| Records |
| Author |
Zaghi, A.E.; Buffière, M.; Brammertz, G.; Batuk, M.; Lenaers, N.; Kniknie, B.; Hadermann, J.; Meuris, M.; Poortmans, J.; Vleugels, J. |
| Title |
Mechanical synthesis of high purity Cu-In-Se alloy nanopowder as precursor for printed CISe thin film solar cells |
Type |
A1 Journal article |
| Year |
2014 |
Publication |
Advanced powder technology |
Abbreviated Journal |
Adv Powder Technol |
| Volume |
25 |
Issue |
4 |
Pages |
1254-1261 |
| Keywords |
A1 Journal article; Electron microscopy for materials research (EMAT) |
| Abstract |
Mechanical alloying and ball milling are low cost, up-scalable techniques for the preparation of high purity chalcogenide nanopowders to be used as precursor material for printing thin film solar cells. In this study, high purity copper indium selenium (Cu-In-Se) alloy nanopowders with 20-200 nm particle size were synthesized from macroscopic elemental Cu, In and Se powders via mechanical alloying and planetary ball milling. The particle size distribution, morphology, composition, and purity level of the synthesized Cu-In-Se alloy nanopowders were investigated. Thin Cu-In-Se alloy nanopowder ink coatings, deposited on Mo-coated glass substrates by doctor blading, were converted into a CuInSe2 semiconductor film by selenization heat treatment in Se vapor. The CuInSe2 film showed semiconducting band gap around 1 eV measured by photoluminescence spectroscopy. CuInSe2 absorber layer based thin film solar cell devices were fabricated to assess their performance. The solar cell device showed a total efficiency of 4.8%, as measured on 0.25 cm(2) area cell. (c) 2014 The Society of Powder Technology Japan. Published by Elsevier B.V. and The Society of Powder Technology Japan. All rights reserved. |
Address  |
|
| Corporate Author |
|
Thesis |
|
| Publisher |
|
Place of Publication |
Zeist |
Editor |
|
| Language |
|
Wos |
000341871700015 |
Publication Date |
2014-03-17 |
| Series Editor |
|
Series Title |
|
Abbreviated Series Title |
|
| Series Volume |
|
Series Issue |
|
Edition |
|
| ISSN |
0921-8831; |
ISBN |
|
Additional Links |
UA library record; WoS full record; WoS citing articles |
| Impact Factor |
2.659 |
Times cited |
10 |
Open Access |
|
| Notes |
|
Approved |
Most recent IF: 2.659; 2014 IF: 2.638 |
| Call Number |
UA @ lucian @ c:irua:119896 |
Serial |
1977 |
| Permanent link to this record |
| |
|
| |
| Author |
Liu, Y.; Norén, L.; Withers, R.L.; Hadermann, J.; Van Tendeloo, G.; Garcia-Garcia, J. |
| Title |
The metastable Ni7\pm xS6 and mixed Ni6\pm x(S1-ySey)5 phases |
Type |
A1 Journal article |
| Year |
2003 |
Publication |
Journal of solid state chemistry |
Abbreviated Journal |
J Solid State Chem |
| Volume |
170 |
Issue |
|
Pages |
351-360 |
| Keywords |
A1 Journal article; Electron microscopy for materials research (EMAT) |
| Abstract |
|
| Address |
|
| Corporate Author |
|
Thesis |
|
| Publisher |
|
Place of Publication |
London |
Editor |
|
| Language |
|
Wos |
000181875200019 |
Publication Date |
2003-06-02 |
| Series Editor |
|
Series Title |
|
Abbreviated Series Title |
|
| Series Volume |
|
Series Issue |
|
Edition |
|
| ISSN |
0022-4596; |
ISBN |
|
Additional Links |
UA library record; WoS full record; WoS citing articles |
| Impact Factor |
2.299 |
Times cited |
5 |
Open Access |
|
| Notes |
|
Approved |
Most recent IF: 2.299; 2003 IF: 1.413 |
| Call Number |
UA @ lucian @ c:irua:42054 |
Serial |
2015 |
| Permanent link to this record |
| |
|
| |
| Author |
Buffière, M.; Brammertz, G.; Batuk, M.; Verbist, C.; Mangin, D.; Koble, C.; Hadermann, J.; Meuris, M.; Poortmans, J. |
| Title |
Microstructural analysis of 9.7% efficient Cu2ZnSnSe4 thin film solar cells |
Type |
A1 Journal article |
| Year |
2014 |
Publication |
Applied physics letters |
Abbreviated Journal |
Appl Phys Lett |
| Volume |
105 |
Issue |
18 |
Pages |
183903 |
| Keywords |
A1 Journal article; Electron microscopy for materials research (EMAT) |
| Abstract |
This work presents a detailed analysis of the microstructure and the composition of our record Cu 2ZnSnSe4 (CZTSe)-CdS-ZnO solar cell with a total area efficiency of 9.7%. The average composition of the CZTSe crystallites is Cu 1.94 Zn 1.12Sn0.95Se3.99. Large crystals of ZnSe secondary phase (up to 400 nm diameter) are observed at the voids between the absorber and the back contact, while smaller ZnSe domains are segregated at the grain boundaries and close to the surface of the CZTSe grains. An underlying layer and some particles of Cu xSe are observed at the Mo-MoSe2-Cu2ZnSnSe4 interface. The free surface of the voids at the back interface is covered by an amorphous layer containing Cu, S, O, and C, while the presence of Cd, Na, and K is also observed in this region. |
| Address |
|
| Corporate Author |
|
Thesis |
|
| Publisher |
American Institute of Physics |
Place of Publication |
New York, N.Y. |
Editor |
|
| Language |
|
Wos |
000345000000086 |
Publication Date |
2014-11-08 |
| Series Editor |
|
Series Title |
|
Abbreviated Series Title |
|
| Series Volume |
|
Series Issue |
|
Edition |
|
| ISSN |
0003-6951;1077-3118; |
ISBN |
|
Additional Links |
UA library record; WoS full record; WoS citing articles |
| Impact Factor |
3.411 |
Times cited |
17 |
Open Access |
|
| Notes |
|
Approved |
Most recent IF: 3.411; 2014 IF: 3.302 |
| Call Number |
UA @ lucian @ c:irua:121329 |
Serial |
2038 |
| Permanent link to this record |
| |
|
| |
| Author |
Dixon, E.; Hadermann, J.; Ramos, S.; Goodwin, A.L.; Hayward, M.A. |
| Title |
Mn(I) in an extended oxide : the synthesis and characterization of La1-xCaxMnO2+\delta (0.6\leq x\leq1) |
Type |
A1 Journal article |
| Year |
2011 |
Publication |
Journal of the American Chemical Society |
Abbreviated Journal |
J Am Chem Soc |
| Volume |
133 |
Issue |
45 |
Pages |
18397-18405 |
| Keywords |
A1 Journal article; Electron microscopy for materials research (EMAT) |
| Abstract |
Reduction of La1xCaxMnO3 (0.6 ≤ x ≤ 1) perovskite phases with sodium hydride yields materials of composition La1xCaxMnO2+δ. The calcium-rich phases (x = 0.9, 1) adopt (La0.9Ca0.1)0.5Mn0.5O disordered rocksalt structures. However local structure analysis using reverse Monte Carlo refinement of models against pair distribution functions obtained from neutron total scattering data reveals lanthanum-rich La1xCaxMnO2+δ (x = 0.6, 0.67, 0.7) phases adopt disordered structures consisting of an intergrowth of sheets of MnO6 octahedra and sheets of MnO4 tetrahedra. X-ray absorption data confirm the presence of Mn(I) centers in La1xCaxMnO2+δ phases with x < 1. Low-temperature neutron diffraction data reveal La1xCaxMnO2+δ (x = 0.6, 0.67, 0.7) phases become antiferromagnetically ordered at low temperature. |
| Address |
|
| Corporate Author |
|
Thesis |
|
| Publisher |
|
Place of Publication |
Washington, D.C. |
Editor |
|
| Language |
|
Wos |
000297381200065 |
Publication Date |
2011-10-14 |
| Series Editor |
|
Series Title |
|
Abbreviated Series Title |
|
| Series Volume |
|
Series Issue |
|
Edition |
|
| ISSN |
0002-7863;1520-5126; |
ISBN |
|
Additional Links |
UA library record; WoS full record; WoS citing articles |
