Abstract |
When strained in tension, high-manganese austenitic twinning induced plasticity (TWIP) steels achieve very high strength and elongation before necking. The main hypotheses available in the literature about the origin of their excellent work hardening include deformation twinning and dynamic strain ageing. In order to provide some answers, various experiments at different scales were conducted on FeMnC steels and the Fe28 wt%Mn3.5 wt%Al2.8 wt%Si alloy. At a macroscopic scale, tensile tests were performed on all the studied grades. It was shown that, though the FeMnAlSi based alloy retains very high elongation, the FeMnC steels properties are even more extraordinary. Tensile tests at different strain rates with the help of digital image correlation were also performed on the Fe20 wt%Mn1.2 wt%C steel to study the PLC effect occurring in this type of steel. It is suggested that supplementary hardening could come from reorientation of MnC pairs in the cores of the dislocations. At a microscopic scale, the Fe20 wt%Mn1.2 wt%C TWIP steel and the FeMnAlSi grade were thoroughly investigated by means of in situ TEM analysis. In the FeMnC steel, the formed twins could also lead to a composite effect, since they contain plenty of sessile dislocations. In the FeMnAlSi alloy, mechanical twins are thicker and contain fewer defects, leading to a lower work hardening than the other grade. |
|