“A methodology for the identification of glass panes of different origin in a single stained glass window: application on two 13th century windows”. Schalm O, de Raedt I, Caen J, Janssens K, Journal of cultural heritage 11, 487 (2010). http://doi.org/10.1016/J.CULHER.2010.05.004
Abstract: The chemical composition of 11 glass panes originating from two 13th century non-figurative windows were analyzed by means of Scanning Electron MicroscopyEnergy Dispersive X-ray system (SEM-EDX). The windows were discovered in the back-wall of the triforium during the restoration of the choir of the cathedral St. Michael and St. Gudule in Brussels (Belgium). In order to determine if these windows were fabricated with glass of different origin or not, the compositional difference between the panes were compared with the variation in composition as a result of the following causes: (1) compositional fluctuation between panes cut from the same sheet of glass, (2) compositional fluctuation caused when panes are cut from different sheets that were made with the same batch, (3) compositional fluctuation caused when the glass is made from different batches at the same production center, and (4) compositional fluctuation as a result of glass produced at different fabrication centers.
Keywords: A1 Journal article; Art; AXES (Antwerp X-ray Analysis, Electrochemistry and Speciation)
Impact Factor: 1.838
Times cited: 7
DOI: 10.1016/J.CULHER.2010.05.004
|
|
|
“Study of the influence of water and oxygen on the morphology and chemistry of pyritized lignite: Implications for the development of a preventive drying protocol”. Odin GP, Belhadj O, Vanmeert F, Janssens K, Wattiaux A, Francois A, Rouchon V, Journal Of Cultural Heritage 42, 117 (2020). http://doi.org/10.1016/J.CULHER.2019.08.004
Abstract: Lignite constitutes a unique testimony of past diversity and evolution of land plants. This material, usually waterlogged, is particularly difficult to dry because of its mechanical sensitivity to moisture changes. In addition, lignite may contain organic and inorganic sulfides, which are susceptible to oxidation once excavated. As a result, the conservation of lignite is particularly complicated and lignite remains scarce in paleobotanical collections. We experimentally test different drying protocols on waterlogged pyritized lignite, while documenting the respective role of water and oxygen on their morphology and chemistry. The results reveal that inorganic sulfides (pyrite) are more prone to oxidation than organic sulfides (thioethers). Critically, water is the main factor responsible for this oxidation, provoking sulfate efflorescence when samples are further exposed to oxygen. On the other hand, an abrupt removal of water provokes significant mechanical damage while sulfur remains mostly present as reduced compounds. The control of water and oxygen exchanges is thus critical for conserving lignite without physical damage and efflorescence. We successfully achieved this by storing the samples in hermetically sealed plastic bags made of semi-permeable films, which slowly release humidity while allowing a gradual influx of oxygen. We advise curators to quickly handle lignite once removed from its waterlogged environment because of the fast kinetics of oxidation, and to choose a drying protocol according to the purpose of the lignite treated. Finally, once dried, we advise to store the lignite in an anhydrous environment. (C) 2019 Elsevier Masson SAS. All rights reserved.
Keywords: A1 Journal article; Art; History; AXES (Antwerp X-ray Analysis, Electrochemistry and Speciation)
Impact Factor: 3.1
DOI: 10.1016/J.CULHER.2019.08.004
|
|
|
“Characterization of uranium and plutonium containing particles originating from the nuclear weapons accident in Thule, Greenland, 1968”. Lind OC, Salbu B, Janssens K, Proost K, Dahlgaard H, Journal of environmental radioactivity 81, 21 (2005). http://doi.org/10.1016/J.JENVRAD.2004.10.013
Keywords: A1 Journal article; AXES (Antwerp X-ray Analysis, Electrochemistry and Speciation)
Impact Factor: 2.31
Times cited: 37
DOI: 10.1016/J.JENVRAD.2004.10.013
|
|
|
“Micro-analytical characterisation of radioactive heterogeneities in samples from Central Asian TENORM sites”. Lind OC, de Nolf W, Janssens K, Salbu B, Journal of environmental radioactivity 123, 63 (2013). http://doi.org/10.1016/J.JENVRAD.2012.02.012
Abstract: The present work focuses on the use of micro-analytical techniques to demonstrate the heterogeneous distribution of radionuclides and metals in soils collected at Former Soviet Union mining sites in Central Asia. Based on digital autoradiography, radionuclides were heterogeneously distributed in soil samples collected at the abandoned uranium mining sites Kurday, Kazakhstan, Kadji Sai, Kyrgyzstan and Taboshar, Tajikistan. Using electron microscopy interfaced with X-ray microanalysis submicron – mm-sized radioactive particles and rock fragments with U, As, Se and toxic metals on the surfaces were identified in Kurday and Kadji Sai samples. Employing scanning and tomographic (3D) synchrotron radiation based micro-X-ray fluorescence (mu-SRXRF) and synchrotron radiation based micro-X-ray diffraction (mu-SRXRD) allowed us to observe the inner structure of the particles without physical sectioning. The distribution of elements in virtual crosssections demonstrated that U and a series of toxic elements were rather heterogeneously distributed also within individual radioactive TENORM particles. Compared to archived data, U in Kadji Sai particles was present as uraninite (U4O9+y or UO2+x) or Na-zippeite aNa(4)(UO2)(6)[(OH)(10)(SO4)(3)]center dot 4H(2)O), i.e. U minerals with very low solubility. The results suggested that TENORM particles can carry substantial amount of radioactivity, which can be subject to re-suspension, atmospheric transport and water transport. Thus, the potential radioecological and radioanalytical impact of radioactive particles at NORM and TENORM sites worldwide should be taken into account. The present work also demonstrates that radioecological studies should benefit from the use of advanced methods such as synchrotron radiation based techniques. (C) 2012 Elsevier Ltd. All rights reserved.
