“Influence of artificial pinning centers on structural and superconducting properties of thick YBCO films on ABAD-YSZ templates”. Pahlke P, Sieger M, Ottolinger R, Lao M, Eisterer M, Meledin A, Van Tendeloo G, Haenisch J, Holzapfel B, Schultz L, Nielsch K, Huehne R, Superconductor science and technology 31, 044007 (2018). http://doi.org/10.1088/1361-6668/AAAFBE
Abstract: Recent efforts in the development of YBa2Cu3O7-x (YBCO) coated conductors are devoted to the increase of the critical current I-c in magnetic fields. This is typically realized by growing thicker YBCO layers as well as by the incorporation of artificial pinning centers. We studied the growth of doped YBCO layers with a thickness of up to 7 mu m using pulsed laser deposition with a growth rate of about 1.2 nm s(-1). Industrially fabricated ion-beam textured YSZ templates based on metal tapes were used as substrates for this study. The incorporation of BaHfO3 (BHO) or Ba2Y(Nb0.5Ta0.5)O-6 (BYNTO) secondary phase additions leads to a denser microstructure compared to undoped films. A purely c-axis-oriented YBCO growth is preserved up to a thickness of about 4 mu m, whereas misoriented texture components were observed in thicker films. The critical temperature is slightly reduced compared to undoped films and independent of film thickness. The critical current density J(c) of the BHO- and BYNTO-doped YBCO layers is lower at 77 K and self-field compared to pure YBCO layers; however, I-c increases up to a thickness of 5 mu m. A comparison between films with a thickness of 1.3 mu m revealed that the anisotropy of the critical current density J(c)(theta) strongly depends on the incorporated pinning centers. Whereas BHO nanorods lead to a strong B vertical bar vertical bar c-axis peak, the overall anisotropy is significantly reduced by the incorporation of BYNTO forming a mixture of short c-axis-oriented nanorods and small (a-b)-oriented platelets. As a result, the J(c) values of the doped films outperform the undoped samples at higher fields and lower temperatures for most magnetic field directions.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.878
Times cited: 9
DOI: 10.1088/1361-6668/AAAFBE
|
|
|
“Microstructure of YBa2Cu3O7-x films on buffered Si for microelectronic applications”. Vasiliev AL, Van Tendeloo G, Boikov Y, Olsson E, Ivanov S, Superconductor science and technology 10, 356 (1997)
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.878
Times cited: 2
|
|
|
“Microstructure of YBa2Cu3O7-\delta Josephson junctions in relation to their properties”. Verbist K, Lebedev OI, Verhoeven MAJ, Winchern R, Rijnders AJHM, Blank DHA, Tafuri F, Bender H, Van Tendeloo G, Superconductor science and technology 11, 13 (1998). http://doi.org/10.1088/0953-2048/11/1/004
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.878
DOI: 10.1088/0953-2048/11/1/004
|
|
|
“YBa2Cu3O7-x Josephson junctions and dc SQUIDs based on 45\text{\textdegree} a-axis tilt and twist grain boundaries : atomically clean interfaces for applications”. Tafuri F, Carillo F, Lombardi F, Granozio FM, dii Uccio US, Testa G, Sarnelli E, Verbist K, Van Tendeloo G, Superconductor science and technology
T2 –, International Superconductive Electronics Conference, JUN 21-25, 1999, BERKELEY, CALIFORNIA 12, 1007 (1999). http://doi.org/10.1088/0953-2048/12/11/393
Abstract: YBa2Cu3O7-x artificial grain boundary Josephson junctions have been fabricated, employing a recently implemented biepitaxial technique. The grain boundaries can be obtained by controlling the orientation of the MgO seed layer and are characterized by a misalignment of the c-axes (45 degrees a-axis tilt or 45 degrees a-axis twist). These types of grain boundaries are still mostly unexplored. We carried out a complete characterization of their transport properties and microstructure. Junctions and de SQUIDs associated with these grain boundaries exhibit an excellent Josephson phenomenology and high values of the ICRN product and of the magnetic flux-to-voltage transfer parameter respectively. Remarkable differences in the transport parameters of tilt and twist junctions have been observed, which can be of interest for several applications. A maximum speed of Josephson vortices as calculated from the voltage step values of the order of 2 x 10(6) m s(-1) is obtained. These devices could also have some impact on experiments designed to study the symmetry of the order parameter, exploiting their microstructure and anisotropic properties. High-resolution electron microscopy showed the presence of perfect basal plane faced boundaries in the cross sections of tilt boundaries.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.878
Times cited: 3
DOI: 10.1088/0953-2048/12/11/393
|
|
|
“Chemical solution deposition: a path towards low cost coated conductors”. Obradors X, Puig T, Pomar A, Sandiumenge F, Piñol S, Mestres N, Castaño O, Coll M, Cavallaro A, Palau A, Gázquez J, González JC, Gutiérrez J, Romá, N, Ricart S, Moretó, JM, Rossell MD, Van Tendeloo G, Superconductor science and technology 17, 1055 (2004). http://doi.org/10.1088/0953-2048/17/8/020
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.878
Times cited: 107
DOI: 10.1088/0953-2048/17/8/020
|
|
|
“The superstructure and superconductivity of Ru1222 based RuSr2Gd2-x-yYyCexCu2O10-\delta compounds”. Tan H, Lebedev OI, McLaughlin AC, Van Tendeloo G, Superconductor science and technology 23, 115013 (2010). http://doi.org/10.1088/0953-2048/23/11/115013
