“ZnAl layered double hydroxide based catalysts (with Cu, Mn, Ti) used as noble metal-free three-way catalysts”. Van Everbroeck T, Wu J, Arenas-Esteban D, Ciocarlan R-G, Mertens M, Bals S, Dujardin C, Granger P, Seftel EM, Cool P, Applied clay science 217, 106390 (2022). http://doi.org/10.1016/j.clay.2021.106390
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT); Laboratory of adsorption and catalysis (LADCA)
Impact Factor: 5.6
Times cited: 6
DOI: 10.1016/j.clay.2021.106390
|
|
|
“Plasma-catalytic ammonia synthesis : packed catalysts act as plasma modifiers”. Ndayirinde C, Gorbanev Y, Ciocarlan R-G, De Meyer R, Smets A, Vlasov E, Bals S, Cool P, Bogaerts A, Catalysis today 419, 114156 (2023). http://doi.org/10.1016/J.CATTOD.2023.114156
Abstract: We studied the plasma-catalytic production of NH3 from H2 and N2 in a dielectric barrier discharge plasma reactor using five different Co-based catalysts supported on Al2O3, namely Co/Al2O3, CoCe/Al2O3, CoLa/Al2O3, CoCeLa/Al2O3 and CoCeMg/Al2O3. The catalysts were characterized via several techniques, including SEM-EDX, and their performance was compared. The best performing catalyst was found to be CoLa/Al2O3, but the dif-ferences in NH3 concentration, energy consumption and production rate between the different catalysts were limited under the same conditions (i.e. feed gas, flow rate and ratio, and applied power). At the same time, the plasma properties, such as the plasma power and current profile, varied significantly depending on the catalyst. Taken together, these findings suggest that in the production of NH3 by plasma catalysis, our catalysts act as plasma modifiers, i.e., they change the discharge properties and hence the gas phase plasma chemistry. Importantly, this effect dominates over the direct catalytic effect (as e.g. in thermal catalysis) defined by the chemistry on the catalyst surface.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT); Laboratory of adsorption and catalysis (LADCA); Plasma Lab for Applications in Sustainability and Medicine – Antwerp (PLASMANT)
Impact Factor: 5.3
Times cited: 3
DOI: 10.1016/J.CATTOD.2023.114156
|
|
|
“Selectivity in ligand functionalization of photocatalytic metal oxide nanoparticles for phase transfer and self‐assembly applications”. Borah R, Ninakanti R, Nuyts G, Peeters H, Pedrazo-Tardajos A, Nuti S, Vande Velde C, De Wael K, Lenaerts S, Bals S, Verbruggen S, Chemistry-A European Journal , chem.202100029 (2021). http://doi.org/10.1002/CHEM.202100029
Abstract: Functionalization of photocatalytic metal oxide nanoparticles of TiO 2 , ZnO, WO 3 and CuO with amine‐terminated (oleylamine) and thiol‐terminated (1‐dodecanethiol) alkyl chained ligands was studied under ambient conditions. A high selectivity was observed in the binding specificity of a ligand towards nanoparticles of these different oxides. It was observed that oleylamine binds stably to only TiO 2 and WO 3 , while 1‐dodecanethiol binds stably only to ZnO and CuO. Similarly, polar to non‐polar solvent phase transfer of TiO 2 and WO 3 nanoparticles could be achieved by using oleylamine, but not by 1‐dodecanethiol, while the contrary holds for ZnO and CuO. The surface chemistry of ligand functionalized nanoparticles was probed by ATR‐FTIR spectroscopy, that enabled to elucidate the occupation of the ligands at the active sites. The photo‐stability of the ligands on the nanoparticle surface was determined by the photocatalytic self‐cleaning properties of the material. While TiO 2 and WO 3 degrade the ligands within 24 hours under both UV and visible light, ligands on ZnO and CuO remain unaffected. The gathered insights are also highly relevant from an application point of view. As an example, since the ligand functionalized nanoparticles are hydrophobic in nature, they can thus be self‐assembled at the air‐water interface, for obtaining nanoparticle films with demonstrated photocatalytic as well as anti‐fogging properties.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT); AXES (Antwerp X-ray Analysis, Electrochemistry and Speciation); Sustainable Energy, Air and Water Technology (DuEL); Intelligence in PRocesses, Advanced Catalysts and Solvents (iPRACS)
Impact Factor: 5.317
Times cited: 15
DOI: 10.1002/CHEM.202100029
|
|
|
“In-situ structural degradation study of quadruple-cation perovskite solar cells with nanostructured charge transfer layer”. Panzic I, Mandic V, Mangalam J, Rath T, Radovanovic-Peric F, Gaboardi M, De Coen B, Bals S, Schrenker N, Ceramics international 49, 24475 (2023). http://doi.org/10.1016/J.CERAMINT.2022.12.222
Abstract: We investigated the structural stability of perovskite solar cells (PSCs) in n-i-p configuration comprising a rubidium-caesium-methylammonium-formamidinium (Rb-Cs-MA-FA) lead iodide/bromide perovskite absorber, interfaced with nanostructured ZnO-nanorod (NR) or mesostructured (MS) TiO2 electron transfer layers (ETL). An in-situ setup was established comprising synchrotron grazing incidence diffraction (GID) and Raman spectroscopy as a function of temperature under ambient and isothermal conditions; measurements of current-voltage (IV) characteristics and electron microscopic investigations were conducted discretely.The aging of the solar cells was performed at ambient conditions or at elevated temperatures directly in the in -situ measurement setup. The diffraction depth profiling results point to different degradation rates for different ETLs; moreover, electron microscopy and atomic force microscopy, as well as energy dispersive spectroscopy clarified surface conditions in terms of the extent of the degradation. Scanning transmission electron microscopy of lamellas, derived by dual beam microscopy, revealed that the origin of the degradation lay in the ETL/ absorber interface. For the case of the nanostructured zincite, the perovskite absorber contained many voids, leading to the conclusion that the investigated quadruple perovskite absorber showed limited compatibility with ZnO NR ETL due to a higher number of defects. Morphological defects promoted the absorber degradation and nullified the advantages initially achieved by nanostructuring. The exchange of the ZnO NR ETL with MS TiO2 improved the stability parameters of the absorber layer.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 5.2
