Abstract: In this work self-supporting tin dioxide disks are characterized using FT-IR spectroscopy in the presence of a reducing gas in air, and in different O2/N2 mixtures at temperatures varying from room temperature up to 450°C. Every factor inducing a change in the oxygen content of the gas atmosphere above the tin dioxide, as for instance a temperature change, a surface reaction or adsorption of another species, induces a broad, intense IR absorption band with discrete weak bands superimposed on it. This broad absorption is assigned to the electronic transition from a native donor level, the oxygen vacancy in the bulk of the domain, to the conduction band of the tin dioxide material. For the interpretation of the narrow, superimposed absorptions, two hypotheses remain. The results demonstrate that FT-IR spectroscopy is an extremely suitable technique for the characterization of semiconducting metal oxide sensors, since it allows to follow in situ the processes in the bulk, at the surface and in the surrounding gas atmosphere of the sensor material at working temperature as well as in the presence of reducing gases in air.

Abstract: The crystal structure of the newly discovered double-Hg-layer copper oxide superconductor (Hg, Pr)(2)Ba-2(Y, Ca)Cu2O8-delta was studied as a function of chemical doping using neutron and electron diffraction and high-resolution transmission electron microscopy (HREM). Rietveld refinements of the structural parameters from neutron powder diffraction data indicate that the oxygen site O3 on the mercury plane is highly defective, being both partially occupied and displaced from the high-symmetry position. The variable concentration of oxygen vacancies partially compensates for the cation doping and, together with the O3 displacement field, makes some of the Hg atoms acquire an unusual pyramidal coordination. HREM images confirm that the structure is of the '2212' type, with very few defects. In some grains, faint superstructure reflections were evidenced by electron diffraction, suggesting that both the oxygen vacancies and the O3 displacement field may order at least on a local scale.

Abstract: For column structures, such as fee-based alloys viewed along the cube direction, the concept of electron channelling through the atom columns is more and more used to interpret the corresponding HREM images. In the case of(partially) disordered columns, the projected potential approach which is used in the channelling description must be questioned since the arrangement of the atoms along the beam direction might affect the exit wave of the electrons. In this paper, we critically inspect this top-bottom effect using multi-slice calculations. A modified channelling theory is introduced which turns out to be very appropriate for the interpretation of these results. For substitutionally disordered column structures, it is also discussed how to link the chemical composition of the material to statistical data of the HREM image. This results in a convenient tool to discern images taken at different thicknesses and focus values.

Abstract: The post-growth modification of diamond-like amorphous hydrogenated carbon a-C:H films by laser treatment has been studied by transmission electron microscopy and Raman spectroscopy. a-C:H films grown on Si substrates by benzene decomposition in a rf glow discharge were irradiated with 15 ns pulses of a KrF-excimer laser with fluences in the ran e of E = 50-700 mJ/cm(2). At fluences below 100 mJ/cm(2) an increase in the number of graphitic clusters and in their ordering was evidenced from Raman spectra, while the film structure remained amorphous according to electron microscopy and electron diffraction observations. At higher fluences the appearance of diamond particles of 2-7 nm size, embedded into the lower crystallized graphitic matrix, was observed and simultaneously a progressive growth of graphite nanocrystals with dimensions from 2 nm to 4 nm was deduced from Raman measurements. The maximum thickness of the crystallized surface layer (approximate to 400 nm) and the degree of laser annealing are limited by the film ablation which starts at E > 250 mJ/cm(2). The laser-treated areas lose their chemical inertness. In particular, chemical etching in chromium acid becomes possible, which may be used for patterning the highly inert carbon films.

Abstract: Several structures and electronic states of the C2N and CN2 molecules have been studied using complete active space SCF (CASSCF), multireference configuration interaction (MRCI), and coupled cluster (CCSD(T)) methods. Both molecules are very stable. Our best computed total atomization energies SIGMAD(e) are 288.6 +/- 2 kcal/mol for CN2, and 294.1 +/- 2 kcal/mol for C2N. The CNC and CCN structures for C2N are nearly isoenergetic. CNN(3PI) lies about 30 kcal/mol above NCN(3PI(g)), but has a high barrier towards interconversion and is therefore observed experimentally. Computed harmonic frequencies for CNN are sensitive to the correlation treatment: they are reproduced well using multireference methods as well as the CCSD(T) method. High spin contamination has a detrimental effect on computed harmonic frequencies at the CCSD(T) level.

Abstract: Catalytic methods for the production of carbon nanotubules have been developed based on the decomposition of acetylene on well-dispersed metal particles strongly adsorbed on a support. Cobalt on silica was found to be the best catalyst-support combination for the production of graphitic tubules. The method for the catalyst preparation and the reaction conditions were optimized. Straight and coiled carbon tubules were obtained with inner and outer diameter of 3-7 and 15-20 nm, respectively, and up to 30 mum in length. These nanotubules were not coated by amorphous carbon. Traces of amorphous carbon could be removed by hydrogen. High resolution electron microscopy images and electron diffraction patterns of the straight nanotubules were similar to those obtained by the arc-discharge method. Coiled nanotubules were revealed by TEM to be regular polygonized helices where the bends are caused by pairs of pentagon-heptagon carbon rings among the hexagonal network.