Abstract: Quantitative electron tomography is proposed to characterize porous materials at a nanoscale. To achieve reliable three-dimensional (3D) quantitative information, the influence of missing wedge artifacts and segmentation methods is investigated. We are presenting the Discrete Algebraic Reconstruction Algorithm as the most adequate tomography method to measure porosity at the nanoscale. It provides accurate 3D quantitative information, regardless the presence of a missing wedge. As an example, we applied our approach to nanovoids in La2Zr2O7 thin films.

Abstract: The anion-excess fluorite-like solid solutions with general composition Bi1−xTex(O,F)2+δ (x > 0.5) have been synthesized by a solid state reaction of TeO2, BiF3 and Bi2O3 at 873 K with following quenching. The homogeneity areas and polymorphism of the I ↔ IV Bi1−xTex(O,F)2+δ phases were investigated. The crystal structure of the low temperature IV-Bi1−xTex(O,F)2+δ phase has been solved using electron diffraction and X-ray powder diffraction (a = 11.53051(9) Å, S.G. Ia-3, RI = 0.046, RP = 0.041). Glass formation area in the Bi2O3BiF3TeO2 (10% TiO2) system was investigated. IVBi1−xTex(O,F)2+δ phase starts to crystallize at short-time (0.53 h) annealing of oxyfluoride glasses at temperatures above Tg (600615 K). The ionic conductivity of the crystalline Bi1−xTex(O,F)2+δ phase and corresponding glass-ceramics was investigated. Activation energy of conductivity Ea = 0.41(2) eV for the IV-Bi1−xTex(O,F)2+δ crystalline samples and Ea = 0.73 eV for the glass-ceramic samples were obtained. Investigation of the oxyfluoride samples with a constant cation ratio demonstrates essential influence of excess fluorine anions on the ionic conductivity.

Abstract: Complex [(La0.7Sr0.3MnO3)(m)(SrTiO3)(n)] [(LSMO)(m)/(STO)(8)](15) superlattices with different layer thicknesses (m=5, 8, 12, 16, 32) have been prepared using pulsed liquid injection metalorganic chemical vapor deposition. Transmission electron microscopy and electron diffraction reveal a very clear and well-separated layer sequence. The remarkable microstructure, as well as the ferromagnetic transition temperature, depends on the LSMO layer thickness. Apart from a very clear layer sequence, electron microscopy shows evidence of a self-assembled nanostructure formation: SrMnO3 nanoinclusions and associated SrTiO3-SrMnO3 thin walls. A formation model and growth mechanism for the self-assembled structure is proposed, based on high resolution and energy filtered elemental imaging. (C) 2003 American Institute of Physics.

Abstract: Searching for novel high-capacity electrode materials combining cationic and anionic redox processes is an ever-growing activity within the field of Li-ion batteries. In this respect, we report on the exploration of the Li3RuyNb1-yO4 (O <= y <= 1) system with an O/M ratio of 4 to maximize the number of oxygen lone pairs, responsible for the anionic redox. We show that this system presents a very rich crystal chemistry with the existence of four structural types, which derive from the rocksalt structure but differ in their cationic arrangement, creating either zigzag, helical, jagged chains or clusters. From an electrochemical standpoint, these compounds are active on reduction via a classical cationic insertion process. The oxidation process is more complex, because of the instability of the delithiated phase. Our results promote the use of the rich Li3MO4 family as a viable platform for a better understanding of the relationships between structure and anionic redox activity.

Abstract: The morphological evolution in La(0.5)Ca(0.5)MnO(3)/SrTiO(3)(100) ultrathin films has been revealed by atomic force microscopy. It was found that ordered linear defects, which are in 1-2 unit cells high and oriented along the cubic [110] and [100] directions, first appear on the smooth surface of films with a thickness of 10 nm. As the epitaxial growth proceeds, these lines on surface develop into a crosshatch pattern for films with a thickness of 25 nm. Using the results of transmission electron microscopy and electrical measurements, we discuss the interplay between the surface pattern formation, the internal dislocation structure, and the variations in the electrical properties.