DOI: 10.1016/J.CERAMINT.2022.12.222
|
|
|
“Homopolymers as nanocarriers for the loading of block copolymer micelles with metal salts : a facile way to large-scale ordered arrays of transition-metal nanoparticles”. Shan L, Punniyakoti S, Van Bael MJ, Temst K, Van Bael MK, Ke X, Bals S, Van Tendeloo G, D'Olieslaeger M, Wagner P, Haenen K, Boyen HG;, Journal of materials chemistry C : materials for optical and electronic devices 2, 701 (2014). http://doi.org/10.1039/c3tc31333f
Abstract: A new and facile approach is presented for generating quasi-regular patterns of transition metal-based nanoparticles on flat substrates exploiting polystyrene-block-poly2vinyl pyridine (PS-b-P2VP) micelles as intermediate templates. Direct loading of such micellar nanoreactors by polar transition metal salts in solution usually results in nanoparticle ensembles exhibiting only short range order accompanied by broad distributions of particle size and inter-particle distance. Here, we demonstrate that the use of P2VP homopolymers of appropriate length as molecular carriers to transport precursor salts into the micellar cores can significantly increase the degree of lateral order within the final nanoparticle arrays combined with a decrease in spreading in particle size. Thus, a significantly extended range of materials is now available which can be exploited to study fundamental properties at the transition from clusters to solids by means of well-organized, well-separated, size-selected metal and metal oxide nanostructures.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 5.256
Times cited: 5
DOI: 10.1039/c3tc31333f
|
|
|
“Atomic resolution electron tomography”. Bals S, Goris B, de Backer A, Van Aert S, Van Tendeloo G, MRS bulletin 41, 525 (2016). http://doi.org/10.1557/mrs.2016.138
Abstract: Over the last two decades, three-dimensional (3D) imaging by transmission electron microscopy or “electron tomography” has evolved into a powerful tool to investigate a variety of nanomaterials in different fields, such as life sciences, chemistry, solid-state physics, and materials science. Most of these results were obtained with nanometer-scale resolution, but different approaches have recently pushed the resolution to the atomic level. Such information is a prerequisite to understand the specific relationship between the atomic structure and the physicochemical properties of (nano) materials. We provide an overview of the latest progress in the field of atomic-resolution electron tomography. Different imaging and reconstruction approaches are presented, and state-of-the-art results are discussed. This article demonstrates the power and importance of electron tomography with atomic-scale resolution.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 5.199
Times cited: 19
DOI: 10.1557/mrs.2016.138
|
|
|
“Plasmonic nanodiamonds : targeted coreshell type nanoparticles for cancer cell thermoablation”. Rehor I, Lee KL, Chen K, Hajek M, Havlik J, Lokajova J, Masat M, Slegerova J, Shukla S, Heidari H, Bals S, Steinmetz NF, Cigler P, Advanced healthcare materials 4, 460 (2015). http://doi.org/10.1002/adhm.201400421
Abstract: Targeted biocompatible nanostructures with controlled plasmonic and morphological parameters are promising materials for cancer treatment based on selective thermal ablation of cells. Here, coreshell plasmonic nanodiamonds consisting of a silica-encapsulated diamond nanocrystal coated in a gold shell are designed and synthesized. The architecture of particles is analyzed and confirmed in detail using electron tomography. The particles are biocompatibilized using a PEG polymer terminated with bioorthogonally reactive alkyne groups. Azide-modified transferrin is attached to these particles, and their high colloidal stability and successful targeting to cancer cells overexpressing the transferrin receptor are demonstrated. The particles are nontoxic to the cells and they are readily internalized upon binding to the transferrin receptor. The high plasmonic cross section of the particles in the near-infrared region is utilized to quantitatively ablate the cancer cells with a short, one-minute irradiation by a pulse 750-nm laser.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 5.11
Times cited: 30
DOI: 10.1002/adhm.201400421
|
|
|
“The uptake of ZnO and CuO nanoparticles in the water-flea Daphnia magna under acute exposure scenarios”. Adam N, Leroux F, Knapen D, Bals S, Blust R, Environmental pollution 194, 130 (2014). http://doi.org/10.1016/j.envpol.2014.06.037
Abstract: In this study the uptake of ZnO and CuO nanoparticles by Daphnia magna was tested. Daphnids were exposed during 48 h to acute concentrations of the nanoparticles and corresponding metal salts. The Daphnia zinc and copper concentration was measured and the nanoparticles were localized using electron microscopy. The aggregation and dissolution in the medium was characterized. A fast dissolution of ZnO in the medium was observed, while most CuO formed large aggregates and only a small fraction dissolved. The Daphnia zinc concentration was comparable for the nanoparticles and salts. Contrarily, a much higher Daphnia copper concentration was observed in the CuO exposure, compared to the copper salt. CuO nanoparticles adsorbed onto the carapace and occurred in the gut but did not internalize in the tissues. The combined dissolution and uptake results indicate that the toxicity of both nanoparticle types was caused by metal ions dissolved from the particles in the medium.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT); Veterinary physiology and biochemistry
Impact Factor: 5.099
Times cited: 45
DOI: 10.1016/j.envpol.2014.06.037
|
|
|
“Enhanced Pomegranate‐Structured SnO2Electrocatalysts for the Electrochemical CO2Reduction to Formate”. Daele KV, Arenas‐Esteban D, Choukroun D, Hoekx S, Rossen A, Daems N, Pant D, Bals S, Breugelmans T, ChemElectroChem (2023). http://doi.org/10.1002/celc.202201024