| Impact Factor |
13.858 |
Times cited |
33 |
Open Access |
|
| Notes |
|
Approved |
Most recent IF: 13.858; 2011 IF: 9.907 |
| Call Number |
UA @ lucian @ c:irua:94030 |
Serial |
2094 |
| Permanent link to this record |
| |
|
| |
| Author |
Zhang, H.; Yang, J.-H.; Shpanchenko, R.V.; Abakumov, A.M.; Hadermann, J.; Clérac, R.; Dikarev, E.V. |
| Title |
New class of single-source precursors for the synthesis of main group-transition metal oxides: heterobimetallic Pb-Mn \beta-diketonates |
Type |
A1 Journal article |
| Year |
2009 |
Publication |
Inorganic chemistry |
Abbreviated Journal |
Inorg Chem |
| Volume |
48 |
Issue |
17 |
Pages |
8480-8488 |
| Keywords |
A1 Journal article; Electron microscopy for materials research (EMAT) |
| Abstract |
Heterometallic lead−manganese â-diketonates have been isolated in pure form by several synthetic methods that include solid-state and solution techniques. Two compounds with different Pb/Mn ratios, PbMn2(hfac)6 (1) and PbMn(hfac)4 (2) (hfac = hexafluoroacetylacetonate), can be obtained in quantitative yield by using different starting materials. Single crystal X-ray investigation revealed that the solid-state structure of 1 contains trinuclear molecules in which lead metal center is sandwiched between two [Mn(hfac)3] units, while 2 consists of infinite chains of alternating [Pb(hfac)2] and [Mn(hfac)2] fragments. The heterometallic structures are held together by strong Lewis acid−base interactions between metal atoms and diketonate ligands acting in chelating-bridging fashion. Spectroscopic investigation confirmed the retention of heterometallic structures in solutions of non-coordinating solvents as well as upon sublimation-deposition procedure. Thermal decomposition of heterometallic diketonates has been systematically investigated in a wide range of temperatures and annealing times. For the first time, it has been shown that thermal decomposition of heterometallic diketonates results in mixed-metal oxides, while both the structure of precursors and the thermolysis conditions have a significant influence on the nature of the resulting oxides. Five different Pb−Mn oxides have been detected by X-ray powder diffraction when studying the decomposition of 1 and 2 in the temperature range 500−800 °C. The phase that has been previously reported as Pb0.43MnO2.18 was synthesized in the pure form by decomposition of 1, and crystallographically characterized. The orthorhombic unit cell parameters of this oxide, obtained by electron diffraction technique, have been subsequently refined using X-ray powder diffraction data. Besides that, a previously unknown lead−manganese oxide has been obtained at low temperature decomposition and short annealing times. The parameters of its monoclinically distorted unit cell have been determined. The EDX analysis revealed that this compound has a Pb/Mn ratio close to 1:4 and contains no appreciable amount of fluorine. |
| Address |
|
| Corporate Author |
|
Thesis |
|
| Publisher |
|
Place of Publication |
Easton, Pa |
Editor |
|
| Language |
|
Wos |
000269313500056 |
Publication Date |
2009-08-04 |
| Series Editor |
|
Series Title |
|
Abbreviated Series Title |
|
| Series Volume |
|
Series Issue |
|
Edition |
|
| ISSN |
0020-1669;1520-510X; |
ISBN |
|
Additional Links |
UA library record; WoS full record; WoS citing articles |
| Impact Factor |
4.857 |
Times cited |
28 |
Open Access |
|
| Notes |
|
Approved |
Most recent IF: 4.857; 2009 IF: 4.657 |
| Call Number |
UA @ lucian @ c:irua:78486 |
Serial |
2308 |
| Permanent link to this record |
| |
|
| |
| Author |
Shpanchenko, R.V.; Tsirlin, A.A.; Kondakova, E.S.; Antipov, E.V.; Bougerol, C.; Hadermann, J.; Van Tendeloo, G.; Sakurai, H.; Takayama-Muromachi, E. |
| Title |
New germanates RCrGeO5 (R=NdEr, Y): synthesis, structure, and properties |
Type |
A1 Journal article |
| Year |
2008 |
Publication |
Journal of solid state chemistry |
Abbreviated Journal |
J Solid State Chem |
| Volume |
181 |
Issue |
9 |
Pages |
2433-2441 |
| Keywords |
A1 Journal article; Electron microscopy for materials research (EMAT) |
| Abstract |
The new complex germanates RCrGeO5 (R=NdEr, Y) have been synthesized and investigated by means of X-ray powder diffraction, electron microscopy, magnetic susceptibility and specific heat measurements. All the compounds are isostructural and crystallize in the orthorhombic symmetry, space group Pbam, and Z=4. The crystal structure of RCrGeO5, as refined using X-ray powder diffraction data, includes infinite chains built by edge-sharing Cr+3O6 octahedra with two alternating Cr−Cr distances. The chains are combined into a three-dimensional framework by Ge2O8 groups consisting of two edge-linked square pyramids oriented in opposite directions. The resulting framework contains pentagonal channels where rare-earth elements are located. Thus, RCrGeO5 germanates present new examples of RMn2O5-type compounds and show ordering of Cr+3 and Ge+4 cations. Electron diffraction as well as high-resolution electron microscopy confirm the structure solution. Magnetic susceptibility data for R=Nd, Sm, and Eu are qualitatively consistent with the presence of isolated 3d (antiferromagnetically coupled Cr+3 cations) and 4f (R+3) spin subsystems in the RCrGeO5 compounds. NdCrGeO5 undergoes long-range magnetic ordering at 2.6 K, while SmCrGeO5 and EuCrGeO5 do not show any phase transitions down to 2 K. |
| Address |
|
| Corporate Author |
|
Thesis |
|
| Publisher |
|
Place of Publication |
London |
Editor |
|
| Language |
|
Wos |
000259415800047 |
Publication Date |
2008-06-06 |
| Series Editor |
|
Series Title |
|
Abbreviated Series Title |
|
| Series Volume |
|
Series Issue |
|
Edition |
|
| ISSN |
0022-4596; |
ISBN |
|
Additional Links |
UA library record; WoS full record; WoS citing articles |
| Impact Factor |
2.299 |
Times cited |
6 |
Open Access |
|
| Notes |
|
Approved |
Most recent IF: 2.299; 2008 IF: 1.910 |
| Call Number |
UA @ lucian @ c:irua:72948 |
Serial |
2314 |
| Permanent link to this record |
| |
|
| |
| Author |
Shpanchenko, R.V.; Lapshina, O.A.; Antipov, E.V.; Hadermann, J.; Kaul, E.E.; Geibel, C. |
| Title |
New lead vanadium phosphate with langbeinite-type structure: Pb1.5V2(PO4)3 |
Type |
A1 Journal article |
| Year |
2005 |
Publication |
Materials research bulletin |
Abbreviated Journal |
Mater Res Bull |
| Volume |
40 |
Issue |
9 |
Pages |
1569-1576 |
| Keywords |
A1 Journal article; Electron microscopy for materials research (EMAT) |
| Abstract |
|
| Address |
|
| Corporate Author |
|
Thesis |
|
| Publisher |
|
Place of Publication |
New York, N.Y. |
Editor |
|
| Language |
|
Wos |
000231208100018 |
Publication Date |
2005-06-01 |
| Series Editor |
|
Series Title |
|
Abbreviated Series Title |
|
| Series Volume |
|
Series Issue |
|
Edition |
|
| ISSN |
0025-5408; |
ISBN |
|
Additional Links |
UA library record; WoS full record; WoS citing articles |
| Impact Factor |
2.446 |
Times cited |
14 |
Open Access |
|
| Notes |
|
Approved |
Most recent IF: 2.446; 2005 IF: 1.380 |
| Call Number |
UA @ lucian @ c:irua:55031 |
Serial |
2320 |
| Permanent link to this record |
| |
|
| |
