Abstract: Stone monuments and buildings are susceptible to weathering. Carbonate-based stones are especially vulnerable in acidic environments, whereas magmatic acidic stones are more susceptible to chemical weathering in basic environments. To slow down surface corrosion of limestone and marble artworks/buildings, protective coatings which inhibit calcite dissolution have been proposed. In this work, samples from two stone types with different porosity were treated with ammonium oxalate (AmOx) to create a protective layer of calcium oxalate (CaOx) using the previously developed brushing method. Two different synchrotron microscopy experiments were performed to determine its protective capability. X-ray powder diffraction (SR-mu-XRPD) in transmission geometry allowed visualization of the distributions of calcium carbonate and oxalates along the sample depths. In a second step, X-ray fluorescence (SR-mu-XRF) was used to check the efficiency/integrity of the protective surface coating layer. This was done by measuring the sulfur distribution on the stone surface after exposing the protected stones to sulfuric acid. XRPD showed the formation of a protective oxalate layer with a thickness of 5-15 mu m on the less porous stone, while a 20-30 mu m thick layer formed on the more porous stone. The XRF study showed that the optimal treatment time depends on the stone porosity. Increasing the treatment time from 1 to 3 h resulted in a decreased efficiency of the protective layer for the low porosity stone. We assume that this is due to the formation of vertical channels (cracks) in the protective layer.

Abstract: Samples of cretaceous limestone have been treated with three application methods (poultice, immersion and brushing) using different concentrations of ammonium oxalate solution (AmOx) and varying treatment time in order to test the efficiency of surface and in-depth formation of a protective layer of calcium oxalate (CaOx). Synchrotron-based microanalytical techniques (SR-mu XRD with 12.5 mu mx7.5 mu m (HxV) probe size, SR-mu FTIR with 10 mu mx10 mu m and 8 mu mx20 mu m probe sizes) and laboratory mu FTIR, XRD and SEM have been employed for analysis of the treated samples. Synchrotron-based techniques showed variations in the CaOx distribution along the surface on a micrometer scale. All treatments resulted in the development of a CaOx layer with a maximum thickness of approximately 40 mu m. Application by the brushing method with 10 1-min applications with 5-min breaks during one hour showed a development of the calcium oxalate layer equivalent to the poultice treatment taking 10 h. This treatment could be preferred for large marble or limestone surfaces where poultice usage is economically not feasible.