Abstract: The main results and conclusions are presented of a round robin study of silicon oxide on silicon reference samples for ellipsometry. The oxide films with nominal thicknesses of 10, 50 and 120 nm are grown by thermal oxidation. The oxide film thicknesses have been determined by single wavelength ellipsometry (SWE), by spectroscopic ellipsometry (SE) and by cross-sectional conventional and high-resolution transmission electron microscopy (TEM and HREM) in different laboratories. The main conclusions are that special precautions have to be taken in order to use TEM as a reliable thickness measurement technique; that single wavelength ellipsometry can be used with great accuracy and reproducibility for the 50 and 120 nm film thicknesses but that it shows some inherent problems for the 10 nm films; and that spectroscopic ellipsometry showed for all film thicknesses an accuracy and reproducibility which is clearly superior to that of SWE.

Abstract: Defects on hollow silica spheres synthesized in a tetraethylorthosilicate-octylamine-HCl-H2O system were recorded by scanning microscope. Based on the results, influences of synthesis composition on the formation of these defects are discussed. It is evidenced that products prepared with different octylamine-to-tetraethylorthosilicate ratios may have surface depressions, cracks and non-hollow microspheres. However, by changing water and acid additions, these defects could be reduced or eliminated. Generally, samples synthesized with a large octylamine addition commonly exhibit surface depressions. A small octylamine or a large water addition benefits the formation of solid silica microspheres among the product. Acid, although is not indispensable for the formation of hollow spheres, helps to eliminate or reduce depressions on the hollow shells. It is explained that the added acid gives rise to a relative localized fast hydrolysis versus condensation, facilitating an easy mobility of hydrolyzed silica species, and consequently the shell surface is smoothened.

Abstract: We review the energy spectrum and transport properties of several types of one-dimensional superlattices (SLs) on single-layer and bilayer graphene. In single-layer graphene, for certain SL parameters an electron beam incident on an SL is highly collimated. On the other hand, there are extra Dirac points generated for other SL parameters. Using rectangular barriers allows us to find analytical expressions for the location of new Dirac points in the spectrum and for the renormalization of the electron velocities. The influence of these extra Dirac points on the conductivity is investigated. In the limit of δ-function barriers, the transmission T through and conductance G of a finite number of barriers as well as the energy spectra of SLs are periodic functions of the dimensionless strength P of the barriers, Graphic, with vF the Fermi velocity. For a KronigPenney SL with alternating sign of the height of the barriers, the Dirac point becomes a Dirac line for P = π/2+nπ with n an integer. In bilayer graphene, with an appropriate bias applied to the barriers and wells, we show that several new types of SLs are produced and two of them are similar to type I and type II semiconductor SLs. Similar to single-layer graphene SLs, extra Dirac points are found in bilayer graphene SLs. Non-ballistic transport is also considered.

Abstract: The recently discovered superconducting mercury-based cuprates HgBa2Can-1CunO2n+2+delta have proved difficult to synthesize as single phases and are sensitive to environment (CO2, moisture). The present paper gives an overview of new series mercury based superconductors, whose stabilisation is based on the fact that a foreign cation with a higher valency than Hg(II) must be introduced in the mercury layers, in order to fill up partially the oxygen vacancies of these layers. By this method, several new series of superconductors involving strontium instead of barium with critical temperatures ranging from 27 K to 95 K have been isolated : Hg0.5Bi0.5Sr2-xLaxCuO4+delta, Hg(0.5)Bi(0.5)Sr(2)Ca(1-x)R(x)Cu(2)O(6+delta) (R Y, Nd, Pr), Pb0.7Hg0.3Sr2-xLaxCuO4+delta, Pb(0.7)Hg(0.3)Sr(2)Ca(1-x)R(x)Cu(2)O(6+delta) (R = Y, Nd) Hg(1-x)Pr(x)Sr(2)A(1-x')Pr(x') Cu2O6+delta (A = Sr, Ca), Pb0.7Hg0.3Sr2Cu2CO3O7 and Hg1-xCrxSr2CuO4+delta. The behaviour of the praseodymium cuprates that exhibit a rather sharp transition and reach a Tc of 85 K is especially discussed. A method to synthesize new ''Ba-Hg'' superconducting cuprates with the 1212 structure at normal pressure with a Tc up to 110 K is also presented.