| Author |
Hadermann, J.; Abakumov, A.M.; Perkisas, T.; d' Hondt, H.; Tan, H.; Verbeeck, J.; Filonenko, V.P.; Antipov, E.V.; Van Tendeloo, G. |
| Title |
New perovskite-based manganite Pb2Mn2O5 |
Type |
A1 Journal article |
| Year |
2010 |
Publication |
Journal of solid state chemistry |
Abbreviated Journal |
J Solid State Chem |
| Volume |
183 |
Issue |
183 |
Pages |
2190-2195 |
| Keywords |
A1 Journal article; Electron microscopy for materials research (EMAT) |
| Abstract |
A new perovskite based compound Pb2Mn2O5 has been synthesized using a high pressure high temperature technique. The structure model of Pb2Mn2O5 is proposed based on electron diffraction, high angle annular dark field scanning transmission electron microscopy and high resolution transmission electron microscopy. The compound crystallizes in an orthorhombic unit cell with parameters a=5.736(1)Å≈√2a p p p (a p the parameter of the perovskite subcell) and space group Pnma. The Pb2Mn2O5 structure consists of quasi two-dimensional perovskite blocks separated by 1/2[110] p (1̄01) p crystallographic shear planes. The blocks are connected to each other by chains of edge-sharing MnO5 distorted tetragonal pyramids. The chains of MnO5 pyramids and the MnO6 octahedra of the perovskite blocks delimit six-sided tunnels accommodating double chains of Pb atoms. The tunnels and pyramidal chains adopt two mirror-related configurations (left L and right R) and layers consisting of chains and tunnels of the same configuration alternate in the structure according to an -LRLR-sequence. The sequence is sometimes locally violated by the appearance of -LL- or -RR-fragments. A scheme is proposed with a JahnTeller distortion of the MnO6 octahedra with two long and two short bonds lying in the ac plane, along two perpendicular orientations within this plane, forming a d-type pattern. |
| Address |
|
| Corporate Author |
|
Thesis |
|
| Publisher |
|
Place of Publication |
London |
Editor |
|
| Language |
|
Wos |
000282139600041 |
Publication Date |
2010-07-25 |
| Series Editor |
|
Series Title |
|
Abbreviated Series Title |
|
| Series Volume |
|
Series Issue |
|
Edition |
|
| ISSN |
0022-4596; |
ISBN |
|
Additional Links |
UA library record; WoS full record; WoS citing articles |
| Impact Factor |
2.299 |
Times cited |
8 |
Open Access |
|
| Notes |
Fwo; Bof; Esteem 026019 |
Approved |
Most recent IF: 2.299; 2010 IF: 2.261 |
| Call Number |
UA @ lucian @ c:irua:85472UA @ admin @ c:irua:85472 |
Serial |
2332 |
| Permanent link to this record |
| |
|
| |
| Author |
Pelloquin, D.; Hadermann, J.; Giot, M.; Caignaert, V.; Michel, C.; Hervieu, M.; Raveau, B. |
| Title |
Novel, oxygen-deficient n=3 RP-member Sr3NdFe3O9-\delta and its topotactic derivatives |
Type |
A1 Journal article |
| Year |
2004 |
Publication |
Chemistry of materials |
Abbreviated Journal |
Chem Mater |
| Volume |
16 |
Issue |
|
Pages |
1715-1724 |
| Keywords |
A1 Journal article; Electron microscopy for materials research (EMAT) |
| Abstract |
|
| Address |
|
| Corporate Author |
|
Thesis |
|
| Publisher |
|
Place of Publication |
Washington, D.C. |
Editor |
|
| Language |
|
Wos |
000221345000019 |
Publication Date |
2004-04-27 |
| Series Editor |
|
Series Title |
|
Abbreviated Series Title |
|
| Series Volume |
|
Series Issue |
|
Edition |
|
| ISSN |
0897-4756;1520-5002; |
ISBN |
|
Additional Links |
UA library record; WoS full record; WoS citing articles |
| Impact Factor |
9.466 |
Times cited |
24 |
Open Access |
|
| Notes |
|
Approved |
Most recent IF: 9.466; 2004 IF: 4.103 |
| Call Number |
UA @ lucian @ c:irua:47318 |
Serial |
2381 |
| Permanent link to this record |
| |
|
| |
| Author |
Abakumov, A.M.; Hadermann, J.; Tsirlin, A.A.; Tan, H.; Verbeeck, J.; Zhang, H.; Dikarev, E.V.; Shpanchenko, R.V.; Antipov, E.V. |
| Title |
Original close-packed structure and magnetic properties of the Pb4Mn9O20 manganite |
Type |
A1 Journal article |
| Year |
2009 |
Publication |
Journal of solid state chemistry |
Abbreviated Journal |
J Solid State Chem |
| Volume |
182 |
Issue |
8 |
Pages |
2231-2238 |
| Keywords |
A1 Journal article; Electron microscopy for materials research (EMAT) |
| Abstract |
The crystal structure of the Pb4Mn9O20 compound (previously known as Pb0.43MnO2.18) was solved from powder X-ray diffraction, electron diffraction, and high resolution electron microscopy data (S.G. Pnma, a=13.8888(2) Å, b=11.2665(2) Å, c=9.9867(1) Å, RI=0.016, RP=0.047). The structure is based on a 6H (cch)2 close packing of pure oxygen h-type (O16) layers alternating with mixed c-type (Pb4O12) layers. The Mn atoms occupy octahedral interstices formed by the oxygen atoms of the close-packed layers. The MnO6 octahedra share edges within the layers, whereas the octahedra in neighboring layers are linked through corner sharing. The relationship with the closely related Pb3Mn7O15 structure is discussed. Magnetization measurements reveal a peculiar magnetic behavior with a phase transition at 52 K, a small net magnetization below the transition temperature, and a tendency towards spin freezing. |
| Address |
|
| Corporate Author |
|
Thesis |
|
| Publisher |
|
Place of Publication |
London |
Editor |
|
| Language |
|
Wos |
000269066400035 |
Publication Date |
2009-06-12 |
| Series Editor |
|
Series Title |
|
Abbreviated Series Title |
|
| Series Volume |
|
Series Issue |
|
Edition |
|
| ISSN |
0022-4596; |
ISBN |
|
Additional Links |
UA library record; WoS full record; WoS citing articles |
| Impact Factor |
2.299 |
Times cited |
5 |
Open Access |
|
| Notes |
The authors are grateful to Christoph Geibel for the help in magnetization measurements. A.Ts. acknowledges MPI CKS for hospitality and financial support during the stay. E.D. thanks the National Science Foundation (CHE-0718900) for financial support. This work was supported by the Russian Foundation of Basic Research (RFBR Grants 07-03-00664-a, 06-03-90168-a and 07-03-00890-a). The authors acknowledge financial support from the European Union under the Framework 6 program under a contract for an Integrated Infrastructure Initiative. Reference 026019 ESTEEM. |
Approved |
Most recent IF: 2.299; 2009 IF: 2.340 |
| Call Number |
UA @ lucian @ c:irua:78935UA @ admin @ c:irua:78935 |
Serial |
2529 |
| Permanent link to this record |
| |
|
| |
| Author |
Antipov, E.V.; Abakumov, A.M.; Alekseeva, A.M.; Rozova, M.G.; Hadermann, J.; Lebedev, O.I.; Van Tendeloo, G. |
| Title |
Oxygen and fluorine doping in Sr2MnGaO5 brownmillerite |
Type |
A1 Journal article |
| Year |
2004 |
Publication |
Physica status solidi: A: applied research |
Abbreviated Journal |
Phys Status Solidi A |
| Volume |
201 |
Issue |
7 |
Pages |
1403-1409 |
| Keywords |
A1 Journal article; Electron microscopy for materials research (EMAT) |
| Abstract |
|
| Address |
|
| Corporate Author |
|
Thesis |
|
| Publisher |
|
Place of Publication |
Berlin |
Editor |
|
| Language |
|
Wos |
000221836300008 |
Publication Date |
2004-04-21 |
| Series Editor |
|
Series Title |
|
Abbreviated Series Title |
|
| Series Volume |
|
Series Issue |
|
Edition |
|
| ISSN |
0031-8965;1521-396X; |
ISBN |
|
Additional Links |