Abstract: For the first time, the local structure and physical properties of Ru1222 based compounds (RuSr(2)Gd(1.4)Ce(0.6)Cu(2)O(10-delta) and RuSr(2)Gd(1.8-x)Y(0.2)CexCu(2)O(10) (x = 0.90-0.55)) have been investigated and analyzed together on the very same compounds. The Ru1222 superstructure was confirmed by TEM at a local scale and was suggested to have an orthorhombic symmetry with space group Aba2 and lattice parameters a(s) similar or equal to root 2a, b(s) similar or equal to root 2a and c(s) = c. This new Ru1222 superstructure distortion from tetragonal symmetry is proposed to have a positive correlation with the superconductivity variation of these compounds. The more the distortion towards orthorhombic symmetry, the higher the critical superconducting temperature these compounds can achieve. The T(c)(0) of RuSr(2)Gd(1.8-x)Y(0.2)Ce(x)Cu(2)O(10-delta) (x = 0.85-0.55) increases monotonically from 4 to 16 K when x decreases from 0.85 to 0.70, then RuSr(2)Gd(2)Cu(2)O(8) defects emerge and the T(c) decreases with decreasing x. Ru1212 defects are observed to intergrow epitaxially with the Ru1222 structure as lamellas along the c-axis in RuSr(2)Gd(1.4)Ce(0.6)Cu(2)O(10-delta). Although Ru1212 is a superconductor, the intergrowth severely restrains its superconductivity.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.878
Times cited: 1
DOI: 10.1088/0953-2048/23/11/115013
|
|
|
“Barrier efficiency of sponge-like La2Zr2O7 buffer layers for YBCO-coated conductors”. Molina L, Tan H, Biermans E, Batenburg KJ, Verbeeck J, Bals S, Van Tendeloo G, Superconductor science and technology 24, 065019 (2011). http://doi.org/10.1088/0953-2048/24/6/065019
Abstract: Solution derived La2Zr2O7 films have drawn much attention for potential applications as thermal barriers or low-cost buffer layers for coated conductor technology. Annealing and coating parameters strongly affect the microstructure of La2Zr2O7, but different film processing methods can yield similar microstructural features such as nanovoids and nanometer-sized La2Zr2O7 grains. Nanoporosity is a typical feature found in such films and the implications for the functionality of the films are investigated by a combination of scanning transmission electron microscopy (STEM), electron energy-loss spectroscopy (EELS) and quantitative electron tomography. Chemical solution based La2Zr2O7 films deposited on flexible Ni5 at.%W substrates with a {100}lang001rang biaxial texture were prepared for an in-depth characterization. A sponge-like structure composed of nanometer-sized voids is revealed by high-angle annular dark-field scanning transmission electron microscopy in combination with electron tomography. A three-dimensional quantification of nanovoids in the La2Zr2O7 film is obtained on a local scale. Mostly non-interconnected highly faceted nanovoids compromise more than one-fifth of the investigated sample volume. The diffusion barrier efficiency of a 170 nm thick La2Zr2O7 film is investigated by STEM-EELS, yielding a 1.8 ± 0.2 nm oxide layer beyond which no significant nickel diffusion can be detected and intermixing is observed. This is of particular significance for the functionality of YBa2Cu3O7 − δ coated conductor architectures based on solution derived La2Zr2O7 films as diffusion barriers.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT); Vision lab
Impact Factor: 2.878
Times cited: 31
DOI: 10.1088/0953-2048/24/6/065019
|
|
|
“Interlayer structure in YBCO-coated conductors prepared by chemical solution deposition”. Molina L, Egoavil R, Turner S, Thersleff T, Verbeeck J, Holzapfel B, Eibl O, Van Tendeloo G, Superconductor science and technology 26, 075016 (2013). http://doi.org/10.1088/0953-2048/26/7/075016
Abstract: The functionality of YBa2Cu3O7−δ (YBCO)-coated conductor technology depends on the reliability and microstructural properties of a given tape or wire architecture. Particularly, the interface to the metal tape is of interest since it determines the adhesion, mechanical stability of the film and thermal contact of the film to the substrate. A trifluoroacetate (TFA)metal organic deposition (MOD) prepared YBCO film deposited on a chemical solution-derived buffer layer architecture based on CeO2/La2Zr2O7 and grown on a flexible Ni5 at.%W substrate with a {100}⟨001⟩ biaxial texture was investigated. The YBCO film had a thickness was 440 nm and a jc of 1.02 MA cm−2 was determined at 77 K and zero external field. We present a sub-nanoscale analysis of a fully processed solution-derived YBCO-coated conductor by aberration-corrected scanning transmission electron microscopy (STEM) combined with electron energy-loss spectroscopy (EELS). For the first time, structural and chemical analysis of the valence has been carried out on the sub-nm scale. Intermixing of Ni, La, Ce, O and Ba takes place at these interfaces and gives rise to nanometer-sized interlayers which are a by-product of the sequential annealing process. Two distinct interfacial regions were analyzed in detail: (i) the YBCO/CeO2/La2Zr2O7 region (10 nm interlayer) and (ii) the La2Zr2O7/Ni5 at.%W substrate interface region (20 nm NiO). This is of particular significance for the functionality of these YBCO-coated conductor architectures grown by chemical solution deposition.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.878
Times cited: 11
DOI: 10.1088/0953-2048/26/7/075016
|
|
|
“Epitaxial YBa2Cu3O7−xnanocomposite thin films from colloidal solutions”. Cayado P, De Keukeleere K, Garzón A, Perez-Mirabet L, Meledin A, De Roo J, Vallés F, Mundet B, Rijckaert H, Pollefeyt G, Coll M, Ricart S, Palau A, Gázquez J, Ros J, Van Tendeloo G, Van Driessche I, Puig T, Obradors X, Superconductor science and technology 28, 124007 (2015). http://doi.org/10.1088/0953-2048/28/12/124007