Abstract: Although most state-of-the-art Sn-based electrocatalysts yield promising results in terms of selectivity and catalyst activity, their stability remains insufficient to date. Here, we demonstrate the successful application of the recently developed pomegranate-structured SnO2 (Pom. SnO2) and SnO2@C (Pom. SnO2@C) nanocomposite electrocatalysts for the efficient electrochemical conversion of CO2 to formate. With an initial selectivity of 83 and 86% towards formate and an operating potential of -0.72 V and -0.64 V vs. RHE, respectively, these pomegranate SnO2 electrocatalysts are able to compete with most of the current state-of-the-art Sn-based electrocatalysts in terms of activity and selectivity. Given the importance of electrocatalyst stability, long-term experiments (24 h) were performed and a temporary loss in selectivity for the Pom. SnO2@C electrocatalyst was largely restored to its initial selectivity upon drying and exposure to air. Of all the used (24 h) electrocatalysts, the pomegranate SnO2@C had the highest selectivity over a time period of one hour, reaching an average recovered FE of 85%, while the commercial SnO2 and bare pomegranate SnO2 electrocatalysts reached an average of 79 and 80% FE towards formate, respectively. Furthermore, the pomegranate structure of Pom. SnO2@C was largely preserved due to the presence of the heterogeneous carbon shell, which acts as a protective layer, physically inhibiting particle segregation/pulverisation and agglomeration.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT); Applied Electrochemistry & Catalysis (ELCAT)
Impact Factor: 4
DOI: 10.1002/celc.202201024
|
|
|
“Synthesis and characterization of a highly electroactive composite based on Au nanoparticles supported on nanoporous activated carbon for electrocatalysis”. Moggia G, Hoekx S, Daems N, Bals S, Breugelmans T, ChemElectroChem , 1 (2023). http://doi.org/10.1002/CELC.202300293
Abstract: A facile, “one-pot”, chemical approach to synthesize gold-based nanoparticles finely dispersed on porous activated carbon (Norit) was demonstrated in this work. The pH of the synthesis bath played a critical role in determining the optimal gold-carbon interaction, which enabled a successful deposition of the gold nanoparticles onto the carbon matrix with a maximized metal utilization of 93 %. The obtained AuNP/C nanocomposite was characterized using SEM, HAADF-STEM electron tomography and electrochemical techniques. It was found that the Au nanoparticles, with diameters between 5 and 20 nm, were evenly distributed over the carbon matrix, both inside and outside the pores. Electrochemical characterization indicated that the composite had a very large electroactive surface area (EASA), as high as 282.4 m2 gAu-1. By exploiting its very high EASA, the catalyst was intended to boost the productivity of glucaric acid in the electrooxidation of its precursor, gluconic acid. However, cyclic voltammetry experiments revealed a very limited reactivity towards gluconic acid oxidation, due to the spacial hindrance of gluconic acid molecule which prevented diffusion inside the catalyst nanopores. On the other hand, the as-synthesized nanocomposite promises to be effective towards the ORR, and might thus find potential application as anode catalyst for fuel cells as well as for the scalability of all those electrochemical reactions involving small molecules with high diffusivity and catalysed by noble metals (i. e. CO2, CH4, N2, etc..). Electrocatalysis: Gold nanoparticles with diameter between 5 and 20 nm evenly distributed onto porous activated carbon (Norit) were obtained using a facile “one-pot” chemical synthesis technique with very high metal utilization. The AuNP/C nanocomposite was characterized using SEM, HAADF-STEM electron tomography and electrochemical techniques, revealing a very large electroactive surface area (EASA). The figure shows the HAADF-STEM image (a) and the respective EDX elemental distribution (b) for the AuNP/C composite with 9.3 % Au-loading developed in this work (Au is marked in red and C in green).image
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT); Applied Electrochemistry & Catalysis (ELCAT)
Impact Factor: 4
Times cited: 1
DOI: 10.1002/CELC.202300293
|
|
|
“The influence of branched alkyl side chains in A-D-A oligothiophenes on the photovoltaic performance and morphology of solution-processed bulk-heterojunction solar cells”. Ata I, Ben Dkhil S, Pfannmoeller M, Bals S, Duche D, Simon J-J, Koganezawa T, Yoshimoto N, Videlot-Ackermann C, Margeat O, Ackermann J, Baeuerle P, Organic chemistry frontiers : an international journal of organic chemistry 4, 1561 (2017). http://doi.org/10.1039/C7QO00222J
Abstract: Besides providing sufficient solubility, branched alkyl chains also affect the film-forming and packing properties of organic semiconductors. In order to avoid steric hindrance as it is present in wide-spread alkyl chains comprising a branching point position at the C2-position, i.e., 2-ethylhexyl, the branching point can be moved away from the pi-conjugated backbone. In this report, we study the influence of the modification of the branching point position from the C2-position in 2-hexyldecylamine (1) to the C4-position in 4-hexyldecylamine (2) connected to the central dithieno[3,2-b: 2', 3'-d] pyrrole (DTP) moiety in a well-studied A-D-A oligothiophene on the optoelectronic properties and photovoltaic performance in solution- processed bulk heterojunction solar cells (BHJSCs) with [6,6]-phenyl-C71-butyric acid methyl ester (PC71BM) as the acceptor material. Post-treatment of the photoactive layers is performed via solvent vapor annealing (SVA) in order to improve the film microstructure of the bulk heterojunction. The time evolution of nanoscale morphological changes is followed by combining scanning transmission electron microscopy with low-energy-loss spectroscopic imaging (STEM-SI), solid-state absorption spectroscopy, and two-dimensional grazing incidence X-ray diffraction (2D-GIXRD). Our results show an improvement of the photovoltaic performance that is dependent on the branching point position in the donor oligomer. Optical spacers are utilized to increase light absorption inside the co-oligomer 2-based BHJSCs leading to increased power conversion efficiencies (PCEs) of 8.2% when compared to the corresponding co-oligomer 1-based devices. A STEM-SI analysis of the respective device cross-sections of active layers containing 1 and 2 as donor materials indeed reveals significant differences in their respective active layer morphologies.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 4.955
