Abstract: The microstructural features of intergranular irradiation-assisted stress corrosion crack tips from a redeemed neutron-irradiated flux thimble tube (60 dpa) have been investigated using focused-ion beam analysis and (scanning) transmission electron microscopy. The current work presents a close examination of the deformation field and oxide assembly associated with intergranular cracking, in addition to the analysis of radiation-induced segregation at leading grain boundaries. Evidence of stress induced martensitic transformation extending from the crack tips is presented. Intergranular crack arrest is demonstrated on the account of the external tensile stress orientation, and as a consequence of MnS inclusion particles segregating close to the fractured grain boundary. Exclusive observations of grain boundary oxidation prior to the cracking are presented, which is in full-agreement with the internal oxidation model.(c) 2022 Elsevier B.V. All rights reserved.

Abstract: The present work reports on the microstructural evolution of a new heat of 24% cold worked austenitic DIN 1.4970 (15-15Ti) nuclear cladding steel subjected to ageing heat treatments of varying duration between 500 and 800 degrees C (by steps of 100 degrees C). The primary aim was studying the finely dispersed Ti-C nanoprecipitate population, which are thought to be beneficial for creep and swelling resistance during service. Their size distribution and number density were estimated through dark field imaging and bright field Moire imaging techniques in the transmission electron microscope. Nanoprecipitates formed at and above 600 degrees C, which is a lower temperature than previously reported. The observed nucleation, growth and coarsening behavior of the nanoprecipitates were consistent with simple diffusion arguments. The formation of nanoprecipitates coincided with significant dissociation of dislocations as evidenced by weak beam dark field imaging. Possible mechanisms, including Silcock's stacking fault growth model and Suzuki segregation, are discussed. Recrystallization observed after extended ageing at 800 degrees C caused the redissolution of nanoprecipitates. Large primary Ti(C,N) and (Ti,Mo)C precipitates that occur in the as-received material, and M23C6 precipitates that nucleate on grain boundaries at low temperatures were also characterized by a selective dissolution procedure involving filtration, X-ray diffraction and quantitative Rietveld refinement. The partitioning of key elements between the different phases was derived by combining these findings and was consistent with thermodynamic considerations and the processing history of the steel. (C) 2018 Elsevier B.V. All rights reserved.

Abstract: This work addresses the dissolution corrosion behaviour of 316L austenitic stainless steels. For this purpose, solution-annealed and cold-deformed 316L steels were simultaneously exposed to oxygen-poor (<10-8 mass%) static liquid lead-bismuth eutectic (LBE) for 253e3282 h at 500 °C. Corrosion was consistently more severe for the cold-drawn steels than the solution-annealed steel, indicating the importance of the steel thermomechanical state. The thickness of the dissolution-affected zone was nonuniform, and sites of locally-enhanced dissolution were occasionally observed. The progress of LBE dissolution attack was promoted by the interplay of certain steel microstructural features (grain boundaries, deformation twin laths, precipitates) with the dissolution corrosion process. The identified dissolution mechanisms were selective leaching leading to steel ferritization, and non-selective leaching; the latter was mainly observed in the solution-annealed steel. The maximum corrosion rate decreased with exposure time and was found to be inversely proportional to the depth of dissolution attack.

Abstract: Soil samples from an abandoned uranium mine have been investigated in order to determine the molecular phases of uranium compounds. The experiments were carried out with soil particulate matter, collected randomly from the area of the formerly exploited ore. To select the particles rich with uranium, scanning electron microscopy with energy-dispersive X-ray attachment (SEM/EDX) was applied first. Afterwards, the particles were relocated and measured by l-Raman spectrometry (MRS). Residues of the main deposit, uraninite UO2, were detected, along with its alteration products. In terms of Raman scattering properties, uranium oxides are quite sensitive to the laser beam wavelength, which results in very specific features of their Raman spectra. In this paper the Raman spectra of uranium oxides of different origin and oxidation states, measured with 514 and 785 nm lasers, are also presented