Abstract: In the last few decades, nanostructuring has driven significant attention towards the development of novel metallic materials with advanced mechanical properties. Nanocrystalline (nc) metals are a class of nanostructured materials with grain sizes smaller than about 100 nm. These exhibit outstanding mechanical strength and fatigue properties compared to their coarse-grained (cg) counterparts. These are promising candidates for application as structural or functional materials. Nc metals in the form of thin films are employed as hard coatings on bulk components, structural components, and conductive layers in various micro-/nanoscale devices. These structural components and devices are often subjected to cyclic stresses or fatigue loading. Under these cyclic stresses, nc metals tend to exhibit the Bauschinger effect (BE). The strength loss during the BE is of great importance concerning the strength-ductility trade-off in nc metals. Furthermore, contact surfaces of the engineering components in service often undergo relative motion and are subject to both friction and wear. These extreme loading conditions demand nc metals with tailored interfacial characteristics for improved tribological performance. Aiming at ensuring high reliability and mechanical robustness for optimum performance of these components, there has been a strong motivation for understanding the mechanical properties and governing deformation mechanisms in nc metallic materials. This thesis aimed at in-depth investigation of microstructures at micro-/nanoscales using state-of-the-art in situ and ex situ transmission electron microscopy (TEM) to develop a closer link between the deformation structure and underlying deformation mechanisms in some nc metallic materials. The thesis has primarily focused on the in situ TEM nanomechanics of the BE and rotational deformation of grains in nc palladium thin films. A sputtered thin film of nc Pd was deformed inside TEM by cyclic loading-unloading experiments and the evolving microstructure was studied in real-time under different TEM imaging modes. The stress-strain response of the film exhibited a characteristic non-linear unloading behavior confirming the BE in the film. The corresponding bright-field TEM imaging revealed evidence of partially reversible dislocation activity. Towards a quantitative understanding of the deformation structure in real-time, in situ nanomechanical testing was coupled with precession-assisted automated crystal orientation mapping in scanning TEM (ACOM-STEM). Global ACOM-STEM analysis offered crystal orientation of a large number of grains at different states of deformation and confirmed partially reversible rotations of nanosized grains fitting to the observed BE during loading and unloading. Analysis of intragranular rotations showed substantial changes in the sub-structure within most of these grains indicating a dominant role of dislocation-based processes in driving these rotations. Globally, an unusually random evolution of texture was seen that demonstrated the influence of deformation heterogeneity and grain interactions on the resulting texture characteristics in nc metals. In the quest of understanding the grain interactions, local investigations based on annular dark-field STEM imaging during loading-unloading showed reversible changes in the contrast of grains with sets of adjoining grains exhibiting a unique cooperative rotation. Local analysis of the density of geometrically necessary dislocations (GNDs) showed the formation of dislocation pile-up at grain boundaries due to the generation of back-stresses during unloading. Critical observations of the evolution of GND density offered greater insights into the mechanism of cooperative grain rotations and these rotations were related to grain structure and grain boundary characteristics. In addition to understanding the influence of grain structure and grain boundaries, the thesis has further investigated the role of heterointerfaces in sputtered Au-Cu and Cu-Cr nanocrystalline multilayered composites (NMCs) deformed under cyclic sliding contact. The microstructural evolution in the NMCs was investigated at different deformation states by classical TEM imaging, ACOM-STEM as well as energy-filtered TEM (EFTEM). Au-Cu NMC with an initial high density of twin boundaries deformed by stress-driven detwinning with a concurrent change in grain structure in both Au and Cu. The formation of a vortex structure was observed due to plastic flow instabilities at Au-Cu interfaces that led to codeformation and mechanical intermixing. Cu-Cr NMC showed a preferential grain growth in Cu layers whereas no noticeable change in the grain sizes was seen in Cr layers. The phase maps revealed sharp interfaces between Cu and Cr layers indicating no intermixing between the immiscible phases. EFTEM results exposed the cracking processes in Cr layers with a concurrent migration of Cu in the cracks. Overall, the thesis has attempted to analyze the competing deformation processes and relate these with the microstructural heterogeneity in terms of grain structure and GB and interfacial characteristics in nc metallic materials.