Abstract: A methodology of general validity to prepare epitaxial nanocomposite films based on the use of colloidal solutions containing different crystalline preformed oxide nanoparticles ( ex situ nanocomposites) is reported. The trifluoroacetate (TFA) metal–organic chemical solution deposition route is used with alcoholic solvents to grow epitaxial YBa 2 Cu 3 O 7 (YBCO) films. For this reason stabilizing oxide nanoparticles in polar solvents is a challenging goal. We have used scalable nanoparticle synthetic methodologies such as thermal and microwave-assisted solvothermal techniques to prepare CeO 2 and ZrO 2 nanoparticles. We show that stable and homogeneous colloidal solutions with these nanoparticles can be reached using benzyl alcohol, triethyleneglycol, nonanoic acid, trifluoroacetic acid or decanoic acid as protecting ligands, thereby allowing subsequent mixing with alcoholic TFA solutions. An elaborate YBCO film growth analysis of these nanocomposites allows the identification of the different relevant growth phenomena, e.g. nanoparticles pushing towards the film surface, nanoparticle reactivity, coarsening and nanoparticle accumulation at the substrate interface. Upon mitigation of these effects, YBCO nanocomposite films with high self-field critical currents ( J c ∼ 3–4 MA cm −2 at 77 K) were reached, indicating no current limitation effects associated with epitaxy perturbation, while smoothed magnetic field dependences of the critical currents at high magnetic fields and decreased effective anisotropic pinning behavior confirm the effectiveness of the novel developed approach to enhance vortex pinning. In conclusion, a novel low cost solution-derived route to high current nanocomposite superconducting films and coated conductors has been developed with very promising features.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.878
Times cited: 32
DOI: 10.1088/0953-2048/28/12/124007
|
|
|
“Atomic and electronic structures of BaHfO3-doped TFA-MOD-derived YBa2Cu3O7−δthin films”. Molina-Luna L, Duerrschnabel M, Turner S, Erbe M, Martinez GT, Van Aert S, Holzapfel B, Van Tendeloo G, Superconductor science and technology 28, 115009 (2015). http://doi.org/10.1088/0953-2048/28/11/115009
Abstract: Tailoring the properties of oxide-based nanocomposites is of great importance for a wide range of materials relevant for energy technology. YBa2Cu3O7−δ (YBCO) superconducting thin films containing nanosized BaHfO3 (BHO) particles yield a significant improvement of the magnetic flux pinning properties and a reduced anisotropy of the critical current density. These films were prepared by chemical solution deposition (CSD) on (100) SrTiO3 (STO) substrates yielding critical current densities up to 3.6 MA cm−2 at 77 K and self-field. Transport in-field J c measurements demonstrated a high pinning force maximum of around 6 GN/m3 for a sample annealed at T = 760 °C that has a doping of 12 mol% of BHO. This sample was investigated by scanning transmission electron microscopy (STEM) in combination with electron energy-loss spectroscopy (EELS) yielding strain and spectral maps. Spherical BHO nanoparticles of 15 nm in size were found in the matrix, whereas the particles at the interface were flat. A 2 nm diffusion layer containing Ti was found at the YBCO (BHO)/STO interface. Local lattice deformation mapping at the atomic scale revealed crystal defects induced by the presence of both sorts of BHO nanoparticles, which can act as pinning centers for magnetic flux lines. Two types of local lattice defects were identified and imaged: (i) misfit edge dislocations and (ii) Ba-Cu-Cu-Ba stacking faults (Y-248 intergrowths). The local electronic structure and charge transfer were probed by high energy resolution monochromated electron energy-loss spectroscopy. This technique made it possible to distinguish superconducting from non-superconducting areas in nanocomposite samples with atomic resolution in real space, allowing the identification of local pinning sites on the order of the coherence length of YBCO (~1.5 nm) and the determination of 0.25 nm dislocation cores.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.878
Times cited: 4
DOI: 10.1088/0953-2048/28/11/115009
|
|
|
“BaHfO3artificial pinning centres in TFA-MOD-derived YBCO and GdBCO thin films”. Erbe M, Hänisch J, Hühne R, Freudenberg T, Kirchner A, Molina-Luna L, Damm C, Van Tendeloo G, Kaskel S, Schultz L, Holzapfel B, Superconductor science and technology 28, 114002 (2015). http://doi.org/10.1088/0953-2048/28/11/114002
Abstract: Chemical solution deposition (CSD) is a promising way to realize REBa2Cu3O7−x (REBCO;RE = rare earth (here Y, Gd))-coated conductors with high performance in applied magnetic fields. However, the preparation process contains numerous parameters which need to be tuned to achieve high-quality films. Therefore, we investigated the growth of REBCO thin films containing nanometre-scale BaHfO3 (BHO) particles as pinning centres for magnetic flux lines, with emphasis on the influence of crystallization temperature and substrate on the microstructure and superconductivity. Conductivity, microscopy and x-ray investigations show an enhanced performance of BHO nano-composites in comparison to pristine REBCO. Further, those measurements reveal the superiority of GdBCO to YBCO—e.g. by inductive critical current densities, Jc, at self-field and 77 K. YBCO is outperformed by more than 1 MA cm−2 with Jc values of up to 5.0 MA cm−2 for 265 nm thick layers of GdBCO(BHO) on lanthanum aluminate. Transport in-field Jc measurements demonstrate high pinning force maxima of around 4 GN m−3 for YBCO(BHO) and GdBCO(BHO). However, the irreversibility fields are appreciably higher for GdBCO. The critical temperature was not significantly reduced upon BHO addition to both YBCO and GdBCO, indicating a low tendency for Hf diffusion into the REBCO matrix. Angular-dependent Jc measurements show a reduction of the anisotropy in the same order of magnitude for both REBCO compounds. Theoretical models suggest that more than one sort of pinning centre is active in all CSD films.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.878
