Abstract: The formation of metal oxalates in paintings has recently gained a great deal of interest within the field of heritage science as several types of oxalate compounds have been identified in oil paintings. The present work investigates the formation of metal oxalates in linseed oil in the presence of the artists' pigments zinc white, calcite, lead white, zinc yellow, chrome yellow, cadmium yellow, cobalt violet, and verdigris. The oil paint films were artificially photo-aged by exposure to UVA light at low and high relative humidity, and afterwards analysed by attenuated total reflectance-Fourier transform infrared spectroscopy (ATR-FTIR). The results showed that, compared to the other pigments investigated, zinc white is especially prone to metal oxalate formation and that high humidity is a crucial factor in this process. Consequently, the reactivity and photo-aging of ZnO in various oil binding media was investigated further under simulated solar radiation and at high relative humidity levels. ATR-FTIR showed that zinc oxalate is formed in all oil binding media while X-ray powder diffraction (PXRD) revealed it was mainly present in an amorphous state. To examine whether atmospheric CO2(g) has any influence on the formation of zinc oxalate, experiments with isotopically enriched (CO2(g))-C-13 were performed. Based on ATR-FTIR measurements, neither (ZnC2O4)-C-13 nor (ZnCO3)-C-13 were formed which suggests that the carbon source for the oxalate formation is most likely the paint itself (and its oil component) and not the surrounding atmosphere.

Abstract: Although it is now relatively straightforward to identify protein binders in works of art, their proper localization within the corresponding layer still represents a significant analytical challenge. Until now, the identification of proteins has mainly been performed by peptide mass fingerprinting using mass spectrometric methods and their localization in polished paint cross-sections have been realized by optical microscopy via the use of fluorescent stain Sypro Ruby (SR). In this work we propose a simplified protocol for immuno-surface enhanced Raman scattering (immuno-SERS) using gold nanoparticles attached to biphenyl-4,4-dithiol (BPDT) as the SERS-nanotag. These nanoparticles are easily obtainable in the lab and have been used to label multilayered mock up samples prepared as cross-sections to estimate the detection limits of the suggested method. The layers contain egg, casein, and different animal glues binders (prepared in various ratios with linseed oil or a carbohydrate component) mixed with the pigments azurite, vermilion and chalk. The sensitivity of staining agent SR is compared to that of the immuno-SERS protocol for the first time.

Abstract: In this study, a combination of elemental analytical techniques (MA-XRF and SEM-EDX) were used to localize arsenic sulfide pigments within a 17th-century Dutch painting and in the stratigraphy of an 18th-century Flemish polychrome sculpture. Once located, Raman spectroscopy was used to obtain the vibrational signature of the arsenic sulfide pigments employed. By means of the latter analytical technique and due to the very distinctive Raman scattering signal of the various arsenic sulfide compounds, it was possible to identify the arsenic-based pigments as natural orpiment and amorphous arsenic sulfide. In the latter case, based on the minor bands observed and the good condition of the paint layers, it was possible to identify pararealgar, the orangey-yellow to yellow degradation product of realgar, as the initial arsenic sulfide material used for the synthesis of the amorphous pigment. To the best of our knowledge, this is the first time that combined pararealgar/amorphous arsenic sulfide Raman spectra are reported in historical samples. Therefore, this would be the first identification of pararealgar as the starting material to produce amorphous, arsenic sulfide pigments used in artworks.

Abstract: A combined Raman and electrochemical study of natural orpiment (As2S3), an arsenic sulfide pigment, was used to assess the quick formation of oxidized species such as arsenic oxide (As2O3) upon exposing the pigment to 405 nm or 532 nm monochromatic light while simultaneously recording the Raman spectra of the exposed sample. During this process, a distortion of the main band at 355 cm−1, associated with the stretching of the AsS3/2 pyramids of natural orpiment, was observed as well as an increased intensity of the 359 cm−1 band, corresponding to covalent AsAs bonds in natural orpiment. The distortion was accompanied by an overall decrease of the global Raman signal for natural orpiment, which could be explained by a loss in the crystal structure. The same phenomena were recorded in reference natural orpiment model paint samples stored for a long time together with verdigris (Cu(OH)2·(CH3COO)2·5H2O) and minium (Pb3O4) paints, the latter two appearing darkened on their sides closest to the orpiment sample as well as in several historical samples containing natural orpiment mixed with various blue pigments. By SEM-EDX and XRPD analysis, respectively on loose material and cast thin-sections of model paint samples, the darkening was identified as dark sulfide species such as chalcocite (Cu2S) and galena (PbS), suggesting the release of volatile sulfide or related species by the natural orpiment paint. XANES analyses of paint samples presenting AsAs bond increase indicated the presence of sulfur species most likely identified as organosulfur compounds formed upon the AsAs bond formation and explained the darkening of the Cu- and Pb-based pigments. To the best of our knowledge, this article reports for the first time the light-induced formation of AsAs bonds in natural orpiment used as an artists' pigment and objectively demonstrates the incompatibility between orpiment and (arsenic) sulfide-sensitive pigments.

Abstract: Orpiment and realgar, both arsenic sulfide pigments respectively used for their vivid yellow and red-orange hues, are two of many artists' pigments that appear not to be stable upon light exposure, quickly degrading to arsenic trioxide and arsenate. This often results in whitening or transparency in the painted surfaces. While conventional techniques such as microscopic Raman (mu-RS) and microscopic Fourier transform infrared (mu-FTIR) spectroscopies can allow a quick and relatively easy identification of the orpiment, realgar, artificial arsenic sulfide glass and, to some extent, arsenic oxide, the identification and visualization of distributions of the degradation products – and especially arsenate compounds – in the paint micro-samples is generally more challenging. This challenge is due to the rather unfavorable limit of detection and low spectral resolution of such conventional spectroscopic techniques. This restricts the conclusions that can be drawn regarding the conservation state of valuable works of art. In this paper, we present how synchrotron radiation (SR) based techniques can overcome this challenge while working on painting cross-sections taken from a 17th-century painting by the Flemish artist Daniel Seghers (oil on canvas, Statens Museum for Kunst, Denmark) and an 18th-century French Chinoiserie (private collection, France). SR micro-X-ray fluorescence (m-XRF) mapping analysis performed on a visually degraded orpiment-containing paint stratigraphy reveals that arsenic is distributed throughout the entire cross-section, while X-ray absorption near edge structure (mu-XANES) demonstrated that the arsenic is present in both arsenite (As-III) and arsenate (As-V) forms. The latter compound(s), despite being barely identifiable by means of FTIR, were not only located at the surface of large and partially altered grains of arsenic sulfide but also spread throughout the entire paint stratigraphy. Their presence and distribution are attributed either to the complete degradation of smaller arsenic sulfide grains or to migration of the arsenates within the paint layer away from their original location of formation. The combination of mu-XRF and mu-XANES was very useful for the characterization of the advanced degradation state of the arsenic-containing pigments in paint systems; this type of information could not be obtained by means of conventional spectroscopic methods of microanalysis.