Times cited: 24
DOI: 10.1039/C7QO00222J
|
|
|
“Self-assembly of Janus Au:Fe₃O₄, branched nanoparticles. From organized clusters to stimuli-responsive nanogel suprastructures”. Reguera J, Flora T, Winckelmans N, Rodriguez-Cabello JC, Bals S, Nanoscale Advances 2, 2525 (2020). http://doi.org/10.1039/D0NA00102C
Abstract: Janus nanoparticles offer enormous possibilities through a binary selective functionalization and dual properties. Their self-assembly has attracted strong interest due to their potential as building blocks to obtain molecular colloids, supracrystals and well-organized nanostructures that can lead to new functionalities. However, this self-assembly has been focused on relatively simple symmetrical morphologies, while for complex nanostructures this process has been unexplored. Here, we study the assembly of plasmonic-magnetic Janus nanoparticles with a branched (nanostar) – sphere morphology. The branched morphology enhances their plasmonic properties in the near-infrared region and therefore their applicability, but at the same time constrains their self-assembly capabilities to obtain more organized or functional suprastructures. We describe the self-assembly of these nanoparticles after amphiphilic functionalization. The role of the nanoparticle branching, as well as the size of the polymer-coating, is explored. We show how the use of large molecular weight stabilizing polymers can overcome the anisotropy of the nanoparticles producing a change in the morphology from small clusters to larger quasi-cylindrical nanostructures. Finally, the Janus nanoparticles are functionalized with a thermo-responsive elastin-like recombinamer. These nanoparticles undergo reversible self-assembly in the presence of free polymer giving rise to nanoparticle-stabilized nanogel-like structures with controlled size, providing the possibility to expand their applicability to multi-stimuli controlled self-assembly.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 4.7
Times cited: 10
DOI: 10.1039/D0NA00102C
|
|
|
“The reduction of benzylbromide at Ag-Ni deposits prepared by galvanic replacement”. Vanrenterghem B, Papaderakis A, Sotiropoulos S, Tsiplakides D, Balomenou S, Bals S, Breugelmans T, Electrochimica acta 196, 756 (2016). http://doi.org/10.1016/j.electacta.2016.02.135
Abstract: A two-step procedure was applied to prepare bimetallic Ag-Ni glassy carbon supported catalysts (Ag-Ni/GC). First Ni layers were prepared by means of electrodeposition in an aqueous deaerated nickel chloride + nickel sulfamate + boric acid solution. Second, the partial replacement of Ni layers by Ag was achieved upon immersion of the latter in solutions containing silver nitrate. Three different pretreatment protocols were used after preparation of the Ag/Ni deposits; as prepared, cathodised in alkali and scanned in acid. After the pretreatment the surface was characterised by means of spectroscopy techniques (scanning electron microscopy and energy dispersive x-ray) and electrochemically in an alkali NaOH solution through cyclic voltammetry (CV). Afterwards the modified electrodes were tested for the reduction of benzylbromide in acetonitrile solutions by using CV and were found to show improved activity compared to bulk Ag electrode. The highest activity towards benzylbromide reduction was observed for pre-cathodised Ag-Ni electrodes. A final stage of the research focuses on the development of a practical Ag/Ni foam catalyst for the reduction of benzylbromide. Due to the high electrochemical active surface area of Ag/Ni foam, a higher conversion of benzyl bromide was obtained in comparison with bulk Ag.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT); Applied Electrochemistry & Catalysis (ELCAT)
Impact Factor: 4.798
Times cited: 21
DOI: 10.1016/j.electacta.2016.02.135
|
|
|
“Tuning of PCDTBT : PC71BM blend nanoparticles for eco-friendly processing of polymer solar cells”. D'Olieslaeger L, Pfannmöller M, Fron E, Cardinaletti I, Van der Auweraer M, Van Tendeloo G, Bals S, Maes W, Vanderzande D, Manca J, Ethirajan A, Solar energy materials and solar cells 159, 179 (2017). http://doi.org/10.1016/J.SOLMAT.2016.09.008
Abstract: We report the controlled preparation of water processable nanoparticles (NPs) employing the push-pull polymer PCDTBT and the fullerene acceptor PC71BM in order to enable solar cell processing using eco-friendly solvent (i.e. water). The presented method provides the possibility to separate the formation of the active layer blend and the deposition of the active layer into two different processes. For the first time, the benefits of aqueous processability for the high-potential class of push-pull polymers, generally requiring high boiling solvents, are made accessible. With our method we demonstrate excellent control over the blend stoichiometry and efficient mixing. Furthermore, we provide visualization of the nano morphology of the different NPs to obtain structural information down to similar to 2 nm resolution using advanced analytical electron microscopy. The imaging directly reveals very small compositional demixing in the PCDTBT:PC71BM blend NPs, in the size range of about <5 nm, indicating fine mixing at the molecular level. The suitability of the proposed methodology and materials towards the aspects of eco-friendly processing of organic solar cells is demonstrated through a processing of lab scale NPs solar cell prototypes reaching a power conversion efficiency of 1.9%. (C) 2016 Elsevier B.V. All rights reserved.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 4.784
Times cited: 32
DOI: 10.1016/J.SOLMAT.2016.09.008
|
|
|
“Improving extracellular vesicles visualization: From static to motion”. Reclusa P, Verstraelen P, Taverna S, Gunasekaran M, Pucci M, Pintelon I, Claes N, de Miguel-Pérez D, Alessandro R, Bals S, Kaushal S, Rolfo C, Scientific Reports 10, 6494 (2020). http://doi.org/10.1038/s41598-020-62920-0