Keywords: A1 Journal article; AXES (Antwerp X-ray Analysis, Electrochemistry and Speciation)
Impact Factor: 2.31
Times cited: 16
DOI: 10.1016/J.JENVRAD.2012.02.012
|
|
|
“Oxidation states of uranium in depleted uranium particles from Kuwait”. Salbu B, Janssens K, Lind OC, Proost K, Gijsels L, Danesi PR, Journal of environmental radioactivity 78, 125 (2004). http://doi.org/10.1016/J.JENVAD.2004.04.001
Abstract: The oxidation states of uranium in depleted uranium (DU) particles were determined by synchrotron radiation based mu-XANES, applied to individual particles isolated from selected samples collected at different sites in Kuwait. Based on scanning electron microscopy with X-ray microanalysis prior to mu-XANES, DU particles ranging from sub-microns to several hundred micrometers were observed. The.median particle size depended on sources and sampling sites; small-sized particles (median 13 mum) were identified in swipes taken from the inside of DU penetrators holes in tanks and in sandy soil collected below DU penetrators, while larger particles (median 44 mum) were associated with fire in a DU ammunition storage facility. Furthermore, the U-236/U-235 ratios obtained from accelerator mass spectrometry demonstrated that uranium in the DU particles originated from reprocessed fuel (about 10(-2) in DU from the ammunition facility, about 10(-3) for DU in swipes). Compared to well-defined standards, all investigated DU particles were oxidized. Uranium particles collected from swipes were characterized as UO2, U3O8 or a mixture of these oxidized forms, similar to that observed in DU affected areas in Kosovo. Uranium particles formed during fire in the DU ammunition facility were, however, present as oxidation state +5 and +6, with XANES spectra similar to solid uranyl standards. Environmental or health impact assessments for areas affected by DU munitions should therefore take into account the presence of respiratory UO2, U3O8 and even UO3 particles, their corresponding weathering rates and the subsequent mobilisation of U from oxidized DU particles. (C) 2004 Elsevier Ltd. All rights reserved.
Keywords: A1 Journal article; AXES (Antwerp X-ray Analysis, Electrochemistry and Speciation)
Impact Factor: 2.31
DOI: 10.1016/J.JENVAD.2004.04.001
|
|
|
“Oxidation states of uranium in DU particles from Kosovo”. Salbu B, Janssens K, Lind OC, Proost K, Danesi PR, Journal of environmental radioactivity 64, 167 (2003). http://doi.org/10.1016/S0265-931X(02)00047-4
Keywords: A1 Journal article; AXES (Antwerp X-ray Analysis, Electrochemistry and Speciation)
Impact Factor: 2.31
DOI: 10.1016/S0265-931X(02)00047-4
|
|
|
“Solid state speciation and potential bioavailability of depleted uranium particles from Kosovo and Kuwait”. Lind OC, Salbu B, Skipperud L, Janssens K, Jaroszewicz J, de Nolf W, Journal of environmental radioactivity 100, 301 (2009). http://doi.org/10.1016/J.JENVRAD.2008.12.018
Abstract: A combination of synchrotron radiation based X-ray microscopic techniques (ì-XRF, ì-XANES, ì-XRD) applied on single depleted uranium (DU) particles and semi-bulk leaching experiments has been employed to link the potential bioavailability of DU particles to site-specific particle characteristics. The oxidation states and crystallographic forms of U in DU particles have been determined for individual particles isolated from selected samples collected at different sites in Kosovo and Kuwait that were contaminated by DU ammunition during the 1999 Balkan conflict and the 1991 Gulf war. Furthermore, small soil or sand samples heavily contaminated with DU particles were subjected to simulated gastrointestinal fluid (0.16 M HCl) extractions. Characteristics of DU particles in Kosovo soils collected in 2000 and in Kuwait soils collected in 2002 varied significantly depending on the release scenario and to some extent on weathering conditions. Oxidized U (+6) was determined in large, fragile and bright yellow DU particles released during fire at a DU ammunition storage facility and crystalline phases such as schoepite (UO3·2.25H2O), dehydrated schoepite (UO3·0.75H2O) and metaschoepite (UO3·2.0H2O) were identified. As expected, these DU particles were rapidly dissolved in 0.16 M HCl (84 ± 3% extracted after 2 h) indicating a high degree of potential mobility and bioavailability. In contrast, the 2 h extraction of samples contaminated with DU particles originating either from corrosion of unspent DU penetrators or from impacted DU ammunition appeared to be much slower (2030%) as uranium was less oxidized (+4 to +6). Crystalline phases such as UO2, UC and metallic U or UTi alloy were determined in impacted DU particles from Kosovo and Kuwait, while the UO2,34 phase, only determined in particles from Kosovo, could reflect a more corrosive environment. Although the results are based on a limited number of DU particles, they indicate that the structure and extractability of DU particles released from similar sources (metallic U penetrators) will depend on the release scenarios (fire, impact) and to some extent environmental conditions. However, most of the DU particles (7396%) in all investigated samples were dissolved in 0.16 M HCl after one week indicating that a majority of the DU material is bioaccessible.
Keywords: A1 Journal article; AXES (Antwerp X-ray Analysis, Electrochemistry and Speciation)
Impact Factor: 2.31
Times cited: 49
DOI: 10.1016/J.JENVRAD.2008.12.018
|
|
|
“Micro-analytical characterization of thorium-rich aggregates from Norwegian NORM sites (Fen Complex, Telemark)”. Cagno S, Lind OC, Popic JM, Skipperud L, De Nolf W, Nuyts G, Vanmeert F, Jaroszewicz J, Janssens K, Salbu B, Journal Of Environmental Radioactivity 219, 106273 (2020). http://doi.org/10.1016/J.JENVRAD.2020.106273
Abstract: In this study we performed microscopic characterization of mineral particles that were collected in the thorium-rich Fen Complex in Norway and identified and isolated based on autoradiography in function of their radioactivity. For this we combined information obtained with X-ray absorption mu-CT, mu-XRF and mu-XRD, both in bi- and in three-dimensional (tomographic) mode. We demonstrate that radionuclides and metals are heterogeneously distributed both within soil samples and within individual Th-enriched aggregates, which are characterised as low-density mineral bulk particles with high density material inclusions, where Th as well as several metals are highly concentrated. For these sites, it is important to take into account how these inhomogeneous distributions could affect the overall environmental behaviour of Th and progeny upon weathering due to human or environmental factors. Moreover, the estimated size of the Th-containing inclusions as determined in this work represents information of importance for the characterization of radionuclides and toxic metals exposure, as well as for assessing the viability of mining for Th and rare-earth metals in the Fen Complex and the associated environmental impact.
