |
|
Series Issue |
|
Edition |
|
ISSN |
0022-4596 |
ISBN |
|
Additional Links |
UA library record; WoS full record; WoS citing articles |
Impact Factor |
2.299 |
Times cited |
1 |
Open Access |
|
Notes |
The authors kindly thank Dr. O. A. Shlyakhtin for the assistance in the freeze-drying synthesis. We are grateful to the Laboratory for Neutron Scattering and Imaging (NLS) at the Paul Scherrer Institut (Villigen, Switzerland) for granting beam time at the HRPT diffractometer and to Dr. D. V. Sheptyakov for the technical support during the experiment. The work was partly supported by Russian Foundation for Basic Research (RFBR grant 13-03-00495a, 14-29-04064 ofim, 16-33-01131 mola), Skoltech Center for Electrochemical Energy Storage and Moscow State University Development Program up to 2020. J. Hadermann, O.M. Karakulina and A.M. Abakumov acknowledge support from FWO under grant G040116N. |
Approved |
Most recent IF: 2.299 |
Call Number ![sorted by Call Number field, descending order (down)](img/sort_desc.gif) |
c:irua:133776 |
Serial |
4075 |
Permanent link to this record |
|
|
|
Author |
Batuk, D.; Tsirlin, A.A.; Filimonov, D.S.; Zakharov, K.V.; Volkova, O.S.; Vasiliev, A.; Hadermann, J.; Abakumov, A.M. |
Title |
Bi(3n+1)Ti7Fe(3n-3)O(9n+11) Homologous Series: Slicing Perovskite Structure with Planar Interfaces Containing Anatase-like Chains |
Type |
A1 Journal article |
Year |
2016 |
Publication |
Inorganic chemistry |
Abbreviated Journal |
Inorg Chem |
Volume |
55 |
Issue |
55 |
Pages |
1245-1257 |
Keywords |
A1 Journal article; Electron microscopy for materials research (EMAT) |
Abstract |
The n = 3-6 members of a new perovskite-based homologous series Bi(3n+1)Ti7Fe(3n-3)O(9n+11) are reported. The crystal structure of the n = 3 Bi10Ti7Fe6O38 member is refined using a combination of X-ray and neutron powder diffraction data (a = 11.8511(2) A, b = 3.85076(4) A, c = 33.0722(6) A, S.G. Immm), unveiling the partially ordered distribution of Ti(4+) and Fe(3+) cations and indicating the presence of static random displacements of the Bi and O atoms. All Bi(3n+1)Ti7Fe(3n-3)O(9n+11) structures are composed of perovskite blocks separated by translational interfaces parallel to the (001)p perovskite planes. The thickness of the perovskite blocks increases with n, while the atomic arrangement at the interfaces remains the same. The interfaces comprise chains of double edge-sharing (Fe,Ti)O6 octahedra connected to the octahedra of the perovskite blocks by sharing edges and corners. This configuration shifts the adjacent perovskite blocks relative to each other over a vector (1/2)[110]p and creates S-shaped tunnels along the [010] direction. The tunnels accommodate double columns of the Bi(3+) cations, which stabilize the interfaces owing to the stereochemical activity of their lone electron pairs. The Bi(3n+1)Ti7Fe(3n-3)O(9n+11) structures can be formally considered either as intergrowths of perovskite modules and polysynthetically twinned modules of the Bi2Ti4O11 structure or as intergrowths of the 2D perovskite and 1D anatase fragments. Transmission electron microscopy (TEM) on Bi10Ti7Fe6O38 reveals that static atomic displacements of Bi and O inside the perovskite blocks are not completely random; they are cooperative, yet only short-range ordered. According to TEM, the interfaces can be laterally shifted with respect to each other over +/-1/3a, introducing an additional degree of disorder. Bi10Ti7Fe6O38 is paramagnetic in the 1.5-1000 K temperature range due to dilution of the magnetic Fe(3+) cations with nonmagnetic Ti(4+). The n = 3, 4 compounds demonstrate a high dielectric constant of 70-165 at room temperature. |
Address |
Center for Electrochemical Energy Storage, Skolkovo Institute of Science and Technology , Nobelya str. 3, 143026 Moscow, Russia |
