Abstract: Reversible macroscopic length changes in nanoporous structures can be achieved by applying electric potentials or by exposing them to different gases or liquids. Thus, these materials are interesting candidates for applications as sensors or actuators. Macroscopic length changes originate from microscopic changes of crystal lattice parameters. In this report, we show spatially resolved measurements of crystal lattice strain in dealloyed nanoporous gold. The results confirm theory by indicating a compression of the lattice along the axis of cylindrically shaped ligaments and an expansion in radial direction. Furthermore, we show that curved npAu surfaces show inward relaxation of the surface layer. [GRAPHICS] .

Abstract: Optical (atomic absorption spectroscopy, AAS; atomic emission spectroscopy, AES; atomic fluorescence spectroscopy, AFS; and optogalvanic spectroscopy) and mass spectrometric (magnetic sector, quadrupolemass analyzer, QMA; quadrupole ion trap, QIT; Fourier transform ion cyclotron resonance, FTICR; and time-of-flight, TOF) instrumentation are well suited for coupling to the glow discharge (GD). The GD is a relatively simple device. A potential gradient (5001500 V) is applied between an anode and a cathode. In most cases, the sample is also the cathode. A noble gas (e.g. Ar, Ne, and Xe) is introduced into the discharge region before power initiation. When a potential is applied, electrons are accelerated toward the anode. As these electrons accelerate, they collide with gas atoms. A fraction of these collisions are of sufficient energy to remove an electron from a support gas atom, forming an ion. These ions are, in turn, accelerated toward the cathode. These ions impinge on the surface of the cathode, sputtering sample atoms from the surface. Sputtered atoms that do not redeposit on the surface diffuse into the excitation/ionization regions of the plasma where they can undergo excitation and/or ionization via a number of collisional processes. GD sources offer a number of distinct advantages that make them well suited for specific types of analyses. These sources afford direct analysis of solid samples, thus minimizing the sample preparation required for analysis. The nature of the plasma also provides mutually exclusive atomization and excitation processes that help to minimize the matrix effects that plague so many other elemental techniques. Unfortunately, the GD source functions optimally in a dry environment, making analysis of solutions more difficult. These sources also suffer from difficulties associated with analyzing nonconductingsamples. In this article, first, the principles of operation of the GD plasma are reviewed, with an emphasis on how those principles relate to optical spectroscopy and mass spectrometry. Basic applications of the GD techniques are considered next. These include bulk analysis, surface analysis, and the analysis of solution samples. The requirements necessary to obtain optical information are addressed following the analytical applications. This section focuses on the instrumentation needed to make optical measurements using the GD as an atomization/excitation source. Finally, mass spectrometric instrumentation and interfaces are addressed as they pertain to the use of a GD plasma as an ion source. GDsources provide analytically useful gas-phase species from solid samples. These sources can be interfaced with avariety of spectroscopic and spectrometric instruments for both quantitative and qualitative analysis.

Abstract: <script type='text/javascript'>document.write(unpmarked('The crystal and defect structure of SnS crystals grown using chemical vapour deposition for application in electronic devices are investigated. The structural analysis shows the presence of two distinct crystal morphologies, that is thin flakes with lateral sizes up to 50 m and nanometer scale thickness, and much thicker but smaller crystallites. Both show similar Raman response associated with SnS. The structural analysis with transmission electron microscopy shows that the flakes are single crystals of -SnS with [010] normal to the substrate. Parallel with the surface of the flakes, lamellae with varying thickness of a new SnS phase are observed. High-resolution transmission electron microscopy (TEM), scanning transmission electron microscopy (STEM), first-principles simulations (DFT) and nanobeam diffraction (NBD) techniques are employed to characterise this phase in detail. DFT results suggest that the phase is a strain stabilised \u0027 one grown epitaxially on the -SnS crystals. TEM analysis shows that the crystallites are also -SnS with generally the [010] direction orthogonal to the substrate. Contrary to the flakes the crystallites consist of two to four grains which are tilted up to 15 degrees relative to the substrate. The various grain boundary structures and twin relations are discussed. Under high-dose electron irradiation, the SnS structure is reduced and -Sn formed. It is shown that this damage only occurs for SnS in direct contact with SiO2. Lay description SnS is a p-type semiconductor, which has attracted significant interest for electronic devices due to its unique properties, low-toxicity and abundance of Sn in nature. Although in the past it has been most extensively studied as the absorber material in solar cells, it has recently garnered interest for application as a p-type two-dimensional semiconductor in nanoelectronic devices due to its anisotropic layered structure similar to the better known phosphorene. Tin sulphide can take the form of several phases and the electronic properties of the material depend strongly on its crystal structure. It is therefore crucial to study the crystal structure of the material in order to predict the electronic properties and gain insight into the growth mechanism. In this work, SnS crystals deposited using a chemical vapour deposition technique are investigated extensively for their crystal and defect structure using transmission electron microscopy (TEM) and related techniques. We find the presence of two distinct crystal morphologies, that is thin flakes with lateral sizes up to 50 m and nm scale thickness, and much thicker but smaller crystallites. The flakes are single crystals of -SnS and contain lamellae with varying thickness of a different phase which appear to be -SnS at first glance. High-resolution scanning transmission electron microscopy is used to characterise these lamellae where the annular bright field (ABF) mode better reveals the position of the sulphur columns. The sulphur columns in the lamellae are found to be shifted relative to the -SnS structure which indicates the formation of a new phase which is a distorted version of the phase which we tentatively refer to as \u0027-SnS. Simulations based on density functional theory (DFT) are used to model the interface and a similar shift of sulphur columns in the -SnS layer is observed which takes place as a result of strong interaction at the interface between the two phases resulting in strain transfer. Nanobeam electron diffraction (NBD) is used to map the lattice mismatch in the thickness of the flakes which reveals good in-plane matching and some expansion out-of-plane in the lamellae. Contrary to the flakes the crystallites are made solely of -SnS and consist of two to four grains which are tilted up to 15 degrees relative to the substrate. The various grain boundary structures and twin relations are discussed. At high electron doses, SnS is reduced to -Sn, however the damage occurs only for SnS in direct contact with SiO2.'));

Abstract: The disordered phases of LiCB11H12 and NaCB11H12 possess superb superionic conductivities that make them suitable as solid electrolytes. In these materials, cation diffusion correlates with high orientational mobilities of the CB11H12- anions; however, the precise relationship has yet to be demonstrated. In this work, ab initio molecular dynamics and quasielastic neutron scattering are combined to probe anion reorientations and their mechanistic connection to cation mobility over a range of timescales and temperatures. It is found that anions do not rotate freely, but rather transition rapidly between orientations defined by the cation sublattice symmetry. The symmetry-breaking carbon atom in CB11H12- also plays a critical role by perturbing the energy landscape along the instantaneous orientation of the anion dipole, which couples fluctuations in the cation probability density directly to the anion motion. Anion reorientation rates exceed 3 x 10(10) s(-1), suggesting the underlying energy landscape fluctuates dynamically on diffusion-relevant timescales. Furthermore, carbon is found to modify the orientational preferences of the anions and aid rotational mobility, creating additional symmetry incompatibilities that inhibit ordering. The results suggest that synergy between the anion reorientational dynamics and the carbon-modified cation-anion interaction accounts for the higher ionic conductivity in CB11H12- salts compared with B12H122-.