Abstract: Defect mediated high temperature ferromagnetism in oxide nanocrystallites is the central feature of this work. Here, we report the development of room temperature ferromagnetism in nanosized Co-doped barium titanate particles with a size of around 14 nm, synthesized by a solvothermal drying method. A combination of x-ray diffraction with state-of-the-art electron microscopy techniques confirms the intrinsic doping of Co into BaTiO3. The development of the room temperature ferromagnetism was tracked down to the different donor defects, namely hydroxyl groups at the oxygen site (\mathrm {OH}_{\mathrm {(O)}}

Abstract: We are reporting an unexpected metal insulator transition at the ferromagnetic phase-transition temperature for thin films of La0.9Sr0.1MnO3 (< 50 nm), grown on a (100) face of SrTiO3 substrate. For the thicker films (> 50 nm), similar to the single crystal, no such transition is observed below T-C. Additionally, we observe the suppression of the features associated with charge or orbital ordering in intentionally La-deficient thin films of La0.88Sr0.1MnO3 (< 75 nm). In thin films, transmission electron microscopy reveals a compressive strain due to the epitaxial growth, that is, lattice parameters adopt those of the cubic lattice of SrTiO3. As the film thickness increases, coherent microtwinning is observed in the films and the films relax to a orthorhombic structure. (C) 2000 American Institute of Physics. [S0003-6951(00)00402-2].

Abstract: Based on a facile one-pot templating synthesis, using a TS-1 zeolite recipe whereby part of the zeolite structure directing agent is replaced by a mesopore templating agent, a trimodal material is formed. The resulting meso-TSM material combines mesoporosity (Ti-MCM-41) with zeolitic features (TS-1) and a unique sheet-like morphology with uniform macroporous voids (macroholes). Moreover, the macrohole formation, mesoporosity and zeolitic properties of the meso-TSM material can be controlled in a straightforward way by adjusting the length of the hydrothermal treatment. This newly developed material may imply great potential for catalytic redox applications and diffusion limitated processes because of its highly tunable character in all three dimensions (micro-, meso- and macroporous scale).

Abstract: The double phosphate Ca9In(PO4)(7) was obtained by solid-state reaction and was studied by room and high-temperature Xray powder diffraction, electron diffraction, high-resolution electron microscopy, second-harmonic generation (SHG) technique, differential scanning calorimetry, dielectric and conductivity measurements. The beta-Ca9In(PO4)(7) room-temperature phase is related to the mineral whitlockite and is similar to beta-Ca-3(PO4)(2). It has space group R (3) over barc, with unit cell parameters: a = 10.4008(1) Angstrom, c = 37.272(1) Angstrom, Z = 6. The structure was refined by the Rietveld method (R-wp = 4.69, R-I = 1.81). A reversible first-order beta <----> beta' phase transition of the ferroelectric type with T-c = 902 K is revealed by SHG, differential scanning calorimetry and dielectric measurements. The centrosymmetric beta'-Ca9In(PO4)(7) (973 K) has space group R (3) over barc, a = 10.4611(2) Angstrom, c = 37.874 (1) Angstrom (R-wp = 4.27, R-I = 4.11). Compared to the low-temperature beta-Ca9In(PO4)(7) structure, beta'-Ca9In(PO4)(7) can be described as an orientational disordering of the P1O(4) tetrahedra together with a calcium disordering on the M3 site. (C) 2002 Elsevier Science (USA).

Abstract: Recently discovered series of high Tc superconductors, characterized by the existence of two types of cations within the same layer, are presented. The first family concerns the mercury based cuprates, Hg(1-x)M(x)A(2)Ca(m-1)Cu(m)O(2m+2+delta), with A = Ba and/or Sr, which exhibit structures closely related to that of the thallium cuprates TlBa2Cam-1CumO2m+3. They differ from the thallium cuprates by a high oxygen deficiency at the level of the mercury layer. It is shown that cations such as M = Cu, Pb, Tl, Bi, Ce, Pr, Cr, V, Mo, W, Ti, Sr, Ca,... can partially substitute for mercury ions, stabilizing the structures. The cationic composition of the layer depends indeed on the nature of the M cation but also on that of the alkaline earth A. For given A and M cations, the a: value remains unchanged even when the number of copper layers varies. M and Hg cations are either statistically distributed over the same site or ordered. Different types of ordering have been detected. Another way of generating mixed layers is to shear periodically the structure, leading to the formation of the so called ''collapsed phase''. In the collapsed bismuth cuprates, bismuth and copper segments, a few octahedra long, alternate in strongly waving layers. In the collapsed oxycarbonates, carbonate groups and M cations are ordered within the intermediate layer so that they can be simply described from a partial and ordered substitution of carbon for Hg,TI, Bi and other M cations building the intermediate layer. The oxycarbonitrates (Y1-xCax)(n)Ba2nCu3n-1(C,N)O3O7n-3 can also be described as an ordered substitution of carbon for copper in the 123 matrix. The different families of superconducting materials which are generated by such mechanisms are described as well as the way the different species are distributed within the mixed layers. Their influence on the physical properties are discussed.