Keywords: A1 Journal article; AXES (Antwerp X-ray Analysis, Electrochemistry and Speciation)
Impact Factor: 2.3
DOI: 10.1016/J.JENVRAD.2020.106273
|
|
|
“Insight to ternary complexes of co-adsorption of norfloxacin and Cu(II) onto montmorillonite at different pH using EXAFS”. Pei Z-G, Shan X-Q, Zhang S-Z, Kong J-J, Wen B, Zhang J, Zheng L-R, Xie Y-N, Janssens K, Journal of hazardous materials 186, 842 (2011). http://doi.org/10.1016/J.JHAZMAT.2010.11.076
Abstract: Co-adsorption of norfloxacin (Nor) and Cu(II) on montmorillonite at pH 4.5, 7.0 and 9.0 was studied by integrated batch adsorption experiments and extended X-ray absorption fine structure (EXAFS) spectroscopy. Under such pH conditions the dominant species of Nor are cation (Nor+), zwitterion (Nor±), and anion (Nor−), respectively. Results indicated that Nor sorption decreased with an increase of solution pH. The presence of Cu(II) slightly suppressed the Nor+ sorption at pH 4.5, while increased Nor± and Nor−sorption on montmorillonite at pH 7.0 and 9.0, respectively. In contrast, Nor increased Cu(II) adsorption at pH 4.5, but had little effect on the adsorption of Cu(II) on montmorillonite at pH 7.0 and 9.0. Spectroscopic results showed that, at pH 4.5, Nor+ was sorbed on montmorillonite by the formation of outer-sphere montmorilloniteNorCu(II) ternary surface complex. At pH 7.0, montmorilloniteNorCu(II) and montmorilloniteCu(II)Nor ternary surface complexes co-exist. At pH 9.0, montmorilloniteCu(II)Nor ternary surface complex was likely formed, which was different to Cu(II)(Nor)2 precipitate of the solution.
Keywords: A1 Journal article; Engineering sciences. Technology; AXES (Antwerp X-ray Analysis, Electrochemistry and Speciation)
Impact Factor: 6.065
Times cited: 25
DOI: 10.1016/J.JHAZMAT.2010.11.076
|
|
|
“Some critical observations about the degradation of glass : the formation of lamellae explained”. Schalm O, Nuyts G, Janssens K, Journal Of Non-Crystalline Solids 569, 120984 (2021). http://doi.org/10.1016/J.JNONCRYSOL.2021.120984
Abstract: This study demonstrates that the mechanism responsible for the transformation of glass into a degradation layer is pH-dependent. In acid conditions, the transformed glass is homogeneous and brittle. In mild alkaline conditions, transformed glass is heterogeneous due to the presence of lamellae composed of silica nanoparticles and the occurrence of Ca-rich inclusions. The fundamental difference between acid and alkaline conditions cannot be explained by the currently accepted degradation mechanism based on ion exchange. To explain this critical observation, we propose a refined degradation mechanism based on existing knowledge that involves several inwardly moving reaction fronts. The fronts responsible for the transformation of the silicate network into amorphous silica are also responsible for the morphology of the transformed glass. We have identified the feedback mechanism that explains the formation of lamellae in alkaline conditions.
Keywords: A1 Journal article; AXES (Antwerp X-ray Analysis, Electrochemistry and Speciation)
Impact Factor: 2.124
DOI: 10.1016/J.JNONCRYSOL.2021.120984
|
|
|
“Micro-Raman analysis for the identification of pigments from 19th and 20th century paintings”. Aibéo CL, Goffin S, Schalm O, van der Snickt G, Laquière N, Eyskens P, Janssens K, Journal of Raman spectroscopy 39, 1091 (2008). http://doi.org/10.1002/JRS.1990
Abstract: In this article, results using confocal µ-Raman to analyse the cross-section of paint samples are presented. Results obtained with light microscopy, scanning electron microscopy (SEM) combined with an energy dispersive X-ray analysis (EDX) and micro-X-ray fluorescence (µ-XRF) are mentioned and compared to the ones obtained with confocal (MRS). In some cases, pigment identification was possible only by combining analytical results from different techniques. The samples were drawn from five paintings belonging to the Academy of Fine Arts of Antwerp, which are part of a collection of 34 paintings made by students from the Academy between 1819 and 1920. Since, on the one hand, the painting techniques and materials, especially pigments, used in this period are still not completely known, and on the other hand, this collection constitutes a very important and reliable resource of information, these paintings were chosen for a systematic investigation. They represent the evolution of painting in Belgium over approximately a century.
Keywords: A1 Journal article; AXES (Antwerp X-ray Analysis, Electrochemistry and Speciation)
Impact Factor: 2.969
Times cited: 28
DOI: 10.1002/JRS.1990
|
|
|
“In vitro validation of a mobile Raman-XRF micro-analytical instrument's capabilities on the diagnosis of Byzantine icons”. Andrikopoulos KS, Daniilia S, Roussel B, Janssens K, Journal of Raman spectroscopy 37, 1026 (2006). http://doi.org/10.1002/JRS.1612
Keywords: A1 Journal article; AXES (Antwerp X-ray Analysis, Electrochemistry and Speciation)
Impact Factor: 2.969
Times cited: 53
DOI: 10.1002/JRS.1612
|
|
|
“Raman study of different crystalline forms of PbCrO4 and PbCr1-xSxO4 solid solutions for the noninvasive identification of chrome yellows in paintings : a focus on works by Vincent van Gogh”. Monico L, Janssens K, Hendriks E, Brunetti BG, Miliani C, Journal of Raman spectroscopy 45, 1034 (2014). http://doi.org/10.1002/JRS.4548
Abstract: Chrome yellows, a class of pigments frequently used by painters of the Impressionism and Post-impressionism period, are known for their different chemical stability; the latter depends on the chemical composition (PbCrO4, PbCr1-xSxO4) and crystalline structure (monoclinic or orthorhombic) of the material. The possibility to distinguish among different forms of this pigment is therefore relevant in order to extend knowledge on the corresponding degradation process that is observed on several original paintings. For this purpose, three paintings conserved at the Van Gogh Museum (Amsterdam) were analyzed using noninvasive Raman spectroscopy, while equivalent investigations employing bench-top instrumentation were performed to obtain information from micro-samples originating from these works of art. In each painting, the chrome yellow was identified either as monoclinic PbCrO4 or in the form of monoclinic PbCr1-xSxO4 (x<0.25) or S-rich orthorhombic PbCr1-xSxO4 (x similar to 0.5). Our ability to make this fairly subtle distinction is based on a Raman study of several oil paint model samples made up of monoclinic and/or orthorhombic crystalline forms of PbCrO4 and PbCr1-xSxO4 (0.1x0.8). These paints were studied using several excitation wavelengths (namely 785.0, 532.0, 514.5, and 488nm). Because of the absence of the resonance Raman effect, which strongly enhances the chromate symmetric stretching band, and the absence of any laser-induced photodecomposition, it is advantageous to acquire data at 785.0nm. The band-shape and the position of the chromate bending modes proved to be more sensitive to the solid solution composition and crystalline structure than the stretching modes and can be used as distinctive spectral markers to discriminate among the different chrome yellow forms that are present. Copyright (c) 2014 John Wiley & Sons, Ltd.