Abstract: In the last decade extracellular vesicles (EVs) have become a hot topic. The findings on EVs content and effects have made them a major field of interest in cancer research. EVs, are able to be internalized through integrins expressed in parental cells, in a tissue specific manner, as a key step of cancer progression and pre-metastatic niche formation. However, this specificity might lead to new opportunities in cancer treatment by using EVs as devices for drug delivery. For future applications of EVs in cancer, improved protocols and methods for EVs isolation and visualization are required. Our group has put efforts on developing a protocol, able to track the EVs for in vivo internalization analysis. We showed, for the first time, the videos of labeled EVs uptake by living lung cancer cells.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 4.6
Times cited: 25
DOI: 10.1038/s41598-020-62920-0
|
|
|
“Catalytic and molecular separation properties of Zeogrids and Zeotiles”. Martens JA, Thybaut JW, Denayer JFM, Sree SP, Aerts A, Reyniers M-F, van Speybroeck V, Waroquier M, Buekenhoudt A, Vankelecom I, Buijs W, Persoons J, Baron GV, Bals S, Van Tendeloo G, Marin GB, Jacobs PA, Kirschhock CEA, Catalysis today 168, 17 (2011). http://doi.org/10.1016/j.cattod.2011.01.036
Abstract: Zeogrids and Zeotiles are hierarchical materials built from assembled MFI zeolite precursor units. Permanent secondary porosity in these materials is obtained through self assembly of nanoparticles encountered in MFI zeolite synthesis in the presence of supramolecular templates. Hereon, the aggregated species are termed nanoslabs. Zeogrids are layered materials with lateral spacings between nanoslabs creating galleries qualifying as supermicropores. Zeotiles present a diversity of tridimensional nanoslab assemblies with mesopores. Zeotile-1, -4 and -6 are hexagonal mesostructures. Zeotile-1 has triangular and hexagonal channels; Zeotile-4 has hexagonal channels interconnected via slits. Zeotile-2 has a cubic structure with gyroid type mesoporosity. The behavior of Zeogrids and Zeotiles in adsorption, membrane and chromatographic separation and catalysis has been characterized and compared with zeolites and mesoporous materials derived from unstructured silica sources. Shape selectivity was detected via adsorption of n- and iso-alkanes. The mesoporosity of Zeotiles can be exploited in chromatographic separation of biomolecules. Zeotiles present attractive separation properties relevant to CO2 sequestration. Because of its facile synthesis procedure without hydrothermal steps Zeogrid is convenient for membrane synthesis. The performance of Zeogrid membrane in gas separation, nanofiltration and pervaporation is reported. In the Beckmann rearrangement of cyclohexanone oxime Zeogrids and Zeotiles display a catalytic activity characteristic of silicalite-1 zeolites. Introduction of acidity and redox catalytic activity can be achieved via incorporation of Al and Ti atoms in the nanoslabs during synthesis. Zeogrids are active in hydrocracking, catalytic cracking, alkylation and epoxidation reactions. Zeogrids and Zeotiles often behave differently from ordered mesoporous materials as well as from zeolites and present a valuable extension of the family of hierarchical silicate based materials.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 4.636
Times cited: 13
DOI: 10.1016/j.cattod.2011.01.036
|
|
|
“Chemistry, local molybdenum clustering, and electrochemistry in the Li2+xMo1-xO3 solid solutions”. Savina AA, Saiutina VV, Morozov AV, Boev AO, Aksyonov DA, Dejoie C, Batuk M, Bals S, Hadermann J, Abakumov AM, Inorganic chemistry 61, 5637 (2022). http://doi.org/10.1021/ACS.INORGCHEM.2C00420
Abstract: A broad range of cationic nonstoichiometry has been demonstratedfor the Li-rich layered rock-salt-type oxide Li2MoO3, which has generally been considered as a phase with a well-defined chemical composition. Li2+xMo1-xO3(-0.037 <= x <= 0.124) solid solutions were synthesized via hydrogen reduction ofLi2MoO4in the temperature range of 650-1100 degrees C, withxdecreasing with theincrease of the reduction temperature. The solid solutions adopt a monoclinicallydistorted O3-type layered average structure and demonstrate a robust localordering of the Li cations and Mo3triangular clusters within the mixed Li/Mocationic layers. The local structure was scrutinized in detail by electron diffractionand aberration-corrected scanning transmission electron microcopy (STEM),resulting in an ordering model comprising a uniform distribution of the Mo3clusters compatible with local electroneutrality and chemical composition. The geometry of the triangular clusters with their oxygenenvironment (Mo3O13groups) has been directly visualized using differential phase contrast STEM imaging. The established localstructure was used as input for density functional theory (DFT)-based calculations; they support the proposed atomic arrangementand provide a plausible explanation for the staircase galvanostatic charge profiles upon electrochemical Li+extraction fromLi2+xMo1-xO3in Li cells. According to DFT, all electrochemical capacity in Li2+xMo1-xO3solely originates from the cationic Moredox process, which proceeds via oxidation of the Mo3triangular clusters into bent Mo3chains where the electronic capacity of the clusters depends on the initial chemical composition and Mo oxidation state defining the width of the first charge low-voltageplateau. Further oxidation at the high-voltage plateau proceeds through decomposition of the Mo3chains into Mo2dimers and further into individual Mo6+cations
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 4.6
Times cited: 3
DOI: 10.1021/ACS.INORGCHEM.2C00420
|
|
|
“Plasmon resonance of gold and silver nanoparticle arrays in the Kretschmann (attenuated total reflectance) vs. direct incidence configuration”. Borah R, Ninakanti R, Bals S, Verbruggen SW, Scientific reports 12, 15738 (2022). http://doi.org/10.1038/S41598-022-20117-7
