Abstract: A combined Raman and electrochemical study of natural orpiment (As2S3), an arsenic sulfide pigment, was used to assess the quick formation of oxidized species such as arsenic oxide (As2O3) upon exposing the pigment to 405 nm or 532 nm monochromatic light while simultaneously recording the Raman spectra of the exposed sample. During this process, a distortion of the main band at 355 cm−1, associated with the stretching of the AsS3/2 pyramids of natural orpiment, was observed as well as an increased intensity of the 359 cm−1 band, corresponding to covalent AsAs bonds in natural orpiment. The distortion was accompanied by an overall decrease of the global Raman signal for natural orpiment, which could be explained by a loss in the crystal structure. The same phenomena were recorded in reference natural orpiment model paint samples stored for a long time together with verdigris (Cu(OH)2·(CH3COO)2·5H2O) and minium (Pb3O4) paints, the latter two appearing darkened on their sides closest to the orpiment sample as well as in several historical samples containing natural orpiment mixed with various blue pigments. By SEM-EDX and XRPD analysis, respectively on loose material and cast thin-sections of model paint samples, the darkening was identified as dark sulfide species such as chalcocite (Cu2S) and galena (PbS), suggesting the release of volatile sulfide or related species by the natural orpiment paint. XANES analyses of paint samples presenting AsAs bond increase indicated the presence of sulfur species most likely identified as organosulfur compounds formed upon the AsAs bond formation and explained the darkening of the Cu- and Pb-based pigments. To the best of our knowledge, this article reports for the first time the light-induced formation of AsAs bonds in natural orpiment used as an artists' pigment and objectively demonstrates the incompatibility between orpiment and (arsenic) sulfide-sensitive pigments.

Abstract: The vibrational level populations of the electronic ground state of the nitrogen molecule have been calculated for typical glow discharge conditions in argonnitrogen mixtures with nitrogen concentrations between 0.1 and 1%. Stationary solutions of the master equations of the vibrational levels have been obtained using numerical methods. The main mechanisms responsible for the population and depopulation of the vibrational levels, and for the overall shape of the vibrational distribution function are pointed out. It has been found that vibrationvibration collisions play only a minor role and therefore the population of the vibrational levels is basically determined by the electron temperature.

Abstract: Many historical documents written with iron gall inks are endangered by the corrosive effects of these inks. In this work, a combination of complementary analytical methods was used for the first time in order to study the phytate process which is used in conservation studios to stabilize damaged manuscripts. This process consists of an antioxidant treatment performed by means of a calcium phytate (CP) solution, followed by a deacidification treatment performed with a calcium carbonate (CC) solution. The antioxidant treatment capitalizes on the properties of myo-inositol hexaphosphoric acid (phytic acid) that inhibits iron through chelation. In order to use relatively low acidic solutions, the pH of the CP solution is increased up to values between 5 and 6, which is in the range of the CP precipitation threshold. This study was performed on laboratory samples made of paper impregnated with iron gall ink and artificially aged in climatic chambers. It aims to investigate how the CP precipitate impacts the efficiency of the treatment. Side effects, such as elemental losses and deposits, were measured by means of several analytical techniques (FeK Edge XANES, SEM/EDS, and ICP-AES). These measurements were crosschecked with a ready to use colour spot test made of bathophenanthroline impregnated paper. It appeared that the CP treatment should necessarily be followed by the deacidification treatment in order to achieve long term stability. The precipitation of CP in the treating solution does finally not impact the efficiency of the treatment despite the fact that it should theoretically lower the availability of phytate to chelate iron. A scenario is proposed to explain this point.

Abstract: The red pigment mercury sulfide, called cinnabar or vermilion, is well known to suffer from an alteration giving rise to a grey, grey-white or black color at the surface of degraded works of art. This phenomenon can dramatically affect the esthetical value of artworks. This work aims at assessing the factors (light, halides) influencing the instability of red mercury sulfide and understanding (by combining thermodynamic and experimental approaches) the chemical equilibria governing the formation and evolution of the different degradation compounds. From the thermodynamic study of the Hg-S-Cl-H2O system, it was concluded that Hg(0), Hg3S2Cl2, and Hg2Cl2 can be formed from the reaction of alpha-HgS with ClO(g). In the second part, the artificial ageing experiments presented were carried out on model samples following the conditions assessed in the first part, in order to reproduce natural ageing observed on red mercury sulfide. Similarly to degradation compounds detected on original works of art, mercury chlorine compounds such as calomel (Hg2Cl2) and corderoite (alpha-Hg3S2Cl2) were identified on the surface of alpha-HgS model samples, when exposed to light and a sodium hypochlorite solution. Sulfates were detected as well, and more particularly gypsum (CaSO4 center dot 2H(2)O) when Ca was originally present in the model sample. The relationship between color and composition is discussed as well.