Abstract: We optimized the deposition of YBa2(Cu1-xZnx)(3)O-7-delta thin-films using inverted cylindrical magnetron sputtering and report here a detailed structural study, especially in relation to crystal growth, associated surface morphology, Y2O3 precipitation and other secondary phases important for flux pinning. We find that the epitaxial quality of the Zn-substituted YBa2Cu3O7-delta films is decreased compared with high-quality pure YBa2Cu3O7-delta films prepared under identical conditions. The pure films have smoother surfaces, while those of Zn-substituted films contain pinholes and outgrowths. Secondary phases and a-axis grains were observed in the Zn-substituted films. Y2O3 precipitates with typical dimensions of 50-100 Angstrom have been found in both pure and Zn-substituted samples. However, their density of about 10(23) m(-3), observed in the pure films, is significantly reduced in the Zn-substituted films when increasing the Zn concentration up to 4%.

Abstract: In this work we have analyzed the properties of a gliding dc discharge in argon at atmospheric pressure. Despite the usual designation of these discharges as ‘gliding arc discharges’, it was found previously that they operate in two different regimes—glow and arc. Here we analyze the differences in both regimes by means of two dimensional fluid modeling. In order to address different aspects of the discharge operation, we use two models—Cartesian and axisymmetric in a cylindrical coordinate system. The obtained results show that the two types of discharges produce a similar plasma column for a similar discharge current. However, the different mechanisms of plasma channel attachment to the cathode could produce certain differences in the plasma parameters (i.e. arc elongation), and this can affect gas treatments applications.

Abstract: For the first time, the local structure and physical properties of Ru1222 based compounds (RuSr(2)Gd(1.4)Ce(0.6)Cu(2)O(10-delta) and RuSr(2)Gd(1.8-x)Y(0.2)CexCu(2)O(10) (x = 0.90-0.55)) have been investigated and analyzed together on the very same compounds. The Ru1222 superstructure was confirmed by TEM at a local scale and was suggested to have an orthorhombic symmetry with space group Aba2 and lattice parameters a(s) similar or equal to root 2a, b(s) similar or equal to root 2a and c(s) = c. This new Ru1222 superstructure distortion from tetragonal symmetry is proposed to have a positive correlation with the superconductivity variation of these compounds. The more the distortion towards orthorhombic symmetry, the higher the critical superconducting temperature these compounds can achieve. The T(c)(0) of RuSr(2)Gd(1.8-x)Y(0.2)Ce(x)Cu(2)O(10-delta) (x = 0.85-0.55) increases monotonically from 4 to 16 K when x decreases from 0.85 to 0.70, then RuSr(2)Gd(2)Cu(2)O(8) defects emerge and the T(c) decreases with decreasing x. Ru1212 defects are observed to intergrow epitaxially with the Ru1222 structure as lamellas along the c-axis in RuSr(2)Gd(1.4)Ce(0.6)Cu(2)O(10-delta). Although Ru1212 is a superconductor, the intergrowth severely restrains its superconductivity.

Abstract: We present a general description of the formalism of symmetry-adapted rotator functions (SARFs) for molecules in cylindrical confinement. Molecules are considered as clusters of interaction centers (ICs), can have any symmetry, and can display different types of ICs. Cylindrical confinement can be realized by encapsulation in a carbon nanotube (CNT). The potential energy of a molecule surrounded by a CNT can be calculated by evaluating a limited number of terms of an expansion into SARFs, which offers a significant reduction of the computation time. Optimal molecular orientations can be deduced from the resulting potential energy landscape. Examples, including the case of a molecule with cubic symmetry inside a CNT, are discussed.