UA library record; WoS full record; WoS citing articles |
| Impact Factor |
|
Times cited |
9 |
Open Access |
|
| Notes |
|
Approved |
Most recent IF: NA |
| Call Number |
UA @ lucian @ c:irua:49464 |
Serial |
2544 |
| Permanent link to this record |
| |
|
| |
| Author |
Gillie, L.J.; Hadermann, J.; Hervieu, M.; Maignan, A.; Martin, C. |
| Title |
Oxygen vacancy ordering in the double-layered Ruddlesden-Popper cobaltite Sm2BaCo2O7-\delta |
Type |
A1 Journal article |
| Year |
2008 |
Publication |
Chemistry of materials |
Abbreviated Journal |
Chem Mater |
| Volume |
20 |
Issue |
19 |
Pages |
6231-6237 |
| Keywords |
A1 Journal article; Electron microscopy for materials research (EMAT) |
| Abstract |
A new oxygen-deficient Ruddlesden−Popper (RP) cobaltite Sm2BaCo2O7−δ (δ ≈ 1.0) has been synthesized and the crystal structure elucidated by Rietveld analysis of X-ray powder diffraction (XRD) data and transmission electron microscopy (TEM). The phase crystallizes in a primitive orthorhombic unit cell, with lattice parameters a = 5.4371(4) Å; b = 5.4405(4) Å and c = 19.8629(6) Å, and space group Pnnm. Contrary to other oxygen-deficient cobalt RP phases, the oxygen vacancies are located in the equatorial positions of the [CoO] layers to give an intralayer structure similar to Sr2Mn2O5, which is not usually observed for cobalt-containing materials. The Sm3+ and Ba2+ cations show a strong preference for distinct sites, with the majority of the larger Ba2+ cations situated in the perovskite block layers and Sm3+ cations predominantly in the rock salt layers. Magnetic susceptibility data demonstrate the strong antiferromagnetic (AFM) character of Sm2BaCo2O7−δ. |
| Address |
|
| Corporate Author |
|
Thesis |
|
| Publisher |
|
Place of Publication |
Washington, D.C. |
Editor |
|
| Language |
|
Wos |
000259871500038 |
Publication Date |
2008-09-13 |
| Series Editor |
|
Series Title |
|
Abbreviated Series Title |
|
| Series Volume |
|
Series Issue |
|
Edition |
|
| ISSN |
0897-4756;1520-5002; |
ISBN |
|
Additional Links |
UA library record; WoS full record; WoS citing articles |
| Impact Factor |
9.466 |
Times cited |
7 |
Open Access |
|
| Notes |
|
Approved |
Most recent IF: 9.466; 2008 IF: 5.046 |
| Call Number |
UA @ lucian @ c:irua:72946 |
Serial |
2548 |
| Permanent link to this record |
| |
|
| |
| Author |
Retuerto, M.; Li, M.R.; Ignatov, A.; Croft, M.; Ramanujachary, K.V.; Chi, S.; Hodges, J.P.; Dachraoui, W.; Hadermann, J.; Tran, T.T.; Halasyamani, P.S.; Grams, C.P.; Hemberger, J.; Greenblatt, M.; |
| Title |
Polar and magnetic layered A-site and rock salt B-site-ordered NaLnFeWO6 (Ln = La, Nd) perovskites |
Type |
A1 Journal article |
| Year |
2013 |
Publication |
Inorganic chemistry |
Abbreviated Journal |
Inorg Chem |
| Volume |
52 |
Issue |
21 |
Pages |
12482-12491 |
| Keywords |
A1 Journal article; Electron microscopy for materials research (EMAT) |
| Abstract |
We have expanded the double perovskite family of materials with the unusual combination of layered order in the A sublattice and rock salt order over the B sublattice to compounds NaLaFeWO6 and NaNdFeWO6. The materials have been synthesized and studied by powder X-ray diffraction, neutron diffraction, electron diffraction, magnetic measurements, X-ray absorption spectroscopy, dielectric measurements, and second harmonic generation. At room temperature, the crystal structures of both compounds can be defined in the noncentrosymmetric monoclinic P2(1) space group resulting from the combination of ordering both in the A and B sublattices, the distortion of the cell due to tilting of the octahedra, and the displacement of certain cations. The magnetic studies show that both compounds are ordered antiferromagnetically below T-N approximate to 25 K for NaLaFeWO6 and at similar to 21 K for NaNdFeWO6. The magnetic structure of NaNdFeWO6 has been solved with a propagation vector k = (1/2 0 1/2) as an antiferromagnetic arrangement of Fe and Nd moments. Although the samples are potential multiferroics, the dielectric measurements do not show a ferroelectric response. |
| Address |
|
| Corporate Author |
|
Thesis |
|
| Publisher |
|
Place of Publication |
Easton, Pa |
Editor |
|
| Language |
|
Wos |
000326669200035 |
Publication Date |
2013-10-18 |
| Series Editor |
|
Series Title |
|
Abbreviated Series Title |
|
| Series Volume |
|
Series Issue |
|
Edition |
|
| ISSN |
0020-1669;1520-510X; |
ISBN |
|
Additional Links |
UA library record; WoS full record; WoS citing articles |
| Impact Factor |
4.857 |
Times cited |
17 |
Open Access |
|
| Notes |
|
Approved |
Most recent IF: 4.857; 2013 IF: 4.794 |
| Call Number |
UA @ lucian @ c:irua:112714 |
Serial |
2656 |
| Permanent link to this record |
| |
|
| |
| Author |
Li, M.R.; Walker, D.; Retuerto, M.; Sarkar, T.; Hadermann, J.; Stephens, P.W.; Croft, M.; Ignatov, A.; Grams, C.P.; Hemberger, J.; Nowik, I.; Halasyamani, P.S.; Tran, T.T.; Mukherjee, S.; Dasgupta, T.S.; Greenblatt, M.; |
| Title |
Polar and magnetic Mn2FeMO6 (M=Nb, Ta) with LiNbO3-type structure : high-pressure synthesis |
Type |
A1 Journal article |
| Year |
2013 |
Publication |
Angewandte Chemie: international edition in English |
Abbreviated Journal |
Angew Chem Int Edit |
| Volume |
52 |
Issue |
32 |
Pages |
8406-8410 |
| Keywords |
A1 Journal article; Electron microscopy for materials research (EMAT) |
| Abstract |
|
| Address |
|
| Corporate Author |
|
Thesis |
|
| Publisher |
|
Place of Publication |
Weinheim |
Editor |
|
| Language |
|
Wos |
000322631600044 |
Publication Date |
2013-06-27 |
| Series Editor |
|
Series Title |
|
Abbreviated Series Title |
|
| Series Volume |
|
Series Issue |
|
Edition |
|
| ISSN |
1433-7851; |
ISBN |
|
Additional Links |
UA library record; WoS full record; WoS citing articles |
| Impact Factor |
11.994 |
Times cited |
53 |
Open Access |
|
| Notes |
|
Approved |
Most recent IF: 11.994; 2013 IF: 11.336 |
| Call Number |
UA @ lucian @ c:irua:110749 |
Serial |
2657 |
| Permanent link to this record |
| |
|
| |
| Author |
Ban, V.; Soloninin, A.V.; Skripov, A.V.; Hadermann, J.; Abakumov, A.; Filinchuk, Y. |
| Title |
Pressure-Collapsed Amorphous Mg(BH4)(2): An Ultradense Complex Hydride Showing a Reversible Transition to the Porous Framework |
Type |
A1 Journal article |
| Year |
2014 |
Publication |
The journal of physical chemistry: C : nanomaterials and interfaces |
Abbreviated Journal |
J Phys Chem C |
| Volume |
118 |
Issue |
40 |
Pages |
23402-23408 |
| Keywords |
A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT) |
| Abstract |
