Abstract: In this study, we evaluated the ease of removal of soot layers from ancient wall paintings by employing double network gels as a controllable and safe cleaning method. The ceiling of the temple of Seti I (Abydos, Egypt) is covered with thick layers of soot; this is especially the case in the sanctuary of Osiris. These layers may have been accumulated during the occupation of the temple by Christians, fleeing the Romans in the first centuries A.D. Soot particulates are one of the most common deposits to be removed during conservation-restoration activities of ancient Egyptian wall paintings. They usually mask the painted reliefs and reduce the permeability of the painted surface. A Polyvinyl alcohol-borax/agarose (PVA-B/AG) double network gel was selected for this task since its properties were expected to be compatible with the cleaning treatment requirements. The gel is characterized by its flexibility, permitting to take the shape of the reliefs, while also having self-healing properties, featuring shape stability and an appropriate capacity to retain liquid. The gel was loaded with several cleaning reagents that proved to be effective for soot removal. Soot removal tests were conducted with these gel composites. The cleaned surfaces were evaluated with the naked eye, a digital microscope, and color measurements in order to select the best gel composite. The gel composite, loaded with a solution of 5% ammonia, 0.3% ammonium carbonate, and 0.3% EDTA yielded the most satisfactory results and allowed to safely remove a crust of thick soot layers from the surface. Thus, during the final phase of the study, it was used successfully to clean a larger area of the ceiling.

Abstract: As part of its conservation-restoration, the 13th century stained-glass panel ‘the Annunciation’, was examined at the micro- and macro level. This window, since 1898 in the collection of the Museum Mayer Van den Bergh (Antwerp, B), was formerly a part of the southern Rose window of the Notre Dame Cathedral (Paris, F). The insigths emerging from a first phase of the analysis, comprising non-invasive analysis techniques such as optical microscopy combined with macroscopic X-ray fluorescence (MA-XRF) and X-ray diffraction (MA-XRPD) mapping, were used to select sampling positions for the second phase of investigation that involved micro-invasive analysis, namely scanning-electron microscopy coupled to energy-dispersive X-ray analysis (SEM-EDX). The aim of the investigation was fourfold: (1) to assess the applicability of MA-XRF scanning for the characterisation of stained glass windows prior to any conservation or restoration procedure, (2) to assess the applicability of MA-XRPD scanning to identify the degradation products formed on the surface of stained glass windows, (3) to establish a method to limit the set of sampled glass fragments taken from a glass panel for quantititive analysis while maintaining sufficient representativeness and (4) to distinguish the original glass panes and grisaille paint from non-original glass panes that were inserted during various past interventions. Most of the panes in this window proved to consist of medieval potash glass, consistent with the 13th c. origin of the window while a limited number of panes were identified as non-original infills, with divergent glass compositional types and/or colorants. Most panes derive their color from the pot metal glass (i.e. homogenously colored) they were made of. Some of the panes that originally had a red flashed layer on their surface, completely or partially lost this layer due to weathering. Three main compositional glass families with similar color could be defined. With the exception of the yellow and orange panes, the chromophoric elements responsible for the dark(er) and light(er) blue (Co), green (Cu), purple (Mn) and red colors (Cu) were identified. Two different grisaille paints were encountered, part of which were restored during the 19th century. On the basis of this information, all missing pieces were replaced by glass panes with appropriate colors and the panel could be successfully conserved to its former glory. On the surface of several panes, typical glass degradation products such as calcite, syngenite and gypsum were identified, together with lead based degradation products such as anglesite and palmierite. In addition, the presence of hematite and melanotekite in the grisailles was observed; also the presence of Zn, uncorrelated to Cu, in the grissailes on the right side of the window became apparent.

Abstract: Twenty-seven glass fragments containing dark coloured grisaille paint layers of different qualities were collected from ten windows of the cathedral St. Michael & St. Gudule in Brussels (Belgium). The windows were made by J.-B. Capronnier (18141891) and cover the period between 1843 and 1878. The samples were cross-sectioned and examined in an electron microscope. Grisaille paint layers are not homogeneous and therefore, it is not meaningful to characterize them in terms of their average composition. Instead, parameters such as granularity, the number of residual gas bubbles per running millimetre of paint, the type of pigments, and the thickness of the paint layer were used to characterize them. The microscopic morphology allows a classification of the grisaille paint layers in four groups, every group associated with a quality level. Moreover, the main causes of the accelerated degradation of some of these paint layers could be explained. The classification made it possible to distinguish two periods in the work of Capronnier: (1) the early period (18431848) is characterized by the presence of either single granular paint layers or of double-layered systems consisting of a granular paint layer on top of a well-melted paint layer. The granular grisaille paint layers tend to pulverize; (2) the later period (18481878) is characterized by the presence of only well-vitrified paint layers. No sign of deterioration was found on the well-vitrified paint layers.

Abstract: The chemical composition of 11 glass panes originating from two 13th century non-figurative windows were analyzed by means of Scanning Electron MicroscopyEnergy Dispersive X-ray system (SEM-EDX). The windows were discovered in the back-wall of the triforium during the restoration of the choir of the cathedral St. Michael and St. Gudule in Brussels (Belgium). In order to determine if these windows were fabricated with glass of different origin or not, the compositional difference between the panes were compared with the variation in composition as a result of the following causes: (1) compositional fluctuation between panes cut from the same sheet of glass, (2) compositional fluctuation caused when panes are cut from different sheets that were made with the same batch, (3) compositional fluctuation caused when the glass is made from different batches at the same production center, and (4) compositional fluctuation as a result of glass produced at different fabrication centers.

Abstract: During the study of a large number of archaeological glass fragments, manganese-rich inclusions in leached layers were observed in a limited number of cases. This phenomenon occurs only in black-coloured leached layers. Since the formation mechanism of such manganese-rich inclusions is still unclear, a combination of several analytical techniques was used in order to investigate this phenomenon and, more specifically, to obtain more information on (a) the composition and morphology of the inclusions, (b) the chemical state of Mn and (c) the 3D morphology of the inclusions. A mechanism that might explain the formation of these inclusions is proposed.