Abstract: 'Natural' platelets are planar defects in {001} planes found in natural type-IaA/B diamonds. 'Man-made' platelets are platelets formed in the laboratory by annealing type-IaA diamonds at temperatures over 2500 degrees C. Careful study shows that the infrared (IR) spectra of the 'man-made' platelets are different from the IR spectra of 'natural' platelets. High-temperature (T greater than or equal to 2000 degrees C) annealing of platelets containing type-IaA/B diamonds modifies the IR absorption spectrum owing to the 'natural' platelets and makes it similar to the IR spectrum of the 'man-made' platelets. It is suggested that such high-temperature annealing changes the structure of the 'natural' platelets. The changes are too subtle to be detected by electron microscopy techniques. Topographic electron-energy-loss spectroscopy shows that platelets contain nitrogen at an average density of 0.7 atoms per a(0)(2); however, high-temperature annealing does not seem to affect the concentration of the nitrogen in the platelets.

Abstract: Aberration-corrected transmission electron microscopy, electron energy-loss spectroscopy, and density functional theory (DFT) calculations are used to solve several key questions about the surface structure, the particle morphology, and the distribution and nature of nitrogen impurities in detonation nanodiamond (DND) cleaned by a recently developed ozone treatment. All microscopy and spectroscopy measurements are performed at a lowered acceleration voltage (80/120kV), allowing prolonged and detailed experiments to be carried out while minimizing the risk of knock-on damage or surface graphitization of the nanodiamond. High-resolution TEM (HRTEM) demonstrates the stability of even the smallest nanodiamonds under electron illumination at low voltage and is used to image the surface structure of pristine DND. High resolution electron energy-loss spectroscopy (EELS) measurements on the fine structure of the carbon K-edge of nanodiamond demonstrate that the typical * pre-peak in fact consists of three sub-peaks that arise from the presence of, amongst others, minimal fullerene-like reconstructions at the nanoparticle surfaces and deviations from perfect sp(3) coordination at defects in the nanodiamonds. Spatially resolved EELS experiments evidence the presence of nitrogen within the core of DND particles. The nitrogen is present throughout the whole diamond core, and can be enriched at defect regions. By comparing the fine structure of the experimental nitrogen K-edge with calculated energy-loss near-edge structure (ELNES) spectra from DFT, the embedded nitrogen is most likely related to small amounts of single substitutional and/or A-center nitrogen, combined with larger nitrogen clusters.

Abstract: In this article, we report on the synthesis of thin, epitaxial films of the transparent conductive oxide Al:ZnO on (0001)-oriented synthetic sapphire substrates by DC sputtering from targets with a nominal 1 at.% Al substitution. The deposition was carried out at an unusually low substrate temperature of only 250 °C in argonoxygen mixtures as well as in pure argon. The impact of the processgas composition on the morphology was analysed by transmission electron microscopy, revealing epitaxial growth in all the cases with a minor impact of the process parameters on the resulting grain sizes. The transport properties resistivity, Hall effect and magnetoresistance were studied in the range from 10 to 300 K in DC and pulsed magnetic fields up to 45 T. While the carrier density and mobility are widely temperature independent, we identified a low fieldlow temperature regime in which the magnetoresistance shows an anomalous, negative behaviour. At higher fields and temperatures, the magnetoresistance exhibits a more conventional, positive curvature with increasing field strength. As a possible explanation, we propose carrier scattering at localised magnetic trace impurities and magnetic correlations.