Hydrogen-storage properties of complex hydrides depend of their form, such as a polymorphic form or an eutectic mixture. This Paper reports on an easy and reproducible way to synthesize a new stable form of magnesium borohydride by pressure-induced collapse of the porous gamma-Mg(BH4)(2). This amorphous complex hydride was investigated by temperature-programmed synchrotron X-ray diffraction (SXRD), transmission electron microscopy (TEM), thermogravimetric analysis, differential scanning calorimetry analysis, and Raman spectroscopy, and the dynamics of the BH4 reorientation was studied by spinlattice relaxation NMR spectroscopy. No long-range order is observed in the lattice region by Raman spectroscopy, while the internal vibration modes of the BH4 groups are the same as in the crystalline state. A hump at 4.9 angstrom in the SXRD pattern suggests the presence of nearly linear MgBH4 Mg fragments constituting all the known crystalline polymorphs of Mg(BH4)(2), which are essentially frameworks built of tetrahedral Mg nodes and linear BH4 linkers. TEM shows that the pressure-collapsed phase is amorphous down to the nanoscale, but surprisingly, SXRD reveals a transition at similar to 90 degrees C from the dense amorphous state (density of 0.98 g/cm(3)) back to the porous ? phase having only 0.55 g/cm(3) crystal density. The crystallization is slightly exothermic, with the enthalpy of -4.3 kJ/mol. The volumetric hydrogen density of the amorphous form is 145 g/L, one of the highest among hydrides. Remarkably, this form of Mg(BH4)2 has different reactivity compared to the crystalline forms. The parameters of the reorientational motion of BH4 groups in the amorphous Mg(BH4)(2) found from NMR measurements differ significantly from those in the known crystalline forms. The behavior of the nuclear spinlattice relaxation rates can be described in terms of a Gaussian distribution of the activation energies centered on 234 +/- 9 meV with the dispersion of 100 +/- 10 meV. |
| Address |
|
| Corporate Author |
|
Thesis |
|
| Publisher |
|
Place of Publication |
Washington, D.C. |
Editor |
|
| Language |
|
Wos |
000343016800067 |
Publication Date |
2014-09-26 |
| Series Editor |
|
Series Title |
|
Abbreviated Series Title |
|
| Series Volume |
|
Series Issue |
|
Edition |
|
| ISSN |
1932-7447;1932-7455; |
ISBN |
|
Additional Links |
UA library record; WoS full record; WoS citing articles |
| Impact Factor |
4.536 |
Times cited |
23 |
Open Access |
|
| Notes |
|
Approved |
Most recent IF: 4.536; 2014 IF: 4.772 |
| Call Number |
UA @ lucian @ c:irua:121113 |
Serial |
2711 |
| Permanent link to this record |
| |
|
| |
| Author |
Hardy, A.; Van Elshocht, S.; De Dobbelaere, C.; Hadermann, J.; Pourtois, G.; De Gendt, S.; Afanas'ev, V.V.; Van Bael, M.K. |
| Title |
Properties and thermal stability of solution processed ultrathin, high-k bismuth titanate (Bi2Ti2O7) films |
Type |
A1 Journal article |
| Year |
2012 |
Publication |
Materials research bulletin |
Abbreviated Journal |
Mater Res Bull |
| Volume |
47 |
Issue |
3 |
Pages |
511-517 |
| Keywords |
A1 Journal article; Electron microscopy for materials research (EMAT); Plasma Lab for Applications in Sustainability and Medicine – Antwerp (PLASMANT) |
| Abstract |
Ultrathin bismuth titanate films (Bi2Ti2O7, 5-25 nm) are deposited onto SiO2/Si substrates by aqueous chemical solution deposition and their evolution during annealing is studied. The films crystallize into a preferentially oriented, pure pyrochlore phase between 500 and 700 degrees C, depending on the film thickness and the total thermal budget. Crystallization causes a strong increase of surface roughness compared to amorphous films. An increase of the interfacial layer thickness is observed after anneal at 600 degrees C, together with intermixing of bismuth with the substrate as shown by TEM-EDX. The band gap was determined to be similar to 3 eV from photoconductivity measurements and high dielectric constants between 30 and 130 were determined from capacitance voltage measurements, depending on the processing conditions. (C) 2012 Elsevier Ltd. All rights reserved. |
| Address |
|
| Corporate Author |
|
Thesis |
|
| Publisher |
|
Place of Publication |
New York, N.Y. |
Editor |
|
| Language |
|
Wos |
000301994100001 |
Publication Date |
2012-01-10 |
| Series Editor |
|
Series Title |
|
Abbreviated Series Title |
|
| Series Volume |
|
Series Issue |
|
Edition |
|
| ISSN |
0025-5408; |
ISBN |
|
Additional Links |
UA library record; WoS full record; WoS citing articles |
| Impact Factor |
2.446 |
Times cited |
|
Open Access |
|
| Notes |
|
Approved |
Most recent IF: 2.446; 2012 IF: 1.913 |
| Call Number |
UA @ lucian @ c:irua:97797 |
Serial |
2727 |
| Permanent link to this record |
| |
|
| |
| Author |
Li, D.Y.; Zeng, Y.J.; Batuk, D.; Pereira, L.M.C.; Ye, Z.Z.; Fleischmann, C.; Menghini, M.; Nikitenko, S.; Hadermann, J.; Temst, K.; Vantomme, A.; Van Bael, M.J.; Locquet, J.P.; Van Haesendonck, C.; |
| Title |
Relaxor ferroelectricity and magnetoelectric coupling in ZnOCo nanocomposite thin films : beyond multiferroic composites |
Type |
A1 Journal article |
| Year |
2014 |
Publication |
ACS applied materials and interfaces |
Abbreviated Journal |
Acs Appl Mater Inter |
| Volume |
6 |
Issue |
7 |
Pages |
4737-4742 |
| Keywords |
A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT) |
| Abstract |
ZnOCo nanocomposite thin films are synthesized by combination of pulsed laser deposition of ZnO and Co ion implantation. Both superparamagnetism and relaxor ferroelectricity as well as magnetoelectric coupling in the nanocomposites have been demonstrated. The unexpected relaxor ferroelectricity is believed to be the result of the local lattice distortion induced by the incorporation of the Co nanoparticles. Magnetoelectric coupling can be attributed to the interaction between the electric dipole moments and the magnetic moments, which are both induced by the incorporation of Co. The introduced ZnOCo nanocomposite thin films are different from conventional strain-mediated multiferroic composites. |
| Address |
|
| Corporate Author |
|
Thesis |
|
| Publisher |
|
Place of Publication |
|
Editor |
|
| Language |
|
Wos |
000334572800018 |
Publication Date |
2014-03-05 |
| Series Editor |
|
Series Title |
|
Abbreviated Series Title |
|
| Series Volume |
|
Series Issue |
|
Edition |
|
| ISSN |
1944-8244;1944-8252; |
ISBN |
|
Additional Links |
UA library record; WoS full record; WoS citing articles |
| Impact Factor |
7.504 |
Times cited |
21 |
Open Access |
|
| Notes |
|
Approved |
Most recent IF: 7.504; 2014 IF: 6.723 |
| Call Number |
UA @ lucian @ c:irua:117063 |
Serial |
2864 |
| Permanent link to this record |
| |
|
| |
| Author |
Dachraoui, W.; Yang, T.; Liu, C.; Ling, G.; Hadermann, J.; Van Tendeloo, G.; Llobet, A.; Greenblatt, M. |
| Title |
Short-range layered A-site ordering in double perovskites NaLaBB'O6 (B = Mn, Fe; B' = Nb, Ta) |
Type |
A1 Journal article |
| Year |
2011 |
Publication |
Chemistry of materials |
Abbreviated Journal |
Chem Mater |
| Volume |
23 |
Issue |
9 |
Pages |
2398-2406 |
| Keywords |
A1 Journal article; Electron microscopy for materials research (EMAT) |
| Abstract |
