“Rapid microwave-assisted synthesis of benzene bridged periodic mesoporous organosilicas”. Smeulders G, Meynen V, van Baelen G, Mertens M, Lebedev OI, Van Tendeloo G, Maes BUW, Cool P, Journal of materials chemistry 19, 3042 (2009). http://doi.org/10.1039/b820792e
Abstract: Following extended use in organic chemistry, microwave-assisted synthesis is gaining more importance in the field of inorganic chemistry, especially for the synthesis of nanoporous materials. It offers some major advantages such as a significant shortening of the synthesis time and an improved promotion of nucleation. In the research here reported, microwave technology is applied for the synthesis of benzene bridged PMOs (periodic mesoporous organosilicas). PMOs are one of the latest innovations in the field of hybrid ordered mesoporous materials and have attracted much attention because of their feasibility in electronics, catalysis, separation and sorption applications. The different synthesis steps (stirring, aging and extraction) of the classical PMO synthesis are replaced by microwave-assisted synthesis steps. The characteristics of the as-synthesized materials are evaluated by X-ray diffraction, N2-sorption, thermogravimetric analysis, scanning- and transmission electron microscopy. The microwave-assisted synthesis drastically reduces the synthesis time by more than 40 hours without any loss in structural properties, such as mesoscale and molecular ordering. The porosity of the PMO materials has even been improved by more than 25%. Moreover, the number of handling/transfer steps and amounts of chemicals and waste are drastically reduced. The study also shows that there is a clear time (1 to 3 hours) and temperature frame (373 K to 403 K) wherein synthesis of benzene bridged PMO is optimal. In conclusion, the microwave-assisted synthesis pathway allows an improved material to be obtained in a more economical way i.e. a much shorter time with fewer chemicals and less waste.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT); Laboratory of adsorption and catalysis (LADCA); Organic synthesis (ORSY)
Times cited: 20
DOI: 10.1039/b820792e
|
“Rational design of Ag/TiO2 nanosystems by a combined RF-sputtering/sol-gel approach”. Armelao L, Barreca D, Bottaro G, Gasparotto A, Maccato C, Tondello E, Lebedev OI, Turner S, Van Tendeloo G, Štangar UL, ChemPhysChem : a European journal of chemical physics and physical chemistry 10, 3249 (2009). http://doi.org/10.1002/cphc.200900571
Abstract: The present work is devoted to the preparation of Ag/TiO2 nanosystems by an original synthetic strategy, based on the radio-frequency (RF) sputtering of silver particles on titania-based xerogels prepared by the sol-gel (SG) route. This approach takes advantage of the synergy between the microporous xerogel structure and the infiltration power characterizing RF-sputtering, whose combination enables the obtainment of a tailored dispersion of Ag-containing particles into the titania matrix. In addition, the systems chemico-physical features can be tuned further through proper ex situ thermal treatments in air at 400 and 600 °C. The synthesized composites are extensively characterized by the joint use of complementary techniques, that is, X-ray photoelectron and X-ray excited Auger electron spectroscopies (XPS, XE-AES), secondary ion mass spectrometry (SIMS), glancing incidence X-ray diffraction (GIXRD), field emission scanning electron microscopy (FE-SEM), transmission electron microscopy (TEM), electron diffraction (ED), high-angle annular dark field scanning TEM (HAADF-STEM), energy-filtered TEM (EF-TEM) and optical absorption spectroscopy. Finally, the photocatalytic performances of selected samples in the decomposition of the azo-dye Plasmocorinth B are preliminarily investigated. The obtained results highlight the possibility of tailoring the system characteristics over a broad range, directly influencing their eventual functional properties.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 3.075
