Abstract: Whereas deformation twinning is known to be an important deformation mechanism for hexagonal materials like magnesium and pure titanium, so far almost no literature exists on the twinning behaviour of the Ti-6Al-4V alloy. In this work it was shown that the activation of twinning as a deformation mechanism could have a pronounced effect on the mechanical behaviour of the Ti-6Al-4V alloy. This effect is even more pronounced under dynamic loading conditions. Transmission electron microscopy showed that only the {1 0 1 2}{1 0 1 1} tensile twin system was activated under certain loading conditions. Light-optical microscopy and electron backscatter diffraction data were afterwards used to experimentally determine the twin fractions. The importance of twinning for the texture evolution was also studied. It was shown that even small twin fractions can lead to distinct texture features, especially due to the discrete reorientation of the c-axes. The experimental results were compared to simulated results that were obtained with a viscoplastic self-consistent crystal plasticity code, after experimental validation that twinning can be reliably modelled as a unidirectional slip system. Although good agreement was obtained for the experimental and simulated stress-strain curves, the simulated results concerning twinning correlated well only on a qualitative basis as the simulated twin fractions were systematically higher than the experimental fractions. This seems to strengthen the hypothesis made by other research groups that complete grains might reorient by twinning. (C) 2011 Elsevier B.V. All rights reserved.

Abstract: This study reports the properties of irradiation assisted stress corrosion crack tips extracted by means of focused-ion beam from 60 to 80 dpa neutron-irradiated O-ring specimens tested under straining conditions under a pressurized-water reactor environment. Various crack tip morphologies and surrounding deformation features were analyzed as a function of applied stress, surface oxidation state and loading form – constant versus cyclic. All investigated cracks exhibit grain boundary oxidation in front of the crack tip, with the extent of oxidation being proportional to applied stress. These findings clearly demonstrate that, under the subcritical crack propagation regime, the grain boundary oxide grows faster than the crack. On the other hand, crack tips appertaining to specimens with removed oxide layer at the outer surface show comparatively less oxidation at the crack tip, which could indicate towards crack initiation from regions that exemplify lower stress, such as the O-ring inner surface. Cyclic loading is found to have a more pronounced effect on the crack tip microstructure, demonstrating increased deformation twinning and -martensitic transformation, which signifies towards an increased susceptibility to intergranular failure. Still, the extent of crack tip grain boundary oxidation in this case agrees well with expected values for maximum stress applied during cyclic loading. All results are interpreted based on the probabilistic subcritical crack propagation mechanism and provide strong support to a stress-driven internal oxidation model.

Abstract: In the present work two different cold working and annealing schemes were utilized, and the asymmetric superelastic response of thermomechanically processed materials were then assessed through cyclic tensile and compressive modes of deformation. The values of transformation stress, transformation strain, and pseudoelastic strain were measured for each treated and solutionized specimens and the asymmetric response was compared. In the solution annealed state, the difference of these parameters at different deformation modes was negligible due to the weak texture of the material, while for thermomechanically treated ones, development of specific deformation and recrystallization texture components was identified to be one of the underlying reasons of intensified asymmetry. The evolved substructure during the thermomechanical processing also played a substantial role in determining the asymmetric response. The presence of fine grains and dense dislocation substructure could hinder the movement of the transformation front, thus limiting the range of transformation. In tensile mode, the transformation stress was lower, but higher transformation strain was achieved, which was discussed relying on the slip activity in specified oriented grains. The lower transformation strain in compression mode led to lower pseudoelastic strain due to the narrow transformation range which finally degraded superelastic response of the material. (C) 2021 Elsevier B.V. All rights reserved.

Abstract: The microstructure of various compounds of the Ti-Ni-Au alloy system is investigated by transmission electron microscopy in relation with changing lattice parameters improving the compatibility conditions between austenite and martensite expressed by the lambda(2) = 1 equation based on the Geometrically NonLinear Theory of Martensite (GNLTM). Although local differences in microstructure are observed, when increasing the gold content compound twins are replaced by Type I twins, while twinned lamellar structures are replaced by untwinned plates and self-accommodating structures when lambda(2) = 1 is approached, all confirming the predictions of the GNLTM. (c) 2013 Elsevier B.V. All rights reserved.

