Abstract: Tempering is widely applied to make carbon atoms beneficially rearrange in high strength steel microstructures after quenching; though the nano-scale interaction of carbon atoms with crystallographic defects is hard to experimentally observe. To improve, we investigate the redistribution of carbon atoms along martensite grain boundaries in a quenched and tempered low carbon steel. We observe the tempering-induced microstructural evolution by in-situ heating in a transmission electron microscope (TEM) and by compositional analysis through atom probe tomography (APT). Probe volumes for APT originate from a single martensite packet but in different tempering conditions, which is achieved via a sequential lift-out with in-between tempering treatments. The complementary use of TEM and APT provides crystallographic as well as chemical information on carbon segregation and subsequent carbide precipitation at martensite grain boundaries. The results show that the amount of carbon segregation to martensite grain boundaries is influenced by the boundary type, e.g. low-angle lath or high-angle block boundaries. Also, the growth behavior of cementite precipitates from grain boundary nucleation sites into neighboring martensite grains differs at low- and high-angle grain boundaries. This is due to the crystallographic constraints arising from the semi-coherent orientation relationship between cementite and adjacent martensite. We also show that slower quenching stabilizes thin retained austenite films between martensite grains because of enhanced carbon segregation during cooling. Finally, we demonstrate the effect of carbon redistribution along martensite grain boundaries on the mechanical properties. Here, we compare micro-scale Vickers hardness results from boundary-containing probe volumes to nanoindentation results from pure bulk martensite (boundary-free) probe volumes.

Abstract: Transmission electron microscopy and finite element-based dislocation simulations were combined to study the development of dislocation microstructures after cyclic deformation of single crystal and bicrystal Ni micropillars oriented for multi-slip. A direct correlation between large accumulation of plastic strain and the presence of dislocation cell walls in the single crystal micropillars was observed, while the presence of the grain boundary hampered the formation of wall-like structures in agreement with a smaller accumulated plastic strain. Automated crystallographic orientation and nanostrain mapping using transmission electron microscopy revealed the presence of lattice heterogeneities associated to the cell walls including long range elastic strain fields. By combining the nanostrain mapping with an inverse modelling approach, information about dislocation density, line orientation and Burgers vector direction was derived, which is not accessible otherwise in such dense dislocation structures. Simulations showed that the image forces associated with the grain boundary in this specific bicrystal configuration have only a minor influence on dislocation behavior. Thus, the reduced occurrence of “mature” cell walls in the bicrystal can be attributed to the available volume, which is too small to accommodate cell structures.

Abstract: The toughness of Al-to-steel welds decreases with increasing thickness of the intermetallic (IM) layer formed at the interface. Co plating has been added as interlayer in Al-to-steel Friction Melt Bonded (FMB) welds to control the nature and thickness of the IM layer. In comparison to a weld without interlayer, Co plating brings about a reduction of the thickness of the IM layer by 70%. The critical energy release rate of the crack propagating in the weld is used as an indicator of toughness. It is evaluated via an adapted crack propagation test using an energy conservation criterion. For a weld without interlayer, critical energy release rate is found to increase when the thickness of the intermetallic layer decreases. When the intermetallic layer is thick, the crack propagates in a brittle manner through the intermetallic whereas, at low layer thickness, the crack deviates and partially propagates through the Al plate, which causes an increase of toughness. The use of a Co interlayer brings about an increase of toughness by causing full deviation of the crack towards the Al plate.

Abstract: Whereas deformation twinning is known to be an important deformation mechanism for hexagonal materials like magnesium and pure titanium, so far almost no literature exists on the twinning behaviour of the Ti-6Al-4V alloy. In this work it was shown that the activation of twinning as a deformation mechanism could have a pronounced effect on the mechanical behaviour of the Ti-6Al-4V alloy. This effect is even more pronounced under dynamic loading conditions. Transmission electron microscopy showed that only the {1 0 1 2}{1 0 1 1} tensile twin system was activated under certain loading conditions. Light-optical microscopy and electron backscatter diffraction data were afterwards used to experimentally determine the twin fractions. The importance of twinning for the texture evolution was also studied. It was shown that even small twin fractions can lead to distinct texture features, especially due to the discrete reorientation of the c-axes. The experimental results were compared to simulated results that were obtained with a viscoplastic self-consistent crystal plasticity code, after experimental validation that twinning can be reliably modelled as a unidirectional slip system. Although good agreement was obtained for the experimental and simulated stress-strain curves, the simulated results concerning twinning correlated well only on a qualitative basis as the simulated twin fractions were systematically higher than the experimental fractions. This seems to strengthen the hypothesis made by other research groups that complete grains might reorient by twinning. (C) 2011 Elsevier B.V. All rights reserved.

Abstract: Ti6Al4V sheet material is subjected to simple shear deformation with strain ratio's of 10%, 30% and 50%. Optical microscopy, transmission electron microscopy and electron backscatter diffraction techniques are applied to study the presence and morphology of deformation twins. Only the View the MathML source type of twins seems to be present with a volume fraction below 1%. These View the MathML source twins show a high density of basal stacking faults of the ABABACAC type identified using atomic resolution transmission electron microscopy. A resolved shear stress analysis shows that twins most often occur on those planes with the highest resolved shear stresses, but that the starting texture is not beneficial for the occurrence of twins. It is further suggested that a transitory strain hardening regime observed around 530 MPa might be related with the onset of twinning.

Abstract: Au particles were prepared by evaporation in ultra high vacuum at high temperature, on the surfaces of TiO2 micro-spheres with the anatase structure. The morphology and the structural deformation in Au deposits were studied by high resolution transmission electron microscopy and image simulations by the multislice technique. The particles were polyhedral, limited by (100) and (111) faces. Patches with a hexagonal lattice were found around the particles, which was interpreted as thin Au islands on the surface. In these islands the Au lattice was deformed and perfectly accommodated to the (110) surface of TiO2. (C) 2001 Elsevier Science B.V. All rights reserved.