Record |
Links |
|
Author |
Zhang, F.; Inokoshi, M.; Batuk, M.; Hadermann, J.; Naert, I.; Van Meerbeek, B.; Vleugels, J. |
|
| |
Title |
Strength, toughness and aging stability of highly-translucent Y-TZP ceramics for dental restorations |
Type |
A1 Journal article |
| |
Year  |
2016 |
Publication |
Dental Materials |
Abbreviated Journal |
Dent Mater |
|
| |
Volume |
32 |
Issue |
32 |
Pages |
e327-e337 |
|
| |
Keywords |
A1 Journal article; Electron Microscopy for Materials Science (EMAT); |
|
| |
Abstract |
OBJECTIVE: The aim was to evaluate the optical properties, mechanical properties and aging stability of yttria-stabilized zirconia with different compositions, highlighting the influence of the alumina addition, Y2O3 content and La2O3 doping on the translucency. METHODS: Five different Y-TZP zirconia powders (3 commercially available and 2 experimentally modified) were sintered under the same conditions and characterized by X-ray diffraction with Rietveld analysis and scanning electron microscopy (SEM). Translucency (n=6/group) was measured with a color meter, allowing to calculate the translucency parameter (TP) and the contrast ratio (CR). Mechanical properties were appraised with four-point bending strength (n=10), single edge V-notched beam (SEVNB) fracture toughness (n=8) and Vickers hardness (n=10). The aging stability was evaluated by measuring the tetragonal to monoclinic transformation (n=3) after accelerated hydrothermal aging in steam at 134 degrees C, and the transformation curves were fitted by the Mehl-Avrami-Johnson (MAJ) equation. Data were analyzed by one-way ANOVA, followed by Tukey's HSD test (alpha=0.05). RESULTS: Lowering the alumina content below 0.25wt.% avoided the formation of alumina particles and therefore increased the translucency of 3Y-TZP ceramics, but the hydrothermal aging stability was reduced. A higher yttria content (5mol%) introduced about 50% cubic zirconia phase and gave rise to the most translucent and aging-resistant Y-TZP ceramics, but the fracture toughness and strength were considerably sacrificed. 0.2mol% La2O3 doping of 3Y-TZP tailored the grain boundary chemistry and significantly improved the aging resistance and translucency. Although the translucency improvement by La2O3 doping was less effective than for introducing a substantial amount of cubic zirconia, this strategy was able to maintain the mechanical properties of typical 3Y-TZP ceramics. SIGNIFICANCE: Three different approaches were compared to improve the translucency of 3Y-TZP ceramics. |
|
| |
Address |
KU Leuven, Department of Materials Engineering, Kasteelpark Arenberg 44, Belgium |
|
| |
Corporate Author |
|
Thesis |
|
|
| |
Publisher |
|
Place of Publication |
|
Editor |
|
|
| |
Language |
English |
Wos |
000389516400003 |
Publication Date |
2016-10-06 |
|
| |
Series Editor |
|
Series Title |
|
Abbreviated Series Title |
|
|
| |
Series Volume |
|
Series Issue |
|
Edition |
|
|
| |
ISSN |
0109-5641 |
ISBN |
|
Additional Links |
UA library record; WoS full record; WoS citing articles |
|
| |
Impact Factor |
4.07 |
Times cited |
|
Open Access |
|
|
| |
Notes |
The authors acknowledge the Research Fund of KU Leu- ven under project 0T/10/052 and the Fund for Scientific Research Flanders (FWO-Vlaanderen) under grant G.0431.10N. F. Zhang thanks the Research Fund of KU Leuven for her post- doctoral fellowship (PDM/15/153). We thank M. Peumans for the translucency measurements. |
Approved |
Most recent IF: 4.07 |
|
| |
Call Number |
EMAT @ emat @ c:irua:136821 |
Serial |
4313 |
|
| Permanent link to this record |