Abstract: Addition of yttrium in HfO(2) thin films prepared on silicon by metal organic chemical vapor deposition is investigated in a wide compositional range (2.0-99.5 at. %). The cubic structure of HfO(2) is stabilized for 6.5 at. %. The permittivity is maximum for yttrium content of 6.5-10 at. %; in this range, the effective permittivity, which results from the contribution of both the cubic phase and silicate phase, is of 22. These films exhibit low leakage current density (5x10(-7) A/cm(2) at -1 V for a 6.4 nm film). The cubic phase is stable upon postdeposition high temperature annealing at 900 degrees C under NH(3). (c) 2006 American Institute of Physics.

Abstract: The crystal structure of the newly discovered double-Hg-layer copper oxide superconductor (Hg, Pr)(2)Ba-2(Y, Ca)Cu2O8-delta was studied as a function of chemical doping using neutron and electron diffraction and high-resolution transmission electron microscopy (HREM). Rietveld refinements of the structural parameters from neutron powder diffraction data indicate that the oxygen site O3 on the mercury plane is highly defective, being both partially occupied and displaced from the high-symmetry position. The variable concentration of oxygen vacancies partially compensates for the cation doping and, together with the O3 displacement field, makes some of the Hg atoms acquire an unusual pyramidal coordination. HREM images confirm that the structure is of the '2212' type, with very few defects. In some grains, faint superstructure reflections were evidenced by electron diffraction, suggesting that both the oxygen vacancies and the O3 displacement field may order at least on a local scale.

Abstract: Graphene sheets have been functionalized with a PAMAM dendron, finding that graphene can be efficiently functionalized all over the surface, or only at the edges, depending on the reactions used in the functionalization process.

Abstract: Under ultrasonication, the production of high quality graphene layers by exfoliation of graphite was achieved via addition of tiopronin as an antioxidant.

Abstract: A robust and easy to handle 3D porous platinum structure was created via replicating the 3D channel system
of an ordered mesoporous silica material using atomic layer deposition (ALD) over micrometer distances.
After ALD of Pt in the silica material, the host template was digested using hydrogen fluoride (HF). A fully
connected ordered Pt nanostructure was obtained with morphology and sizes corresponding to that of
the pores of the host matrix, as revealed with high-resolution scanning transmission electron
microscopy and electron tomography. The Pt nanostructure consisted of hexagonal Pt rods originating
from the straight mesopores (11 nm) of the host structure and linking features resulting from Pt
replication of the interconnecting mesopore segments (2–4 nm) present in the silica host structure.
Electron tomography of partial replicas, made by incomplete infilling of Zeotile-4 material with Pt,
provided insight in the connectivity and formation mechanism of the Pt nanostructure by ALD. The Pt
replica was evaluated for its potential use as electrocatalyst for the hydrogen evolution reaction, one of
the half-reactions of water electrolysis, and as microelectrode for biomedical sensing. The Pt replica
showed high activity for the hydrogen evolution reaction and electrochemical characterization revealed
a large impedance improvement in comparison with reference Pt electrodes.

Abstract: In this work, the chemical and microstructural stability of YBiO3 buffer layers during the growth of YBa2Cu3O7-δ (YBCO) was studied. The superconducting YBCO films were deposited via both Pulsed Laser Deposition as well as Chemical Solution Deposition. Although excellent superconducting properties are obtained in both cases, self-field critical current densities of 3.6 and 1.2 MA/cm2 respectively, chemical instability of the YBiO3 buffer layer is observed. An elaborate transmission electron microscopy study showed that in the case of vacuum deposited YBCO, the YBiO3 becomes unstable and Bi2O3 sublimates out of the architecture. Due to this structural instability, an intermediate Y2O3 layer is obtained which maintains it microstructural orientation relation with the substrate and acts as growth template for YBCO. For chemical solution deposited YBCO, reaction of YBCO with the YBiO3 buffer layer is observed, leading to large grains of YBa2BiO6 which are pushed towards the surface of the films and strongly reduce the superconducting properties. Upon using high growth temperatures for the superconducting layer, these secondary phases decompose, which subsequently leads to Bi2O3 sublimation and a textured YBCO film which directly nucleated onto the LaAlO3 single crystal substrate. Hence, this electron microscopy study indicates that bismuth-based buffer layers systems are not suitable for implementation in coated conductors.

