Abstract: In this work, we report an anomalous phenomenon on superelastic cycling of NiTi shape memory alloys when deforming at the temperature close to the border of superelastic window. New unexpected effects are found-(i) critical stress for inducing martensite transformation during the second loading cycle is higher than that of the first cycle; ( ii ) the plateau stress of the second cycle decreases to the original level when the strain overcomes the limit of the first cycle; ( iii ) transition from good superelasticity in the first cycle to fully irreversible strain in the second. We propose that defects generated during the first superelastic cycle close to the border of superelastic window impede following stress-induced martensitic transformations, leading to the increase of critical stress beyond yield stress of the B2 matrix, and thus functional fatigue of NiTi alloys. (c) 2021 Acta Materialia Inc. Published by Elsevier Ltd. All rights reserved.

Abstract: The effect of thermal cycling parameters on the phase transformation temperatures of micron and submicron grain size recrystallized Ni-Ti microwires was investigated. The suppression of martensitic transformation by thermal cycling was found to enhance when combined with room temperature aging between the cycles and enhances even more when aged at elevated temperature of 100 degrees C. While aging at room temperature alone has no clear effect on the martensitic transformation, elevated temperature aging at 100 degrees C alone suppresses the martensitic transformation. All aforementioned effects were found to be stronger in large grain samples than in small grain samples. Martensitic transformation suppression in all cases was in line with the formation of Ni4Ti3 precursors in the form of < 111 & rang;(B2) Ni clusters as concluded from the observed diffuse intensity in the electron diffraction patterns revealing short-range ordering enhancement. Performing thermal cycling in some different temperature ranges to separate the effect of martensitic transformation and high temperature range of DSC cycling revealed that both high temperature- and martensitic transformation-included cycles enhance the short-range ordering.

Abstract: Various low temperature treatments of Ni50.6Ti49.4 have shown an unexpected effect on the martensitic start temperature. Periodic diffuse intensity distributions in reciprocal space indicate the formation of short pure Ni strings along the <111> directions in the B2 ordered lattice, precursing the formation of Ni4Ti3 precipitates formed at higher annealing temperatures.

Abstract: In order to take advantage of both grain refinement and precipitation hardening effects, nanoscaled Ni4Ti3 precipitates are introduced in a Ti50.8 at.% Ni alloy with micron-sized grains (average grain size of 1.7 μm). Calorimetry, electrical resistance studies and thermomechanical tests were employed to study the transformation behavior and functional properties in relation to the obtained microstructure. A significant suppression of martensite transformation by the obtained microstructure is observed. The thermomechanical tests show that the advantageous properties of both grain refinement and precipitation hardening are combined in the developed materials, resulting in superior shape memory characteristics and stability of pseudoelasticity. It is concluded that introducing nanoscaled Ni4Ti3 precipitates into small grains is a new approach to improve the functional properties of NiTi shape memory alloys.

Abstract: A Ti-50.8at.%Ni wire produced using a co-drawing method and a commercial Ti-50.8at.%Ni wire were annealed at different temperatures between 450°C and 700°C. Grains with diameter less than 100nm were revealed by transmission electron microscopy for both wires before annealing treatment. However, the microstructural heterogeneity of the co-drawn wire is more obvious than that of the commercial wire. Multi-stage martensitic transformation was observed in the co-drawn wire, compared with the one-stage A↔M transformation in the commercial wire after annealing at 600°C for 30min. The differences of total elongation, plateau strain and pseudoelastic recoverable strain between the commercial wire and the co-drawn wire were also observed. The differences of the transformation behavior and mechanical properties between the commercial wire and the co-drawn wire are attributed to the microstructural difference between these two wires.