Abstract: In this work, a simple method to measure the indirect band gap of diamond with electron energy loss spectroscopy (EELS) in transmission electron microscopy (TEM) is showed. The authors discuss the momentum space resolution achievable with EELS and the possibility of deliberately selecting specific transitions of interest. Based on a simple 2 parabolic band model of the band structure, the authors extend our predictions from the direct band gap case discussed in previous work, to the case of an indirect band gap. Finally, the authors point out the emerging possibility to partly reconstruct the band structure with EELS exploiting our simplified model of inelastic scattering and support it with experiments on diamond.

Abstract: The amorphous oxide semiconductor Indium-Gallium-Zinc-Oxide (a-IGZO) has gained a large technological relevance as a semiconductor for thin-film transistors in active-matrix displays. Yet, major questions remain unanswered regarding the atomic origin of threshold voltage control, doping level, hysteresis, negative bias stress (NBS), and negative bias illumination stress (NBIS). We undertake a systematic study of the effects of oxygen vacancies on the properties of a-IGZO by relating experimental observations to microscopic insights gained from first-principle simulations. It is found that the amorphous nature of the semiconductor allows unusually large atomic relaxations. In some cases, oxygen vacancies are found to behave as perfect shallow donors without the formation of structural defects. Once structural defects are formed, their transition states can vary upon charge and discharge cycles. We associate this phenomenon to a possible presence of hysteresis in the transfer curve of the devices. Under NBS, the creation of oxygen vacancies becomes energetically very stable, hence thermodynamically very likely. This generation process is correlated with the occurrence of the negative bias stress instabilities observed in a-IGZO transistors. While oxygen vacancies can therefore be related to NBS and hysteresis, it appears unlikely from our results that they are direct causes of NBIS, contrary to common belief.

Abstract: Evolution of crystalline phases with temperature has been studied in materials produced by high-pressure high-temperature treatment of 9-borabicyclo[3.3.1]nonane dimer (9BBN), triphenylborane and trimesitylborane. The boron-doped diamond nanoparticles with a size below 10 nm were obtained at 8–9 GPa and temperatures 970–1250 °C from 9BBN only. Bridged structure and the presence of boron atom in the carbon cycle of 9BBN were revealed to be a key point for the direct synthesis of doped diamond nanocrystals. The diffusional transformation of the disordered carbon phase is suggested to be the main mechanism of the nanodiamond formation from 9BBN in the temperature range of 970–1400 °C. Aqueous suspensions of primary boron-doped diamond nanocrystals were prepared upon removal of non-diamond phases that opens wide opportunities for application of this new nanomaterial in electronics and biotechnologies.

Abstract: Aberration-corrected transmission electron microscopy, electron energy-loss spectroscopy, and density functional theory (DFT) calculations are used to solve several key questions about the surface structure, the particle morphology, and the distribution and nature of nitrogen impurities in detonation nanodiamond (DND) cleaned by a recently developed ozone treatment. All microscopy and spectroscopy measurements are performed at a lowered acceleration voltage (80/120kV), allowing prolonged and detailed experiments to be carried out while minimizing the risk of knock-on damage or surface graphitization of the nanodiamond. High-resolution TEM (HRTEM) demonstrates the stability of even the smallest nanodiamonds under electron illumination at low voltage and is used to image the surface structure of pristine DND. High resolution electron energy-loss spectroscopy (EELS) measurements on the fine structure of the carbon K-edge of nanodiamond demonstrate that the typical * pre-peak in fact consists of three sub-peaks that arise from the presence of, amongst others, minimal fullerene-like reconstructions at the nanoparticle surfaces and deviations from perfect sp(3) coordination at defects in the nanodiamonds. Spatially resolved EELS experiments evidence the presence of nitrogen within the core of DND particles. The nitrogen is present throughout the whole diamond core, and can be enriched at defect regions. By comparing the fine structure of the experimental nitrogen K-edge with calculated energy-loss near-edge structure (ELNES) spectra from DFT, the embedded nitrogen is most likely related to small amounts of single substitutional and/or A-center nitrogen, combined with larger nitrogen clusters.

Abstract: The depth strain profile in silicon from the Si (001) substrate to the surface of a 2 nm thick Si/12 nm thick SiGe/bulk Si heterostructure has been determined by medium energy ion scattering (MEIS). It shows with sub-nanometer resolution and high strain sensitivity that the thin Si cap presents residual compressive strain caused by Ge diffusion coming from the fully strained SiGe layer underneath. The strain state of the SiGe buffer have been checked by X-ray diffraction (XRD) and nano-beam electron diffraction (NBED) measurements.

Abstract: The problem of the epitaxial growth of the high temperature superconducting R1+xBa2xCu3O7δ (R = Y or rare earth except Ce and Tb) films has been addressed. Using in situ ultra high vacuum Scanning Tunneling Microscopy (UHV-STM) we have studied the role of cationic substitution and substrate mismatch on the growth mode of stoichiometric and Nd-rich Nd1+xBa2xCu3O7δ thin films. The results are compared to the growth of Y1Ba2Cu3O7δ, Dy1Ba2Cu3O7δ and Gd1Ba2Cu3O7δ epitaxial films. Two main phenomena are investigated: a) the first stage of the direct nucleation on the substrate and b) the crossover between 2D and 3D growth upon increasing the film thickness. At the first stage of the growth, pseudo-cubic perovskite (Re,Ba)CuO3 nuclei are formed. While they disappear after the growth of a few nm in stoichiometric films, they persist on the surface of Nd-rich films of up to 110 nm thickness. Stoichiometric R1+xBa2xCu3O7δ films exhibit a rough morphology with increasing thickness due to island growth mode, whereas Nd-rich films remain smooth and continue to grow layer by layer. It is proposed that linear defects (like anti-phase boundaries), which are formed due to the misalignment of growth fronts, are the source of screw dislocations in stoichiometric films. In Nd-rich films, linear defects are eliminated through the insertion of (Nd,Ba)CuO3 extra layers without introduction of any screw dislocations.

Abstract: In situ irradiation experiments in a high resolution electron microscope JEOL-4000EX at room temperature resulted in discovery of the isolated and combined clustering of vacancies and self-interstitial atoms on {111}- and {113}-habit planes both leading to an extended defect formation in Si crystals. The type of the defect is strongly affected by the type of supersaturation of point defects depending on the crystal thickness during electron irradiation. Because of the existence of energy barriers against recombination of interstitials with the extended aggregates of vacancies, a large family of intermediate defect configurations (IDCs) is formed on {113}- and {111}-habit planes at a low temperature under interstitial supersaturation in addition to the well-known {133}-defects of interstitial type. The formation of metastable IDCs inside vacancy aggregates prevents a way of recombination of defects in extended shape.