“Insight to ternary complexes of co-adsorption of norfloxacin and Cu(II) onto montmorillonite at different pH using EXAFS”. Pei Z-G, Shan X-Q, Zhang S-Z, Kong J-J, Wen B, Zhang J, Zheng L-R, Xie Y-N, Janssens K, Journal of hazardous materials 186, 842 (2011). http://doi.org/10.1016/J.JHAZMAT.2010.11.076
Abstract: Co-adsorption of norfloxacin (Nor) and Cu(II) on montmorillonite at pH 4.5, 7.0 and 9.0 was studied by integrated batch adsorption experiments and extended X-ray absorption fine structure (EXAFS) spectroscopy. Under such pH conditions the dominant species of Nor are cation (Nor+), zwitterion (Nor±), and anion (Nor−), respectively. Results indicated that Nor sorption decreased with an increase of solution pH. The presence of Cu(II) slightly suppressed the Nor+ sorption at pH 4.5, while increased Nor± and Nor−sorption on montmorillonite at pH 7.0 and 9.0, respectively. In contrast, Nor increased Cu(II) adsorption at pH 4.5, but had little effect on the adsorption of Cu(II) on montmorillonite at pH 7.0 and 9.0. Spectroscopic results showed that, at pH 4.5, Nor+ was sorbed on montmorillonite by the formation of outer-sphere montmorilloniteNorCu(II) ternary surface complex. At pH 7.0, montmorilloniteNorCu(II) and montmorilloniteCu(II)Nor ternary surface complexes co-exist. At pH 9.0, montmorilloniteCu(II)Nor ternary surface complex was likely formed, which was different to Cu(II)(Nor)2 precipitate of the solution.
Keywords: A1 Journal article; Engineering sciences. Technology; AXES (Antwerp X-ray Analysis, Electrochemistry and Speciation)
Impact Factor: 6.065
Times cited: 25
DOI: 10.1016/J.JHAZMAT.2010.11.076
|
“Relative sensitivity factors in glow discharge mass spectrometry: the role of charge transfer ionization”. Bogaerts A, Gijbels R, Journal of analytical atomic spectrometry 11, 841 (1996). http://doi.org/10.1039/ja9961100841
Keywords: A1 Journal article; Plasma Lab for Applications in Sustainability and Medicine – Antwerp (PLASMANT)
Impact Factor: 3.466
Times cited: 38
DOI: 10.1039/ja9961100841
|
“Destruction of magnetophonon resonance in high mobility heterojunctions from competition between elastic and inelastic scattering”. Xu W, Leadley DR, Peeters FM, Devreese JT, Nicholas RJ, Harris JJ, Foxon CT, Proceedings of the International Conference on the Physics of Semiconductors 22, 839 (1994)
Keywords: P3 Proceeding; Condensed Matter Theory (CMT); Theory of quantum systems and complex systems
|
“Synergistic effect of electric field and lipid oxidation on the permeability of cell membranes”. Yusupov M, Van der Paal J, Neyts EC, Bogaerts A, Biochimica et biophysica acta : G : general subjects 1861, 839 (2017). http://doi.org/10.1016/j.bbagen.2017.01.030
Abstract: Background: Strong electric fields are knownto affect cell membrane permeability,which can be applied for therapeutic purposes, e.g., in cancer therapy. A synergistic enhancement of this effect may be accomplished by the presence of reactive oxygen species (ROS), as generated in cold atmospheric plasmas. Little is known about the synergy between lipid oxidation by ROS and the electric field, nor on howthis affects the cell membrane permeability.
Method: We here conduct molecular dynamics simulations to elucidate the dynamics of the permeation process under the influence of combined lipid oxidation and electroporation. A phospholipid bilayer (PLB), consisting of di-oleoyl-phosphatidylcholine molecules covered with water layers, is used as a model system for the plasma membrane.
Results and conclusions:Weshow howoxidation of the lipids in the PLB leads to an increase of the permeability of the bilayer to ROS, although the permeation free energy barriers still remain relatively high. More importantly, oxidation of the lipids results in a drop of the electric field threshold needed for pore formation (i.e., electroporation) in the PLB. The created pores in the membrane facilitate the penetration of reactive plasma species deep into the cell interior, eventually causing oxidative damage.
General significance: This study is of particular interest for plasma medicine, as plasma generates both ROS and electric fields, but it is also of more general interest for applications where strong electric fields and ROS both come into play.