Corporate Author |
|
Thesis |
|
Publisher |
|
Place of Publication |
|
Editor |
|
Language |
English |
Wos |
000369356800031 |
Publication Date |
2016-01-09 |
Series Editor |
|
Series Title |
|
Abbreviated Series Title |
|
Series Volume |
|
Series Issue |
|
Edition |
|
ISSN |
0020-1669 |
ISBN |
|
Additional Links |
UA library record; WoS full record; WoS citing articles |
Impact Factor |
4.857 |
Times cited |
3 |
Open Access |
|
Notes |
We are grateful to the Laboratory for Neutron Scattering and Imaging of Paul Scherrer Institut (LNS PSI, Villigen, Switzerland) for granting beam time at the HRPT diffrac- tometer and to Dr. Denis Sheptyakov for the technical support during the experiment. We are also grateful to Valery Verchenko for his help with magnetization measurements. The work has been supported by the Russian Science Foundation (grant 14-13-00680). A.A.T. was partly supported by the Federal Ministry for Education and Science through a Sofja Kovalevskaya Award of Alexander von Humboldt Foundation. |
Approved |
Most recent IF: 4.857 |
Call Number ![sorted by Call Number field, descending order (down)](img/sort_desc.gif) |
c:irua:132247 |
Serial |
4073 |
Permanent link to this record |
|
|
|
Author |
Drozhzhin, O.A.; Sumanov, V.D.; Karakulina, O.M.; Abakumov, A.M.; Hadermann, J.; Baranov, A.N.; Stevenson, K.J.; Antipov, E.V. |
Title |
Switching between solid solution and two-phase regimes in the Li1-xFe1-yMnyPO4 cathode materials during lithium (de)insertion: combined PITT, in situ XRPD and electron diffraction tomography study |
Type |
A1 Journal article |
Year |
2016 |
Publication |
Electrochimica acta |
Abbreviated Journal |
Electrochim Acta |
Volume |
191 |
Issue |
191 |
Pages |
149-157 |
Keywords |
A1 Journal article; Electron microscopy for materials research (EMAT) |
Abstract |
The electrochemical properties and phase transformations during (de)insertion of Li+ in LiFePO4, LiFe0.9Mn0.1PO4 and LiFe0.5Mn0.5PO4 are studied by means of galvanostatic cycling, potential intermittent titration technique (PITT) and in situ X-ray powder diffraction. Different modes of switching between the solid solution and two-phase regimes are revealed which are influenced by the Mn content in Li1-xFe1-yMnyPO4. Additionally, an increase in electrochemical capacity with the Mn content is observed at high rates of galvanostatic cycling (10C, 20C), which is in good agreement with the numerically estimated contribution of the solid solution mechanism determined from PITT data. The observed asymmetric behavior of the phase transformations in Li1-xFe0.5Mn0.5PO4 during charge and discharge is discussed. For the first time, the crystal structures of electrochemically deintercalated Li1-xFe0.5Mn0.5PO4 with different Li content – LiFe0.5Mn0.5PO4, Li0.5Fe0.5Mn0.5PO4 and Li0.1Fe0.5Mn0.5PO4 – are refined, including the occupancy factors of the Li position. This refinement is done using electron diffraction tomography data. The crystallographic analyses of Li1-xFe0.5Mn0.5PO4 reveal that at x = 0.5 and 0.9 the structure retains the Pnma symmetry and the main motif of the pristine x = 0 structure without noticeable short range order effects. |
Address |
|
Corporate Author |
|
Thesis |
|
Publisher |
|
Place of Publication |
|
Editor |
|
Language |
|
Wos |
000371143200018 |
Publication Date |
2016-01-13 |
Series Editor |
|
Series Title |
|
Abbreviated Series Title |
|
Series Volume |
|
Series Issue |
|
Edition |
|
ISSN |
0013-4686 |
ISBN |
|
Additional Links |
UA library record; WoS full record; WoS citing articles |
Impact Factor |
4.798 |
Times cited |
27 |
Open Access |
|
Notes |
This work was supported by the Russian Foundation of Basic Research (grants No. 14-29-04064 and 14-03-31473), Skolkovo Institute of Science and Technology, and the Lomonosov Moscow State University Program of Development. J. Hadermann, O. M. Karakulina and A. M. Abakumov acknowl- edge support from FWO under grant G040116N. |