Times cited: 56
DOI: 10.1002/cphc.200900571
|
“Rational synthesis of a nanocrystalline calcium phosphate cement exhibiting rapid conversion to hydroxyapatite”. Neira IS, Kolen'ko YV, Lebedev OI, Van Tendeloo G, Gupta HS, Matsushita N, Yoshimura M, Guitian F, Materials science and engineering: part C: biomimetic materials 29, 2124 (2009). http://doi.org/10.1016/j.msec.2009.04.011
Abstract: The rational synthesis, comprehensive characterization, and mechanical and micromechanical properties of a calcium phosphate cement are presented. Hydroxyapatite cement biomaterial was synthesized from reactive sub-micrometer-sized dicalcium phosphate dihydrate and tetracalcium phosphate via a dissolution-precipitation reaction using water as the liquid phase. As a result nanostructured, Ca-deficient and carbonated B-type hydroxyapatite is formed. The cement shows good processibility, sets in 22 ± 2 min and entirely transforms to the end product after 6 h of setting reaction, one of the highest conversion rates among previously reported for calcium phosphate cements based on dicalcium and tetracalcium phosphates. The combination of all elucidated physical-chemical traits leads to an essential bioactivity and biocompatibility of the cement, as revealed by in vitro acellular simulated body fluid and cell culture studies. The compressive strength of the produced cement biomaterial was established to be 25 ± 3 MPa. Furthermore, nanoindentation tests were performed directly on the cement to probe its local elasticity and plasticity at sub-micrometer/micrometer level. The measured elastic modulus and hardness were established to be Es = 23 ± 3.5 and H = 0.7 ± 0.2 GPa, respectively. These values are in close agreement with those reported in literature for trabecular and cortical bones, reflecting good elastic and plastic coherence between synthesized cement biomaterial and human bones.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 4.164
Times cited: 18
DOI: 10.1016/j.msec.2009.04.011
|
“Synthesis of highly stable pure-silica thin-walled hexagonally ordered mesoporous material”. Verlooy P, Aerts A, Lebedev OI, Van Tendeloo G, Kirschhock C, Martens JA, Chemical communications , 4287 (2009). http://doi.org/10.1039/b901796h
Abstract: Hexagonally ordered mesoporous silica with a very narrow mesopore size distribution and exceptionally high stability paired with unusually thin pore walls was prepared using piperidine and cetyltrimethylammonium bromide.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 6.319
Times cited: 17
DOI: 10.1039/b901796h
|
“A-site ordering and stripe phases in manganite films”. Sudheendra L, Moshnyaga V, Lebedev OI, Gehrke K, Belenciuc A, Shapoval O, Van Tendeloo G, Samwer K, Physica: B : condensed matter
T2 –, International Conference on Strongly Correlated Electron Systems (SCES, 2007), MAY 13-18, 2007, Houston, TX 403, 1645 (2008). http://doi.org/10.1016/j.physb.2007.10.332
Abstract: Insulating and metallic stripes above and below the Curie temperature, T-C, respectively, were observed by a high-resolution scanning tunneling microscopy (STM) and/or spectroscopy (STS) in A-site ordered and macroscopically strain free epitaxial La0.75Ca0.25MnO3 film grown on MgO substrate. The “insulating” stripes were found to be incommensurable to the lattice and aligned along (110) direction. Metallic stripes were commensurable with periodicity 2a(p)similar to 0.8 nm and aligned parallel to the crystallographic a/b-axis. Formation of these stripes involves competing charge, orbital, and lattice orders and is an outcome of an overlapping of electron wave functions mediated by the local lattice-strain distribution, existed even in A-site ordered film due to the difference in cation radii of La and Ca. (C) 2007 Elsevier B.V. All rights reserved.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 1.386