Keywords: A1 Journal article; Plasma Lab for Applications in Sustainability and Medicine – Antwerp (PLASMANT)
Impact Factor: 4.702
DOI: 10.1016/j.bbagen.2017.01.030
|
“Early deformation mechanisms in the shear affected region underneath a copper sliding contact”. Haug C, Ruebeling F, Kashiwar A, Gumbsch P, Kübel C, Greiner C, Nature Communications 11, 839 (2020). http://doi.org/10.1038/S41467-020-14640-2
Abstract: Dislocation mediated plastic deformation decisively influences the friction coefficient and the microstructural changes at many metal sliding interfaces during tribological loading. This work explores the initiation of a tribologically induced microstructure in the vicinity of a copper twin boundary. Two distinct horizontal dislocation traces lines (DTL) are observed in their interaction with the twin boundary beneath the sliding interface. DTL formation seems unaffected by the presence of the twin boundary but the twin boundary acts as an indicator of the occurring deformation mechanisms. Three concurrent elementary processes can be identified: simple shear of the subsurface area in sliding direction, localized shear at the primary DTL and crystal rotation in the layers above and between the DTLs around axes parallel to the transverse direction. Crystal orientation analysis demonstrates a strong compatibility of these proposed processes. Quantitatively separating these different deformation mechanisms is crucial for future predictive modeling of tribological contacts.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 16.6
DOI: 10.1038/S41467-020-14640-2
|
“Spatial and temporal variations in particulate Polycyclic Aromatic Hydrocarbon (PAH) levels over Menen (Belgium) and their relation with air mass trajectories”. Ravindra K, Wauters E, Van Grieken R page 838 (2007).
Keywords: H3 Book chapter; AXES (Antwerp X-ray Analysis, Electrochemistry and Speciation)
|
“Magnetic properties of bcc-Fe(001)/C-60 interfaces for organic spintronics”. Tran TLA, Çakir D, Wong PKJ, Preobrajenski AB, Brocks G, van der Wiel WG, de Jong MP, Acs Applied Materials &, Interfaces 5, 837 (2013). http://doi.org/10.1021/AM3024367
Abstract: The magnetic structure of the interfaces between organic semiconductors and ferromagnetic contacts plays a key role in the spin injection and extraction processes in organic spintronic devices. We present a combined computational (density functional theory) and experimental (X-ray magnetic circular dichroism) study on the magnetic properties of interfaces between bcc-Fe(001) and C-60 molecules. C-60 is an interesting candidate for application in organic spintronics due to the absence of hydrogen atoms and the associated hyperfine fields. Adsorption of C-60 on Fe(001) reduces the magnetic moments on the top Fe layers by similar to 6%, while inducing an antiparrallel magnetic moment of similar to-0.2 mu(B) on C-60. Adsorption of C-60 on a model ferromagnetic substrate consisting of three Fe monolayers on W(001) leads to a different structure but to very similar interface magnetic properties.
Keywords: A1 Journal article; Condensed Matter Theory (CMT)
Impact Factor: 7.504
Times cited: 28
DOI: 10.1021/AM3024367
|
van de Vijver FL, Verbueken AH, Visser WJ, Van Grieken RE, de Broe ME (1984) Localisation of aluminium and iron by histochemical and laster microprobe mass analytical techniques in bone marrow cells of chronic hemodialysis patients. 837–838
Keywords: L1 Letter to the editor; AXES (Antwerp X-ray Analysis, Electrochemistry and Speciation); Laboratory Experimental Medicine and Pediatrics (LEMP)
DOI: 10.1136/JCP.37.7.837-B
|
“Phase boundaries of superconducting mesoscopic square loops”. Fomin VM, Misko VR, Devreese JT, Moshchalkov VV, 12th International Conference on the Electronic Properties of Two-Dimensional Systems (EP2DS), Tokyo, 835 (1997)
Keywords: A1 Journal article; Electron Microscopy for Materials Science (EMAT);
|
“K₅Eu(MoO₄)₄, red phosphor for solid state lighting applications, prepared by different techniques”. Posokhova SMM, Morozov VA, Deyneko DVV, Redkin BSS, Spassky DAA, Nagirnyi V, Belik AAA, Hadermann J, Pavlova ETT, Lazoryak BII, CrystEngComm 25, 835 (2023). http://doi.org/10.1039/D2CE01107G