Abstract: Catalytic synthesis and transmission electron microscopy (TEM) of multi-wall carbon nanotubes are presented. Silica, zeolite and alumina supported cobalt catalysts were prepared by different methods (impregnation and ion-adsorption precipitation) and were used to produce nanotubes. The synthesis was carried out in a fixed bed flow reactor and the process was optimized in order to produce carbon nanotubes on a gram scale. The influence of various parameters such as the method of catalyst preparation, the nature of the support, cobalt concentration and reaction conditions on the formation of nanotubes was investigated. The carbon deposits were measured and the quality of nanotubes was determined by low and high resolution TEM. Multi-wall straight and coiled nanotubes were found to be fairly regular with an average inner (outer) diameter of 4-7 nm (8-23 nm) and with lengths up to 0.1 mm.

Abstract: Well tuned: ZSM-5 with platinum nanoparticles preferably hydrogenates trans fatty acids over cis isomers in model triacylglycerols for geometric reasons. The central fatty acid chain reacts faster, pointing to pore mouth adsorption in a tuning fork conformation (see picture). This conformation induces stepwise hydrogenation, resulting in fast removal of the unstable central triene, while formation of saturated chains is limited.

Abstract: The recent revival of the Na-ion battery concept has prompted intense activities in the search for new Na-based layered oxide positive electrodes. The largest capacity to date was obtained for a Na-deficient layered oxide that relies on cationic redox processes only. To go beyond this limit, we decided to chemically manipulate these Na-based layered compounds in a way to trigger the participation of the anionic network. We herein report the electrochemical properties of a Na-rich phase Na2IrO3, which can reversibly cycle 1.5 Na+ per formula unit while not suffering from oxygen release nor cationic migrations. Such large capacities, as deduced by complementary XPS, X-ray/neutron diffraction and transmission electron microscopy measurements, arise from cumulative cationic and anionic redox processes occurring simultaneously at potentials as low as 3.0 V. The inability to remove more than 1.5 Na+ is rooted in the formation of an O1-type phase having highly stabilized Na sites as confirmed by DFT calculations, which could rationalize as well the competing metal/oxygen redox processes in Na2IrO3. This work will help to define the most fertile directions in the search for novel high energy Na-rich materials based on more sustainable elements than Ir.

Abstract: Mesoporous carbon, which can be replicated from mesoporous silica and whose surface is hydrophobic, can be an ideal catalyst for the esterification of fatty acids. Here we report an easy and low cost way to prepare sulfonic acid group-functionalized mesoporous carbon. A sample of calcined mesoporous silica SBA-15 was added to an aqueous sucrose solution followed by drying and calcination at different temperatures. In contrast to existing procedures, the obtained hybrid Si/C material was then first sulfonated in H2SO4, before the final removal of the silica template in order to stabilize the porous structure towards the liquid phase sulfonation treatment. Thus the silicacarbon composites, instead of the mesoporous carbon, were successfully sulfonated to introduce SO3H groups, while keeping the ordered mesoporous structure intact. The influence of carbonization temperature was investigated, suggesting an optimum temperature of 873 K. The SO3H group-functionalized mesoporous carbon, denoted as CMK-3-873-SO3H, was characterized by means of XRD, N2 physisorption, SEM, FT-IR, elemental analysis and TEM. It followed that a uniform mesoporous carbon was obtained with an average pore size of 3.89 nm, a specific surface of 807 m2/g and a SO3H group loading of 0.39 meq/g of dry material. Compared with other solid acid catalysts, the resulting material shows enhanced activity in the acid-catalyzed esterification of oleic acid with methanol, and can be used repeatedly. The increased catalytic performance is attributed to the hydrophobic surface and larger pore size of the new catalyst. It can effectively accommodate long chain fatty acids and reject formed water, making the active sites easily accessible.