DOI: 10.1016/j.physb.2007.10.332
|
“Classification and control of the origin of photoluminescence from Si nanocrystals”. Godefroo S, Hayne M, Jivanescu M, Stesmans A, Zacharias M, Lebedev OI, Van Tendeloo G, Moshchalkov VV, Nature nanotechnology 3, 174 (2008). http://doi.org/10.1038/nnano.2008.7
Abstract: Silicon dominates the electronics industry, but its poor optical properties mean that III-V compound semiconductors are preferred for photonics applications. Photoluminescence at visible wavelengths was observed from porous Si at room temperature in 1990, but the origin of these photons (do they arise from highly localized defect states or quantum confinement effects?) has been the subject of intense debate ever since. Attention has subsequently shifted from porous Si to Si nanocrystals, but the same fundamental question about the origin of the photoluminescence has remained. Here we show, based on measurements in high magnetic fields, that defects are the dominant source of light from Si nanocrystals. Moreover, we show that it is possible to control the origin of the photoluminescence in a single sample: passivation with hydrogen removes the defects, resulting in photoluminescence from quantum-confined states, but subsequent ultraviolet illumination reintroduces the defects, making them the origin of the light again.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 38.986
Times cited: 426
DOI: 10.1038/nnano.2008.7
|
“Crosshatching on La0.5Ca0.5MnO3 ultrathin films epitaxially grown on SrTiO3(100)”. Wang Z-H, Lebedev OI, Van Tendeloo G, Cristiani G, Habermeier H-U, Physical review : B : condensed matter and materials physics 77, 1 (2008). http://doi.org/10.1103/PhysRevB.77.115330
Abstract: The morphological evolution in La(0.5)Ca(0.5)MnO(3)/SrTiO(3)(100) ultrathin films has been revealed by atomic force microscopy. It was found that ordered linear defects, which are in 1-2 unit cells high and oriented along the cubic [110] and [100] directions, first appear on the smooth surface of films with a thickness of 10 nm. As the epitaxial growth proceeds, these lines on surface develop into a crosshatch pattern for films with a thickness of 25 nm. Using the results of transmission electron microscopy and electrical measurements, we discuss the interplay between the surface pattern formation, the internal dislocation structure, and the variations in the electrical properties.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 3.836
Times cited: 8
DOI: 10.1103/PhysRevB.77.115330
|
“Crystalline and amorphous frameworks with giant pores: what information ca we expect from advanced TEM?”.Lebedev OI, Van Tendeloo G, Electron microscopy and multiscale modeling: proceedings of the AIP conference proceedings 999, 245 (2008)
Keywords: P1 Proceeding; Electron microscopy for materials research (EMAT)
|
“Direct imaging of loaded metal-organic framework materials (metal@MOF-5)”. Turner S, Lebedev OI, Schroeder F, Fischer RA, Van Tendeloo G, Chemistry of materials 20, 5622 (2008). http://doi.org/10.1021/cm801165s
Abstract: We illustrate the potential of advanced transmission electron microscopy for the characterization of a new class of soft porous materials: metal@Zn4O(bdc)3 (metal@MOF-5; bdc = 1,4-benzenedicarboxylate). By combining several electron microscopy techniques (transmission electron microscopy (TEM), high-resolution transmission electron microscopy (HRTEM), electron diffraction (ED), high-angle annular dark-field scanning transmission electron microscopy (HAADF-STEM), and electron tomography) and by carefully reducing the electron dose to avoid beam damage, it is possible to simultaneously characterize the MOF-5 framework material and the loaded metal nanoparticles. We also demonstrate that electron tomography can be used to accurately determine the position and distribution of the particles within the MOF-5 framework. To demonstrate the implementation of these microscopy techniques and what kind of results can be expected, measurements on gas-phase-loaded metal−organic framework materials Ru@MOF-5 and Pd@MOF-5 are presented.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 9.466