Approved |
Most recent IF: 4.798 |
Call Number ![sorted by Call Number field, descending order (down)](img/sort_desc.gif) |
c:irua:131911 |
Serial |
4032 |
Permanent link to this record |
|
|
|
Author |
Fedotov, S.S.; Khasanova, N.R.; Samarin, A.S.; Drozhzhin, O.A.; Batuk, D.; Karakulina, O.M.; Hadermann, J.; Abakumov, A.M.; Antipov, E.V. |
Title |
AVPO4F (A = Li, K): A 4 V Cathode Material for High-Power Rechargeable Batteries |
Type |
A1 Journal article |
Year |
2016 |
Publication |
Chemistry of materials |
Abbreviated Journal |
Chem Mater |
Volume |
28 |
Issue |
28 |
Pages |
411-415 |
Keywords |
A1 Journal article; Electron microscopy for materials research (EMAT) |
Abstract |
A novel potassium-based fluoride-phosphate, KVPO4F, with a KTiOPO4 (KTP) type structure is synthesized and characterized. About 85% of potassium has been electrochemically extracted on oxidation producing a cathode material with attractive performance for Li-ion batteries. The material operates at the electrode potential near 4V vs Li/Li+ exhibiting a sloping voltage profile, extremely low polarization, small volume change of about 2% and excellent rate capability, maintaining more than 75% of the initial capacity at 40C discharge rate without significant fading. |
Address |
|
Corporate Author |
|
Thesis |
|
Publisher |
|
Place of Publication |
|
Editor |
|
Language |
|
Wos |
000368949900002 |
Publication Date |
2016-01-04 |
Series Editor |
|
Series Title |
|
Abbreviated Series Title |
|
Series Volume |
|
Series Issue |
|
Edition |
|
ISSN |
0897-4756 |
ISBN |
|
Additional Links |
UA library record; WoS full record; WoS citing articles |
Impact Factor |
9.466 |
Times cited |
46 |
Open Access |
|
Notes |
The authors kindly thank Dr. S. N. Putilin for XRD measurements, Dr. O. A. Shlyakhtin for the assistance in cryochemical synthesis, Ph.D. students A. A. Sadovnikov and E. A. Karpukhina for SEM imaging and FTIR spectra respectively. The work was partly supported by Russian Science Foundation (grant 16-19-00190), Skoltech Center for Electrochemical Energy Storage and Moscow State University Devel-opment Program up to 2020. J. Hadermann, O.M. Karakulina and A.M. Abakumov acknowledge support from FWO under grant G040116N. |
Approved |
Most recent IF: 9.466 |
Call Number ![sorted by Call Number field, descending order (down)](img/sort_desc.gif) |
c:irua:131583 |
Serial |
4001 |
Permanent link to this record |
|
|
|
Author |
Batuk, D.; Batuk, M.; Tsirlin, A.A.; Hadermann, J.; Abakumov, A.M. |
Title |
Trapping of Oxygen Vacancies at Crystallographic Shear Planes in Acceptor-Doped Pb-Based Ferroelectrics |
Type |
A1 Journal article |
Year |
2015 |
Publication |
Angewandte Chemie: international edition in English |
Abbreviated Journal |
Angew Chem Int Edit |
Volume |
54 |
Issue |
54 |
Pages |
14787-14790 |
Keywords |
A1 Journal article; Electron microscopy for materials research (EMAT) |
Abstract |
The defect chemistry of the ferroelectric material PbTiO3 after doping with Fe(III) acceptor ions is reported. Using advanced transmission electron microscopy and powder X-ray and neutron diffraction, we demonstrate that even at concentrations as low as circa 1.7% (material composition approximately ABO2.95), the oxygen vacancies are trapped into extended planar defects, specifically crystallographic shear planes. We investigate the evolution of these defects upon doping and unravel their detailed atomic structure using the formalism of superspace crystallography, thus unveiling their role in nonstoichiometry in the Pb-based perovskites. |
Address |
Chemistry Department, Moscow State University, 119991, Moscow (Russia). artem.abakumov@uantwerpen.be |
Corporate Author |