Abstract: We report on cooperative grain rotation accompanied by a strong Bauschinger effect in nanocrystalline (nc) palladium thin film. A thin film of nc Pd was subjected to cyclic loading-unloading using in situ TEM nanomechanics, and the evolving microstructural characteristics were investigated with ADF-STEM imaging and quantitative ACOM-STEM analysis. ADF-STEM imaging revealed a partially reversible rotation of nanosized grains with a strong out-of-plane component during cyclic loading-unloading experiments. Sets of neighboring grains were shown to rotate cooperatively, one after the other, with increasing/decreasing strain. ACOM-STEM in conjunction with these experiments provided information on the crystallographic orientation of the rotating grains at different strain levels. Local Nye tensor analysis showed significantly different geometrically necessary dislocation (GND) density evolution within grains in close proximity, confirming a locally heterogeneous deformation response. The GND density analysis revealed the formation of dislocation pile-ups at grain boundaries (GBs), indicating the generation of back stresses during unloading. A statistical analysis of the orientation changes of individual grains showed the rotation of most grains without global texture development, which fits to both dislocation- and GB sliding-based mechanisms. Overall, our quantitative in situ experimental approach explores the roles of these different deformation mechanisms operating in nanocrystalline metals during cyclic loading.

Abstract: Singlet molecular oxygen (1O2) has continuously attracted researchers' interest because of its involvement in various processes, such as in photodynamic reactions in biological and chemical systems. 1O2 is an effective electrophile and potent oxidizing agent and can be easily generated by photosensitization via the illumination of organic dyes with visible light. As described in Chapter 1, 1O2 has gained prominence in various applications such as wastewater treatment, photodynamic therapy of cancer, organic synthesis, and recently developed 1O2-based photoelectrochemical (PEC) sensing of phenolic compounds. Phenolic compounds are a potential source of contaminants that originates from industrial effluents and waste products of chemical and pharmaceutical industries. These phenolic compounds pose severe threats to humans and aquatic life after reaching the environment. Therefore, it is imperative to develop photoactive materials that efficiently generate 1O2 and oxidize phenolic compounds and antibiotics. The existing 1O2 generating photosensitizers (PSs) include porphyrins, phthalocyanines (Pcs), subphthalocyanines (SubPcs), and other dyes such as derivatives of xanthene (e.g., Rose Bengal (RB)), and fluorinated boron-dipyrromethene (BODIPYs), and phenothiazinium dyes (e. g. Methylene Blue (MB)) which display long-lived triplet excited state and can be used in 1O2-based applications. This thesis focuses on preparing efficient hybrid materials based on newly synthesized Pcs, different surface area titanium dioxide (TiO2) and plasmonic gold nanoparticles (AuNPs) for their use in the PEC detection of phenolic compounds. The first focus was on developing a fast amperometric method to test the photo-electrocatalytic activity of 1O2 producing PSs dissolved in MeOH based on the redox cycling of an electroactive phenolic compound, hydroquinone (HQ) (Chapter 2). This method of testing PSs does not require the accumulation of a reaction product since the amperometric signal develops near instantly when the light is on, which enables dynamic monitoring of a PSs activity at varying conditions in a single experiment. This method was crucial to measure high 1O2 quantum yield and low yield in the same experimental conditions. Moreover, the obtained results revealed a range of working parameters affecting the PEC activity of PSs. The next goal was to immobilize tert-butyl substituted aluminum Pc (t-BuPcAlCl) on the solid support, which showed a high 1O2 quantum yield. However, before immobilizing Pc on a solid support such as TiO2, it is essential to know the electronic energy level of Pcs for the possible electron transfers from Pcs to TiO2. Therefore, Chapter 3 explored the (spectro)electrochemical properties of t-BuPcAlCl Pc. Next, in Chapter 4, t-BuPcAlCl Pc and other tert-butyl substituted Pcs with Zn central metal, t-BuPcZn, and its metal-free derivative t-BuPcH2 were immobilized on different surface area TiO2. The PEC activity of immobilized Pcs on TiO2 toward different phenols and antibiotics was studied, and the action mechanism was revealed and compared with sterically hindered fluorinated Pc F64PcZn. In the final part of this thesis plasmonic AuNPs were introduced combined with trimethylsilane-protected acetylene functionalized ZnPc (TMSZnPc) to study the synergistic effect that boosts the overall activity toward the detection of phenols under visible light illumination (Chapter 5) . The TMSZnPc was coupled with AuNPs via a click chemistry approach. The 1O2 quantum yield of TMSZnPc improved significantly after conjugating with AuNPs, and, subsequently, the PEC activity for detecting HQ. The theoretical and experimental investigation demonstrated that the plasmonic enhancement of TMSZnPc is driven by the near-field mechanism. This shows the importance of plasmonic AuNPs with other photoactive species for their use in 1O2-based applications. The fundamental knowledge obtained in this doctoral study will ultimately deepen the understanding of developing 1O2-based PEC sensors for detecting phenolic compounds and pharmaceuticals in the wastewater stream, helping to choose efficient materials and, in the last instance, a more sustainable future especially access to clean water for everyone.

