Abstract |
We examine the effect of CuO intergrowths on the superconductivity in epitaxial
La 2/3 Ca 1/3 MnO 3 / YBa 2 Cu 3 O 7−δ La2/3Ca1/3MnO3/YBa2Cu3O7−δ
(LCMO/YBCO) thin-film heterostructures. Scanning transmission electron microscopy on bilayer LCMO/YBCO thin films revealed double CuO-chain intergrowths which form regions with the 247 lattice structure in the YBCO layer. These nanoscale 247 regions do not appear in x-ray diffraction, but can physically account for the reduced critical temperature (Tc) of bilayer thin films relative to unilayer films with the same YBCO thickness, at least down to ∼25 nm. We attribute the CuO intergrowths to the bilayer heteroepitaxial mismatch and the Tc reduction to the generally lower Tc seen in bulk 247 samples. These epitaxially-induced CuO intergrowths provide a microstructural mechanism for the attenuation of superconductivity in LCMO/YBCO heterostructures. |
|