Times cited: 36
DOI: 10.1088/0953-2048/28/11/114002
|
|
|
“Novel poly(butylene succinate) nanocomposites containing strontium hydroxyapatite nanorods with enhanced osteoconductivity for tissue engineering applications”. Nerantzaki M, Filippousi M, Van Tendeloo G, Terzopoulou Z, Bikiaris D, Goudouri OM, Detsch R, Grueenewald A, Boccaccini AR, Express polymer letters 9, 773 (2015). http://doi.org/10.3144/expresspolymlett.2015.73
Abstract: Three series of poly(butylene succinate) (PBSu) nanocomposites containing 0.5, 1 and 2.5 wt% strontium hydroxyapatite [Sr-5(PO4)(3)OH] nanorods (SrHAp nrds) were prepared by in situ polymerisation. The structural effects of Sr-5(PO4)(3)OH nanorods, for the different concentrations, inside the polymeric matrix (PBSu), were studied through high angle annular dark field scanning transmission electron microscopy (HAADF-STEM). HAADF-STEM measurements revealed that the SrHAp nanorods at low concentrations are dispersed inside the polymeric PBSu matrix while in 1 wt% some aggregates are formed. These aggregations affect the mechanical properties giving an enhancement for the concentration of 0.5 wt% SrHAp nrds in tensile strength, while a reduction is recorded for higher loadings of the nanofiller. Studies on enzymatic hydrolysis revealed that all nanocomposites present higher hydrolysis rates than neat PBSu, indicating that nanorods accelerate the hydrolysis degradation process. In vitro bioactivity tests prove that SrHAp nrds promote the formation of hydroxyapatite on the PBSu surface. All nanocomposites were tested also in relevant cell culture using osteoblast-like cells (MG-63) to demonstrate their biocompatibility showing SrHAp nanorods support cell attachment.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.983
Times cited: 21
DOI: 10.3144/expresspolymlett.2015.73
|
|
|
“Texturing of hydrothermally synthesized BaTiO3 in a strong magnetic field by slip casting”. Özen M, Mertens M, Snijkers F, Van Tendeloo G, Cool P, Ceramics international 42, 5382 (2016). http://doi.org/10.1016/j.ceramint.2015.12.073
Abstract: Barium titanate powder was processed by slip casting in a rotating strong magnetic field of 9.4 T. The orientation factor of the sintered compact was analyzed by the X-ray diffraction technique and the microstructure (grain-size) was analyzed by scanning electron microscope. The hydrothermally prepared barium titanate was used as matrix material and the molten-salt synthesized barium titanate, with a larger particle-size, was used as template for the templated grain-growth process. Addition of large template particles was observed to increase the orientation factor of the sintered cast (5 vol% loading). Template particles acted as starting grains for the abnormal grain-growth process and the average grain-size was increased after sintering. Increasing the solid loading (15 vol%) resulted in a similar orientation factor with a decrease of the average grain size by more than half. However, addition of templates to the 15 vol% cast had a negative effect on the orientation factor. The impingement of growing particles was stated as the primary cause of particle misorientation resulting in a low orientation factor after sintering. Different heating conditions were tested and it was determined that a slow heating rate gave the highest orientation factor, the smallest average grain-size and the highest relative density. (C) 2015 Elsevier Ltd and Techna Group S.r.l. All rights reserved.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT); Laboratory of adsorption and catalysis (LADCA)
Impact Factor: 2.986
Times cited: 11
DOI: 10.1016/j.ceramint.2015.12.073
|
|
|
“Unprecedented and highly stable lithium storage capacity of (001) faceted nanosheet-constructed hierarchically porous TiO₂/rGO hybrid architecture for high-performance Li-ion batteries”. Yu W-B, Hu Z-Y, Jin J, Yi M, Yan M, Li Y, Wang H-E, Gao H-X, Mai L-Q, Hasan T, Xu B-X, Peng D-L, Van Tendeloo G, Su B-L, National Science Review 7, 1046 (2020). http://doi.org/10.1093/NSR/NWAA028
Abstract: Active crystal facets can generate special properties for various applications. Herein, we report a (001) faceted nanosheet-constructed hierarchically porous TiO2/rGO hybrid architecture with unprecedented and highly stable lithium storage performance. Density functional theory calculations show that the (001) faceted TiO2 nanosheets enable enhanced reaction kinetics by reinforcing their contact with the electrolyte and shortening the path length of Li+ diffusion and insertion-extraction. The reduced graphene oxide (rGO) nanosheets in this TiO2/rGO hybrid largely improve charge transport, while the porous hierarchy at different length scales favors continuous electrolyte permeation and accommodates volume change. This hierarchically porous TiO2/rGO hybrid anode material demonstrates an excellent reversible capacity of 250 mAh g(-1) at 1 C (1 C = 335 mA g(-1)) at a voltage window of 1.0-3.0 V. Even after 1000 cycles at 5 C and 500 cycles at 10 C, the anode retains exceptional and stable capacities of 176 and 160 mAh g(-1), respectively. Moreover, the formed Li2Ti2O4 nanodots facilitate reversed Li+ insertion-extraction during the cycling process. The above results indicate the best performance of TiO2-based materials as anodes for lithium-ion batteries reported in the literature.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 20.6
Times cited: 3
DOI: 10.1093/NSR/NWAA028
|
|
|
“Magnetic monopole field exposed by electrons”. Béché, A, Van Boxem R, Van Tendeloo G, Verbeeck J, Nature physics 10, 26 (2014). http://doi.org/10.1038/NPHYS2816