Abstract: Dye-sensitized TiO(2 )has found many applications for dye sensitized solar cells (DSSC), solar-to-chemical energy conversion, water/air purification systems, and (electro)chemical sensors. We report an electrochemical system for testing dye-sensitized materials that can be utilized in photoelectrochemical (PEC) sensors and energy conversion. Unlike related systems, the reported system does not require a direct electron transfer from semiconductors to electrodes. Rather, it relies on electron shuttling by redox mediators. A range of model photocatalytic materials were prepared using three different TiO2 materials (P25, P90, and PC500) and three sterically hindered phthalocyanines (Pcs) with electron-rich tert-butyl substituents (t-Bu4PcZn, t-Bu4PcAlCl, and t-Bu4PcH2). The materials were compared with previously developed TiO(2 )modified by electron-deficient, also sterically hindered fluorinated phthalocyanine F64PcZn, a singlet oxygen (O-1(2)) producer, as well as its metal-free derivative, F64PcH2. The PEC activity depended on the redox mediator, as well as the type of TiO2 and Pc. By comparing the responses of one-electron shuttles, such as K4Fe(CN)(4), and O-1(2)-reactive electron shuttles, such as phenol, it is possible to reveal the action mechanism of the supported photosensitizers, while the overall activity can be assessed using hydroquinone. t-Bu4PcAlCl showed significantly lower blank responses and higher specific responses toward chlorophenols compared to t-Bu4PcZn due to the electron-withdrawing effect of the Al3+ metal center. The combination of reactivity insights and the need for only microgram amounts of sensing materials renders the reported system advantageous for practical applications.

Abstract: Anew recycling process, according to the zero-waste concept, was investigated for an iron rich waste stream, more specifically a secondary lead smelting matte. The process consists of a selective citrate leaching of Pb, Cu, Ni and Zn in combination with a roasting step, leading to a simultaneous recovery of hematite as a secondary iron resource. The parameters, such as leaching time, leaching temperature, H2O2 concentration and roasting temperature, were experimentally optimized. The maximum Pb leaching efficiency was 93% and the leachability of Cu (33%) and Zn (11%) increased slightly in the presence of 0.5 M H2O2 in 1 M citrate at 25 degrees C and pH 5.5. Importantly, almost no Fe was leached (< 0.6%) from the iron rich matrix material at this condition allowing for a maximal recovery of hematite as a secondary resource after further treatment (i.e. roasting or sulfur removal). The leachability of Pb, Cu, Ni and Zn was strongly affected by the roasting temperature. Maximum leaching efficiency in 1 M citrate (25 degrees C, L/S ratio 10, pH 6.5) was 93% for Pb, 80% for Cu and 60% for Zn at a roasting temperature of 600 degrees C, while for Ni the maximum leaching efficiency of 53% was reached after roasting at 650 degrees C. Furthermore, when oxidative roasting was applied, the leaching residue consists dominantly of hematite (Fe2O3) with minor quantities of PbSO4, which can be used as pig iron ore (Fe > 60 wt%). (C) 2017 Elsevier B.V. All rights reserved.