Abstract: Utilization of Au and nanocrystalline diamond ( NCD) as interlayers noticeably modifies the microstructure and field electron emission ( FEE) properties of hexagonal boron nitride nanowalls ( hBNNWs) grown on Si substrates. The FEE properties of hBNNWs on Au could be turned on at a low turn-on field of 14.3V mu m(-1), attaining FEE current density of 2.58mAcm(-2) and life-time stability of 105 min. Transmission electron microscopy reveals that the Au-interlayer nucleates the hBN directly, preventing the formation of amorphous boron nitride ( aBN) in the interface, resulting in enhanced FEE properties. But Au forms as droplets on the Si substrate forming again aBN at the interface. Conversely, hBNNWs on NCD shows superior in life-time stability of 287 min although it possesses inferior FEE properties in terms of larger turn-on field and lower FEE current density as compared to that of hBNNWs-Au. The uniform and continuous NCD film on Si also circumvents the formation of aBN phases and allows hBN to grow directly on NCD. Incorporation of carbon in hBNNWs from the NCD-interlayer improves the conductivity of hBNNWs, which assists in transporting the electrons efficiently from NCD to hBNNWs that results in better field emission of electrons with high life-time stability. (C) 2016 WILEY-VCH Verlag GmbH & Co. KGaA, Weinheim

Abstract: In this work, a simple method to measure the indirect band gap of diamond with electron energy loss spectroscopy (EELS) in transmission electron microscopy (TEM) is showed. The authors discuss the momentum space resolution achievable with EELS and the possibility of deliberately selecting specific transitions of interest. Based on a simple 2 parabolic band model of the band structure, the authors extend our predictions from the direct band gap case discussed in previous work, to the case of an indirect band gap. Finally, the authors point out the emerging possibility to partly reconstruct the band structure with EELS exploiting our simplified model of inelastic scattering and support it with experiments on diamond.

Abstract: It is important to understand the effect of the interfaces between the oxide electrode layers and the ferroelectric layer on the polarization response for optimizing the device performance of all-oxide ferroelectric devices. Herein, the effects of the oxide La0.07Ba0.93SnO3 (LBSO) as an electrode material in an PbZr0.52Ti0.48O3 (PZT) ferroelectric capacitor are compared with those of the more commonly used SrRuO3 (SRO) electrode. SRO (top)/PZT/SRO (bottom), SRO/PZT/LBSO, and SRO/PZT/2 nm SRO/LBSO devices are fabricated. Only marginal differences in crystalline properties, determined by X-ray diffraction and scanning transmission electron microscopy, are found. High-quality polarization loops are obtained, but with a much larger coercive field for the SRO/PZT/LBSO device. In contrast to the SRO/PZT/SRO device, the polarization decreases strongly with increasing field cycling. This fatigue problem can be remedied by inserting a 2 nm SRO layer between PZT and LBSO. It is argued that strongly increased charge injection into the PZT occurs at the bottom interface, because of the low PZT/LBSO interfacial barrier and the much lower carrier density in LBSO, as compared with that in SRO, causing a low dielectric constant, depleted layer in LBSO. The charge injection creates a trapped space charge in the PZT, causing the difference in fatigue behavior.

Abstract: In situ irradiation experiments in a high resolution electron microscope JEOL-4000EX at room temperature resulted in discovery of the isolated and combined clustering of vacancies and self-interstitial atoms on {111}- and {113}-habit planes both leading to an extended defect formation in Si crystals. The type of the defect is strongly affected by the type of supersaturation of point defects depending on the crystal thickness during electron irradiation. Because of the existence of energy barriers against recombination of interstitials with the extended aggregates of vacancies, a large family of intermediate defect configurations (IDCs) is formed on {113}- and {111}-habit planes at a low temperature under interstitial supersaturation in addition to the well-known {133}-defects of interstitial type. The formation of metastable IDCs inside vacancy aggregates prevents a way of recombination of defects in extended shape.

Abstract: Broad area as well as buried heterostructure lasers based on In0.72Ga0.28As0.62P0.38/InP and emitting at 1.3 mum are grown by liquid phase epitaxy and are studied in detail by means of transmission electron microscopy, X-ray diffraction, secondary ion mass-spectrometry, and electroluminescence. The InGaAsP epilayer is found to be well lattice-matched and of good structural quality. A tentative explanation is presented for the spinodal decomposition observed in the InGaAsP alloy. We also report on the high performance characteristics of the infrared lasers.