Abstract: The deposition of ultra-thin tungsten films and their related 2D chalcogen compounds on large area dielectric substrates by gas phase reactions is challenging. The lack of nucleation sites complicates the adsorption of W-related precursors and subsequent sulfurization usually requires high temperatures. We propose here a technique in which a thin solid amorphous silicon film is used as reductant for the gas phase precursor WF6 leading to the conversion to metallic W. The selectivity of the W conversion towards the underlying dielectric surfaces is demonstrated. The role of the Si surface preparation, the conversion temperature, and Si thickness on the formation process is investigated. Further, the in situ conversion of the metallic tungsten into thin stoichiometric WS2 is achieved by a cyclic approach based on WF6 and H2S pulses at the moderate temperature of 450 1C, which is much lower than usual oxide sulfurization processes.

Abstract: Crystalline superlattices consisting of alternating periods of Si layers and O-atomic layers are potential new channel materials for scaled CMOS devices. In this letter, we investigate Chemical Vapor Deposition (CVD) for the controlled deposition of O-atoms with O-3 as precursor on Si(100) substrates and Si epitaxy on the O-layer. The O-3 reaction at 50 degrees C on the H-terminated Si results in the formation of Si-OH and/or Si-O-Si-H surface species with monolayer O-content. Defect-free epitaxial growth of Si on an O-layer containing 6.4E+14 O-atoms/cm(2) is achieved from SiH4 at 500 degrees C. (C) 2013 The Electrochemical Society. All rights reserved.

Abstract: This study is dedicated to a better understanding of the processes occurring under ion bombardment of ultra-thin ZrO2/SiO2/Si gate dielectric stacks. Complex-shaped depth profiles were obtained by using TOF-SIMS with dual beam (500 eV for sputtering and 10 keV for analysis) Ar+ ions. The SIMS intensities of all the elements depend critically on the amount of oxygen at any moment of the sputtering process. Increased intensity is observed at the surface and at the ZrO2/SiO2 interface. A long tail of the Zr signal is present in the Si substrate, even after the second (SiO2/Si) interface, and a double bump structure in the Zr-90 and ZrO dimer is observed, which is more pronounced with increasing thickness of the interfacial SiO2 layer. Computer simulations using the dynamic Monte Carlo code (TRIDYN) are performed in order to distinguish the ion bombardment-induced effects from changes in the ionization degree. The original code is extended with simple models for the ionization mechanism and for the molecular yield during sputtering. Oxygen preferential sputtering at the surface and ballistic transport of Zr towards and through the interface are clearly demonstrated, but there is also evidence that due to recoil implantation oxygen gets piled-up near the ZrO2/SiO2 interface. (C) 2004 Elsevier B.V. All rights reserved.

Abstract: The reaction of a Ti (8 nm) capped Co film (15 nm) with a Si3N4 layer (150 nm) is studied after rapid thermal annealing at 660 degreesC for 120 s in a N-2 ambient. X-ray photoelectron spectroscopy, transmission electron microscopy, electron energy-loss spectroscopy, and Auger electron spectroscopy are used to study the reaction products. Combining the results of the different analyses yields a layer stack consisting of: TiO2/TiO/unreacted Co/(Ti,Co)(2)N/Co2Si, followed by amorphous Si3N4. The reaction mechanisms are discussed. Conclusions concerning the risk for degradation of nitride spacers in advanced devices are drawn. (C) 2000 American Institute of Physics. [S0003-6951(00)05248-7].