Abstract: The 3D size, morphology and distribution of autocatalytic-grown Ni4Ti3 precipitates in a Ni51Ti49 single crystal were characterized via a FIB/SEM Slice-and-View procedure and phase-field simulation. Important parameters on size and shape of the precipitates were measured. The pair distribution function and the minimum distance between two precipitates from different variants were calculated to describe the 3D distribution of the autocatalytic-grown Ni4Ti3 precipitates in single crystal Ni-Ti, with a comparison to the polycrystalline Ni50.8Ti49.2 alloy. Phase-field simulation was conducted to study the nucleation behavior of precipitates in the single crystal Ni-Ti. (C) 2012 Elsevier B.V. All rights reserved.

Abstract: Anti-phase boundaries (APBs) in an ordered CoPt alloy are planar defects which disturb the ordered structure in their vicinity and decrease the magnetic properties. However, it has not yet been clarified to what extend the APBs disturb the ordering. In this study, high-resolution HAADF-STEM images are statistically analysed based on the image intensities estimated by the statistical parameter estimation theory. In the procedure, averaging intensities, fitting the intensity profiles to specific functions, and assessment based on a statistical test are performed. As a result, the APBs in the stable CoPt are found to be characterised by two atomic planes, and a contrast transition range as well as the centre of an inclined APB is determined. These results show that the APBs are quite sharp and therefore may have no notable effect on the net magnetic properties due to their small volume fraction. (C) 2015 Elsevier B.V. All rights reserved.

Abstract: The effects of high dose ion irradiation in β CuZnAl were investigated between room temperature and 150 °C. Single crystal samples with surface normal close to [001]β were irradiated with 300 keV Cu+ ions. Microstructural changes were characterized using transmission electron microscopy. Irradiation induced cavities located on the surface exposed to the irradiation were observed. The morphology, size and density distribution of these cavities were analyzed as a function of different irradiation conditions. The shape and location of the cavities with respect to the irradiation surface were not affected by irradiation temperature or irradiation dose. Instead, the cavity size distribution showed a bi-modal shape for a dose of 15 dpa, regardless of irradiation temperature. For a dose of 30 dpa the bi-modal distribution was only observed after room temperature irradiation. The diffusion effects of vacancies produced by irradiation are analyzed in shape memory CuZnAl alloys, which main characteristic is the diffusionless martensitic transformation. Particularly, the cavity size distributions were analyzed in terms of nucleation, growth and coalescence.

Abstract: Stained glass windows incorporating dark blue and purple enamel paint layers are in some cases subject to severe degradation while others from the same period survived the ravages of time. A series of dark blue, greenblue and purple enamel glass paints from the same region (Northwestern Europe) and from the same period (16early 20th centuries) has been studied by means of a combination of microscopic X-ray fluorescence analysis, electron probe micro analysis and transmission electron microscopy with the aim of better understanding the causes of the degradation. The chemical composition of the enamels diverges from the average chemical composition of window glass. Some of the compositions appear to be unstable, for example those with a high concentration of K2O and a low content of CaO and PbO. In other cases, the deterioration of the paint layers was caused by the less than optimal vitrification of the enamel during the firing process. Recipes and chemical compositions indicate that glassmakers of the 1617th century had full control over the color of the enamel glass paints they made. They mainly used three types of coloring agents, based on Co (dark blue), Mn (purple) and Cu (light-blue or greenblue) as coloring elements. Bluepurple enamel paints were obtained by mixing two different coloring agents. The coloring agent for redpurple enamel, introduced during the 19th century, was colloidal gold embedded in grains of lead glass.

Abstract: In-situ bright field transmission electron microscopy (TEM) nanomechanical tensile testing and in-situ automated crystallographic orientation mapping in TEM were combined to unravel the elementary mechanisms controlling the plasticity of ultrafine grained Aluminum freestanding thin films. The characterizations demonstrate that deformation proceeds with a transition from grain rotation to intragranular dislocation glide and starvation plasticity mechanism at about 1% deformation. The grain rotation is not affected by the character of the grain boundaries. No grain growth or twinning is detected. (C) 2014 AIP Publishing LLC.

Abstract: The orientation relationship of an austenite-to-ferrite phase transformation in 316L stainless steels induced by the loss of austenite stabilizers resulting from the steel dissolution corrosion in liquid Pb-Bi eutectic was studied by means of electron backscatter diffraction. The misorientations at the austenite/ferrite interface were compared to the prevailing orientation relationship models in steels. The Pitsch orientation relationship model was found to be predominant, which is unusual for austenite-to-ferrite bulk transformations in steels. The nature of this particular transformation, which involves loss of steel alloying elements and the presence of an interfacial liquid metal layer, is discussed to explain this finding. (C) 2019 Acta Materialia Inc. Published by Elsevier Ltd. All rights reserved.