Keywords: A1 Journal article; AXES (Antwerp X-ray Analysis, Electrochemistry and Speciation)
Impact Factor: 2.969
Times cited: 34
DOI: 10.1002/JRS.4548
|
|
|
“Assessing the stability of arsenic sulfide pigments and influence of the binding media on their degradation by means of spectroscopic and electrochemical techniques”. Vermeulen M, Janssens K, Sanyova J, Rahemi V, McGlinchey C, De Wael K, Microchemical journal 138, 82 (2018). http://doi.org/10.1016/J.MICROC.2018.01.004
Abstract: In this paper, we used the semiconducting and lightfastness properties of synthetic and mineral arsenic sulfide pigments to study their stability by means of electrochemical and microfadometric techniques. A combination of these techniques shows that in the early stage of the degradation process, amorphous arsenic sulfides are more stable than both crystalline forms, while upon longer exposure time, amorphous pigments will fade more than both mineral pigments, making it less suitable. While the stability study was carried out on unbound pigments, the influence of the organic binder on the relative degradation of the arsenic sulfide pigments was investigated through a multi-analytical approach on pigment/binder mock-up paint samples. For this purpose, the formation of arsenic trioxide was assessed by micro Fourier transform infrared (μ-FTIR) spectroscopy while the influence of the binder on the formation of sulfates was studied by means of synchrotron radiation X-ray near edge structure (μ-XANES). Both techniques elucidate a higher stability of all pigments in gum arabic while the use of egg yolk as binder leads to the most degradation, most likely due to its sulfur-rich composition. In the context of the degradation of arsenic sulfide pigments, other binders such as animal glue, egg white or linseed oil show an intermediate impact.
Keywords: A1 Journal article; AXES (Antwerp X-ray Analysis, Electrochemistry and Speciation)
Impact Factor: 3.034
Times cited: 4
DOI: 10.1016/J.MICROC.2018.01.004
|
|
|
“Chemical imaging of stained-glass windows by means of macro X-ray fluorescence (MA-XRF) scanning”. van der Snickt G, Legrand S, Caen J, Vanmeert F, Alfeld M, Janssens K, Microchemical journal 124, 615 (2016). http://doi.org/10.1016/J.MICROC.2015.10.010
Abstract: Since the recent development of a mobile setup, MA-XRF scanning proved a valuable tool for the non-invasive, technical study of paintings. In this work, the applicability of MA-XRF scanning for investigating stained-glass windows inside a conservation studio is assessed by analysis of a high-profile, well-studied late-mediaeval panel. Although accurate quantification of components is not feasible with this analytical imaging technique, plotting the detected intensities of K versus Ca in a scatter plot allowed distinguishing glass fragments of different compositional types within the same panel. In particular, clusters in the Ca/K correlation plot revealed the presence of two subtypes of potash glass and three subtypes of high lime low alkali glass. MA-XRF results proved consistent with previous quantitative SEM-EDX analysis on two samples and analytical-based theories on glass production in the Low Countries formulated in literature. A bi-plot of the intensities of the more energetic Rb-K versus Sr-K emission lines yielded a similar glass type differentiation and is here presented as suitable alternative in case the Ca/K signal ratio is affected by superimposed weathering crusts. Apart from identification of the chromophores responsible for the green, blue and red glass colors, contrasting the associated elemental distribution maps obtained on the exterior and interior side of the glass permitted discriminating between colored pot metal glass and multi-layered flashed glass as well. Finally, the benefit of obtaining compositional information from the entire surface, as opposed to point analysis, was illustrated by the discovery of what appears to be a green cobalt glass a feature that was previously missed on this well-studied stained-glass window, both by connoisseurs and spectroscopic sample analysis. (C) 2015 Elsevier B.V. All rights reserved.
Keywords: A1 Journal article; AXES (Antwerp X-ray Analysis, Electrochemistry and Speciation); Antwerp Cultural Heritage Sciences (ARCHES)
Impact Factor: 3.034
Times cited: 22
DOI: 10.1016/J.MICROC.2015.10.010
|
|
|
“Chromium speciation methods and infrared spectroscopy for studying the chemical reactivity of lead chromate-based pigments in oil medium”. Monico L, Janssens K, Cotte M, Sorace L, Vanmeert F, Brunetti BG, Miliani C, Microchemical journal
T2 –, TECHNART Conference, APR 27-30, 2015, Catania, ITALY 124, 272 (2016). http://doi.org/10.1016/J.MICROC.2015.08.028
Abstract: Environmental factors, such as light, humidity and temperature are triggering agents for the alteration of organic and/or inorganic constituents of oil paintings. The oxidation of the organic material is favored by increasing of relative humidity and temperature, whereas processes involving changes of the oxidation states of a number of inorganic pigments (e.g., vermilion, cadmium yellows, zinc yellows, chrome yellows) are mainly activated by light-exposure. In view of the optimization of the long-term conservation and restoration strategies of paintings it is of relevant interest to establish the consequences of thermal parameters (temperature and relative humidity) on the chemical/photochemical-reactivity and the nature of the alteration products of light sensitive-pigments in oil medium. To this aim here we propose a multi-method analytical approach based on the combination of diffuse reflectance UV-Vis, FTIR, synchrotron radiation (SR)-based micro X-ray fluorescence (mu-XRF)/micro-X-ray absorption neat edge structure ()CANES) and electron paramagnetic resonance (EPR) spectroscopies for studying the effects of different relative humidity conditions before and after light exposure on the reactivity of a series of lead chromate-based pigments [such as PbCrO4 center dot PbO (monoclinic), PbCrO4 (monoclinic) and PbCr0.2S0.8O4 (orthorhombic)] in an oil medium. The investigation of paint models was also compared to that of a late 19th century historical orthorhombic PbCr0.4S0.6O4 oil paint. Diffuse reflectance UV-Vis and FTIR spectroscopies were used to obtain information associated with chromatic changes and the formation of organo-metal degradation products at the paint surface. SR-based Cr K-edge mu-XANES/mu-XRF mapping analysis and EPR spectroscopy were employed in a complementary fashion to determine the amount, nature and distribution of Cr(III) and Cr(V)-based alteration compounds within the paints with micrometric spatial resolution. Under the employed thermal aging conditions, lead(II)-carboxylates and reduced Cr-compounds (in abundance of up to about 35% at the surface) have been identified in the lead chromate-based paints. The tendency of chromates to become reduced increased with increasing moisture levels and was favored for the orthorhombic PbCr0.2S0.8O4 compounds. The redox process gave rise to the formation of Cr(V)-species in relative amount much higher than that was formed in the equivalent paint which was exposed only to light. After light-exposure of the thermally aged paints, compounds ascribable to the oxidation of the organic binder were detected for all the types of pigments. Nevertheless, the previous thermal treatment increased the tendency toward photo-reduction of only the PbCr0.2S0.8O4 pigment. For this light-sensitive compound, the thickness variation of the reduced Cr-rich (ca. 70%) photo-alteration layer with moisture levels could be ascribed to a surface passivation phenomenon that had already occurred before photochemical aging. (C) 2015 Elsevier B.V. All rights reserved.