Abstract: The experimental search for magnetic monopole particles(1-3) has, so far, been in vain. Nevertheless, these elusive particles of magnetic charge have fuelled a rich field of theoretical study(4-10). Here, we created an approximation of a magnetic monopole in free space at the end of a long, nanoscopically thin magnetic needle(11). We experimentally demonstrate that the interaction of this approximate magnetic monopole field with a beam of electrons produces an electron vortex state, as theoretically predicted for a true magnetic monopole(3,11-18). This fundamental quantum mechanical scattering experiment is independent of the speed of the electrons and has consequences for all situations where electrons meet such monopole magnetic fields, as, for example, in solids. The set-up not only shows an attractive way to produce electron vortex states but also provides a unique insight into monopole fields and shows that electron vortices might well occur in unexplored solid-state physics situations.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 22.806
Times cited: 131
DOI: 10.1038/NPHYS2816
|
|
|
“Unveiling the intrinsic structure and intragrain defects of organic-inorganic hybrid perovskites by ultralow dose transmission electron microscopy”. Yang C-Q, Zhi R, Rothmann MU, Xu Y-Y, Li L-Q, Hu Z-Y, Pang S, Cheng Y-B, Van Tendeloo G, Li W, Advanced materials , 1 (2023). http://doi.org/10.1002/ADMA.202211207
Abstract: Transmission electron microscopy (TEM) is a powerful tool for unveiling the structural, compositional, and electronic properties of organic-inorganic hybrid perovskites (OIHPs) at the atomic to micrometer length scales. However, the structural and compositional instability of OIHPs under electron beam radiation results in misunderstandings of the microscopic structure-property-performance relationship in OIHP devices. Here, ultralow dose TEM is utilized to identify the mechanism of the electron-beam-induced changes in OHIPs and clarify the cumulative electron dose thresholds (critical dose) of different commercially interesting state-of-the-art OIHPs, including methylammonium lead iodide (MAPbI(3)), formamidinium lead iodide (FAPbI(3)), FA(0.83)Cs(0.17)PbI(3), FA(0.15)Cs(0.85)PbI(3), and MAPb(0.5)Sn(0.5)I(3). The critical dose is related to the composition of the OIHPs, with FA(0.15)Cs(0.85)PbI(3) having the highest critical dose of approximate to 84 e angstrom(-2) and FA(0.83)Cs(0.17)PbI(3) having the lowest critical dose of approximate to 4.2 e angstrom(-2). The electron beam irradiation results in the formation of a superstructure with ordered I and FA vacancies along (c), as identified from the three major crystal axes in cubic FAPbI(3), (c), (c), and (c). The intragrain planar defects in FAPbI(3) are stable, while an obvious modification is observed in FA(0.83)Cs(0.17)PbI(3) under continuous electron beam exposure. This information can serve as a guide for ensuring a reliable understanding of the microstructure of OIHP optoelectronic devices by TEM.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 29.4
DOI: 10.1002/ADMA.202211207
|
|
|
“Substitutional phosphorus incorporation in nanocrystalline CVD diamond thin films”. Janssen W, Turner S, Sakr G, Jomard F, Barjon J, Degutis G, Lu YG, D'Haen J, Hardy A, Bael MV, Verbeeck J, Van Tendeloo G, Haenen K, Physica status solidi: rapid research letters 8, 705 (2014). http://doi.org/10.1002/pssr.201409235
Abstract: Nanocrystalline diamond (NCD) thin films were produced by chemical vapor deposition (CVD) and doped by the addition of phosphine to the gas mixture. The characterization of the films focused on probing the incorporation and distribution of the phosphorus (P) dopants. Electron microscopy evaluated the overall film morphology and revealed the interior structure of the nanosized grains. The homogeneous films with distinct diamond grains featured a notably low sp(2):sp(3)-ratio as confirmed by Raman spectroscopy. High resolution spectroscopy methods demonstrated a homogeneous P-incorporation, both in-depth and in-plane. The P concentration in the films was determined to be in the order of 10(19) cm(-3) with a significant fraction integrated at substitutional donor sites. (C) 2014 WILEY-VCH Verlag GmbH Co. KGaA, Weinheim
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 3.032
Times cited: 20
DOI: 10.1002/pssr.201409235
|
|
|
“Rational design of Ag/TiO2 nanosystems by a combined RF-sputtering/sol-gel approach”. Armelao L, Barreca D, Bottaro G, Gasparotto A, Maccato C, Tondello E, Lebedev OI, Turner S, Van Tendeloo G, Štangar UL, ChemPhysChem : a European journal of chemical physics and physical chemistry 10, 3249 (2009). http://doi.org/10.1002/cphc.200900571
Abstract: The present work is devoted to the preparation of Ag/TiO2 nanosystems by an original synthetic strategy, based on the radio-frequency (RF) sputtering of silver particles on titania-based xerogels prepared by the sol-gel (SG) route. This approach takes advantage of the synergy between the microporous xerogel structure and the infiltration power characterizing RF-sputtering, whose combination enables the obtainment of a tailored dispersion of Ag-containing particles into the titania matrix. In addition, the systems chemico-physical features can be tuned further through proper ex situ thermal treatments in air at 400 and 600 °C. The synthesized composites are extensively characterized by the joint use of complementary techniques, that is, X-ray photoelectron and X-ray excited Auger electron spectroscopies (XPS, XE-AES), secondary ion mass spectrometry (SIMS), glancing incidence X-ray diffraction (GIXRD), field emission scanning electron microscopy (FE-SEM), transmission electron microscopy (TEM), electron diffraction (ED), high-angle annular dark field scanning TEM (HAADF-STEM), energy-filtered TEM (EF-TEM) and optical absorption spectroscopy. Finally, the photocatalytic performances of selected samples in the decomposition of the azo-dye Plasmocorinth B are preliminarily investigated. The obtained results highlight the possibility of tailoring the system characteristics over a broad range, directly influencing their eventual functional properties.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 3.075