Abstract: The fluorination of La2CuO4 can lead to different oxyfluoride compounds depending on the TF2 temperature of the fluorine gas treatment. When 150-degrees-C T(F2) less-than-or-equal-to 200-degrees-c less-than-or-equal-to 200-degrees-C a superconducting material is obtained. Previous neutron diffraction experiments as well as the EXAFS measurements at the La L(III) edge indicate that extra anions lie in an interstitial site between the two (LaO) layers. Electron diffraction patterns clearly show the existence of an incommensurate modulation due to the presence of shear planes. A second phase is also pointed out which can be obtained as a major component when the fluorination temperature is raised to 230-degrees-C. This phase which is not a superconductor crystallizes with the monoclinic symmetry.

Abstract: The Pb2Fe2O5 compound with a layered intergrowth structure has been prepared by a solid-state reaction at 700 °C. The incommensurate compound crystallizes in a tetragonal system with a = 3.9037(2) Å, c = 3.9996(4) Å, and q = 0.1186(4)c*, or when treated as a commensurate approximant, a = 3.9047(2) Å, c = 36.000(3) Å, space group I4/mmm. The crystal structure of Pb2Fe2O5 was resolved from transmission electron microscopy data. Atomic coordinates and occupancies of the cation positions were estimated from high-angle annular dark-field scanning transmission electron microscopy data. Direct visualization of the positions of the oxygen atoms was possible using annular bright-field scanning transmission electron microscopy. The structure can be represented as an intergrowth of perovskite blocks and partially disordered blocks with a structure similar to that of the Bi2O2 blocks in Aurivillius-type phases. The A-cation positions at the border of the perovskite block and the cation positions in the Aurivillius-type blocks are jointly occupied by Pb2+ and Fe3+ cations, resulting in a layer sequence along the c axis: PbOFeO2PbOFeO2Pb7/8Fe1/8O1xFe5/8Pb3/8O2Fe5/8Pb3/8. Upon heating, the layered Pb2Fe2O5 structure transforms into an anion-deficient perovskite modulated by periodically spaced crystallographic shear (CS) planes. Considering the layered Pb2Fe2O5 structure as a parent matrix for the nucleation and growth of CS planes allows an explanation of the specific microstructure observed for the CS structures in the PbFeO system.

Abstract: We compare the magnetic properties of pure and oxidized Co nanoparticles embedded in an amorphous Al2O3 matrix. Nanoparticles with diameters of 2 or 3 nm were prepared by alternate pulsed laser deposition in high vacuum conditions, and some of them were exposed to O-2 after production and before being embedded. The nanoparticles are organized in layers, the effective edge-to-edge in-depth separation being 5 or 10 nm. The lower saturation magnetizations per Co atom for the samples containing oxidized nanoparticles provide evidence for the formation of antiferromagnetic CoO shells in the nanoparticles. None of the samples with Co/CoO nanoparticles show exchange bias, while vertical hysteresis loop shifts and enhanced coercivities (as compared to samples with pure Co nanoparticles) are observed. This constitutes evidence for the nanoparticles size being in all cases smaller than the critical size for exchange bias. The difference in coercivity versus temperature dependences for the samples with pure and oxidized Co nanoparticles shows that the exchange anisotropy in Co/CoO nanoparticles appears at temperatures lower than 50 K. (c) 2007 American Institute of Physics.

Abstract: We study the interface between carbon nanotubes (CNTs) and surface-deposited titanium using electron microscopy and photoemission spectroscopy, supported by density functional calculations. Charge transfer from the Ti atoms to the nanotube and carbide formation is observed at the interface which indicates strong interaction. Nevertheless, the presence of oxygen between the Ti and the CNTs significantly weakens the Ti-CNT interaction. Ti atoms at the surface will preferentially bond to oxygenated sites. Potential sources of oxygen impurities are examined, namely oxygen from any residual atmosphere and pre-existing oxygen impurities on the nanotube surface, which we enhance through oxygen plasma surface pre-treatment. Variation in literature data concerning Ohmic contacts between Ti and carbon nanotubes is explained via sample pre-treatment and differing vacuum levels, and we suggest improved treatment routes for reliable Schottky barrier-free Ti-nanotube contact formation.