Times cited: 112
DOI: 10.1021/cm801165s
|
“Dynamics of nanoclustering in Te+ implanted Si after application of high frequency electromagnetic field and thermal annealing”. Kalitzova M, Lebedev OI, Zollo G, Gesheva K, Vlakhov E, Marinov Y, Ivanova T;, Applied physics A : materials science &, processing 91, 515 (2008). http://doi.org/10.1007/s00339-008-4441-2
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 1.455
DOI: 10.1007/s00339-008-4441-2
|
“Gas-phase loading of [Zn4O(btb)2] (MOF-177) with organometallic CVD-precursors: inclusion compounds of the type [LnM]a@MOF-177 and the formation of Cu and Pd nanoparticles inside MOF-177”. Müller M, Lebedev OI, Fischer RA, Journal of materials chemistry 18, 5274 (2008). http://doi.org/10.1039/b810989c
Abstract: The highly porous and desolvated (activated) coordination polymer [Zn4O(btb)2] (btb = benzene-1,3,5-tribenzoate; MOF-177) was loaded with the organometallic compounds [Cp2Fe], [Cp*2Zn], [Cu(OCHMeCH2NMe2)2], [CpCuL] (L = PMe3, CNtBu) and [CpPd(3-C3H5)] via solvent-free adsorption from the gas-phase. The inclusion compounds of the type [LnM]a@MOF-177, where [LnM] indicates the respective compound and the parameter a denotes the number of molecules per formula unit of the MOF-177, were characterised by elemental analysis, FT-IR, solid-state NMR spectroscopy and by powder X-ray diffraction (PXRD). Remarkably high effective loadings of up to 11 molecules [Cp2Fe] and 10 molecules [CpPd(3-C3H5)] per cavity were determined. The analytical data prove that the host lattice and the guest molecules interact only by weak van-der-Waals forces without any significant change of the framework or the chemical nature of the included molecules. Cu nanoparticles showing the typical surface plasmon resonance at 580 nm and Pd nanoparticles of about 2.6 nm in size were formed inside the cavities of MOF-177 by the thermally activated hydrogenolysis of the inclusion compounds [CpCuCNtBu]2@MOF-177 and by photolysis of [CpPd(3-C3H5)]10@MOF-177 in an inert atmosphere (Ar). PXRD, FT-IR and NMR studies revealed that the MOF-177 matrix remained unchanged during the decomposition process of the precursors. N2 adsorption studies of the obtained materials Cu@MOF-177 (e.g. 10.6 wt.% Cu, 2309 m2 g-1) and Pd@MOF-177 (e.g. 32.5 wt.%, 1063 m2 g-1) reveal high remaining specific surface areas (Langmuir model).
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Times cited: 65
DOI: 10.1039/b810989c
|
“Highly disordered crystal structure and thermoelectric properties of Sn3P4”. Zaikina JV, Kovnir KA, Sobolev AN, Presniakov IA, Kytin VG, Kulbachinskii VA, Olenev AV, Lebedev OI, Van Tendeloo G, Dikarev EV, Shevelkov AV, Chemistry of materials 20, 2476 (2008). http://doi.org/10.1021/cm702655g
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 9.466
Times cited: 33
DOI: 10.1021/cm702655g
|
“The merging of silica-surfactant microspheres under hydrothermal conditions”. Liu S, Lebedev OI, Mertens M, Meynen V, Cool P, Van Tendeloo G, Vansant EF, Microporous and mesoporous materials: zeolites, clays, carbons and related materials 116, 141 (2008). http://doi.org/10.1016/j.micromeso.2008.03.034