|
Thesis |
|
Publisher |
|
Place of Publication |
|
Editor |
|
Language |
English |
Wos |
000367723400031 |
Publication Date |
2015-10-21 |
Series Editor |
|
Series Title |
|
Abbreviated Series Title |
|
Series Volume |
|
Series Issue |
|
Edition |
|
ISSN |
1433-7851 |
ISBN |
|
Additional Links |
UA library record; WoS full record; WoS citing articles |
Impact Factor |
11.994 |
Times cited |
3 |
Open Access |
|
Notes |
A.M.A. is grateful to the Russian Science Foundation (grant 14-13-00680). AT was funded by the Mobilitas grant MTT77 of the ESF and by the Federal Ministry for Education and Research through the Sofja Kovalevskaya Award of Alexander von Humboldt Foundation. |
Approved |
Most recent IF: 11.994; 2015 IF: 11.261 |
Call Number ![sorted by Call Number field, descending order (down)](img/sort_desc.gif) |
c:irua:131104 |
Serial |
4080 |
Permanent link to this record |
|
|
|
Author |
McCalla, E.; Abakumov, A.M.; Saubanere, M.; Foix, D.; Berg, E.J.; Rousse, G.; Doublet, M.-L.; Gonbeau, D.; Novak, P.; Van Tendeloo, G.; Dominko, R.; Tarascon, J.-M. |
Title |
Visualization of O-O peroxo-like dimers in high-capacity layered oxides for Li-ion batteries |
Type |
A1 Journal article |
Year |
2015 |
Publication |
Science |
Abbreviated Journal |
Science |
Volume |
350 |
Issue |
350 |
Pages |
1516-1521 |
Keywords |
A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT) |
Abstract |
Lithium-ion (Li-ion) batteries that rely on cationic redox reactions are the primary energy source for portable electronics. One pathway toward greater energy density is through the use of Li-rich layered oxides. The capacity of this class of materials (>270 milliampere hours per gram) has been shown to be nested in anionic redox reactions, which are thought to form peroxo-like species. However, the oxygen-oxygen (O-O) bonding pattern has not been observed in previous studies, nor has there been a satisfactory explanation for the irreversible changes that occur during first delithiation. By using Li2IrO3 as a model compound, we visualize the O-O dimers via transmission electron microscopy and neutron diffraction. Our findings establish the fundamental relation between the anionic redox process and the evolution of the O-O bonding in layered oxides. |
Address |
College de France, Chimie du Solide et de l'Energie, FRE 3677, 11 Place Marcelin Berthelot, 75231 Paris Cedex 05, France. ALISTORE-European Research Institute, FR CNRS 3104, 80039 Amiens, France. Reseau sur le Stockage Electrochimique de l'Energie (RS2E), FR CNRS 3459, France. Sorbonne Universites-UPMC Univ Paris 06, 4 Place Jussieu, F-75005 Paris, France. jean-marie.tarascon@college-de-france.fr |
Corporate Author |
|
Thesis |
|
Publisher |
|
Place of Publication |
|
Editor |
|
Language |
English |
Wos |
000366591100056 |
Publication Date |
2015-12-17 |
Series Editor |
|
Series Title |
|
Abbreviated Series Title |
|
Series Volume |
|
Series Issue |
|
Edition |
|
ISSN |
0036-8075 |
ISBN |
|
Additional Links |
UA library record; WoS full record; WoS citing articles |
Impact Factor |
37.205 |
Times cited |
281 |
Open Access |
|
Notes |
E.M. thanks the Fonds de Recherche du Québec–Nature et Technologies and ALISTORE–European Research Institute for funding this work, as well as the European community I3 networks for funding the neutron scattering research trip. This work was also funded by the Slovenian Research Agency research program P2-0148. This work is partially based on experiments performed at the Institut Laue Langevin. We thank J. Rodriguez-Carvajal for help with neutron scattering experiments and for fruitful discussions. We also thank M. T. Sougrati for performing the Sn-Mössbauer measurements. Use of the Advanced Photon Source at Argonne National Laboratory was supported by the U.S. Department of Energy, Office of Science, Office of Basic Energy Sciences, under contract no. DE-AC02- 06CH11357. M.S. and M.-L.D. acknowledge high-performance computational resources from GENCI-CCRT/CINES (grant cmm6691). J.-M.T. acknowledges funding from the European Research Council (ERC) (FP/2014-2020)/ERC Grant-Project670116-ARPEMA. |
