Abstract: Over the past years a number of studies have described the instability of the pigment cadmium yellow (CdS). In a previous paper we have shown how cadmium sulfide on paintings by James Ensor oxidizes to CdSO4 center dot H2O. The degradation process gives rise to the fading of the bright yellow color and the formation of disfiguring white crystals that are present on the paint surface in approximately 50 mu m sized globular agglomerations. Here, we study cadmium yellow in the painting “Flowers in a blue vase” by Vincent van Gogh. This painting differs from the Ensor case in the fact that (a) a varnish was superimposed onto the degraded paint surface and (b) the CdS paint area is entirely covered with an opaque crust. The latter obscures the yellow color completely and thus presents a seemingly more advanced state of degradation. Analysis of a cross-sectioned and a crushed sample by combining scanning microscopic X-ray diffraction (mu-XRD), microscopic X-ray absorption near-edge spectroscopy (mu-XANES), microscopic X-ray fluorescence (mu-XRF) based chemical state mapping and scanning microscopic Fourier transform infrared (mu-FT-IR) spectrometry allowed unravelling the complex alteration pathway. Although no crystalline CdSO4 compounds were identified on the Van Gogh paint samples, we conclude that the observed degradation was initially caused by oxidation of the original CdS pigment, similar as for the previous Ensor case. However, due to the presence of an overlying varnish containing lead-based driers and oxalate ions, secondary reactions took place. In particular, it appears that upon the photoinduced oxidation of its sulfidic counterion, the Cd2+ ions reprecipitated at the paint/varnish interface after having formed a complex with oxalate ions that themselves are considered to be degradation products of the resin and/or oil in the varnish. The SO42- anions, for their part, found a suitable reaction partner in Pb2+ ions stemming from a dissolved lead-based siccative that was added to the varnish to promote its drying. The resulting opaque anglesite compound in the varnish, in combination with the underlying CdC2O4 layer at the paint/varnish interface, account for the orange-gray crust that is disfiguring the painting on a macroscopic level. In this way, the results presented in this paper demonstrate how, through a judicious combined use of several microanalytical methods with speciation capabilities, many new insights can be obtained from two minute, but highly complex and heterogeneous paint samples.

Abstract: Many western manuscripts were written using iron gall inks. These inks can damage the paper via two major mechanisms: (a) acid hydrolysis, enhanced by humidity, and (b) oxidative depolymerization provoked by the presence of oxygen and free iron(II) ions. The degradation of unsized Whatman paper impregnated with different combinations of iron sulfate, gallic acid, and gum arabic was studied at room temperature in order to assess the relative importance of each mechanism. The samples were stored in various environments including a dry and/or an oxygen-free atmosphere. The cellulose depolymerization was monitored by viscometry and related to changes in the oxidation state of iron, determined by X-ray absorption near-edge spectrometry. The results indicate that residual amounts of oxygen (less than 0.1%) promote cellulose depolymerization, whereas the level of relative humidity has no impact. The cellulose depolymerization also appears closely correlated to oxidative mechanisms. Regarding the oxidation of iron, it only occurs in the simultaneous presence of oxygen and moisture, suggesting the occurrence of rustlike oxidative mechanisms. Finally, the presence of gallic acid has a strong influence, which is only partially explained by its capacity to reduce iron(III) to iron(II).