Keywords: A1 Journal article; AXES (Antwerp X-ray Analysis, Electrochemistry and Speciation)
Impact Factor: 3.034
Times cited: 23
DOI: 10.1016/J.MICROC.2015.08.028
|
|
|
“Development of a new portable X-ray powder diffractometer and its demonstration to on-site analysis of two selected old master paintings from the Rijksmuseum”. Hirayama A, Abe Y, van Loon A, De Keyser N, Noble P, Vanmeert F, Janssens K, Tantrakarn K, Taniguchi K, Nakai I, Microchemical journal 138, 266 (2018). http://doi.org/10.1016/J.MICROC.2018.01.003
Abstract: A portable X-ray powder diffractometer (p-XRD) PT-APXRD III has been developed for onsite analysis of paintings and archaeological samples. By using a Cu anode X-ray tube and a silicon drift diode (SDD) detector, diffraction patterns with a high signalnoise (S/N) ratio can be recorded. The X-ray tube can be operated at a maximum voltage of 60 kV, which makes it possible to simultaneously record X-ray fluorescence spectra up to the high-energy region. The total weight of this instrument is 16 kg, which can be carried anywhere and the goniometer unit (5.6 kg) can be placed on a tripod for analysis of mural paintings. We brought the instrument to the Rijksmuseum in the Netherlands to examine its applicability for the analysis of oil paintings. We successfully analyzed two seventeenthcentury oil paintings by Johannes Vermeer and Jan Davidsz de Heem (copy after). Ultramarine blue, leadtin yellow type I, and Naples yellow were identified from the diffraction patterns, demonstrating the high practicality of this instrument. Furthermore, it was found from the SEM-EDX analysis of a paint cross section that the yellow pigment was applied in separate layers rather than being mixed. This diffractometer will be commercially available in the near future and will have many applications in the field of material analysis. (C) 2018 Elsevier B.V. All rights reserved.
Keywords: A1 Journal article; AXES (Antwerp X-ray Analysis, Electrochemistry and Speciation)
Impact Factor: 3.034
Times cited: 2
DOI: 10.1016/J.MICROC.2018.01.003
|
|
|
“In situ macro X-ray fluorescence (MA-XRF) scanning as a non-invasive tool to probe for subsurface modifications in paintings by PP Rubens”. van der Snickt G, Legrand S, Slama I, Van Zuien E, Gruber G, Van der Stighelen K, Klaassen L, Oberthaler E, Janssens K, Microchemical journal 138, 238 (2018). http://doi.org/10.1016/J.MICROC.2018.01.019
Abstract: Within the last decade, the established synchrotron- and laboratory-based micro-XRF scanning technology inspired the development of mobile instruments that allow performing in situ experiments on paintings on a macro scale. Since the development of the first mobile scanner at the start of this decade, this chemical imaging technique has brought new insights with respect to several iconic paintings, especially in cases when standard imaging techniques such as X-Ray Radiography (XRR) or Infrared Refiectography (IRR) yielded ambiguous results. The ability of scanning MA-XRF to visualise the distribution of elements detected at and below the paint surface renders this spectrometric method particularly helpful for studying painting techniques and revealing materials that remain hidden below the paint surface. The latter aspect is especially relevant for the technical study of works by Pieter Paul Rubens (1577-1640) as this highly productive seventeenth century master is particularly renowned for the continuous application of modifications during (and even after) the entire course of the creative process. In this work, the added value of MA-XRF scanning experiments for visualising these subsurface features is exemplified by interpreting the chemical images obtained on three of Rubens' key works. Special attention is given to three types of adjustments that are particularly relevant for the technical study of Rubens' oeuvre: (1) compositional changes ('pentimenti'), exemplified by results obtained on The Portrait of Helene Fourment (ca. 1638), (2) extensions to the support ('Anstlickungen.), illustrated by imaging experiments performed on the Venus Frigida (1614) and (3) Rubens' intriguing halos around flesh tones, as found amongst others in The Incredulity of Saint Thomas (1613). The ensuing insights in the paint stratigraphy and the underlying supporting structure illustrate the potential of MA-XRF scanning for the non-invasive, comparative study of Rubens' oeuvre. The results do not only augment the understanding of the complex genesis of Rubens' works of art and his efficient painting technique, but prove valuable during conservation treatments as well, as addressed in this paper. (C) 2018 Elsevier B.V. All rights reserved.
Keywords: A1 Journal article; AXES (Antwerp X-ray Analysis, Electrochemistry and Speciation)
Impact Factor: 3.034
Times cited: 5
DOI: 10.1016/J.MICROC.2018.01.019
|
|
|
“Macro X-ray fluorescence (MA-XRF) scanning of illuminated manuscript fragments: potentialities and challenges”. Ricciardi P, Legrand S, Bertolotti G, Janssens K, Microchemical journal
T2 –, TECHNART Conference, APR 27-30, 2015, Catania, ITALY 124, 785 (2016). http://doi.org/10.1016/J.MICROC.2015.10.020
Abstract: Macro X-ray fluorescence scanning (MA-XRF) is gradually becoming an established technique for the non-invasive analytical investigation of painted surfaces. This paper discusses some of the benefits and limitations of employing MA-XRF for the study of manuscript illuminations. Art historical research on this type of artefacts that is based on scientific measurements is often limited by the fact that usually no sampling can take place. Hence there is a need for non-invasive analytical tools that make it possible to conduct systematic investigations. As a representative example of this type of objects, a 15th century Italian manuscript fragment from the collection of the Fitzwilliam Museum in Cambridge (UK) is investigated. The aims of the study were to gain insight into the materials and techniques employed by Renaissance illuminators and to help answer specific questions regarding the fragment's authorship and geographic origin. The complementarity and advantages of MA-XRF mapping versus site-specific analyses are discussed. For this purpose, MA-XRF data are evaluated and compared with the results of other analytical techniques. The interpretation of the elemental maps is discussed along with the challenges faced during the analysis. (C) 2015 Elsevier B.V. All rights reserved.