Approved |
Most recent IF: 37.205; 2015 IF: 33.611 |
Call Number ![sorted by Call Number field, descending order (down)](img/sort_desc.gif) |
c:irua:130202 |
Serial |
4005 |
Permanent link to this record |
|
|
|
Author |
Morozov, V.A.; Arakcheeva, A.V.; Pattison, P.; Meert, K.W.; Smet, P.F.; Poelman, D.; Gauquelin, N.; Verbeeck, J.; Abakumov, A.M.; Hadermann, J. |
Title |
KEu(MoO4)2 : polymorphism, structures, and luminescent properties |
Type |
A1 Journal article |
Year |
2015 |
Publication |
Chemistry of materials |
Abbreviated Journal |
Chem Mater |
Volume |
27 |
Issue |
27 |
Pages |
5519-5530 |
Keywords |
A1 Journal article; Electron microscopy for materials research (EMAT) |
Abstract |
In this paper, with the example of two different polymorphs of KEu(MoO4)2, the influence of the ordering of the A-cations on the luminescent properties in scheelite related compounds (A′,A″)n[(B′,B″)O4]m is investigated. The polymorphs were synthesized using a solid state method. The study confirmed the existence of only two polymorphic forms at annealing temperature range 9231203 K and ambient pressure: a low temperature anorthic α-phase and a monoclinic high temperature β-phase with an incommensurately modulated structure. The structures of both polymorphs were solved using transmission electron microscopy and refined from synchrotron powder X-ray diffraction data. The monoclinic β-KEu(MoO4)2 has a (3+1)-dimensional incommensurately modulated structure (superspace group I2/b(αβ0)00, a = 5.52645(4) Å, b = 5.28277(4) Å, c = 11.73797(8) Å, γ = 91.2189(4)o, q = 0.56821(2)a*0.12388(3)b*), whereas the anorthic α-phase is (3+1)-dimensional commensurately modulated (superspace group I1̅(αβγ)0, a = 5.58727(22) Å, b = 5.29188(18)Å, c = 11.7120(4) Å, α = 90.485(3)o, β = 88.074(3)o, γ = 91.0270(23)o, q = 1/2a* + 1/2c*). In both cases the modulation arises due to Eu/K cation ordering at the A site: the formation of a 2-dimensional Eu3+ network is characteristic for the α-phase, while a 3-dimensional Eu3+-framework is observed for the β-phase structure. The luminescent properties of KEu(MoO4)2 samples prepared under different annealing conditions were measured, and the relation between their optical properties and their structures is discussed. |
Address |
|
Corporate Author |
|
Thesis |
|
Publisher |
|
Place of Publication |
|
Editor |
|
Language |
|
Wos |
000360323700011 |
Publication Date |
2015-07-29 |
Series Editor |
|
Series Title |
|
Abbreviated Series Title |
|
Series Volume |
|
Series Issue |
|
Edition |
|
ISSN |
0897-4756;1520-5002; |
ISBN |
|
Additional Links |
UA library record; WoS full record; WoS citing articles |
Impact Factor |
9.466 |
Times cited |
26 |
Open Access |
|
Notes |
278510 Vortex; Fwo G039211n; G004413n ECASJO_; |
Approved |
Most recent IF: 9.466; 2015 IF: 8.354 |
Call Number ![sorted by Call Number field, descending order (down)](img/sort_desc.gif) |
c:irua:127244 |
Serial |
3537 |
Permanent link to this record |
|
|
|
Author |
Pinheiro, C.B.; Abakumov, A.M. |
Title |
Superspace crystallography : a key to the chemistry and properties |
Type |
A1 Journal article |
Year |
2015 |
Publication |
IUCrJ |
Abbreviated Journal |
Iucrj |
Volume |
2 |
Issue |
2 |
Pages |
137-154 |
Keywords |
A1 Journal article; Electron microscopy for materials research (EMAT) |
Abstract |