Abstract: Sr2FeMoO6/SrTiO3/CoFe2 trilayers grown by pulsed laser deposition on SrTiO3 (001) are investigated by transmission electron microscopy and electron energy loss spectroscopy. The stack is epitaxial, independent of whether the CoFe2 electrode is grown at 500 or at 50 degrees C. Thus it is possible to obtain epitaxy near room temperature. The SrTiO3/CoFe2 interface is quite sharp, while the Sr2FeMoO6/SrTiO3 interface presents regions of Fe depletion. The chemical composition of the films is close to the nominal stoichiometries. These results could be useful for the growth of heteroepitaxial devices and magnetic tunnel junctions. (C) 2007 American Institute of Physics.

Abstract: Tetrahedral chain ordering in the Sr2MnGaO5 structure is studied using electron diffraction (ED) and high-resolution electron microscopy. The ED patterns show the presence of satellite reflections, which indicate a commensurately modulated structure with a = 5.4056(8) Angstrom b 16.171(3) Angstrom, c = 5.5592(7) Angstrom, q – 1/2c*, superspace group Immma(00gamma,)s00. The Superstructure arises due to ordering of the two types of symmetry related tetrahedral chains (L and R) according to a ... LRLR ... sequence, where L and R chains alternate along the c-axis within the same (GaO) layer. Numerous defects at different structural levels were observed, comprising interleaving L and R chains, violation of the ... LRLR ... chain sequence within one layer, different stacking modes of the ... LRLR ... ordered layers with subsequent alternation of blocks of different width along the h-axis of the brownmillerite subcell and island fragmentation of the modulated superstructure. By in situ heating ED experiments it is found that the long-range ordering of the tetrahedral chains is stable tip to 665degreesC and is completely suppressed at 905degreesC. (C) 2003 Elsevier Inc. All rights reserved.

Abstract: The microstructural and compositional evolution during initial annealing of a superconducting (Bi,Pb)(2)Sr2Ca2Cu3O10+delta/Ag tape is studied using quantitative transmission electron microscopy. Special attention is devoted to the occurrence of Pb-rich liquids, which are crucial for the Bi2Sr2CaCu2O8+delta to (Bi,Pb)(2)Sr2Ca2Cu3O10+delta transformation. Ca and/or Pb-rich (Bi,Pb)(2)Sr2CaCu2O8+delta grains dissolve into a liquid, which reacts with Ca-rich phases to increase the liquid's Ca-content. This leads to (Bi,Pb)(2)Sr2Ca2Cu3O10+delta formation. Apparently, a Ca/Sr ratio of around I is sufficient to keep (Bi,Pb)(2)Sr2Ca2Cu3O10+delta nucleation going. It is confirmed that Ag particles are transported from the Ag-sheath into the oxide core by the liquid and not by mechanical treatment of the tape.

Abstract: The structure and defect structure of Bi2-xPbxSr3.5Cu2 (CO3)O8-delta compounds with 0 less-than-or-equal-to x less-than-or-equal-to 0.75 are carefully investigated by electron diffraction and high-resolution electron microscopy. All compounds have an orthorhombic structure with a almost-equal-to b almost-equal-to 5.4 angstrom and c almost-equal-to 39.5 angstrom. The length of the b-axis decreases monotonically with increasing x. The space group for the basic structure is Abm2. The structure can be considered as an intergrowth of Bi2Sr2CuO6 lamellae with Sr2CuO2 (CO3) lamellae along the c-axis. CO3 groups behave as bridges connecting the CuO6 octahedra. In the x = 0 compound the carbon atoms are shifted away from their symmetry positions; the orientational ordering of the CO3 groups (or the carbon shift) in successive CO planes alternates along +b and -b. Typical Bi-type and Pb-type modulations are found along the b-axis up to a Pb content x = 0.5. Electron beam irradiation destroys the ordering of the CO3 groups and alters the modulated structure. (C) 1994 Academic press, inc.

Abstract: High-resolution transmission electron microscopy was performed on compacted Ni(3)Al nanostructured material prepared by the inert gas condensation technique. From electron diffraction data an incomplete L1(2) ordering of the crystallites is observed in the free particles as well as in the room temperature compacted samples. However, a completely ordered L1(2) structure with much bigger and well-defined crystallites exhibiting several defects is observed in material compacted and annealed at 773 K. Sharp crystallite boundaries as well as amorphous material and voids are observed in between crystallites in all samples, the former being dominant in the annealed material, the latter in the as-prepared one.