Abstract: This paper discusses the nucleation behaviour of the CoSi to CoSi2 transformation from cobalt silicide thin films grown by deposition at elevated substrate temperatures ranging from 375 °C to 600 °C. A combination of channelling, real-time Rutherford backscattering spectrometry, real-time x-ray diffraction, and transmission electron microscopy was used to investigate the effect of the deposition temperature on the subsequent formation temperature of CoSi2, its growth behaviour, and the epitaxial quality of the CoSi2 thus formed. The temperature at which deposition took place was observed to exert a significant and systematic influence on both the formation temperature of CoSi2 and its growth mechanism. CoSi films grown at the lowest temperatures were found to increase the CoSi2 nucleation temperature above that of CoSi2 grown by conventional solid phase reaction, whereas the higher deposition temperatures reduced the nucleation temperature significantly. In addition, a systematic change in growth mechanism of the subsequent CoSi2 growth occurs as a function of deposition temperature. First, the CoSi2 growth rate from films grown at the lower reactive deposition temperatures is substantially lower than that grown at higher reactive deposition temperatures, even though the onset of growth occurs at a higher temperature, Second, for deposition temperatures below 450 °C, the growth appears columnar, indicating nucleation controlled growth. Elevated deposition temperatures, on the other hand, render the CoSi2 formation process layer-by-layer which indicates enhanced nucleation of the CoSi2 and diffusion controlled growth. Our results further indicate that this observed trend is most likely related to stress and changes in microstructure introduced during reactive deposition of the CoSi film. The deposition temperature therefore provides a handle to tune the CoSi2 growth mechanism.

Abstract: In 1999, phytoremediation was applied at the site of a Belgian car factory to contain two BTEX plumes. This case study evaluates the cost effectiveness of phytoremediation compared to other remediation options, applying a tailored approach for economic evaluation. Generally, when phytoremediation is addressed as being cost effective, the cost effectiveness is only determined on an average basis. This study however, demonstrates that an incremental analysis may provide a more nuanced conclusion. When the cost effectiveness is calculated on an average basis, in this particular case, the no containment strategy (natural attenuation) has the lowest cost per unit mass removed and hence, should be preferred. However, when the cost effectiveness is determined incrementally, no containment should only be preferred if the value of removing an extra gram of contaminant mass is lower than 320. Otherwise, a permeable reactive barrier should be adopted. A similar analysis is provided for the effect determined on the basis of remediation time. Phytoremediation is preferred compared to no containment if reaching the objective one year earlier is worth 7 000.

Abstract: Bioremediation is a remediation strategy, which has considerable strength but also certain limitations. Complex and uncertain relationships among biomass, contaminants, and nutrients lead to an uncertain level of removal efficiency. The uncertainty inherent to a bioremediation strategy should be addressed in the remediation selection process. In order to evaluate the bioremediation strategy economically, this study takes into account the reversibility of a decision. A decision tree structures the different remediation strategies, thus giving the possible courses of action open to the decision maker. The option value indicates the importance of having the possibility to reverse a previously made decision. Compared with conventional economic evaluation tools, more information to ground the selection made is revealed.

Abstract: The high-rate sensitivity of nanostructured metallic materials demonstrated in the recent literature is related to the predominance of thermally activated deformation mechanisms favoured by a large density of internal interfaces. Here we report time-resolved high-resolution electron transmission microscopy creep tests on thin nanograined films using on-chip nanomechanical testing. Tests are performed on ​palladium, which exhibited unexpectedly large creep rates at room temperature. Despite the small 30-nm grain size, relaxation is found to be mediated by dislocation mechanisms. The dislocations interact with the growth nanotwins present in the grains, leading to a loss of coherency of twin boundaries. The density of stored dislocations first increases with applied deformation, and then decreases with time to drive additional deformation while no grain boundary mechanism is observed. This fast relaxation constitutes a key issue in the development of various micro- and nanotechnologies such as ​palladium membranes for hydrogen applications.

Abstract: Whereas deformation twinning is known to be an important deformation mechanism for hexagonal materials like magnesium and pure titanium, so far almost no literature exists on the twinning behaviour of the Ti-6Al-4V alloy. In this work it was shown that the activation of twinning as a deformation mechanism could have a pronounced effect on the mechanical behaviour of the Ti-6Al-4V alloy. This effect is even more pronounced under dynamic loading conditions. Transmission electron microscopy showed that only the {1 0 1 2}{1 0 1 1} tensile twin system was activated under certain loading conditions. Light-optical microscopy and electron backscatter diffraction data were afterwards used to experimentally determine the twin fractions. The importance of twinning for the texture evolution was also studied. It was shown that even small twin fractions can lead to distinct texture features, especially due to the discrete reorientation of the c-axes. The experimental results were compared to simulated results that were obtained with a viscoplastic self-consistent crystal plasticity code, after experimental validation that twinning can be reliably modelled as a unidirectional slip system. Although good agreement was obtained for the experimental and simulated stress-strain curves, the simulated results concerning twinning correlated well only on a qualitative basis as the simulated twin fractions were systematically higher than the experimental fractions. This seems to strengthen the hypothesis made by other research groups that complete grains might reorient by twinning. (C) 2011 Elsevier B.V. All rights reserved.

Abstract: The origin of the ferroelectric polarization switching in orthorhombic HfO2 has been investigated by first principles calculations. The phenomenon can be regarded as being the coordinated displacement of four O ions in the orthorhombic unit cell, which can lead to a saturated polarization as high as 53 mu C/cm(2). We show the correlation between the computed polarization reversal barrier and the experimental coercive fields. (C) 2014 AIP Publishing LLC.