Abstract: Post-synthesis hydrothermal treatments have been used to improve the quality of MCM-41 materials. In our latest work, merging of surfactant-containing silica microspheres during the hydrothermal treatments was observed. Mechanistic insights and the different stages that are involved in the merging process can be summarized as follows. First, the surfaces of the starting microspheres open up due to the dissolution of silica. Then the dissolved silica species provide mass source for the formation of particle necks connecting two neighboring microspheres. Gradually, surfaces of the starting microspheres are flattened to meet the needs of further growth of the necks. Finally, some chain-like highly-ordered mesoporous structures up to several micrometers are formed. The observed merging of the surfactant-containing microspheres is a re-assembling process, which is under the control of electrostatic force between the dissolved silica species and the surfactant cations. The occluded surfactant cations in the precursor spheres play important roles in the merging process.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT); Laboratory of adsorption and catalysis (LADCA)
Impact Factor: 3.615
Times cited: 5
DOI: 10.1016/j.micromeso.2008.03.034
|
“Mesoporous material formed by acidic hydrothermal assembly of silicalite-1 precursor nanoparticles in the absence of meso-templates”. Stevens WJJ, Meynen V, Bruijn E, Lebedev OI, Van Tendeloo G, Cool P, Vansant EF, Microporous and mesoporous materials: zeolites, clays, carbons and related materials 110, 77 (2008). http://doi.org/10.1016/j.micromeso.2007.09.007
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT); Laboratory of adsorption and catalysis (LADCA)
Impact Factor: 3.615
Times cited: 21
DOI: 10.1016/j.micromeso.2007.09.007
|
“Multi-step loading of titania on mesoporous silica: influence of the morphology and the porosity on the catalytic degradation of aqueous pollutants and VOC's”. de Witte K, Meynen V, Mertens M, Lebedev OI, Van Tendeloo G, Sepúlveda-Escribano A, Rodríguez-Reinoso F, Vansant EF, Cool P, Applied catalysis : B : environmental 84, 125 (2008). http://doi.org/10.1016/j.apcatb.2008.03.015
Abstract: Titania nanoparticles have been deposited on inert porous silica supports with high specific surface area. These materials have potential applications in paint and textile industry as the titania particles selectively deposited on the inner surface of the silica supports act as a photocatalyst. The inert external surface is necessary to avoid photodegradation of the textile material or the paint components. The photocatalytic activity of the catalysts has been evaluated with two catalytic setups. One setup in aqueous phase, for the degradation of dyes such as rhodamine-6G, is commonly used. The second setup is a continuous flow gaseous phase setup which was used for the mineralization of ethanol as a representative volatile organic compound (VOC). The influence of the porosity and the morphology of the silica supports on the photocatalytic activity are discussed.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT); Laboratory of adsorption and catalysis (LADCA)
Impact Factor: 9.446
Times cited: 24
DOI: 10.1016/j.apcatb.2008.03.015
|
“Ruthenium nanoparticles inside porous (Zn40(bdC)(3)) by hydrogenolysis of adsorbed (Ru(cod)(cot)): a solid-state reference system for surfactant-stabilized ruthenium colloids”. Schröder F, Esken D, Cokoja M, van den Berg MWE, Lebedev OI, Van Tendeloo G, Walaszek B, Buntkowsky G, Limbach HH, Chaudret B, Fischer RA;, Journal of the American Chemical Society 130, 6119 (2008). http://doi.org/10.1021/ja078231u
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 13.858
Times cited: 272
DOI: 10.1021/ja078231u
|
“Deposition of vanadium silicalite-1 nanoparticles on SBA-15 materials: structural and transport characteristics of SBA-VS-15”. Meynen V, Cool P, Vansant EF, Kortunov P, Grinberg F, Kärger J, Mertens M, Lebedev OI, Van Tendeloo G, Microporous and mesoporous materials 99, 14 (2007). http://doi.org/10.1016/j.micromeso.2006.08.029
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT); Laboratory of adsorption and catalysis (LADCA)
Impact Factor: 3.615
Times cited: 23
DOI: 10.1016/j.micromeso.2006.08.029
|