Abstract: Redox processes activated by environmental factors have been identified as the main cause of the chromatic alterations of a number of artists' pigments, including the yellow pigment orpiment (As2S3). Although a general comprehension of the mechanisms has been provided through characterization of degradation compounds of As2S3, experimental evidences to prove how other paint components and how different environmental agents influence the formation pathways of specific secondary compounds are still lacking. Thus, it becomes fundamental to develop a methodological strategy which enable achieving a discrimination among the causes affecting the chemical stability of more heterogenous As2S3-based paints and defining the mechanism through which the alteration establishes and evolves, with the ultimate goal of optimizing the preventive conservation measures of unique masterpieces. In this paper, we propose a comprehensive multi-material and multi-method approach based on the combination of synchrotron radiation X-ray micro-analytical techniques (i.e., X-ray diffraction, X-ray fluorescence and X-ray absorption near edge structure spectroscopy at S K-/Ag L-3-/As K-edges) and vibrational micro-spectroscopy methods to unveil the causes and mechanism of darkening of “fake-gilded” decorations in tempera paintings, originally consisting of an unusual mixture of As2S3 and metallic silver (Ag-0). Such degradation process is a not yet understood phenomenon threatening a series of Old Master paintings, including those by the Italian painters Cimabue and Pietro Lorenzetti. The high specificity, sensitivity and lateral resolution of the employed analytical methods allowed providing first-time evidence for the presence of black acanthite (alpha-Ag2S), mimetite [Pb-5(AsO4)(3)Cl] and syngenite [K2Ca(SO4)(2)center dot H2O] as degradation products of the “fake-gilded” decorations in the Maesta by Cimabue (Church of Santa Maria dei Servi, Bologna, Italy). Furthermore, the study of the painting combined with that of tempera paint mock-ups permitted to explore and define the environmental agents and internal factors causing the darkening, by proving that: (i) Ag-0 and moisture are key-factors for triggering the transformation of As2S3 to alpha-Ag2S and As-oxides; (ii) S2--ions arising from the degradation of As2S3 are the main responsible for the formation of alpha-Ag2S; (iii) light exposure strengthens the tendency of the paint components towards alteration. Based on our findings, we finally propose a degradation mechanism of As2S3/Ag-0-based tempera paints.

Abstract: A combination of synchrotron radiation (SR) micro X-ray fluorescence (m-XRF) and XRF mode X-ray absorption near edge structure (XANES) measurements at the Cr K-edge already allowed us to establish that the photo-reduction of chromates to Cr(III) compounds is the cause of darkening of chrome yellow pigments (PbCr1-xSxO4, 0 <= x <= 0.8) in a number of paintings by Vincent van Gogh and in corresponding artificially aged paint models. A silicon drift detector (SDD) was employed to record the Cr-K XRF radiation in these X-ray micro beam-based measurements. However, in view of the limited count rate capabilities and collection solid angle of a single device, m-XRF and m-XANES employing single element SDDs (or similar) are primarily suited for collection of spectral data from individual points. Additionally, collection of XRF maps via point-by-point scanning with relatively long dwell times per point is possible but is usually confined to small areas. The development of the 384 silicon-diode array Maia XRF detector has provided valuable solutions in terms of data acquisition rate, allowing for full spectral (FS) XANES imaging in XRF mode, i.e., where spectroscopic information is available at each pixel in the scanned map. In this paper, the possibilities of SR Cr K-edge FS-XANES imaging in XRF mode using the Maia detector are examined as a new data collection strategy to study the speciation and distribution of alteration products of lead chromate-based pigments in painting materials. The results collected from two micro-samples taken from two Van Gogh paintings and an aged paint model show the possibility to perform FS-XANES imaging in practical time frames (from several minutes to a few hours) by scanning regions of sample sizes of the same order (more than 500 mm). The sensitivity and capabilities of FS-XANES imaging in providing representative chemical speciation information at the microscale (spatial resolution from similar to 2 to 0.6 mm) over the entire scanned area are demonstrated by the identification of Cr(OH) 3, Cr(III) sulfates and/or Cr(III) organometallic compounds in the corresponding phase maps, as alteration products. Comparable Cr-speciation results were obtained by performing equivalent higher spatial resolution SR m-XRF/single-point m-XANES analysis using a more conventional SDD from smaller regions of interest of each sample. Thus, large-area XRF mode FS-XANES imaging (Maia detector) is here proposed as a valuable and complementary data collection strategy in relation to “ zoomed-in” high-resolution m-XRF mapping and single-point m-XANES analysis (SDD).

Abstract: The present study analyses a specific laser ablation cell, the High Efficiency Aerosol Dispersion (HEAD) cell (see J. Pisonero et al., J. Anal. At. Spectrom., 2006, 21, 922931), by means of computational fluid dynamics (CFD) simulations. However, this cell consists of different modular parts, therefore, the results are probably of interest for the further development of other ablation cells. In the HEAD cell, the ablation spot is positioned below an orifice in the ceiling of the sample chamber. The particle transport through this orifice has been analysed for a ceiling height of 0.8 mm. The critical velocity for the onset of particle losses was found to be independent on the ejection angle at the crater spot. The deceleration of the particles can be described as the stopping in an effectively steady gas. Particle losses were negligible in this modular part of the cell at the evaluated laser ablation conditions. The transport efficiency through the Venturi chamber was investigated for different sample gas flow rates. In this case, it was found that small particles were predominantly lost at low flow rates, the large particles at higher flow rates. Making use of the simulation results, it was possible to design a modification of the HEAD cell that results in extremely short calculated washout times. The simulations yielded a signal of less than 10 ms, which was produced by more than 99% of the introduced mass.

Abstract: Over the past few years a number of innovative imaging techniques have been introduced for the visualization of hidden paint layers in Old Master Paintings. These include X-ray fluorescence scanning, TeraHertz imaging, optical coherence tomography and other acoustics-based forms of visualization. All of these techniques are usually a trade-off between their penetrative capability on the one side and their analytical precision in terms of spatial resolution and material identification on the other. Here, we present the first-time use of High-Energy X-ray Powder Diffraction imaging (HE-XRPD) in the study of hidden layers in paintings. As an imaging tool, it combines high-depth sensitivity with fingerprint identification of most inorganic painting materials. The potential as well as some limitations of this technique are demonstrated using model paintings as well as an authentic 16th century painting.