Abstract: While the behaviour of plasmonic solid thin films in the Kretschmann (also known as Attenuated Total Reflection, ATR) configuration is well-understood, the use of discrete nanoparticle arrays in this optical configuration is not thoroughly explored. It is important to do so, since close packed plasmonic nanoparticle arrays exhibit exceptionally strong light-matter interactions by plasmonic coupling. The present work elucidates the optical properties of plasmonic Au and Ag nanoparticle arrays in both the direct normal incidence and Kretschmann configuration by numerical models, that are validated experimentally. First, hexagonal close packed Au and Ag nanoparticle films/arrays are obtained by air–liquid interfacial assembly. The numerical models for the rigorous solution of the Maxwell’s equations are validated using experimental optical spectra of these films before systematically investigating various parameters. The individual far-field/near-field optical properties, as well as the plasmon relaxation mechanism of the nanoparticles, vary strongly as the packing density of the array increases. In the Kretschmann configuration, the evanescent fields arising from p – and s -polarized (or TM and TE polarized) incidence have different directional components. The local evanescent field intensity and direction depends on the polarization, angle of incidence and the wavelength of incidence. These factors in the Kretschmann configuration give rise to interesting far-field as well as near-field optical properties. Overall, it is shown that plasmonic nanoparticle arrays in the Kretschmann configuration facilitate strong broadband absorptance without transmission losses, and strong near-field enhancement. The results reported herein elucidate the optical properties of self-assembled nanoparticle films, pinpointing the ideal conditions under which the normal and the Kretschmann configuration can be exploited in multiple light-driven applications.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT); Sustainable Energy, Air and Water Technology (DuEL)
Impact Factor: 4.6
Times cited: 11
DOI: 10.1038/S41598-022-20117-7
|
|
|
“Plasmon mapping in Au@Ag nanocube assemblies”. Goris B, Guzzinati G, Fernández-López C, Pérez-Juste J, Liz-Marzán LM, Trügler A, Hohenester U, Verbeeck J, Bals S, Van Tendeloo G, The journal of physical chemistry: C : nanomaterials and interfaces 118, 15356 (2014). http://doi.org/10.1021/jp502584t
Abstract: Surface plasmon modes in metallic nanostructures largely determine their optoelectronic properties. Such plasmon modes can be manipulated by changing the morphology of the nanoparticles or by bringing plasmonic nanoparticle building blocks close to each other within organized assemblies. We report the EELS mapping of such plasmon modes in pure Ag nanocubes, Au@Ag coreshell nanocubes, and arrays of Au@Ag nanocubes. We show that these arrays enable the creation of interesting plasmonic structures starting from elementary building blocks. Special attention will be dedicated to the plasmon modes in a triangular array formed by three nanocubes. Because of hybridization, a combination of such nanotriangles is shown to provide an antenna effect, resulting in strong electrical field enhancement at the narrow gap between the nanotriangles.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 4.536
Times cited: 41
DOI: 10.1021/jp502584t
|
|
|
“Synthesis and characterization of photoreactive TiO2carbon nanosheet composites”. Kurttepeli M, Deng S, Verbruggen SW, Guzzinati G, Cott DJ, Lenaerts S, Verbeeck J, Van Tendeloo G, Detavernier C, Bals S, The journal of physical chemistry: C : nanomaterials and interfaces 118, 21031 (2014). http://doi.org/10.1021/jp5067499
Abstract: We report the atomic layer deposition of titanium dioxide on carbon nanosheet templates and investigate the effects of postdeposition annealing in a helium environment using different characterization techniques. The crystallization of the titanium dioxide coating upon annealing is observed using in situ X-ray diffraction. The (micro)structural characterization of the films is carried out by scanning electron microscopy and advanced transmission electron microscopy techniques. Our study shows that the annealing of the atomic layer deposition processed and carbon nanosheets templated titanium dioxide layers in helium environment resulting in the formation of a porous, nanocrystalline and photocatalytically active titanium dioxide-carbon nanosheet composite film. Such composites are suitable for photocatalysis and dye-sensitized solar cells applications.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT); Sustainable Energy, Air and Water Technology (DuEL)
Impact Factor: 4.536
Times cited: 9
DOI: 10.1021/jp5067499
|
|
|
“New insights into the early stages of nanoparticle electrodeposition”. Ustarroz J, Ke X, Hubin A, Bals S, Terryn H, The journal of physical chemistry: C : nanomaterials and interfaces 116, 2322 (2012). http://doi.org/10.1021/jp210276z
Abstract: Electrodeposition is an increasingly important method to synthesize supported nanoparticles, yet the early stages of electrochemical nanoparticle formation are not perfectly understood. In this paper, the early stages of silver nanoparticle electrodeposition on carbon substrates have been studied by aberration-corrected TEM, using carbon-coated TEM grids as electrochemical electrodes. In this manner we have access to as-deposited nanoparticle size distribution and structural characterization at the atomic scale combined with electrochemical measurements, which represents a breakthrough in a full understanding of the nanoparticle electrodeposition mechanisms. Whereas classical models, based upon characterization at the nanoscale, assume that electrochemical growth is only driven by direct attachment, the results reported hereafter indicate that early nanoparticle growth is mostly driven by nanocluster surface movement and aggregation. Hence, we conclude that electrochemical nulceation and growth models should be revised and that an electrochemical aggregative growth mechanism should be considered in the early stages of nanoparticle electrodeposition.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 4.536
Times cited: 104
DOI: 10.1021/jp210276z
|
|
|