“Hybrid diamond-graphite nanowires produced by microwave plasma chemical vapor deposition”. Vlasov IL, Lebedev OI, Ralchenko VG, Goovaerts E, Bertoni G, Van Tendeloo G, Konov VI, Advanced materials 19, 4058 (2007). http://doi.org/10.1002/adma.200700442
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT); Nanostructured and organic optical and electronic materials (NANOrOPT)
Impact Factor: 19.791
Times cited: 75
DOI: 10.1002/adma.200700442
|
“Structural and luminescence investigation on gadolinium gallium garnet nanocrystalline powders prepared by solution combustion synthesis”. Krsmanovic R, Morozov VA, Lebedev OI, Polizzi S, Speghini A, Bettinelli M, Van Tendeloo G, Nanotechnology 18, 325604 (2007). http://doi.org/10.1088/0957-4484/18/32/325604
Abstract: Nanocrystalline powders of undoped and lanthanide (Pr3+, Tm3+)- doped gadolinium gallium garnet, Gd3Ga5O12 (GGG), were prepared by propellant synthesis and studied by x-ray powder diffraction (XRD), electron diffraction (ED), high-resolution electron microscopy (HREM) and luminescence spectroscopy. The x-ray diffraction patterns of the GGG samples were analysed using the Rietveld method. The Rietveld refinement reveals the existence of two garnet-type phases: both are cubic (space group Ia $(3) over bar $d) with a slightly different lattice parameter and probably a slightly different composition. Electron diffraction and electron microscopy measurements confirm the x-ray diffraction results. EDX measurements for lanthanide-doped samples show that stable solid solutions with composition Gd(3-x)Ln(x)Ga(5)O(12), x approximate to 0.3 ( Ln = Pr; Tm) have been obtained. The luminescence properties of the Tm3+ -doped nanocrystalline GGG samples were measured and analysed.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 3.44
Times cited: 33
DOI: 10.1088/0957-4484/18/32/325604
|
“Sn20.5-3.5As22I8: a largely disordered cationic clathrate with a new type of superstructure and abnormally low thermal conductivity”. Zaikina JV, Kovnir KA, Sobolev AV, Presniakov IA, Prots Y, Baitinger M, Schnelle W, Olenev AV, Lebedev OI, Van Tendeloo G, Grin Y, Shevelkov AV, Chemistry: a European journal 13, 5090 (2007). http://doi.org/10.1002/chem.200601772
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 5.317
Times cited: 44
DOI: 10.1002/chem.200601772
|
“Thin films and superlattices of multiferroic hexagonal rare earth manganites”. Dubourdieu C, Huot G, Gelard I, Roussel H, Lebedev OI, Van Tendeloo G, Philosophical magazine letters 87, 203 (2007). http://doi.org/10.1080/09500830601137173
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 0.941
Times cited: 17
DOI: 10.1080/09500830601137173
|
“Biaxially aligned titanium nitride thin films deposited by reactive unbalanced magnetron sputtering”. Mahieu S, Ghekiere P, de Winter G, de Gryse R, Depla D, Van Tendeloo G, Lebedev OI, Surface and coatings technology 200, 2764 (2006). http://doi.org/10.1016/j.surfcoat.2004.09.012
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.589
Times cited: 36
DOI: 10.1016/j.surfcoat.2004.09.012
|
“Crystal structures of superconducting sodium intercalates of hafnium nitride chloride”. Oró-Solé, J, Frontera C, Beltrán-Porter D, Lebedev OI, Van Tendeloo G, Fuertes A, Materials research bulletin 41, 934 (2006). http://doi.org/10.1016/j.materresbull.2006.03.018
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.446
Times cited: 8
DOI: 10.1016/j.materresbull.2006.03.018
|
“Crystallization of PZT in porous alumina membrane channels”. Zhigalina OM, Mishina ED, Sherstyuk NE, Vorotilov KA, Vasiljev VA, Sigov AS, Lebedev OI, Grigoriev YV, de Santo MP, Barberi R, Rasing T, Ferroelectrics 336, 247 (2006). http://doi.org/10.1080/00150190600697756
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 0.551
Times cited: 10
DOI: 10.1080/00150190600697756
|
“Defect structure of ferromagnetic superconducting RuSr2GdCu2O8”. Lebedev OI, Van Tendeloo G, Attfield JP, McLaughlin AC, Physical review : B : condensed matter and materials physics 73 (2006). http://doi.org/10.1103/PhysRevB.73.224524