Abstract: The influence of preparation techniques on the structure and luminescent properties of K5Eu(MoO4)(4) (KEMO) was investigated. KEMO phosphors were synthesized by three different techniques: solid state and sol-gel (sg) methods as well as the Czochralski (CZ) crystal growth technique. Laboratory powder X-ray diffraction (PXRD) studies revealed that all KEMO samples had a structure analogous to that of other high temperature alpha-K5R(MoO4)(4) palmierite-type phases (space group (SG) R3m). Contrary to laboratory PXRD data, electron diffraction revealed that the KEMO crystal grown by the CZ technique had a (3 + 1)D incommensurately modulated structure (super space group (SSG) C2/m(0 beta 0)00) with the modulation vector q = 0.689b*. A detailed analysis of electron diffraction patterns has shown formation of three twin domains rotated along the c axis of the R-subcell at 60 degrees with respect to each other. Synchrotron XRD patterns showed additional ultra-wide reflexes in addition to reflections of the R-subcell of the palmierite. However, the insufficient number of reflections, their low intensity and large width in the synchrotron X-ray diffraction patterns made it impossible to refine the structure as incommensurately modulated C2/m(0 beta 0)00. An average structure was refined in the C2/m space group with random distribution of K1 and Eu1 in [M1A(2)O(8)]-layers of the palmierite-type structure. The dependence of luminescent properties on utilized synthesis techniques was studied. The emission spectra of all samples exhibit intense red emission originating from the D-5(0) -> F-7(2) Eu3+ transition. The integrated intensity of the emission from the Eu3+ 5D0 term was found to be the highest in the crystal grown by the CZ technique. The quantum yield measured for KEMO crystals demonstrates a very high value of 66.5%. This fact confirms that KEMO crystals are exceptionally attractive for applications as a near-UV converting red phosphor for LEDs.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 3.1
DOI: 10.1039/D2CE01107G
|
“Fingerprinting of South African ordinary Portland cements, cement blends and mortars for identification purposes: discrimination with starplots and PCA”. Potgieter-Vermaak SS, Potgieter JH, Worobiec A, Van Grieken R, Marjanovic L, Moeketsi S, Cement and concrete research 37, 834 (2007). http://doi.org/10.1016/J.CEMCONRES.2007.02.013
Keywords: A1 Journal article; AXES (Antwerp X-ray Analysis, Electrochemistry and Speciation); Laboratory Experimental Medicine and Pediatrics (LEMP)
DOI: 10.1016/J.CEMCONRES.2007.02.013
|
“Analysis of Malagasy medical herbs by X-ray fluorescence in total reflectivity”. Razafindramisa FL, Andriambololona R, Brunel M, Van Grieken RE, Journal de physique: 4 6, 833 (1996)
Keywords: A1 Journal article; AXES (Antwerp X-ray Analysis, Electrochemistry and Speciation)
|
“Relation between microstructure and 2DEG properties of AlGaN/GaN structures”. van Daele B, Van Tendeloo G, Germain M, Leys M, Bougrioua Z, Moerman I, Physica status solidi: B: basic research 234, 830 (2002). http://doi.org/10.1002/1521-3951(200212)234:3<830::AID-PSSB830>3.0.CO;2-O
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 1.674
Times cited: 1
DOI: 10.1002/1521-3951(200212)234:3<830::AID-PSSB830>3.0.CO;2-O
|
“Atmospheric pressure glow discharge for CO2 conversion : model-based exploration of the optimum reactor configuration”. Trenchev G, Nikiforov A, Wang W, Kolev S, Bogaerts A, Chemical engineering journal 362, 830 (2019). http://doi.org/10.1016/J.CEJ.2019.01.091
Abstract: We investigate the performance of an atmospheric pressure glow discharge (APGD) reactor for CO2 conversion in three different configurations, through experiments and simulations. The first (basic) configuration utilizes the well-known pin-to-plate design, which offers a limited conversion. The second configuration improves the reactor performance by employing a vortex-flow generator. The third, “confined” configuration is a complete redesign of the reactor, which encloses the discharge in a limited volume, significantly surpassing the conversion rate of the other two designs. The plasma properties are investigated using an advanced plasma model.
