Both an organically modified commercial clay of montmorillonite type (MMT) and its nanocomposites, based either on polyamide 6 (PA6) or an epoxy resin, as matrix polymer, have been characterized by transmission electron microscopy (TEM). Sample micrographs, taken at increasing exposure times (t(e)), have shown the gradual disappearance of clay layers, because of an amorphisation of the MMT crystalline structures caused by prolonged sample exposure to electron beam. Indeed, the above phenomenon, which is mostly evident in the case of intercalated nanocomposites, makes the detection of the layered silicate dispersion in the polymer matrix rather difficult and compels to perform TEM measurements using very short exposure times. Moreover, the microscopy accelerating voltage has turned out to affect sample stability; namely, when decreasing the above parameter, the disappearance of clay structure occurs at lower exposure times. (C) 2006 Elsevier B.V. All rights reserved. |
|