Abstract: Lattice deformations and concentration gradients surrounding Ni4Ti3 precipitates grown by appropriate annealing in a Ni51Ti49 B2 austenite matrix are determined by a combination of TEM techniques. Quantitative Fourier analysis of HRTEM images reveals a deformed nanoscale region with lattice deformations up to 2% while EELS and EDX indicate a Ni depleted zone up to 150 nm away from the matrix-precipitate interface.

Abstract: The concept of resolution in high-resolution electron microscopy (HREM) is the power to resolve neighboring atoms. Since the resolution is related to the width of the point spread function of the microscope, it could in principle be determined from the image of a point object. However, in electron microscopy there are no ideal point objects. The smallest object is an individual atom. If the width of an atom is much smaller than the resolution of the microscope, this atom can still be considered as a point object. As the resolution of the microscope enters the sub-Å regime, information about the microscope is strongly entangled with the information about the atoms in HREM images. Therefore, we need to find an alternative method to determine the resolution in an object-independent way. In this work we propose to use the image wave of a crystalline object in zone axis orientation. Under this condition, the atoms of a column act as small lenses so that the electron beam channels through the atom column periodically. Because of this focusing, the image wave of the column can be much more peaked than the constituting atoms and can thus be a much more sensitive probe to measure the resolution. Our approach is to use the peakiness of the image wave of the atom column to determine the resolution. We will show that the resolution can be directly linked to the total curvature of the atom column wave. Moreover, we can then directly obtain the resolution of the microscope given that the contribution from the object is known, which is related to the bounding energy of the atom. The method is applied on an experimental CaTiO3 image wave.

Abstract: Control of the texture and the biaxial alignment of sputter deposited films has provoked a great deal of interest due to its technological importance. indeed, many physical properties of thin films are influenced by the biaxial alignment. In this context, extensive research has been established to understand the growth mechanism of biaxially aligned Yttria Stabilized Zirconia (YSZ) as a buffer layer for high temperature superconducting copper oxides. In this work, the growth mechanism in general and the mechanism responsible of the biaxial alignment in detail were investigated for thin films of YSZ and TiN deposited by unbalanced magnetron sputtering using non-aligned polycrystalline stainless steel substrates. The mechanism responsible for the preferential out-of-plane alignment has been investigated by performing depositions on a non-tilted substrate. However, to study the in-plane alignment a tilted substrate was used. The microstructure of the deposited layers was characterised by Scanning Electron Microscopy (SEM) and Transmission Electron Microscopy (TEM). The crystallographic alignment has been investigated by X-ray diffraction (XRD) (angular scans and pole figures) and by Selective Area Diffraction (SAD). It was observed that the deposited layers show a zone T or zone II structure and the layers with a zone T structure consist of faceted grains. There seems to be a correlation between the crystal habit of these faceted grains and the measured biaxial alignment. A model for the preferential out-of-plane orientation, the in-plane alignment and the correlation between the microstructure and the biaxial alignment is proposed.

Abstract: We studied the morphology of ramps in REBa2CU3O7 (REBCO) epitaxial films on SrTiO3 substrates, fabricated by RF magnetron sputter deposition and pulsed laser deposition (PLD), by scanning probe microscopy (SPM) and high resolution electron microscopy (HREM). The ramps were fabricated by Ar ion beam etching using masks of standard photoresist and TIN. AFM-studies on ramps in sputter deposited films show a strong dependence, i.e. formation of facets and ridges, on the angle of incidence of the ion beam with respect to the substrate surface as well as the rotation angle with respect to the crystal axes of the substrate. Ramps in pulsed laser deposited films did not show this dependence, Furthermore, we studied the effect of an anneal step prior to the deposition of barrier layers (i.e. PrBa2CU3O7, SrTiO3, CeO2) on the ramp. First results show a recrystallization of the ramp surface, resulting in terraces and a non-homogeneous growth of the barrier material on top of it. The thickness variations, for thin layers of barrier material, con even become much larger than expected from the amount of deposited material and are dependent on the deposition and anneal conditions. HREM studies show a well defined interface between barrier layer and electrodes. The angle of the ramp depends on the etch rate of the mask and REBCO, and on the angle of incidence of the ion beam. TiN has a much lower etch rate compared to photoresist, resulting in an angle of the ramp comparable to the angle of incidence, resulting in a low etching rate on the ramp. These results will lead to improved electrical characteristics of ramp-type junctions.

Abstract: Infrared absorption spectra of oxygen precipitates in boron doped silicon with a boron concentration between 10(17) and 10(19) cm(-3) are analyzed, applying the spectral function theory of the composite precipitates. The aspect ratio of the platelet precipitates has been determined by transmission electron microscopy measurements. Our analysis shows that in samples with moderate doping levels (<10(18) B cm(-3)) SiOgamma precipitates are formed with stoichiometry as in the lightly doped case. In the heavily (>10(18) cm(-3)) boron doped samples, however, the measured spectra of the precipitates are consistent with a mixture of SiO2 and B2O3. with a volume fraction of B2O3 as high as 0.41 in the most heavily doped case.

Abstract: Rutherford backscattering and channeling spectrometry (RBS), photoluminescence (PL) spectroscopy and transmission electron microscopy (TEM) have been used to investigate macroscopic and microscopic segregation in MOCVD grown InGaN layers. The PL peak energy and In content (measured by RES) were mapped at a large number of distinct points on the samples. An indium concentration of 40%, the highest measured in this work, corresponds to a PL peak of 710 nn strongly suggesting that the light-emitting regions of the sample me very indium-rich compared to the average measured by RES. Cross-sectional TEM observations show distinctive layering of the InGaN films. The TEM study further reveals that these layers consist of amorphous pyramidal contrast features with sizes of order 10 nm The composition of these specific contrast features is shown to be In-rich compared to the nitride matrix.

Abstract: Defects in AgG tabular crystals with {111} surfaces are characterised by transmission electron microscopy (TEM) and their influence on the growth process is discussed. In the tabular crystals, twins parallel to the tabular face as well as dislocations along different directions are observed. The twins induce the tabular growth, while the dislocations do not influence the morphology. In 10 to 30% of the crystals that have been characterised, thickness growth is observed and it is shown that in all cases twins on other planes than the tabular ones are present. Two configurations occur more frequently and are analysed in detail. For the first group, twins parallel to the tabular face as well as a microtwin along a non-parallel {111} plane and ending inside the crystal are present. In the crystals of the second group only one extra non-parallel twin occurs giving rise to a bicrystal built up by a tetrahedral shaped part and a flat triangular or trapezoidal part. More complex twin configurations give rise to various, less characteristic morphologies.