Keywords: A1 Journal article; Plasma Lab for Applications in Sustainability and Medicine – Antwerp (PLASMANT)
Impact Factor: 6.216
Times cited: 4
DOI: 10.1016/J.CEJ.2019.01.091
|
“Unveiling the binding mode of perfluorooctanoic acid to human serum albumin”. Maso L, Trande M, Liberi S, Moro G, Daems E, Linciano S, Sobott F, Covaceuszach S, Cassetta A, Fasolato S, Moretto LM, De Wael K, Cendron L, Angelini A, Protein Science 30, 830 (2021). http://doi.org/10.1002/PRO.4036
Abstract: Perfluorooctanoic acid (PFOA) is a toxic compound that is absorbed and distributed throughout the body by noncovalent binding to serum proteins such as human serum albumin (hSA). Though the interaction between PFOA and hSA has been already assessed using various analytical techniques, a high resolution and detailed analysis of the binding mode is still lacking. We report here the crystal structure of hSA in complex with PFOA and a medium-chain saturated fatty acid (FA). A total of eight distinct binding sites, four occupied by PFOAs and four by FAs, have been identified. In solution binding studies confirmed the 4:1 PFOA-hSA stoichiometry and revealed the presence of one high and three low affinity binding sites. Competition experiments with known hSA-binding drugs allowed locating the high affinity binding site in sub-domain IIIA. The elucidation of the molecular basis of the interaction between PFOA and hSA might provide not only a better assessment of the absorption and elimination mechanisms of these compounds in vivo but also have implications for the development of novel molecular receptors for diagnostic and biotechnological applications.
Keywords: A1 Journal article; AXES (Antwerp X-ray Analysis, Electrochemistry and Speciation)
Impact Factor: 2.523
DOI: 10.1002/PRO.4036
|
“The phase transition and crystal structures of Ba3RM2O7.5 complex oxides (R=rare-earth elements, M = Al,Ga)”. Abakumov AM, Shpanchenko RV, Lebedev OI, Van Tendeloo G, Amelinckx S, Antipov EV, Acta crystallographica: section A: foundations of crystallography 55, 828 (1999). http://doi.org/10.1107/S0108767399002068
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 5.725
Times cited: 7
DOI: 10.1107/S0108767399002068
|
“Taxonomical study of marine oscillatorian strains (Cyanobacteria) with narrow trichomes: 2: nucleotide sequence analysis of the 16S ribosomal RNA”. Wilmotte A, Turner S, van de Peer Y, Pace NR, Journal Of Phycology 28, 828 (1992). http://doi.org/10.1111/j.0022-3646.1992.00828.x
Keywords: A1 Journal article; Electron Microscopy for Materials Science (EMAT);
Impact Factor: 2.844
Times cited: 58
DOI: 10.1111/j.0022-3646.1992.00828.x
|
“Leaching of two fungicides in spent mushroom substrate amended soil : I influence of amendment rate, fungicide ageing and flow condition”. Álvarez-Martín A, Sanchez-Martin MJ, Ordax JM, Marin-Benito JM, Sonia Rodriguez-Cruz M, The science of the total environment 584, 828 (2017). http://doi.org/10.1016/J.SCITOTENV.2017.01.126
Abstract: A study has been conducted on the leaching of two fungicides, tebuconazole and cymoxanil, in a soil amended with spent mushroom substrate (SMS), with an evaluation of how different factors influence this process.The objective was based on the potential use of SMS as a biosorbent for immobilizing pesticides in vulnerable soils, and the need to know how it could affect the subsequent transport of these retained compounds. Breakthrough curves (BTCs) for C-14-fungicides, non-incubated and incubated over 30 days, were obtained in columns packed with an unamended soil (S), and this soil amended with SMS at rates of 5% (S + SMS5) and 50% (S + SMS50) under saturated and saturated-unsaturated flows. The highest leaching of tebuconazole (> 50% of the total C-14 added) was found in S when a saturated water flow was applied to the column, but the percentage of leached fungidde decreased when a saturated-unsaturated flow was applied in both SMS-amended soils. Also a significant decrease in teaching was observed for tebuconazole after incubation in the column, especially in S + SMS50 when both flows were applied. Furthermore, cymoxanil leaching was complete in S and S + SMS when a saturated flow was applied, and maximum peak concentrations were reached at 1 pore volume (PV), although BTCs showed peaks with lower concentrations in S + SMS. The amounts of cymoxanil retained only increased in S + SMS when a saturated-unsaturated flow was applied. A more relevant effect of SMS for reducing the leaching of fungidde was observed when cymoxanil was previously incubated in the column, although mineralization was enhanced in this case. These results are of interest for extending SMS application on the control of the leaching of fungicides with different physicochemical characteristics after different ageing times in the soil and water flow conditions applied. (C) 2017 Elsevier B.V. All rights reserved.