Times cited: 56
DOI: 10.1002/cphc.200900571
|
|
|
“The role of oxygen at the interface between titanium and carbon nanotubes”. Felten A, Suarez-Martinez I, Ke X, Van Tendeloo G, Ghijsen J, Pireaux J-J, Drube W, Bittencourt C, Ewels CP, ChemPhysChem : a European journal of chemical physics and physical chemistry 10, 1799 (2009). http://doi.org/10.1002/cphc.200900193
Abstract: We study the interface between carbon nanotubes (CNTs) and surface-deposited titanium using electron microscopy and photoemission spectroscopy, supported by density functional calculations. Charge transfer from the Ti atoms to the nanotube and carbide formation is observed at the interface which indicates strong interaction. Nevertheless, the presence of oxygen between the Ti and the CNTs significantly weakens the Ti-CNT interaction. Ti atoms at the surface will preferentially bond to oxygenated sites. Potential sources of oxygen impurities are examined, namely oxygen from any residual atmosphere and pre-existing oxygen impurities on the nanotube surface, which we enhance through oxygen plasma surface pre-treatment. Variation in literature data concerning Ohmic contacts between Ti and carbon nanotubes is explained via sample pre-treatment and differing vacuum levels, and we suggest improved treatment routes for reliable Schottky barrier-free Ti-nanotube contact formation.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 3.075
Times cited: 38
DOI: 10.1002/cphc.200900193
|
|
|
“Spectroscopy and defect identification for fluorinated carbon nanotubes”. Bittencourt C, van Lier G, Ke X, Suarez-Martinez I, Felten A, Ghijsen J, Van Tendeloo G, Ewels CO, ChemPhysChem : a European journal of chemical physics and physical chemistry 10, 920 (2009). http://doi.org/10.1002/cphc.200800851
Abstract: Multi-wall carbon nanotubes (MWCNTs) were exposed to a CF4 radio-frequency (rf) plasma. High-resolution photoelectron spectroscopy shows that the treatment effectively grafts fluorine atoms onto the MWCNTs, altering the valence electronic states. Fluorine surface concentration can be tuned by varying the exposure time. Evaporation of gold onto MWCNTs is used to mark active site formation. High-resolution transmission electron microscopy coupled with density functional theory (DFT) modelling is used to characterise the surface defects formed, indicating that the plasma treatment does not etch the tube surface. We suggest that this combination of theory and microscopy of thermally evaporated gold atoms onto the CNT surface may be a powerful approach to characterise both surface defect density as well as defect type.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 3.075
Times cited: 14
DOI: 10.1002/cphc.200800851
|
|
|
“ZnO nanorod arrays by plasma-enhanced CVD for light-activated functional applications”. Bekermann D, Gasparotto A, Barreca D, Devi A, Fischer RA, Kete M, Štangar UL, Lebedev OI, Maccato C, Tondello E, Van Tendeloo G, ChemPhysChem : a European journal of chemical physics and physical chemistry 11, 2337 (2010). http://doi.org/10.1002/cphc.201000333
Abstract: Switch of the surface properties: Supported ZnO nanorod arrays with tailored roughness and aspect ratios are successfully synthesized by plasma-enhanced chemical vapor deposition. Such nanostructures exhibit significant superhydrophilic and photocatalytic properties tunable as a function of their morphological organization (see picture). This renders them promising building blocks for the fabrication of stimuli-responsive materials.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 3.075
Times cited: 38
DOI: 10.1002/cphc.201000333
|
|
|
“Au particles supported on (110) anatase-TiO2”. Giorgio S, Henry CR, Pauwels B, Van Tendeloo G, Microstructure And Processing 297, 197 (2001). http://doi.org/10.1016/S0921-5093(00)01261-2
Abstract: Au particles were prepared by evaporation in ultra high vacuum at high temperature, on the surfaces of TiO2 micro-spheres with the anatase structure. The morphology and the structural deformation in Au deposits were studied by high resolution transmission electron microscopy and image simulations by the multislice technique. The particles were polyhedral, limited by (100) and (111) faces. Patches with a hexagonal lattice were found around the particles, which was interpreted as thin Au islands on the surface. In these islands the Au lattice was deformed and perfectly accommodated to the (110) surface of TiO2. (C) 2001 Elsevier Science B.V. All rights reserved.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 3.094
Times cited: 40
DOI: 10.1016/S0921-5093(00)01261-2
|
|
|
“3D interconnected hierarchically macro-mesoporous TiO2networks optimized by biomolecular self-assembly for high performance lithium ion batteries”. Ren X-N, Wu L, Jin J, Liu J, Hu Z-Y, Li Y, Hasan T, Yang X-Y, Van Tendeloo G, Su B-L, RSC advances 6, 26856 (2016). http://doi.org/10.1039/C6RA00332J