Keywords: A1 Journal article; AXES (Antwerp X-ray Analysis, Electrochemistry and Speciation)
Impact Factor: 3.034
Times cited: 24
DOI: 10.1016/J.MICROC.2015.10.020
|
|
|
“Non-invasive analysis of a 15th century illuminated manuscript fragment: point-based vs imaging spectroscopy”. Legrand S, Ricciardi P, Nodari L, Janssens K, Microchemical journal 138, 162 (2018). http://doi.org/10.1016/J.MICROC.2018.01.001
Abstract: Illuminated manuscript fragments are some of the best preserved objects of Western cultural heritage. Therefore, scholars are limited to non-invasive – often point-based – methods, to answer questions on material usage, technique, origin and previous treatments. These powerful methods yield specific information; however, the information is limited to the number of points analyzed. Imaging spectroscopies such as MA-XRF and MA-rFTIR combine specificity with the power of imaging, resulting in distribution images that are interpretable by non-spectroscopists and the public at large. In this paper the possible added value of using imaging spectroscopy is discussed. Do these methods yield the same results as an extensive point-based spectroscopic campaign and can they bring novel information? As a case study, a 15th century illuminated manuscript fragment is employed in order to explore the differences between these approaches and present an inventory of their advantages and limitations. (C) 2018 Elsevier B.V. All rights reserved.
Keywords: A1 Journal article; AXES (Antwerp X-ray Analysis, Electrochemistry and Speciation)
Impact Factor: 3.034
Times cited: 12
DOI: 10.1016/J.MICROC.2018.01.001
|
|
|
“Protecting and stimulating effect on the degradation of eosin lakes. Part 1 : lead white and cobalt blue”. Alvarez-Martin A, Janssens K, Microchemical journal 141, 51 (2018). http://doi.org/10.1016/J.MICROC.2018.05.005
Abstract: An important problem encountered during the preservation of paintings and other artworks is the fading of the original colors due to exposure of the colorants to light. This fact is clearly evidenced in some of Vincent Van Gogh's paintings in which an organic red, eosin or geranium lake, is present. The identification of eosin and the characterization of its degradation products in paintings represents a challenge because of (i) the generally low concentration of the pigment remaining after an aging period of ca 100 years, (ii) the scarcity of the paint micro samples available for analysis and the difficulty of obtaining additional ones and (iii) the complexity of the degradation behavior of eosin when it is mixed with organic or inorganic pigments, binding media or varnish. This study presents an accelerated aging experiment of eosin paint models in order to understand better the discoloration process; more specifically the influence of different metals with which eosin forms complexes and of the presence of admixture pigments such as lead white and cobalt blue on the lightfastness of eosin is evaluated. Paint model samples were prepared using eosin, lead white, and cobalt blue in different mixing ratios and were characterized with several techniques before and after aging. The possible formation of intermediate molecular forms during the aging experiment and the influence of pigment ratios on the discoloration process were monitored at periodic intervals using a combination of LTV Visible and attenuated total Reflectance-Fourier transform infrared (ATR-FTIR) spectroscopies. Raman spectroscopy, scanning electron microscopy coupled to energy-dispersive X-ray analysis (SEM-EDX) and optical microscopy (OM) analyses were performed to gain information about the discoloration processes taking place within the paint models. Eosin precipitated on lead, aluminum and potassium/aluminum salts was used. These three lakes showed similar discoloration rates under light exposure. In contrast, the presence and relative abundance of the admixture pigments lead white and cobalt blue had a significant influence on the (speed of the) eosin discoloration process. The presence of lead white and cobalt blue appears to stimulate the eosin degradation. However, the cobalt blue shows less influence in the discoloration process, showing a protective effect during the first stages of the aging. This may be qualitatively explained in terms of the ability of lead white to scatter light towards eosin molecules and the absorption characteristics of cobalt blue in the green range of the electromagnetic spectrum, shielding eosin from incoming light. The color changes observed in the paint reconstructions are similar to discoloration phenomena visible in some Van Gogh paintings and can offer an explanation of the gradual discoloration process that took place over the years. These insights will be helpful to estimate the original hues color used/intended by the artist.
Keywords: A1 Journal article; AXES (Antwerp X-ray Analysis, Electrochemistry and Speciation)
Impact Factor: 3.034
Times cited: 3
DOI: 10.1016/J.MICROC.2018.05.005
|
|
|
“Rembrandt's 'Saul and David' (c. 1652) : use of multiple types of smalt evidenced by means of non-destructive imaging”. Janssens K, van der Snickt G, Alfeld M, Noble P, van Loon A, Delaney J, Conover D, Zeibel J, Dik J, Microchemical journal 126, 515 (2016). http://doi.org/10.1016/J.MICROC.2016.01.013
Abstract: The painting Saul and David, considered to date from c. 1652 and previously attributed to Rembrandt van Rijn and/or his studio, is a complex work of art that has been recently subjected to intensive investigation and conservation treatment. The goal of the research was to give insight into the painting's physical construction and condition in preparation for conservation treatment. It was also anticipated that analysis would shed light on authenticity questions and Rembrandt's role in the creation of the painting. The painting depicts the Old Testament figures of King Saul and David. At left is Saul, seated, holding a spear and wiping a tear from his eye with a curtain. David kneels before him at the right playing his harp. In the past, the large sections with the life-size figures were cut apart and later reassembled. A third piece of canvas was added to replace a missing piece of canvas above the head of David. As part of the investigation into the authenticity of the curtain area, a number of paint micro samples were examined with LM and SEM-EDX. Given that the earth, smalt and lake pigments used in the painting could not be imaged with traditional imaging techniques, the entire painting was also examined with state of the art non-destructive imaging techniques. Special attention was devoted to the presence of cobalt-containing materials, specifically the blue glass pigment smalt considered characteristic for the late Rembrandt. A combination of quantitative electron microprobe analysis and macroscopic X-ray fluorescence scanning revealed that three types of cobalt-containing materials are present in the painting. The first type is a cobalt drier that was found in the overpaint used to cover up the canvas inset and the joins that were added in the 19th century. The other two Co-containing materials are part of the original paint used by Rembrandt and comprise two varieties of smalt, a K-rich glass pigment that derives its gray-blue color by doping with Co-ions. Smalt paint with a higher Ni content (NiO:CoO ratio of around 1:4) was used to depict the blue stripes in Saul's colorful turban, while smalt with a lower Ni content was employed (NiO:CoO ratio of around 1:5) for the broad expanses of Saul's garments. The presence of two types of smalt not only supports the recent re-attribution of the painting to Rembrandt, but also that the picture was painted in two phases. Saul's dark red garment is painted in a rough, “loose” manner and the now discolored smalt-rich layer was found to have been partially removed during a past restoration treatment/s. In contrast, the blue-green smalt in the turban is much better preserved and provides a colorful accent. While the use of different types of smalt in a Rembrandt painting has been previously identified using quantitative EDX analysis of paint cross-sections, to the best of our knowledge this is the first time such a distinction has been observed in a 17th-century painting using non-destructive imaging techniques. In addition to the XRF-based non-invasive elemental mapping, hyperspectral imaging in the visual to near-infrared (VNIR) region was also carried out. (C) 2016 Elsevier B.V. All rights reserved.