Keywords: A1 Journal article; AXES (Antwerp X-ray Analysis, Electrochemistry and Speciation)
DOI: 10.1016/J.SCITOTENV.2017.01.126
|
“Nanocluster superstructures assembled via surface ligand switching at high temperature”. Johnson G, Yang MY, Liu C, Zhou H, Zuo X, Dickie DA, Wang S, Gao W, Anaclet B, Perras FA, Ma F, Zeng C, Wang D, Bals S, Dai S, Xu Z, Liu G, Goddard III WA, Zhang S, Nature synthesis 2, 828 (2023). http://doi.org/10.1038/S44160-023-00304-8
Abstract: Superstructures with nanoscale building blocks, when coupled with precise control of the constituent units, open opportunities in rationally designing and manufacturing desired functional materials. Yet, synthetic strategies for the large-scale production of superstructures are scarce. We report a scalable and generalized approach to synthesizing superstructures assembled from atomically precise Ce24O28(OH)8 and other rare-earth metal-oxide nanoclusters alongside a detailed description of the self-assembly mechanism. Combining operando small-angle X-ray scattering, ex situ molecular and structural characterizations, and molecular dynamics simulations indicates that a high-temperature ligand-switching mechanism, from oleate to benzoate, governs the formation of the nanocluster assembly. The chemical tuning of surface ligands controls superstructure disassembly and reassembly, and furthermore, enables the synthesis of multicomponent superstructures. This synthetic approach, and the accurate mechanistic understanding, are promising for the preparation of superstructures for use in electronics, plasmonics, magnetics and catalysis. Synthesizing superstructures with precisely controlled nanoscale building blocks is challenging. Here the assembly of superstructures is reported from atomically precise Ce24O28(OH)8 and other rare-earth metal-oxide nanoclusters and their multicomponent combinations. A high-temperature ligand-switching mechanism controls the self-assembly.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Times cited: 2
DOI: 10.1038/S44160-023-00304-8
|
“Preparation of hollow silica spheres with different mesostructures”. Liu S, Rao J, Sui X, Cool P, Vansant EF, Van Tendeloo G, Cheng X, Journal of non-crystalline solids 354, 826 (2008). http://doi.org/10.1016/j.jnoncrysol.2007.08.026
Abstract: Hollow silica spheres were quickly synthesized by an octylamine (OA) templating method using tetraethyl orthosilicate (TEOS) as the silica source. N2-sorption results indicate that the hollow spheres have high surface areas and pore volumes. XRD and TEM measurements reveal that the structure of the hollow spheres depends on the amount of TEOS used in the synthesis. When low amount of TEOS is added, the template-containing precursor spheres depict an XRD pattern with two peaks, which can be indexed to a lamellar phase. After the removal of the template, the obtained hollow spheres show no diffraction peaks in the XRD pattern, suggesting that the nanopores in the silica shells are disordered. If increasing the amount of TEOS, either the uncalcined or the calcined sample gives an XRD pattern with a single diffraction peak. The mesostructure of these hollow silica spheres is typically as HMS materials. TGA analyses suggest that the interaction between the silica species and surfactant is stronger in the latter case.
Keywords: A1 Journal article; Laboratory of adsorption and catalysis (LADCA); Electron microscopy for materials research (EMAT)
Impact Factor: 2.124
Times cited: 26
DOI: 10.1016/j.jnoncrysol.2007.08.026
|
“Magnetoexcitons in semiconductor quantum rings with complicated (Kane's) dispersion law”. Avetisyan AA, Ghazaryan AV, Djotyan AP, Kirakosyan AA, Moulopoulos K, Acta physica Polonica: A: general physics, solid state physics, applied physics
T2 –, 4th Workshop on Quantum Chaos and Localisation Phenomena, MAY 22-24, 2009, Polish Acad Sci, Ctr Theoret Phys, Inst Phys, Polish Acad Sci, Ctr Theoret Phys, Inst Phys, War 116, 826 (2009). http://doi.org/10.12693/APHYSPOLA.116.826
Abstract: The influence of the nonparabolicity of charge carriers dispersion law (Kane's dispersion) on a magnetoexciton energy spectrum in InSb quantum rings is theoretically investigated The analytical expression for the energy spectrum of exciton in a narrow-gap semiconductor nanoring in a magnetic field is obtained. The Aharonov – Bohm oscillations in the energy of excited states are studied.