Abstract: Biomolecular self-assembly is an effective synthesis strategy for materials fabrication with unique structural complexity and properties. For the first time, we intergrate inner-particle mesoporosity in a three-dimensional (3D) interconnected macroporous TiO2 structure via the mediation of biomolecular self-assembly of the lipids and proteins from rape pollen coats and P123 to optimize the structure for high performance lithium storage. Benefitting from the hierarchically 3D interconnected macro-mesoporous structure with high surface area, small nanocrystallites and good electrolyte permeation, such unique porous structure demonstrates superior electrochemical performance, with high initial coulombic efficiency (94.4% at 1C) and a reversible discharge capacity of 161, 145, 127 and 97 mA h g-1 at 2, 5, 10 and 20C for 1000 cycles, with 79.3%, 89.9%, 90.1% and 87.4% capacity retention, respectively. Using SEM, TEM and HRTEM observations on the TiO2 materials before and after cycling, we verify that the inner-particle mesoporosity and the Li2Ti2O4 nanocrystallites formed during the cycling process in interconnected macroporous structure largely enhance the cycle life and rate performance. Our demonstration here offers opportunities towards developing and optimizing hierarchically porous structures for energy storage applications via biomolecular self-assembly.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 3.108
Times cited: 16
DOI: 10.1039/C6RA00332J
|
|
|
“Anatase TiO2nanoparticle coating on porous COK-12 platelets as highly active and reusable photocatalysts”. Wee LH, Meledina M, Turner S, Custers K, Kerkhofs S, Sree SP, Gobechiya E, Kirschhock CEA, Van Tendeloo G, Martens JA, RSC advances 6, 46678 (2016). http://doi.org/10.1039/C6RA06141A
Abstract: Nanoscale TiO2 photocatalysts are widely used for biomedical applications, self-cleaning processes and wastewater treatments. The impregnation/deposition of TiO2 nanoparticles is indispensable for facile handling and separation as well as the improvement of their photocatalytic performance. In the present study, ordered mesoporous COK-12 silica thin platelets with a high-aspect-ratio and rough surfaces are demonstrated as a potential nanoporous support for homogeneous TiO2 nanoparticle coatings with high loading up to 16.7 wt%. The photocatalytic composite of COK-12 platelets and TiO2 nanoparticles is characterized in detail by HRSEM, SAXS, XRD, N2 physisorption analysis, solid-state UV-vis spectroscopy, HAADF-STEM, EDX analysis, and electron tomography. HAADF-STEM-EDX and electron tomography studies reveal a homogeneous dispersion of nanosized TiO2 nanoparticles over COK-12 platelets. The final composite material with anatase TiO2 nanoparticles that demonstrate a blueshifted semiconductor band gap energy of 3.2 eV coated on a highly porous COK-12 support shows exceptional photocatalytic catalytic activity for photodegradation of organic dyes (rhodamine 6G and methylene blue) and an organic pollutant (1-adamantanol) under UV light radiation, outperforming the commercial P25 TiO2 (Degussa) catalyst.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 3.108
Times cited: 6
DOI: 10.1039/C6RA06141A
|
|
|
“Probing the electrochemical behavior of {111} and {110} faceted hollow Cu2O microspheres for lithium storage”. Yu W-B, Hu Z-Y, Yi M, Huang S-Z, Chen D-S, Jin J, Li Y, Van Tendeloo G, Su B-L, RSC advances 6, 97129 (2016). http://doi.org/10.1039/C6RA21026K
Abstract: Transition metal oxides with exposed highly active facets have become of increasing interest as anode materials for lithium ion batteries, because more dangling atoms exposed at the active surface facilitate the reaction between the transition metal oxides and lithium. In this work, we probed the electrochemical behavior of hollow Cu2O microspheres with {111} and {110} active facets on the polyhedron surface as anodes for lithium storage. Compared to commercial Cu2O nanoparticles, hollow Cu2O microspheres with {111} and {110} active facets show a rising specific capacity at 30 cycles which then decreases after 110 cycles during the cycling process. Via advanced electron microscopy characterization, we reveal that this phenomenon can be attributed to the highly active {111} and {110} facets with dangling “Cu” atoms facilitating the conversion reaction of Cu2O and Li, where part of the Cu2O is oxidized to CuO during the charging process. However, as the reaction proceeds, more and more formed Cu nanoparticles cannot be converted to Cu2O or CuO. This leads to a decrease of the specific capacity. We believe that our study here sheds some light on the progress of the electrochemical behavior of transition metal oxides with respect to their increased specific capacity and the subsequent decrease via a conversion reaction mechanism. These results will be helpful to optimize the design of transition metal oxide micro/nanostructures for high performance lithium storage.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 3.108
Times cited: 5
DOI: 10.1039/C6RA21026K
|
|
|
“Luminescence of oxyfluoride glasses co-doped with Ag nanoclusters and Yb3+ ions”. Tikhomirov VK, Vosch T, Fron E, Rodríguez VD, Velázquez JJ, Kirilenko D, Van Tendeloo G, Hofkens J, Van der Auweraer M, Moshchalkov VV, RSC advances 2, 1496 (2012). http://doi.org/10.1039/c1ra01026c
Abstract: Bulk oxyfluoride glasses co-doped with Ag nanoclusters and Yb3+ ions have been prepared by a melt quenching technique. When excited in the absorption band of the Ag nanoclusters between 300 to 500 nm, these glasses emit a broad band characteristic of the Ag nanoclusters between 400 to 750 nm as well as an emission band between 900 to 1100 nm, originating from Yb3+ ions. The intensity ratio of the Yb3+/Ag emission bands increases with the Ag doping level at a fixed concentration of Yb3+, indicating the presence of energy transfer mechanism from the Ag nanoclusters to the Yb3+ ions. Comparison of time-resolved decay kinetics of the luminescence in the respectively Ag nanocluster-Yb3+ co-doped and single Ag nanocluster doped glasses, hints towards an energy transfer from the red and infrared emitting Ag nanoclusters to the Yb3+ ions.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 3.108
Times cited: 46
DOI: 10.1039/c1ra01026c
|
|
|
“Fluorine doped Fe2O3 nanostructures by a one-pot plasma-assisted strategy”. Carraro G, Gasparotto A, Maccato C, Bontempi E, Lebedev OI, Turner S, Sada C, Depero LE, Van Tendeloo G, Barreca D, RSC advances 3, 23762 (2013). http://doi.org/10.1039/c3ra43775b