An overview is given of the recent advances in the field of modulated molecular and inorganic crystals with an emphasis on the links between incommensurability, intermolecular and interatomic interactions and, wherever possible, the properties of the materials. The importance of detailed knowledge on the modulated structure for understanding the crystal chemistry and the functional properties of modulated phases is shown using selected examples of incommensurate modulations in organic molecular compounds and inorganic complex oxides. |
Address |
|
Corporate Author |
|
Thesis |
|
Publisher |
Int union crystallography |
Place of Publication |
Chester |
Editor |
|
Language |
|
Wos |
000356865900016 |
Publication Date |
2014-12-17 |
Series Editor |
|
Series Title |
|
Abbreviated Series Title |
|
Series Volume |
|
Series Issue |
|
Edition |
|
ISSN |
2052-2525; |
ISBN |
|
Additional Links |
UA library record; WoS full record; WoS citing articles |
Impact Factor |
5.793 |
Times cited |
15 |
Open Access |
|
Notes |
|
Approved |
Most recent IF: 5.793; 2015 IF: NA |
Call Number ![sorted by Call Number field, descending order (down)](img/sort_desc.gif) |
c:irua:127058 |
Serial |
3382 |
Permanent link to this record |
|
|
|
Author |
Tyablikov, O.A.; Batuk, D.; Tsirlin, A.A.; Batuk, M.; Verchenko, V.Y.; Filimonov, D.S.; Pokholok, K.V.; Sheptyakov, D.V.; Rozova, M.G.; Hadermann, J.; Antipov, E.V.; Abakumov, A.M.; |
Title |
{110}-Layered B-cation ordering in the anion-deficient perovskite Pb2.4Ba2.6Fe2Sc2TiO13 with the crystallographic shear structure |
Type |
A1 Journal article |
Year |
2015 |
Publication |
Journal of the Chemical Society : Dalton transactions |
Abbreviated Journal |
Dalton T |
Volume |
44 |
Issue |
44 |
Pages |
10753-10762 |
Keywords |
A1 Journal article; Electron microscopy for materials research (EMAT) |
Abstract |
A novel anion-deficient perovskite-based compound, Pb2.4Ba2.6Fe2Sc2TiO13, was synthesized via the citrate-based route. This compound is an n = 5 member of the A(n)B(n)O(3n-2) homologous series with unit-cell parameters related to the perovskite subcell a(p) approximate to 4.0 angstrom as a(p)root 2 x a(p) x 5a(p)root 2. The crystal structure of Pb2.4Ba2.6Fe2Sc2TiO13 consists of quasi-2D perovskite blocks with a thickness of three octahedral layers separated by the 1/2[110]((1) over bar 01)(p) crystallographic shear (CS) planes, which are parallel to the {110} plane of the perovskite subcell. The CS planes transform the corner-sharing octahedra into chains of edge-sharing distorted tetragonal pyramids. Using a combination of neutron powder diffraction, Fe-57 Mossbauer spectroscopy and atomic resolution electron energy-loss spectroscopy we demonstrate that the B-cations in Pb2.4Ba2.6Fe2Sc2TiO13 are ordered along the {110} perovskite layers with Fe3+ in distorted tetragonal pyramids along the CS planes, Ti4+ preferentially in the central octahedra of the perovskite blocks and Sc3+ in the outer octahedra of the perovskite blocks. Magnetic susceptibility and Mossbauer spectroscopy indicate a broadened magnetic transition around T-N similar to 45 K and the onset of local magnetic fields at low temperatures. The magnetic order is probably reminiscent of that in other A(n)B(n)O(3n-2) homologues, where G-type AFM order within the perovskite blocks has been observed. |
Address |
|
Corporate Author |
|
Thesis |
|
Publisher |
|
Place of Publication |
London |
Editor |
|
Language |
|
Wos |
000355701000026 |
Publication Date |
2015-01-26 |
Series Editor |
|
Series Title |
|
Abbreviated Series Title |
|
Series Volume |
|
Series Issue |
|
Edition |
|
ISSN |
1477-9226;1477-9234; |
ISBN |
|
Additional Links |
UA library record; WoS full record; WoS citing articles |
Impact Factor |
4.029 |
Times cited |
1 |
Open Access |
|
Notes |
|
Approved |
Most recent IF: 4.029; 2015 IF: 4.197 |
Call Number ![sorted by Call Number field, descending order (down)](img/sort_desc.gif) |
c:irua:127001 |
Serial |
22 |
Permanent link to this record |