Keywords: A1 Journal article; Condensed Matter Theory (CMT)
DOI: 10.12693/APHYSPOLA.116.826
|
“VEGF-targeted magnetic nanoparticles for MRI visualization of brain tumor”. Abakumov MA, Nukolova NV, Sokolsky-Papkov M, Shein SA, Sandalova TO, Vishwasrao HM, Grinenko NF, Gubsky IL, Abakumov AM, Kabanov AV, Chekhonin VP;, Nanomedicine: nanotechnology, biology and medicine 11, 825 (2015). http://doi.org/10.1016/j.nano.2014.12.011
Abstract: This work is focused on synthesis and characterization of targeted magnetic nanoparticles as magnetic resonance imaging (MRI) agents for in vivo visualization of gliomas. Ferric oxide (Fe3O4) cores were synthesized by thermal decomposition and coated with bovine serum albumin (BSA) to form nanoparticles with D-eff of 53 +/- 9 nm. The BSA was further cross-linked to improve colloidal stability. Monoclonal antibodies against vascular endothelial growth factor (mAbVEGF) were covalently conjugated to BSA through a polyethyleneglycol linker. Here we demonstrate that 1) BSA coated nanoparticles are stable and non-toxic to different cells at concentration up to 2.5 mg/mL; 2) conjugation of monoclonal antibodies to nanoparticles promotes their binding to VEGF-positive glioma C6 cells in vitro; 3) targeted nanoparticles are effective in MRI visualization of the intracranial glioma. Thus, mAbVEGF-targeted BSA-coated magnetic nanoparticles are promising MRI contrast agents for glioma visualization. (C) 2015 Elsevier Inc. All rights reserved.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 5.72
Times cited: 62
DOI: 10.1016/j.nano.2014.12.011
|
“Comparative study of the magnetic properties of La3Ni2B'O9 for B' = Nb, Ta or Sb”. Chin C-M, Battle PD, Blundell SJ, Hunter E, Lang F, Hendrickx M, Sena RP, Hadermann J, Journal of solid state chemistry 258, 825 (2018). http://doi.org/10.1016/J.JSSC.2017.12.018
Abstract: Polycrystalline samples of La3Ni2NbO9 and La3Ni2TaO9 have been characterised by X-ray and neutron diffraction, electron microscopy, magnetometry and muon spin relaxation (mu SR); the latter technique was also applied to La3Ni2SbO9. On the length scale of a neutron diffraction experiment, the six-coordinate sites of the monoclinic perovskite structure are occupied in a 1:1 ordered manner by Ni and a random 1/3Ni/2/3B' mixture. Electron microscopy demonstrated that this 1:1 ordering is maintained over microscopic distances, although diffuse scattering indicative of short-range ordering on the mixed site was observed. No magnetic Bragg scattering was observed in neutron diffraction patterns collected from La3Ni2B'O-9 (B' = Nb or Ta) at 5 K although in each case mu SR identified the presence of static spins below 30 K. Magnetometry showed that La3Ni2NbO9 behaves as a spin glass below 29 K but significant short-range interactions are present in La3Ni2NbO9 below 85 K. The contrasting properties of these compounds are discussed in terms of their microstructure.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.299
Times cited: 6
DOI: 10.1016/J.JSSC.2017.12.018
|
“Energy-dispersive X-ray spectrometry : present state and trends”. Van Grieken R, Markowicz A, Török S, Fresenius' Zeitschrift für analytische Chemie 324, 825 (1986). http://doi.org/10.1007/BF00473177
Abstract: Recent development, present state and expected future developments in energy-dispersive X-ray spectrometry are discussed. Attention is paid to the improvements in analytical selectivity, sensitivity, detection limit, quantitative character and applicability range, which are the result of new or better excitation sources, detectors, instrument design, automation, computer software and theoretical developments.
