Abstract: The atomic configurations at macrotwin interfaces between microtwinned martensite plates in Ni65Al35 material are investigated using transmission electron microscopy. The observed structures are interpreted in view of possible formation mechanisms for these interfaces. A distinction is made between cases in which the microtwins, originating from mutually perpendicular {110} austenite planes, enclose a final angle larger or smaller than 90degrees. Two different configurations, a crossing and a step type are described. Depending on the actual case, tapering, bending and tip splitting of the smaller microtwinvariants are observed. The most reproducible deformations occur in a region of approximately 5-10 nm width around the interface while a variety of structural defects are observed further away from the interface. These structures and deformations are interpreted in terms of the coalescence of two separately nucleated microtwinned martensite plates and the need to accommodate remaining stresses. (C) 2003 Acta Materialia Inc. Published by Elsevier Science Ltd. All rights reserved.

Abstract: We propose a microscopic model for double exchange in GaAs:Mn, GaP:Mn which is based on the interaction between the transition metal impurities and the heavy holes of host semiconductor. The kinematic exchange is derived and the Curie temperature is calculated which agrees with recent experiments. (C) 2003 Elsevier Science B.V. All rights reserved.

Abstract: Calibration curves with two quasi-linear sections ("double sloping'') were observed for the medium volatile elements, Cr and Cu, with the use of a SIMAA 6000 graphite furnace atomic absorption spectrometer under interrupted internal gas flow conditions. If a standard transversally heated graphite atomizer (THGA) tube was shortened by 0.5 mm at both of its ends, (i.e. the gaps were enlarged between graphite furnace housing and tube ends), a stronger declination of the calibration curves resulted. Elements with fairly high diffusion coefficients (>5.8 cm(2) s(-1)) and with short appearance time of their transients (<0.6 s), such as Cr and Cu, have shown the most characteristic sensitivity drop towards higher concentrations. This anomalous feature could be eliminated in three different ways; (1) by applying end-capped THGA tubes, (2) using mini-flow (50 cm(3) min(-1)) conditions during the atomization stage, and (3) by adding Pd-Mg chemical modifier. For the low volatile Mo and V, the calibration curves had no irregular shape. For Ag, Co, Cr, Cu, Mn and Ni, the mini-flow settings improved the linearity of the calibration curves and extended the upper limit of the linear calibration range by a factor of 1.5-2.0. The irregular characteristic of the analytical curves was interpreted as an increased vapour loss at higher analyte concentrations through the opened ends of the standard THGA tubes. This vapour loss was associated with the significantly diverse expulsion velocities of atoms, caused by the difference in temperature and concentration gradients, when evaporating amounts of analytes with more than one order of magnitude difference.

Abstract: Gas discharge plasmas are used for a wide range of applications. To improve our understanding about gas discharges, which is necessary to obtain good results in the various application fields, we perform numerical modelling of gas discharge plasmas. Various kinds of modelling approaches, for various types of gas discharges, are being used in our group. In this paper, some examples of this modelling work are outlined. (C) 2002 Elsevier Science Ltd. All rights reserved.