“Gold Nanostar-Coated Polystyrene Beads as Multifunctional Nanoprobes for SERS Bioimaging”. Serrano-Montes AB, Langer J, Henriksen-Lacey M, Jimenez de Aberasturi D, Solís DM, Taboada JM, Obelleiro F, Sentosun K, Bals S, Bekdemir A, Stellacci F, Liz-Marzán LM, The journal of physical chemistry: C : nanomaterials and interfaces 120, 20860 (2016). http://doi.org/10.1021/acs.jpcc.6b02282
Abstract: Hybrid colloidal nanocomposites comprising polystyrene beads and plasmonic gold nanostars are reported as multifunctional optical nanoprobes. Such self-assembled structures are excellent Raman enhancers for bio-applications as they feature plasmon modes in the near infrared “first biological transparency window”. In this proof of concept study, we used 4- mercaptobenzoic acid as a Raman-active molecule to optimize the density of gold nanostars on polystyrene beads, improving SERS performance and thereby allowing in vitro cell culture imaging. Interestingly, intermediate gold nanostar loadings were found to yield higher SERS response, which was confirmed by electromagnetic modeling. These engineered hybrid nanostructures notably improve the possibilities of using gold nanostars as SERS tags. Additionally, when fluorescently labeled polystyrene bead are used as colloidal carriers, the composite particles can be applied as promising tools for multimodal bioimaging.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 4.536
Times cited: 64
DOI: 10.1021/acs.jpcc.6b02282
|
|
|
“A Comprehensive Study of the Electrodeposition of Nickel Nanostructures from Deep Eutectic Solvents: Self-Limiting Growth by Electrolysis of Residual Water”. Mernissi Cherigui EA, Sentosun K, Bouckenooge P, Vanrompay H, Bals S, Terryn H, Ustarroz J, The journal of physical chemistry: C : nanomaterials and interfaces 121, 9337 (2017). http://doi.org/10.1021/acs.jpcc.7b01104
Abstract: The electrodeposition of nickel nanostructures on glassy carbon was investigated in 1:2 choline chloride – urea (1:2 ChCl-U) deep eutectic solvent (DES). By combining electrochemical techniques with ex-situ FE-SEM, XPS, HAADF-STEM and EDX, the electrochemical processes occurring during nickel deposition were better understood. Special attention was given to the interaction between the solvent and the growing nickel nanoparticles. The application of a suffciently negative potential results into the electrocatlytic hydrolisis of residual water in the DES, which leads to the formation of a mixed layer of Ni/Ni(OH)2(ads). In addition, hydrogen bonds between hydroxide species and the DES components could be formed, quenching the growth of the nickel clusters favouring their aggregation. Due to these processes, a highly dense distribution of nickel nanostructures can be obtained within a wide potential range. Understanding the role of residual water and the interactions at the interface during metal electrodeposition from DESs is essential to produce supported nanostructures in a controllable way for a broad range of applications and technologies.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 4.536
Times cited: 66
DOI: 10.1021/acs.jpcc.7b01104
|
|
|
“Bottom-Up Mechanical Nanometrology of Granular Ag Nanoparticles Thin Films”. Benetti G, Caddeo C, Melis C, Ferrini G, Giannetti C, Winckelmans N, Bals S, J Van Bael M, Cavaliere E, Gavioli L, Banfi F, The journal of physical chemistry: C : nanomaterials and interfaces 121, 22434 (2017). http://doi.org/10.1021/acs.jpcc.7b05795
Abstract: Ultrathin metal nanoparticles coatings, synthesized by gas-phase deposition, are emerging as go-to materials in a variety of fields ranging from pathogens control, sensing to energy storage. Predicting their morphology and mechanical properties beyond a trial-and-error approach is a crucial issue limiting their exploitation in real-life applications. The morphology and mechanical properties of Ag nanoparticles ultrathin films, synthesized by supersonic cluster beam deposition, are here assessed adopting a bottom-up, multi-technique approach. A virtual film model is proposed merging high resolution scanning transmission electron microscopy, supersonic cluster beam dynamics and molecular dynamics simulations. The model is validated against mechanical nanometrology measurements and is readily extendable to metals other than Ag. The virtual film is shown to be a flexible and reliable predictive tool to access morphology-dependent properties such as mesoscale gas-dynamics and elasticity of ultrathin films synthesized by gas-phase deposition.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 4.536
Times cited: 30
DOI: 10.1021/acs.jpcc.7b05795
|
|
|
“Mechanistic Insight into the Photocatalytic Working of Fluorinated Anatase {001} Nanosheets”. Kus M, Altantzis T, Vercauteren S, Caretti I, Leenaerts O, Batenburg KJ, Mertens M, Meynen V, Partoens B, Van Doorslaer S, Bals S, Cool P, The journal of physical chemistry: C : nanomaterials and interfaces 121, 26275 (2017). http://doi.org/10.1021/acs.jpcc.7b05586
Abstract: Anatase nanosheets with exposed {001} facets
have gained increasing interest for photocatalytic applications. To
fully understand the structure-to-activity relation, combined
experimental and computational methods have been exploited.
Anatase nanosheets were prepared under hydrothermal conditions
in the presence of fluorine ions. High resolution scanning
transmission electron microscopy was used to fully characterize
the synthesized material, confirming the TiO2 nanosheet
morphology. Moreover, the surface structure and composition
of a single nanosheet could be determined by annular bright-field
scanning transmission electron microscopy (ABF-STEM) and
STEM electron energy loss spectroscopy (STEM-EELS). The photocatalytic activity was tested for the decomposition of organic
dyes rhodamine 6G and methyl orange and compared to a reference TiO2 anatase sample. The anatase nanosheets with exposed
{001} facets revealed a significantly lower photocatalytic activity compared to the reference. In order to understand the
mechanism for the catalytic performance, and to investigate the role of the presence of F−, light-induced electron paramagnetic
resonance (EPR) experiments were performed. The EPR results are in agreement with TEM, proving the presence of Ti3+
species close to the surface of the sample and allowing the analysis of the photoinduced formation of paramagnetic species.