Keywords: A1 Journal article; AXES (Antwerp X-ray Analysis, Electrochemistry and Speciation)
Impact Factor: 3.034
Times cited: 18
DOI: 10.1016/J.MICROC.2016.01.013
|
|
|
“Simplex Volume Maximization (SiVM): a matrix factorization algorithm with non-negative constrains and low computing demands for the interpretation of full spectral X-ray fluorescence imaging data”. Alfeld M, Wahabzada M, Bauckhage C, Kersting K, van der Snickt G, Noble P, Janssens K, Wellenreuther G, Falkenberg G, Microchemical journal 132, 179 (2017). http://doi.org/10.1016/J.MICROC.2017.02.001
Abstract: Technological progress allows for an ever-faster acquisition of hyperspectral data, challenging the users to keep up with interpreting the recorded data. Matrix factorization, the representation of data sets by bases (or loads) and coefficient (or score) images is long used to support the interpretation of complex data sets. We propose in this publication Simplex Volume Maximization (SiVM) for the analysis of X-ray fluorescence (XRF) imaging data sets. SiVM selects archetypical data points that represents the data set and thus provides easily understandable bases, preserves the non-negative character of XRF data sets and has low demands concerning computing resources. We apply SiVM on an XRF data set of Hans Memling's Portrait of a man from the Lespinette family from the collection of the Mauritshuis (The Hague, NL) and discuss capabilities and shortcomings of SiVM. (C) 2017 Elsevier B.V. All rights reserved.
Keywords: A1 Journal article; AXES (Antwerp X-ray Analysis, Electrochemistry and Speciation)
Impact Factor: 3.034
Times cited: 8
DOI: 10.1016/J.MICROC.2017.02.001
|
|
|
“Combined MA-XRF, MA-XRPD and SEM-EDX analysis of a medieval stained-glass panel formerly from Notre Dame, Paris reveals its material history”. Gestels A, Van der Snickt G, Caen J, Nuyts G, Legrand S, Vanmeert F, Detry F, Janssens K, Steenackers G, Microchemical journal 177, 107304 (2022). http://doi.org/10.1016/J.MICROC.2022.107304
Abstract: As part of its conservation-restoration, the 13th century stained-glass panel ‘the Annunciation’, was examined at the micro- and macro level. This window, since 1898 in the collection of the Museum Mayer Van den Bergh (Antwerp, B), was formerly a part of the southern Rose window of the Notre Dame Cathedral (Paris, F). The insigths emerging from a first phase of the analysis, comprising non-invasive analysis techniques such as optical microscopy combined with macroscopic X-ray fluorescence (MA-XRF) and X-ray diffraction (MA-XRPD) mapping, were used to select sampling positions for the second phase of investigation that involved micro-invasive analysis, namely scanning-electron microscopy coupled to energy-dispersive X-ray analysis (SEM-EDX). The aim of the investigation was fourfold: (1) to assess the applicability of MA-XRF scanning for the characterisation of stained glass windows prior to any conservation or restoration procedure, (2) to assess the applicability of MA-XRPD scanning to identify the degradation products formed on the surface of stained glass windows, (3) to establish a method to limit the set of sampled glass fragments taken from a glass panel for quantititive analysis while maintaining sufficient representativeness and (4) to distinguish the original glass panes and grisaille paint from non-original glass panes that were inserted during various past interventions. Most of the panes in this window proved to consist of medieval potash glass, consistent with the 13th c. origin of the window while a limited number of panes were identified as non-original infills, with divergent glass compositional types and/or colorants. Most panes derive their color from the pot metal glass (i.e. homogenously colored) they were made of. Some of the panes that originally had a red flashed layer on their surface, completely or partially lost this layer due to weathering. Three main compositional glass families with similar color could be defined. With the exception of the yellow and orange panes, the chromophoric elements responsible for the dark(er) and light(er) blue (Co), green (Cu), purple (Mn) and red colors (Cu) were identified. Two different grisaille paints were encountered, part of which were restored during the 19th century. On the basis of this information, all missing pieces were replaced by glass panes with appropriate colors and the panel could be successfully conserved to its former glory. On the surface of several panes, typical glass degradation products such as calcite, syngenite and gypsum were identified, together with lead based degradation products such as anglesite and palmierite. In addition, the presence of hematite and melanotekite in the grisailles was observed; also the presence of Zn, uncorrelated to Cu, in the grissailes on the right side of the window became apparent.
Keywords: A1 Journal article; Engineering sciences. Technology; Art; Antwerp Cultural Heritage Sciences (ARCHES); Antwerp X-ray Imaging and Spectroscopy (AXIS)
Impact Factor: 4.8
DOI: 10.1016/J.MICROC.2022.107304
|
|
|
“Multi-modal approach for the characterization of resin carriers in Daylight Fluorescent Pigments”. Álvarez-Martín A, De Winter S, Nuyts G, Hermans J, Janssens K, van der Snickt G, Microchemical Journal 159, 105340 (2020). http://doi.org/10.1016/J.MICROC.2020.105340
Abstract: Almost seventy years after artists such as Frank Stella (1936), Andy Warhol (1928-1987), James Rosenquist (1933-2017), Herb Aach (1923-1985) and Richard Bowman (1918-2001) started to incorporate Daylight Fluorescent Pigments (DFPs) in their artworks, the extent of the conservation problems that are associated with these pigments has increased progressively. Since their first appearance on the market, their composition has constantly been improved in terms of permanency. However, conservation practices on the artworks that are used in, are complicated by the fact that the composition of DFPs is proprietary and the information provided by the manufactures is limited. To be able to propose adequate conservation strategies for artworks containing DFPs, a thorough understanding of the DFPs composition must be acquired. In contrast with previous research that concentrated on identification of the coloring dye, this paper focuses on the characterization of the resin, used as the carrier for the dye. The proposed approach, involving ATR-FTIR, SPME-GC-MS and XRF analysis, provided additional insights on the organic and inorganic components of the resin. Using this approach, we investigated historical DFPs and new formulations, as well as different series from the main manufacturing companies (DayGlo, Swada, Radiant Color and Kremer) in order to obtain a full characterization of DFPs used by the artists along the years. First, the initial PCA-assisted ATR-FTIR spectroscopy allowed for an efficient classification of the main monomers in the resin polymer. Next, a further distinction was made by mass spectrometry and XRF which were optimized to allow a more specific classification of the resin and for detection of additives. In this paper we show the potential of SPME-GC-MS, never applied for the characterization of artistic materials, at present undervalued for heritage science purposes. We anticipate that this information will be highly relevant in the future stability studies and for defining (preventive) conservation strategies of fluorescent artworks.