Abstract: The structure and defect structure of superconducting ferromagnetic bulk RuSr2GdCu2O8 has been investigated using high-resolution transmission electron microscopy and high-resolution scanning transmission microscopy. Two distinct, but closely related structures, due to ordering of rotated RuO6 octahedra and due to Cu substitution in the Ru-O layer, have been revealed. The structure of Ru1-xSr2GdCu2+xO8-delta can be described as a periodic alteration along the c axis of CuO4 planes and RuO6 octahedra. The unit-cell parameters of this phase are root 2a(p) x root 2a(p) x 2c. The possible influence of this phase and defect structure on the sensitivity of the superconductivity and magnetic properties is discussed. Local defects such as 90 S domain boundaries, (130) antiphase boundaries, and the associated dislocations are analyzed.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 3.836
Times cited: 11
DOI: 10.1103/PhysRevB.73.224524
|
“The determination of the interface structure between ionocovalent compounds: the general case study of the Al2O3/ZrO2 large mis-fit system”. Trolliard G, Benmechta R, Mercurio D, Lebedev OI, Journal of materials chemistry 16, 3640 (2006). http://doi.org/10.1039/b604232e
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Times cited: 6
DOI: 10.1039/b604232e
|
“Hydrothermal synthesis and characterization of nanorods of various titanates and titanium dioxide”. Kolen'ko YV, Kovnir KA, Gavrilov AI, Garshev AV, Frantti J, Lebedev OI, Churagulov BR, Van Tendeloo G, Yoshimura M, The journal of physical chemistry : B : condensed matter, materials, surfaces, interfaces and biophysical 110, 4030 (2006). http://doi.org/10.1021/jp055687u
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 3.177
Times cited: 234
DOI: 10.1021/jp055687u
|
“Ion beam synthesis of Te and Bi nanoclusters in silicon: the effect of post-implantation high frequency electromagnetic field”. Kalitzova M, Peeva A, Ignatova V, Lebedev OI, Zollo G, Vitali G, Nuclear instruments and methods in physics research: B: beam interactions with materials and atoms 242, 209 (2006). http://doi.org/10.1016/j.nimb.2005.08.017
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 1.109
Times cited: 1
DOI: 10.1016/j.nimb.2005.08.017
|
“Mixed (Sr1-xCax)33Bi24Al48O141 fullerenoids: the defect structure analysed by (S)TEM techniques”. Lebedev OI, Bals S, Van Tendeloo G, Snoeck GE, Retoux R, Boudin S, Hervieu M, International journal of materials research 97, 978 (2006). http://doi.org/10.3139/146.101328
Abstract: (Sr1-xCax)(33)Bi-24,partial derivative Al48O141+3 partial derivative/2 fullerenoid solid solutions have been synthesized and the effect of partial substitution of Sr by Ca has been characterized by (scanning) transmission electron microscopy, applying different imaging methods. Most of the defects commonly observed in face centered cubic compounds, have also been observed in (Sr1-xCax)(33)Bi24-partial derivative Al48O141+3 partial derivative/2. Based on purely geometrical and topological models, structural presentations for the coherent twin boundaries and stacking faults have been constructed on the basis of complex spherical “Al84O210” units. The results are compared to defects observed in the crystallite fullerite C-60.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 0.681
Times cited: 1
DOI: 10.3139/146.101328
|
“A-site ordering versus electronic inhomogeneity in colossally magnetoresistive manganite films”. Moshnyaga V, Sudheendra L, Lebedev OI, Koster SA, Gehrke K, Shapoval O, Belenchuk A, Damaschke B, Van Tendeloo G, Samwer K, Physical review letters 97, 107205 (2006). http://doi.org/10.1103/PhysRevLett.97.107205
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 8.462
Times cited: 43
DOI: 10.1103/PhysRevLett.97.107205
|