Abstract: Two routes were investigated to selectively recover lead and minor metals (Cu, Ni, Zn) from a sulfide-rich lead smelter residue, matte. The first route comprises a two-step leaching process that combines Fe(III)-HNO3 leaching with roasting, followed by water leaching. In the first step, the efficiency of Pb leaching was 90% at the optimum condition (L/S ratio 8, 0.5 mol.L-1 HNO3, 0.15 mol.L-1 Fe(III), 25 degrees C). In the second step, roasting at 600 degrees C followed by water leaching at 50 degrees C selectively leached Ni, Cu, and Zn while fully converting iron sulfides to oxides. One-step oxidative pressure leaching in HNO3 was investigated as an alternative to simultaneously leach Pb, Cu, Ni and Zn. At the optimal conditions (130 degrees C, 60 min, 0.3 mol.L-1 HNO3, 0.07 mol.L-1 Fe(III), L/S ratio 20), Pb, Cu, Zn and Ni leaching were 92, 60, 70 and 66%, respectively, while Fe leaching remained low (2%). The leachates obtained from both leaching routes were treated by ion-exchange adsorption with diethylenetriaminepentaacetic acid (DTPA) functionalized chitosan-silica hybrid materials to investigate the selective recovery of Cu, Zn and Ni. The adsorption order appeared to be in the same order as the corresponding stability constants for complexes between the respective metal ions and free DTPA: Ca(II) < Zn(II) < Pb (II) approximate to Ni(II) < Cu(II). This allows not only to selectively recover Cu, Zn and Ni from the leachates, but also to mutually separate them by using the functionalized resin as a stationary phase in column chromatography. To avoid adsorbent contamination, Fe(III) and Pb(II) may be removed from the leachates in a pre-treatment step. Based on these results, the investigated methods can be combined as process steps of two possible routes for the selective recovery of valuable metals from the studied secondary lead smelting residue. The two-step leaching process seems to be superior since a more concentrated solution of Cu, Ni, and Zn is produced in the 2nd leaching step with low capital cost.

Abstract: This study focuses on the recycling of stainless steel (SS) slags containing about 1.2 wt% of chromium (Cr). The selective recovery of Cr from SS slag by a hydrometallurgical method (alkaline pressure leaching) was investigated. Leaching experiments were carried out based on 2(4-1) factorial design of experiment (DOE) with the following parameters: NaOH concentration, temperature, leaching time, and mechanical activation (MA). Results show that temperature and MA are the most influencing factors for an enhanced Cr leaching. The maximum Cr leaching was 46% at 1 M NaOH, 240 degrees C, 6 h, MA 30 min, while the matrix material was dissolved only to a limited extent (Al 2.88%, Si 0.12%, Ca 0.05%). After Cr leaching followed by alkali washing, a carbonation treatment is proposed to stabilize the remaining Cr in the matrix material and make the subsequent recycling of the matrix material as a construction material possible. (C) 2016 Elsevier Ltd. All rights reserved.

Abstract: During the conservation treatment of Memling’s Christ with Singing and Music-making Angels, three panel paintings that are among the most monumental works in early Netherlandish art, the conservators came across insoluble surface layers containing calcium oxalates. A very thin and irregular layer of this type, hardly visible to the naked eye, was spread across the surface of all three panels. A much thicker layer forming an opaque and highly disfiguring crust that obscured the composition (Figs. 15.1 and 15.7) was locally present on areas of dark copper-containing paint, where multiple layers of old discolored coatings and accretions remained in place before the most recent cleaning. This article describes the application of a wide range of analytical techniques in order to fully understand the stratigraphy and composition of the crusts on the Memling paintings. FTIR spectroscopy in transmission and reflection mode, micro-ATR-FTIR imaging and macro-rFTIR scanning, SEM-EDX, mobile XRD, and SR-μXRD showed that the crusts contained two related Ca-based oxalate salts, whewellite and weddellite, and were separated from the original paint surface by varnish, indicating that they did not originate from degradation of the original paint but from a combination of microbial action and a thick accumulation of dirt. Supported by the results from these different analytical techniques, which when used together proved to be very effective in providing complementary information that addressed this specific conservation problem, and aided by the presence of the intermediate varnish layer(s), the conservators were able to remove most of the crusts with spectacular results.