The new compounds NaLaFeTaO6, NaLaFeNbO6, NaLaMnTaO6, and NaLaMnNbO6 have been synthesized and characterized with a combination of transmission electron microscopy, X-ray powder diffraction (XRPD), neutron powder diffraction (NPD), and magnetization measurements. Through electron microscopy study, a local layered order of the A-cations has been detected without the typical occurrence of rock salt order at the B-cation site. Satellite reflections in the electron diffraction related to the local layered order are not visible on the XRPD or NPD patterns. The occurrence of local layered order is supported by pair distribution function analysis, which also reveals the presence of uncorrelated displacements of the Nb and Ta cations. The octahedra are tilted according to the system a−b+a−, and the coordinates were refined from XRPD and NPD with a disordered cation distribution in the space group Pnma. The magnetic exchange interactions in NaLaFeTaO6 and NaLaFeNbO6 are antiferromagnetic, while they are ferromagnetic in NaLaMnTaO6 and NaLaMnNbO6. Long-range magnetic ordering is not observed down to 4 K for any of the compositions. |
| Address |
|
| Corporate Author |
|
Thesis |
|
| Publisher |
|
Place of Publication |
Washington, D.C. |
Editor |
|
| Language |
|
Wos |
000290063600016 |
Publication Date |
2011-04-14 |
| Series Editor |
|
Series Title |
|
Abbreviated Series Title |
|
| Series Volume |
|
Series Issue |
|
Edition |
|
| ISSN |
0897-4756;1520-5002; |
ISBN |
|
Additional Links |
UA library record; WoS full record; WoS citing articles |
| Impact Factor |
9.466 |
Times cited |
14 |
Open Access |
|
| Notes |
Esteem 026019 |
Approved |
Most recent IF: 9.466; 2011 IF: 7.286 |
| Call Number |
UA @ lucian @ c:irua:89944 |
Serial |
2996 |
| Permanent link to this record |
| |
|
| |
| Author |
Abakumov, A.M.; Hadermann, J.; Batuk, M.; d' Hondt, H.; Tyablikov, O.A.; Rozova, M.G.; Pokholok, K.V.; Filimonov, D.S.; Sheptyakov, D.V.; Tsirlin, A.A.; Niermann, D.; Hemberger, J.; Van Tendeloo, G.; Antipov, E.V. |
| Title |
Slicing the Perovskite structure with crystallographic shear planes : the AnBnO3n-2 homologous series |
Type |
A1 Journal article |
| Year |
2010 |
Publication |
Inorganic chemistry |
Abbreviated Journal |
Inorg Chem |
| Volume |
49 |
Issue |
20 |
Pages |
9508-9516 |
| Keywords |
A1 Journal article; Electron microscopy for materials research (EMAT) |
| Abstract |
A new AnBnO3n−2 homologous series of anion-deficient perovskites has been evidenced by preparation of the members with n = 5 (Pb2.9Ba2.1Fe4TiO13) and n = 6 (Pb3.8Bi0.2Ba2Fe4.2Ti1.8O16) in a single phase form. The crystal structures of these compounds were determined using a combination of transmission electron microscopy and X-ray and neutron powder diffraction (S.G. Ammm, a = 5.74313(7), b = 3.98402(4), c = 26.8378(4) Å, RI = 0.035, RP = 0.042 for Pb2.9Ba2.1Fe4TiO13 and S.G. Imma, a = 5.7199(1), b = 3.97066(7), c = 32.5245(8) Å, RI = 0.032, RP = 0.037 for Pb3.8Bi0.2Ba2Fe4.2Ti1.8O16). The crystal structures of the AnBnO3n−2 homologues are formed by slicing the perovskite structure with (01)p crystallographic shear (CS) planes. The shear planes remove a layer of oxygen atoms and displace the perovskite blocks with respect to each other by the 1/2[110]p vector. The CS planes introduce edge-sharing connections of the transition metal−oxygen polyhedra at the interface between the perovskite blocks. This results in intrinsically frustrated magnetic couplings between the perovskite blocks due to a competition of the exchange interactions between the edge- and the corner-sharing metal−oxygen polyhedra. Despite the magnetic frustration, neutron powder diffraction and Mssbauer spectroscopy reveal that Pb2.9Ba2.1Fe4TiO13 and Pb3.8Bi0.2Ba2Fe4.2Ti1.8O16 are antiferromagnetically ordered below TN = 407 and 343 K, respectively. The Pb2.9Ba2.1Fe4TiO13 and Pb3.8Bi0.2Ba2Fe4.2Ti1.8O16 compounds are in a paraelectric state in the 5−300 K temperature range. |
| Address |
|
| Corporate Author |
|
Thesis |
|
| Publisher |
|
Place of Publication |
Easton, Pa |
Editor |
|
| Language |
|
Wos |
000282783400051 |
Publication Date |
2010-09-24 |
| Series Editor |
|
Series Title |
|
Abbreviated Series Title |
|
| Series Volume |
|
Series Issue |
|
Edition |
|
| ISSN |
0020-1669;1520-510X; |
ISBN |
|
Additional Links |
UA library record; WoS full record; WoS citing articles |
| Impact Factor |
4.857 |
Times cited |
23 |
Open Access |
|
| Notes |
Esteem 026019; Fwo |
Approved |
Most recent IF: 4.857; 2010 IF: 4.326 |
| Call Number |
UA @ lucian @ c:irua:84963 |
Serial |
3041 |
| Permanent link to this record |
| |
|
| |
| Author |
Hadermann, J.; Abakumov, A.M.; Turner, S.; Hafideddine, Z.; Khasanova, N.R.; Antipov, E.V.; Van Tendeloo, G. |
| Title |
Solving the structure of Li ion battery materials with precession electron diffraction : application to Li2CoPo4F |
Type |
A1 Journal article |
| Year |
2011 |
Publication |
Chemistry of materials |
Abbreviated Journal |
Chem Mater |
| Volume |
23 |
Issue |
15 |
Pages |
3540-3545 |
| Keywords |
A1 Journal article; Electron microscopy for materials research (EMAT) |
| Abstract |
The crystal structure of the Li2CoPO4F high-voltage cathode for Li ion rechargeable batteries has been completely solved from precession electron diffraction (PED) data, including the location of the Li atoms. The crystal structure consists of infinite chains of CoO4F2 octahedra sharing common edges and linked into a 3D framework by PO4 tetrahedra. The chains and phosphate anions together delimit tunnels filled with the Li atoms. This investigation demonstrates that PED can be successfully applied for obtaining structural information on a variety of Li-containing electrode materials even from single micrometer-sized crystallites. |
| Address |
|
| Corporate Author |
|
Thesis |
|
| Publisher |
|
Place of Publication |
Washington, D.C. |
Editor |
|
| Language |
|
Wos |
000293357100019 |
Publication Date |
2011-07-11 |
| Series Editor |
|
Series Title |
|
Abbreviated Series Title |
|
| Series Volume |
|
Series Issue |
|
Edition |
|
| ISSN |
0897-4756;1520-5002; |
ISBN |
|
Additional Links |
UA library record; WoS full record; WoS citing articles |
| Impact Factor |
9.466 |
Times cited |
46 |
Open Access |
|
| Notes |
Fwo; Bof |
Approved |
Most recent IF: 9.466; 2011 IF: 7.286 |
| Call Number |
UA @ lucian @ c:irua:90357 |
Serial |
3053 |
| Permanent link to this record |
| |
|
| |
| Author |
Tsirlin, A.A.; Shpanchenko, R.V.; Antipov, E.V.; Bougerol, C.; Hadermann, J.; Van Tendeloo, G.; Schnelle, W.; Rosner, H. |
| Title |
Spin ladder compound Pb0.55Cd0.45V2O5: synthesis and investigation |
Type |
A1 Journal article |
| Year |
2007 |
Publication |
Physical review : B : condensed matter and materials physics |
Abbreviated Journal |
Phys Rev B |
| Volume |
76 |
Issue |
10 |
Pages |
104429,1-7 |
| Keywords |
A1 Journal article; Electron microscopy for materials research (EMAT) |
| Abstract |
|
| Address |
|
| Corporate Author |
|
Thesis |
|
| Publisher |
|
Place of Publication |
Lancaster, Pa |
Editor |
|
| Language |
|
Wos |
000249786300074 |
Publication Date |
2007-09-25 |
| Series Editor |
|
Series Title |
|
Abbreviated Series Title |
|
| Series Volume |
|
Series Issue |
|
Edition |
|
| ISSN |
1098-0121;1550-235X; |
ISBN |
|
Additional Links |
UA library record; WoS full record; WoS citing articles |
| Impact Factor |
3.836 |
Times cited |
1 |
Open Access |
|
| Notes |
|
Approved |
Most recent IF: 3.836; 2007 IF: 3.172 |
| Call Number |
UA @ lucian @ c:irua:65594 |
Serial |
3091 |
| Permanent link to this record |
| |
|
| |
| Author |
