Abstract: It is known that the neutral image tone of a developed photographic film becomes brownish when the thickness of the original silver halide tabular crystals is reduced. We investigate by electron microscopy to what extent the silver filament structure has changed and how it induces the shift in image tone. Therefore, two samples of AgBr {111} tabular crystals with average thicknesses of 160 nm and 90 nm respectively, are compared. It is shown that the dimensions and defect structure of the filaments are comparable, but that the 90 nm crystals result in a more widely spaced structure, which explains the shift in image tone on a qualitative level. The influence of the addition of an image toner, i.e., phenylmercaptotetrazole, on the filament structure is also investigated. An even more open filament structure of longer, but smaller filaments was observed.

Abstract: Defects in AgG tabular crystals with {111} surfaces are characterised by transmission electron microscopy (TEM) and their influence on the growth process is discussed. In the tabular crystals, twins parallel to the tabular face as well as dislocations along different directions are observed. The twins induce the tabular growth, while the dislocations do not influence the morphology. In 10 to 30% of the crystals that have been characterised, thickness growth is observed and it is shown that in all cases twins on other planes than the tabular ones are present. Two configurations occur more frequently and are analysed in detail. For the first group, twins parallel to the tabular face as well as a microtwin along a non-parallel {111} plane and ending inside the crystal are present. In the crystals of the second group only one extra non-parallel twin occurs giving rise to a bicrystal built up by a tetrahedral shaped part and a flat triangular or trapezoidal part. More complex twin configurations give rise to various, less characteristic morphologies.

Abstract: A two-step process for the formation of sensitivity centers different from earlier described two-step processes was found for sulfur sensitized emulsions. After deposition of sulfur in the first step, it was found that the second step does not consist of rearrangement of sulfur over the surface, but of the supply of silver interstitial ions towards the deposited sulfur clusters. The two processes could be separated by adsorbing and desorbing TAI (4-hydroxy-1, 3,3a, 7-tetraazaindene) at/from the silver halide surface. When 1.5 mmol TAI/mol Ag is added before the sulfur reaction, the silver interstitials are immobilized but sulfur still can be deposited at the same level. By lowering the pH to 2.50 after this sulfur reaction, TAI is desorbed from the surface and the released interstitials then cause a restoration of the properties of a sulfur system without TAI. These effects could be demonstrated via diffuse reflectance spectroscopy (DRS), sensitometry and dielectric loss measurements. We could also confirm the isolation of silver sulfide clusters by TAI from other chemicals in the solution, by adsorption of TAI on the clusters.

Abstract: Not much about the effect of thiocyanate addition on the sulphur ripening is known, although it is used for many applications in photographic practice. Via a combination of tracer analysis and diffuse reflectance spectroscopy the effect of thiocyanate addition on the sulphur and sulphur-plus-gold ripening could be unveiled. When thiocyanate is added prior to the sulphur addition, it appears to rearrange the silver halide surface in such way that the sulphur deposition rate is enhanced, but the supply of interstitials is limited. Addition of thiocyanate after the sulphur reaction results in the formation of thiocyanate complexes with silver, from which a silver ion is more easily deposited in a surface cell of the silver sulphide clusters thus enhancing the sensitization rate. For sulphur-plus-gold sensitized emulsions it was observed that part of the gold ions could be removed out of the Ag2-xAuxS clusters by addition of thiocyanate ions and subsequent washing. Hence, it was concluded that two different types of gold ions are present in the silver sulphide clusters; 1. gold ions which are substitutional for silver (bound between sulphur and bromide ions) 2. gold ions which bridge two or three sulphur atoms. Incorporation of gold ions into silver sulphide clusters suppresses their optical absorption in diffuse reflectance spectroscopy. Since the optical absorption at 505 nm can completely be restored by addition of thiocyanate, it is assumed that the entity absorbing at this wavelength is a monomer of silver sulphide.

Abstract: The occurrence and origin of diffuse intensity contours in electron micrographs of AgBr crystals are investigated. The observations are interpreted in terms of a model, which attributes diffuse scattering to the presence of predominant atom or vacancy clusters of a particular polyhedral type. It is shown that irrespective of the crystal morphology, interstitial Ag ions order in AgBr material in clusters of finite size along 001 type planes. A different geometry of the diffuse intensity locus observed for triangular and hexagonal tabular grains is explained in terms of the different twin plane morphology of these grains.