Keywords: A1 Journal article; AXES (Antwerp X-ray Analysis, Electrochemistry and Speciation); Antwerp Cultural Heritage Sciences (ARCHES)
Impact Factor: 4.8
DOI: 10.1016/J.MICROC.2020.105340
|
|
|
“Multianalytical study of patina formed on archaeological metal objects from Bliesbruck-Reinheim”. Wadsak M, Constantinides I, Vittiglio G, Adriaens A, Janssens K, Schreiner M, Adams FC, Brunella P, Wuttmann M, Microchimica acta 133, 159 (2000). http://doi.org/10.1007/S006040070086
Keywords: A1 Journal article; AXES (Antwerp X-ray Analysis, Electrochemistry and Speciation)
Impact Factor: 4.58
DOI: 10.1007/S006040070086
|
|
|
“Type II quantum dots in magnetic fields: excitonic behaviour”. Janssens KL, Partoens B, Peeters FM, Microelectronics journal 34, 347 (2003). http://doi.org/10.1016/S0026-2692(03)00023-5
Keywords: A1 Journal article; Condensed Matter Theory (CMT)
Impact Factor: 1.163
Times cited: 1
DOI: 10.1016/S0026-2692(03)00023-5
|
|
|
“Microanalysis (micro-XRF, micro-XANES, and micro-XRD) of a tertiary sediment using microfocused synchrotron radiation”. Denecke MA, Somogyi A, Janssens K, Simon R, Dardenne K, Noseck U, Microscopy and microanalysis 13, 165 (2007). http://doi.org/10.1017/S1431927607070316
Keywords: A1 Journal article; AXES (Antwerp X-ray Analysis, Electrochemistry and Speciation)
Impact Factor: 1.891
Times cited: 31
DOI: 10.1017/S1431927607070316
|
|
|
“PXRF, \mu-XRF, vacuum \mu-XRF, and EPMA analysis of Email Champlevé, objects present in Belgian museums”. van der Linden V, Meesdom E, Devos A, van Dooren R, Nieuwdorp H, Janssen E, Balace S, Vekemans B, Vincze L, Janssens K, Microscopy and microanalysis 17, 674 (2011). http://doi.org/10.1017/S1431927611011950
Abstract: The enamel of 20 Email Champlevé objects dating between the 12th and 19th centuries was investigated by means of microscopic and portable X-ray fluorescence analysis (μ-XRF and PXRF). Seven of these objects were microsampled and the fragments were analyzed with electron probe microanalysis (EPMA) and vacuum μ-XRF to obtain quantitative data about the composition of the glass used to produce these enameled objects. As a result of the evolution of the raw materials employed to produce the base glass, three different compositional groups could be discriminated. The first group consisted of soda-lime-silica glass with a sodium source of mineral origin (with low K content) that was opacified by addition of calcium antimonate crystals. This type of glass was only used in objects made in the 12th century. Email Champlevé objects from the beginning of the 13th century onward were enameled with soda-lime-silica glass with a sodium source of vegetal origin. This type of glass, which has a higher potassium content, was opacified with SnO2 crystals. The glass used for 19th century Email Champlevé artifacts was produced with synthetic and purified components resulting in a different chemical composition compared to the other groups. Although the four analytical techniques employed in this study have their own specific characteristics, they were all found to be suitable for classifying the objects into the different chronological categories.
Keywords: A1 Journal article; AXES (Antwerp X-ray Analysis, Electrochemistry and Speciation)
Impact Factor: 1.891
Times cited: 9
DOI: 10.1017/S1431927611011950
|
|
|
“The “Historical Materials BAG&rdquo, : a new facilitated access to synchrotron X-ray diffraction analyses for cultural heritage materials at the European Synchrotron Radiation Facility”. Cotte M, Gonzalez V, Vanmeert F, Monico L, Dejoie C, Burghammer M, Huder L, de Nolf W, Fisher S, Fazlic I, Chauffeton C, Wallez G, Jimenez N, Albert-Tortosa F, Salvado N, Possenti E, Colombo C, Ghirardello M, Comelli D, Avranovich Clerici E, Vivani R, Romani A, Costantino C, Janssens K, Taniguchi Y, McCarthy J, Reichert H, Susini J, Molecules: a journal of synthetic chemistry and natural product chemistry 27, 1997 (2022). http://doi.org/10.3390/MOLECULES27061997
Abstract: The European Synchrotron Radiation Facility (ESRF) has recently commissioned the new Extremely Brilliant Source (EBS). The gain in brightness as well as the continuous development of beamline instruments boosts the beamline performances, in particular in terms of accelerated data acquisition. This has motivated the development of new access modes as an alternative to standard proposals for access to beamtime, in particular via the “block allocation group” (BAG) mode. Here, we present the recently implemented “historical materials BAG”: a community proposal giving to 10 European institutes the opportunity for guaranteed beamtime at two X-ray powder diffraction (XRPD) beamlines-ID13, for 2D high lateral resolution XRPD mapping, and ID22 for high angular resolution XRPD bulk analyses-with a particular focus on applications to cultural heritage. The capabilities offered by these instruments, the specific hardware and software developments to facilitate and speed-up data acquisition and data processing are detailed, and the first results from this new access are illustrated with recent applications to pigments, paintings, ceramics and wood.
Keywords: A1 Journal article; Antwerp X-ray Imaging and Spectroscopy (AXIS)
Impact Factor: 4.6
DOI: 10.3390/MOLECULES27061997
|
|