Abakumov, A.M.; Batuk, M.; Tsirlin, A.A.; Tyablikov, O.A.; Sheptyakov, D.V.; Filimonov, D.S.; Pokholok, K.V.; Zhidal, V.S.; Rozova, M.G.; Antipov, E.V.; Hadermann, J.; Van Tendeloo, G.; |
| Title |
Structural and magnetic phase transitions in the AnBnO3n-2 anion-deficient perovskites Pb2Ba2BiFe5O13 and Pb1.5Ba2.5Bi2Fe6O16 |
Type |
A1 Journal article |
| Year |
2013 |
Publication |
Inorganic chemistry |
Abbreviated Journal |
Inorg Chem |
| Volume |
52 |
Issue |
14 |
Pages |
7834-7843 |
| Keywords |
A1 Journal article; Electron microscopy for materials research (EMAT) |
| Abstract |
Novel anion-deficient perovskite-based ferrites Pb2Ba2BiFe5O13 and Pb1.5Ba2.5Bi2Fe6O16 were synthesized by solid-state reaction in air. Pb2Ba2BiFe5O13 and Pb1.5Ba2.5Bi2Fe6O16 belong to the perovskite-based AnBnO3n2 homologous series with n = 5 and 6, respectively, with a unit cell related to the perovskite subcell ap as ap√2 × ap × nap√2. Their structures are derived from the perovskite one by slicing it with 1/2[110]p(1̅01)p crystallographic shear (CS) planes. The CS operation results in (1̅01)p-shaped perovskite blocks with a thickness of (n 2) FeO6 octahedra connected to each other through double chains of edge-sharing FeO5 distorted tetragonal pyramids which can adopt two distinct mirror-related configurations. Ordering of chains with a different configuration provides an extra level of structure complexity. Above T ≈ 750 K for Pb2Ba2BiFe5O13 and T ≈ 400 K for Pb1.5Ba2.5Bi2Fe6O16 the chains have a disordered arrangement. On cooling, a second-order structural phase transition to the ordered state occurs in both compounds. Symmetry changes upon phase transition are analyzed using a combination of superspace crystallography and group theory approach. Correlations between the chain ordering pattern and octahedral tilting in the perovskite blocks are discussed. Pb2Ba2BiFe5O13 and Pb1.5Ba2.5Bi2Fe6O16 undergo a transition into an antiferromagnetically (AFM) ordered state, which is characterized by a G-type AFM ordering of the Fe magnetic moments within the perovskite blocks. The AFM perovskite blocks are stacked along the CS planes producing alternating FM and AFM-aligned FeFe pairs. In spite of the apparent frustration of the magnetic coupling between the perovskite blocks, all n = 4, 5, 6 AnFenO3n2 (A = Pb, Bi, Ba) feature robust antiferromagnetism with similar Néel temperatures of 623632 K. |
| Address |
|
| Corporate Author |
|
Thesis |
|
| Publisher |
|
Place of Publication |
Easton, Pa |
Editor |
|
| Language |
|
Wos |
000322087100006 |
Publication Date |
2013-02-13 |
| Series Editor |
|
Series Title |
|
Abbreviated Series Title |
|
| Series Volume |
|
Series Issue |
|
Edition |
|
| ISSN |
0020-1669;1520-510X; |
ISBN |
|
Additional Links |
UA library record; WoS full record; WoS citing articles |
| Impact Factor |
4.857 |
Times cited |
10 |
Open Access |
|
| Notes |
Countatoms |
Approved |
Most recent IF: 4.857; 2013 IF: 4.794 |
| Call Number |
UA @ lucian @ c:irua:109213 |
Serial |
3196 |
| Permanent link to this record |
| |
|
| |
| Author |
Hadermann, J.; Abakumov, A.M.; Lebedev, O.I.; Antipov, E.V.; Van Tendeloo, G. |
| Title |
Structural changes in fluorinated T{'} and T* phases |
Type |
P3 Proceeding |
| Year |
2000 |
Publication |
|
Abbreviated Journal |
|
| Volume |
|
Issue |
|
Pages |
193-194 |
| Keywords |
P3 Proceeding; Electron microscopy for materials research (EMAT) |
| Abstract |
|
| Address |
|
| Corporate Author |
|
Thesis |
|
| Publisher |
|
Place of Publication |
s.l. |
Editor |
|
| Language |
|
Wos |
|
Publication Date |
0000-00-00 |
| Series Editor |
|
Series Title |
|
Abbreviated Series Title |
|
| Series Volume |
|
Series Issue |
|
Edition |
|
| ISSN |
|
ISBN |
|
Additional Links |
UA library record |
| Impact Factor |
|
Times cited |
|
Open Access |
|
| Notes |
|
Approved |
Most recent IF: NA |
| Call Number |
UA @ lucian @ c:irua:36044 |
Serial |
3212 |
| Permanent link to this record |
| |
|
| |
| Author |
Gál, Z.A.; Rutt, O.J.; Smura, C.F.; Overton, T.P.; Barrier, N.; Clarke, S.J.; Hadermann, J. |
| Title |
Structural chemistry and metamagnetism of an homologous series of layered manganese oxysulfides |
Type |
A1 Journal article |
| Year |
2006 |
Publication |
Journal of the American Chemical Society |
Abbreviated Journal |
J Am Chem Soc |
| Volume |
128 |
Issue |
26 |
Pages |
8530-8540 |
| Keywords |
A1 Journal article; Electron microscopy for materials research (EMAT) |
| Abstract |
|
| Address |
|
| Corporate Author |
|
Thesis |
|
| Publisher |
|
Place of Publication |
Washington, D.C. |
Editor |
|
| Language |
|
Wos |
000238590000040 |
Publication Date |
2006-06-10 |
| Series Editor |
|
Series Title |
|
Abbreviated Series Title |
|
| Series Volume |
|
Series Issue |
|
Edition |
|
| ISSN |
0002-7863;1520-5126; |
ISBN |
|
Additional Links |
UA library record; WoS full record; WoS citing articles |
| Impact Factor |
13.858 |
Times cited |
39 |
Open Access |
|
| Notes |
Iap V-1 |
Approved |
Most recent IF: 13.858; 2006 IF: 7.696 |
| Call Number |
UA @ lucian @ c:irua:60030 |
Serial |
3225 |
| Permanent link to this record |
| |
|
| |
| Author |
Gardner, G.P.; Go, Y.B.; Robinson, D.M.; Smith, P.F.; Hadermann, J.; Abakumov, A.; Greenblatt, M.; Dismukes, G.C. |
| Title |
Structural requirements in lithium cobalt oxides for the catalytic oxidation of water |
Type |
A1 Journal article |
| Year |
2012 |
Publication |
Angewandte Chemie: international edition in English |
Abbreviated Journal |
Angew Chem Int Edit |
| Volume |
51 |
Issue |
7 |
Pages |
1616-1619 |
| Keywords |
A1 Journal article; Electron microscopy for materials research (EMAT) |
| Abstract |
|
| Address |
|
| Corporate Author |
|
Thesis |
|
| Publisher |
|
Place of Publication |
Weinheim |
Editor |
|
| Language |
|
Wos |
000299946400020 |
Publication Date |
2012-01-11 |
| Series Editor |
|
Series Title |
|
Abbreviated Series Title |
|
| Series Volume |
|
Series Issue |
|
Edition |
|
| ISSN |
1433-7851; |
ISBN |
|
Additional Links |
UA library record; WoS full record; WoS citing articles |
| Impact Factor |
11.994 |
Times cited |
119 |
Open Access |
|
| Notes |
|
Approved |
Most recent IF: 11.994; 2012 IF: 13.734 |
| Call Number |
UA @ lucian @ c:irua:99173 |
Serial |
3258 |
| Permanent link to this record |
| |
|
| |
| Author |
Hadermann, J.; Van Tendeloo, G.; Abakumov, A.M.; Pavlyuk, B.P.; Rozova, M.G.; Antipov, E.V. |
| Title |
Structural transformation in fluorinated LaACuGaO5 (A=Ca, Sr) brownmillerites |
Type |
A1 Journal article |
| Year |
2000 |
Publication |
International journal of inorganic materials |
Abbreviated Journal |
Int J Inorg Mater |
| Volume |
2 |
Issue |
6 |
Pages |
493-502 |
| Keywords |
A1 Journal article; Electron microscopy for materials research (EMAT) |
| Abstract |
|
| Address |
|
| Corporate Author |
|
Thesis |
|
| Publisher |
|
Place of Publication |
Amsterdam |
Editor |
|
| Language |
|
Wos |
000165985400005 |
Publication Date |
2002-07-25 |
| Series Editor |
|
Series Title |
|
Abbreviated Series Title |
|
| Series Volume |
|
Series Issue |
|
Edition |
|
| ISSN |
1466-6049; |
ISBN |
|
Additional Links |
UA library record; WoS full record; WoS citing articles |