Further, ab initio calculations of the anisotropic effective mass of electrons and electron holes in anatase show a very high effective
mass of electrons in the [001] direction, having a negative impact on the mobility of electrons toward the {001} surface and thus
the photocatalysis. Finally, motivated by the experimental results that indicate the presence of fluorine atoms at the surface, we
performed ab initio calculations to determine the position of the band edges in anatase slabs with different terminations of the
{001} surface. The presence of fluorine atoms near the surface is shown to strongly shift down the band edges, which indicates
another reason why it can be expected that the prepared samples with a large amount of {001} surface, but with fluorine atoms
near the surface, show only a low photocatalytic activity.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT); Condensed Matter Theory (CMT); Laboratory of adsorption and catalysis (LADCA)
Impact Factor: 4.536
Times cited: 20
DOI: 10.1021/acs.jpcc.7b05586
|
|
|
“Multimode Electron Tomography as a Tool to Characterize the Internal Structure and Morphology of Gold Nanoparticles”. Winckelmans N, Altantzis T, Grzelczak M, Sánchez-Iglesias A, Liz-Marzán LM, Bals S, The journal of physical chemistry: C : nanomaterials and interfaces 122, 13522 (2018). http://doi.org/10.1021/acs.jpcc.7b12379
Abstract: Three dimensional (3D) characterization of structural defects in nanoparticles by transmission electron microscopy is far from straightforward. We propose the use of a dose-efficient approach, so-called multimode tomography, during which tilt series of low and high angle annular dark field scanning transmission electron microscopy projection images are acquired simultaneously. In this manner, not only reliable information can be obtained concerning the shape of the nanoparticles, but also the twin planes can be clearly visualized in 3D. As an example, we demonstrate the application of this approach to identify the position of the seeds with respect to the twinning planes in anisotropic gold nanoparticles synthesized using a seed mediated growth approach.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 4.536
Times cited: 23
DOI: 10.1021/acs.jpcc.7b12379
|
|
|
“Do Binary Supracrystals Enhance the Crystal Stability?”.Yang Z, Altantzis T, Bals S, Tendeloo GV, Pileni M-P, The journal of physical chemistry: C : nanomaterials and interfaces 122, 13515 (2018). http://doi.org/10.1021/acs.jpcc.7b12373
Abstract: We study the oxygen thermal stability of two binary
systems. The larger particles are magnetic amorphous Co (7.2 nm) or
Fe3O4 (7.5 nm) nanocrystals, whereas the smaller ones (3.7 nm) are
Au nanocrystals. The nanocrystal ordering as well as the choice of the
magnetic nanoparticles very much influence the stability of the binary
system. A perfect crystalline structure is obtained with the Fe3O4/Au
binary supracrystals. For the Co/Au binary system, oxidation of Co
results in the chemical transformation from Co to CoO, where the size
of the amorphous Co nanoparticles increases from 7.2 to 9.8 nm in
diameter. During the volume expansion of the Co nanoparticles, Au
nanoparticles within the binary assemblies coalesce and are at the
origin of the instability of the binary nanoparticle supracrystals. On the
other hand, for the Fe3O4/Au binary system, the oxidation of Fe3O4 to
γ-Fe2O3 does not lead to a size change of the nanoparticles, which
maintains the stability of the binary nanoparticle supracrystals. A similar behavior is observed for an AlB2-type Co−Ag binary
system: The crystalline structure is maintained, whereas in disordered assemblies, coalescence of Ag nanocrystals is observed.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 4.536
Times cited: 5
DOI: 10.1021/acs.jpcc.7b12373
|
|
|
“On the control and effect of water content during the electrodeposition of Ni nanostructures from deep eutectic solvents”. Cherigui EAM, Şentosun K, Mamme MH, Lukaczynska M, Terryn H, Bals S, Ustarroz J, The journal of physical chemistry: C : nanomaterials and interfaces 122, 23129 (2018). http://doi.org/10.1021/acs.jpcc.8b05344
Abstract: The electrodeposition of nickel nanostructures on glassy carbon was investigated in 1:2 choline chloride urea deep eutectic solvent (DES) containing different amounts of water. By combining electrochemical techniques, with ex situ field emission scanning electron microscopy, high-angle annular dark field scanning transmission electron microscopy, and energy-dispersive X-ray spectroscopy, the effect of water content on the electrochemical processes occurring during nickel deposition was better understood. At highly negative potentials and depending on water content, Ni growth is halted due to water splitting and formation of a mixed layer of Ni/NiOx(OH)(2(1-x)(ads)). Moreover, under certain conditions, the DES components can also be (electro)chemically reduced at the electrode surface, blocking further three-dimensional growth of the Ni NPs. Hence, a two-dimensional crystalline Ni-containing network can be formed in the interparticle region.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 4.536
Times cited: 27
DOI: 10.1021/acs.jpcc.8b05344
|
|
|
“Cuboidal supraparticles self-assembled from cubic CsPbBr3 perovskite nanocrystals”. van der Burgt JS, Geuchies JJ, van der Meer B, Vanrompay H, Zanaga D, Zhang Y, Albrecht W, Petukhov AV, Filion L, Bals S, Swart I, Vanmaekelbergh D, The journal of physical chemistry: C : nanomaterials and interfaces 122, 15706 (2018). http://doi.org/10.1021/ACS.JPCC.8B02699
Abstract: Colloidal CsPbBr3 nanocrystals (NCs) have emerged as promising candidates for various opto-electronic applications, such as light-emitting diodes, photodetectors, and solar cells. Here, we report on the self-assembly of cubic NCs from an organic suspension into ordered cuboidal supraparticles (SPs) and their structural and optical properties. Upon increasing the NC concentration or by addition of a nonsolvent, the formation of the SPs occurs homogeneously in the suspension, as monitored by in situ X-ray scattering measurements. The three-dimensional structure of the SPs was resolved through high-angle annular dark-field scanning transmission electron microscopy and electron tomography. The NCs are atomically aligned but not connected. We characterize NC vacancies on superlattice positions both in the bulk and on the surface of the SPs. The occurrence of localized atomic-type NC vacancies-instead of delocalized ones-indicates that NC-NC attractions are important in the assembly, as we verify with Monte Carlo simulations. Even when assembled in SPs, the NCs show bright emission, with a red shift of about 30 meV compared to NCs in suspension.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 4.536
Times cited: 60
DOI: 10.1021/ACS.JPCC.8B02699
|
|
|
“Nd3+-Doped Lanthanum Oxychloride Nanocrystals as Nanothermometers”. Renero-Lecuna C, Herrero A, Jimenez de Aberasturi D, Martínez-Flórez M, Valiente R, Mychinko M, Bals S, Liz-Marzán LM, Journal Of Physical Chemistry C 125, 19887 (2021). http://doi.org/10.1021/acs.jpcc.1c05828
Abstract: The development of optical nanothermometers operating in the near-infrared (NIR) is of high relevance toward temperature measurements in biological systems. We propose herein the use of Nd3+-doped lanthanum oxychloride nanocrystals as an efficient system with intense photoluminescence under NIR irradiation in the first biological transparency window and emission in the second biological window with excellent emission stability over time under 808 nm excitation, regardless of Nd3+ concentration, which can be considered as a particular strength of our system. Additionally, surface passivation through overgrowth of an inert LaOCl shell around optically active LaOCl/Nd3+ cores was found to further enhance the photoluminescence intensity and also the lifetime of the 1066 nm, 4F3/2 to 4I11/2 transition, without affecting its (ratiometric) sensitivity toward temperature changes. As required for biological applications, we show that the obtained (initially hydrophobic) nanocrystals can be readily transferred into aqueous solvents with high, long-term stability, through either ligand exchange or encapsulation with an amphiphilic polymer.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 4.536
Times cited: 9
DOI: 10.1021/acs.jpcc.1c05828
|
|