Abstract: The present work reports on the synthesis of fluorine doped Fe2O3 nanomaterials by a single-step plasma enhanced-chemical vapor deposition (PE-CVD) strategy. In particular, Fe(hfa)2TMEDA (hfa = 1,1,1,5,5,5-hexafluoro-2,4-pentanedionate; TMEDA = N,N,N′,N′-tetramethylethylenediamine) was used as molecular source for both Fe and F in Ar/O2 plasmas. The structure, morphology and chemical composition of the synthesized nanosystems were thoroughly analyzed by two-dimensional X-ray diffraction (XRD2), field emission-scanning electron microscopy (FE-SEM), X-ray photoelectron spectroscopy (XPS), secondary ion mass spectrometry (SIMS) and transmission electron microscopy (TEM). A suitable choice of processing parameters enabled the selective formation of α-Fe2O3 nanomaterials, characterized by an homogeneous F doping, even at 100 °C. Interestingly, a simultaneous control of the system nanoscale organization and fluorine content could be achieved by varying the sole growth temperature. The tailored properties of the resulting materials can be favourably exploited for several technological applications, ranging from photocatalysis, to photoelectrochemical cells and gas sensing.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 3.108
Times cited: 23
DOI: 10.1039/c3ra43775b
|
|
|
“Polyhedral iron oxide coreshell nanoparticles in a biodegradable polymeric matrix : preparation, characterization and application in magnetic particle hyperthermia and drug delivery”. Filippousi M, Altantzis T, Stefanou G, Betsiou M, Bikiaris DN, Angelakeris M, Pavlidou E, Zamboulis D, Van Tendeloo G, RSC advances 3, 24367 (2013). http://doi.org/10.1039/c3ra43747g
Abstract: Polyhedral magnetic iron oxide nanocrystals with multiple facets have been embedded in biocompatible and biodegradable polymeric matrices in order to study their structural, magnetic features and alternating-current (AC) magnetic heating efficiency. The encapsulation of iron oxide nanoparticles into a polymer matrix was confirmed by transmission electron microscopy and further corroborated by high angle annular dark field scanning transmission electron microscopy (HAADF-STEM). HAADF-STEM tomography proved that the iron oxide nanocrystals consist of well-defined polyhedral structures with multiple facets. The magnetic features were found to be in good agreement with the structural and morphological features and are maintained even after encapsulation. Furthermore, the magnetic nanoparticles inside these matrices may be considered as good candidates for biomedical applications in hyperthermia treatments because of their high heating capacity exhibited under an alternating magnetic field. The anticancer Taxol drug was encapsulated in these nanoparticles and its physical state and release rate at 37 and 42 °C was studied.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 3.108
Times cited: 19
DOI: 10.1039/c3ra43747g
|
|
|
“Rational synthesis of F-doped iron oxides on Al2O3(0001) single crystals”. Carraro G, Gasparotto A, Maccato C, Bontempi E, Lebedev OI, Sada C, Turner S, Van Tendeloo G, Barreca D, RSC advances 4, 52140 (2014). http://doi.org/10.1039/c4ra09021g
Abstract: A plasma enhanced-chemical vapor deposition (PE-CVD) route to Fe2O3-based materials on Al2O3(0001) single crystals at moderate growth temperatures (200-400 degrees C) is reported. The use of the fluorinated Fe(hfa)(2)TMEDA (hfa = 1,1,1,5,5,5-hexafluoro-2,4-pentanedionate; TMEDA = N,N,N',N'-tetramethylethylenediamine) molecular precursor in Ar/O-2 plasmas enabled an in situ F-doping of iron oxide matrices, with a fluorine content tunable as a function of the adopted preparative conditions. Variations of the thermal energy supply enabled control of the system phase composition, resulting in gamma-Fe2O3 at 200 degrees C and alpha-Fe2O3 nanostructures at higher deposition temperatures. Notably, at 400 degrees C the formation of highly oriented alpha-Fe2O3 nanocolumns characterized by an epitaxial relation with the Al2O3(0001) substrate was observed. Beside fluorine content, phase composition and nano-organization, even the system optical properties and, in particular, energy gap values, could be tailored by proper modifications of processing parameters.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 3.108
Times cited: 4
DOI: 10.1039/c4ra09021g
|
|
|
“Rational synthesis of F-doped iron oxides on Al2O3(0001) single crystals”. Carraro G, Gasparotto A, Maccato C, Bontempi E, Lebedev OI, Sada C, Turner S, Van Tendeloo G, Barreca D, Rsc Advances , 52140 (2014). http://doi.org/10.1039/C4RA09021G
Abstract: A plasma enhanced-chemical vapor deposition (PE-CVD) route to Fe2O3-based materials on Al2O3(0001) single crystals at moderate growth temperatures (200400 °C) is reported. The use of the fluorinated Fe(hfa)2TMEDA (hfa = 1,1,1,5,5,5-hexafluoro-2,4-pentanedionate; TMEDA = N,N,N′,N′-tetramethylethylenediamine) molecular precursor in Ar/O2 plasmas enabled an in situ F-doping of iron oxide matrices, with a fluorine content tunable as a function of the adopted preparative conditions. Variations of the thermal energy supply enabled control of the system phase composition, resulting in γ-Fe2O3 at 200 °C and α-Fe2O3 nanostructures at higher deposition temperatures. Notably, at 400 °C the formation of highly oriented α-Fe2O3 nanocolumns characterized by an epitaxial relation with the Al2O3(0001) substrate was observed. Beside fluorine content, phase composition and nano-organization, even the system optical properties and, in particular, energy gap values, could be tailored by proper modifications of processing parameters.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 3.108
Times cited: 4
DOI: 10.1039/C4RA09021G
|
|