| Impact Factor |
|
Times cited |
13 |
Open Access |
|
| Notes |
|
Approved |
Most recent IF: NA |
| Call Number |
UA @ lucian @ c:irua:36043 |
Serial |
3265 |
| Permanent link to this record |
| |
|
| |
| Author |
Hadermann, J.; Abakumov, A.M.; Lebedev, O.I.; Van Tendeloo, G.; Rozova, M.G.; Shpanchenko, R.V.; Pavljuk, B.P.; Kopnin, E.M.; Antipov, E.V. |
| Title |
Structural transformations in the fluorinated T* phase |
Type |
A1 Journal article |
| Year |
1999 |
Publication |
Journal of solid state chemistry |
Abbreviated Journal |
J Solid State Chem |
| Volume |
147 |
Issue |
|
Pages |
647-656 |
| Keywords |
A1 Journal article; Electron microscopy for materials research (EMAT) |
| Abstract |
|
| Address |
|
| Corporate Author |
|
Thesis |
|
| Publisher |
|
Place of Publication |
London |
Editor |
|
| Language |
|
Wos |
000083652600028 |
Publication Date |
2002-10-07 |
| Series Editor |
|
Series Title |
|
Abbreviated Series Title |
|
| Series Volume |
|
Series Issue |
|
Edition |
|
| ISSN |
0022-4596; |
ISBN |
|
Additional Links |
UA library record; WoS full record; WoS citing articles |
| Impact Factor |
2.299 |
Times cited |
8 |
Open Access |
|
| Notes |
|
Approved |
Most recent IF: 2.299; 1999 IF: 1.547 |
| Call Number |
UA @ lucian @ c:irua:29279 |
Serial |
3266 |
| Permanent link to this record |
| |
|
| |
| Author |
Batuk, M.; Tyablikov, O.A.; Tsirlin, A.A.; Kazakov, S.M.; Rozova, M.G.; Pokholok, K.V.; Filimonov, D.S.; Antipov, E.V.; Abakumov, A.M.; Hadermann, J. |
| Title |
Structure and magnetic properties of a new anion-deficient perovskite Pb2Ba2BiFe4ScO13 with crystallographic shear structure |
Type |
A1 Journal article |
| Year |
2013 |
Publication |
Materials research bulletin |
Abbreviated Journal |
Mater Res Bull |
| Volume |
48 |
Issue |
9 |
Pages |
3459-3465 |
| Keywords |
A1 Journal article; Electron microscopy for materials research (EMAT) |
| Abstract |
Pb2Ba2BiFe4ScO13, a new n = 5 member of the oxygen-deficient perovskite-based A(n)B(n)O(3n-2) homologous series, was synthesized using a solid-state method. The crystal structure of Pb2Ba2BiFe4ScO13 was investigated by a combination of synchrotron X-ray powder diffraction, electron diffraction, high-angle annular dark-field scanning transmission electron microscopy and Mossbauer spectroscopy. At 900 K, it crystallizes in the Ammm space group with the unit cell parameters a = 5.8459(1) angstrom, b = 4.0426(1) angstrom, and c=27.3435(1) angstrom. In the Pb2Ba2BiFe4ScO13 structure, quasi-two-dimensional perovskite blocks are periodically interleaved with 1/2[1 1 0] ((1) over bar 0 1)(p) crystallographic shear (CS) planes. At the CS planes, the corner-sharing FeO6 octahedra are transformed into chains of edge-sharing FeO5 distorted tetragonal pyramids. B-positions of the perovskite blocks between the CS planes are jointly occupied by Fe3+ and Sc3+. The chains of the FeO5 pyramids and (Fe,Sc)O-6 octahedra delimit six-sided tunnels that are occupied by double columns of cations with a lone electron pair (Pb2+). The remaining A-cations (Bi3+, Ba2+) occupy positions in the perovskite block. According to the magnetic susceptibility measurements, Pb2Ba2BiFe4ScO13 is antiferromagnetically ordered below T-N approximate to 350 K. (C) 2013 Elsevier Ltd. All rights reserved. |
| Address |
|
| Corporate Author |
|
Thesis |
|
| Publisher |
|
Place of Publication |
New York, N.Y. |
Editor |
|
| Language |
|
Wos |
000322354000076 |
Publication Date |
2013-05-17 |
| Series Editor |
|
Series Title |
|
Abbreviated Series Title |
|
| Series Volume |
|
Series Issue |
|
Edition |
|
| ISSN |
0025-5408; |
ISBN |
|
Additional Links |
UA library record; WoS full record; WoS citing articles |
| Impact Factor |
2.446 |
Times cited |
2 |
Open Access |
|
| Notes |
|
Approved |
Most recent IF: 2.446; 2013 IF: 1.968 |
| Call Number |
UA @ lucian @ c:irua:109756 |
Serial |
3282 |
| Permanent link to this record |
| |
|
| |
| Author |
Dixon, E.; Hadermann, J.; Hayward, M.A. |
| Title |
Structures and magnetism of La1-xSrxMnO3-(0.5+x)/2 (0.67\leq x\leq1) phases |
Type |
A1 Journal article |
| Year |
2012 |
Publication |
Chemistry of materials |
Abbreviated Journal |
Chem Mater |
| Volume |
24 |
Issue |
8 |
Pages |
1486-1495 |
| Keywords |
A1 Journal article; Electron microscopy for materials research (EMAT) |
| Abstract |
Topotactic reduction of La1-xSrxMnO3 (0.67 <= x <= 1) phases with sodium hydride yields a series of isoelectronic materials of composition La1-xSrxMnO3-(0.5+x)/2. Lanthanum rich members of the series (0.67 <= x <= 0.83) adopt anion deficient perovskite structures with a 6-layer -OTOOT'O- stacking sequence of sheets of octahedra/square-based pyramids (O) and sheets of tetrahedra (T). The strontium rich members of the series (0.83 <= x <= 1) incorporate “step defects” into this 6-layer structure in which the OTOOT'O stacking sequence is converted into either OOTOOT' or TOOT'OO at a defect plane which runs perpendicular to the [201] lattice plane. The step defects appear to provide a mechanism to relieve lattice strain and accommodate additional anion deficiency in phases with x > 0.83. Magnetization and neutron diffraction data indicate La1-xSrxMnO3-(0.5+x)/2 phases adopt antiferromagnetically ordered states at low-temperature in which the ordered arrangement of magnetic spins is incommensurate with the crystallographic lattice. |
| Address |
|
| Corporate Author |
|
Thesis |
|
| Publisher |
|
Place of Publication |
Washington, D.C. |
Editor |
|
| Language |
|
Wos |
000303092300011 |
Publication Date |
2012-03-28 |
| Series Editor |
|
Series Title |
|
Abbreviated Series Title |
|
| Series Volume |
|
Series Issue |
|
Edition |
|
| ISSN |
0897-4756;1520-5002; |
ISBN |
|
Additional Links |
UA library record; WoS full record; WoS citing articles |
| Impact Factor |
9.466 |
Times cited |
13 |
Open Access |
|
| Notes |
Esteem 026019 |
Approved |
Most recent IF: 9.466; 2012 IF: 8.238 |
| Call Number |
UA @ lucian @ c:irua:98253 |
Serial |
3318 |
| Permanent link to this record |
| |
|
| |
| Author |
Hadermann, J.; Khasanova, N.R.; Van Tendeloo, G.; Abakumov, A.M.; Rozova, M.G.; Alekseeva, A.M.; Antipov, E.V. |
| Title |
Suppression of modulations in fluorinated Bi-2201 phases |
Type |
A1 Journal article |
| Year |
2001 |
Publication |
Journal of solid state chemistry |
Abbreviated Journal |
J Solid State Chem |
| Volume |
156 |
Issue |
|
Pages |
445-451 |
| Keywords |
A1 Journal article; Electron microscopy for materials research (EMAT) |
| Abstract |
|
| Address |
|
| Corporate Author |
|
Thesis |
|
| Publisher |
|
Place of Publication |
London |
Editor |
|
| Language |
|
Wos |
000167252000027 |
Publication Date |
2002-09-18 |
| Series Editor |
|
Series Title |
|
Abbreviated Series Title |
|
| Series Volume |
|
Series Issue |
|
Edition |
|
| ISSN |
0022-4596; |
ISBN |
|
Additional Links |
UA library record; WoS full record; WoS citing articles |
| Impact Factor |
2.299 |
Times cited |
8 |
Open Access |
|
| Notes |
|
Approved |
Most recent IF: 2.299; 2001 IF: 1.614 |
| Call Number |
UA @ lucian @ c:irua:36046 |
Serial |
3386 |
| Permanent link to this record |