Keywords: A3 Journal article; AXES (Antwerp X-ray Analysis, Electrochemistry and Speciation)
DOI: 10.1007/BF00473177
|
“Molecular and elemental characterisation of mineral particles by means of parallel micro-Raman spectrometry and Scanning Electron Microscopy/Energy Dispersive X-ray Analysis”. Stefaniak EA, Worobiec A, Potgieter-Vermaak S, Alsecz A, Török S, Van Grieken R, Spectrochimica acta: part B : atomic spectroscopy 61, 824 (2006). http://doi.org/10.1016/J.SAB.2006.04.009
Keywords: A1 Journal article; Laboratory Experimental Medicine and Pediatrics (LEMP); AXES (Antwerp X-ray Analysis, Electrochemistry and Speciation)
DOI: 10.1016/J.SAB.2006.04.009
|
“Electron mobility in Si delta-doped GaAs”. Hai GQ, Studart N, Peeters FM, Devreese JT, Koenraad PM, van de Stadt AFW, Wolter JH, Proceedings of the International Conference on the Physics of Semiconductors 22, 823 (1994)
Keywords: P3 Proceeding; Condensed Matter Theory (CMT); Theory of quantum systems and complex systems
|
“Modulating the Antioxidant Response for Better Oxidative Stress-Inducing Therapies: How to Take Advantage of Two Sides of the Same Medal?”.Shaw P, Kumar N, Sahun M, Smits E, Bogaerts A, Privat-Maldonado A, Biomedicines 10, 823 (2022). http://doi.org/10.3390/biomedicines10040823
Abstract: Oxidative stress-inducing therapies are characterized as a specific treatment that involves the production of reactive oxygen and nitrogen species (RONS) by external or internal sources. To protect cells against oxidative stress, cells have evolved a strong antioxidant defense system to either prevent RONS formation or scavenge them. The maintenance of the redox balance ensures signal transduction, development, cell proliferation, regulation of the mechanisms of cell death, among others. Oxidative stress can beneficially be used to treat several diseases such as neurodegenerative disorders, heart disease, cancer, and other diseases by regulating the antioxidant system. Understanding the mechanisms of various endogenous antioxidant systems can increase the therapeutic efficacy of oxidative stress-based therapies, leading to clinical success in medical treatment. This review deals with the recent novel findings of various cellular endogenous antioxidant responses behind oxidative stress, highlighting their implication in various human diseases, such as ulcers, skin pathologies, oncology, and viral infections such as SARS-CoV-2.
Keywords: A1 Journal article; Pharmacology. Therapy; Plasma Lab for Applications in Sustainability and Medicine – Antwerp (PLASMANT); Center for Oncological Research (CORE)
DOI: 10.3390/biomedicines10040823
|
“Selenium in environmental waters : determination, speciation and concentration levels”. Robberecht H, Van Grieken R, Talanta : the international journal of pure and applied analytical chemistry 29, 823 (1982). http://doi.org/10.1016/0039-9140(82)80252-X
Abstract: This article reviews the different methods used for the determination of selenium species in all types of environmental waters. Basic difficulties are discussed and the efficiency of the methods is explained in view of the sub-μg/1. concentration levels. Special attention is paid to preconcentration steps. Published data on speciation and concentration levels in various water samples are critically reviewed.
Keywords: A1 Journal article; AXES (Antwerp X-ray Analysis, Electrochemistry and Speciation)
DOI: 10.1016/0039-9140(82)80252-X
|
“Deeply coloured and black glass in the Northern provinces of the Roman Empire : differences and similarities in chemical composition before and after AD 150”. van der Linden V, Cosyns P, Schalm O, Cagno S, Nys K, Janssens K, Nowak A, Wagner B, Bulska E, Archaeometry 51, 822 (2009). http://doi.org/10.1111/J.1475-4754.2008.00434.X
Abstract: In this work we attempt to elucidate the chronological and geographical origin of deeply coloured and black glass dating between 100 bc and ad 300 on the basis of their major and trace element compositions. Samples from the western and eastern parts of the Roman Empire were analysed. Analytical data were obtained by means of a scanning electron microscope – energy-dispersive system (SEM-EDS, 63 samples analysed) and laser ablation – inductively coupled plasma – mass spectrometry (LA-ICP-MS, 41 samples analysed). Among the glass fragments analysed, dark brown, dark purple and dark green hues could be distinguished. Only among the dark green fragments could a clear compositional distinction be observed between fragments dated to the periods before and after ad 150. In the early samples (first century bc to first century ad), iron, responsible for the green hue, was introduced by using impure sand containing relatively high amounts of Ti. In contrast, a Ti-poor source of iron was employed, containing Sb, Co and Pb in trace quantities, in order to obtain the dark green colour in the later glass samples. The analytical results obtained by combining SEM-EDS and LA-ICP-MS are therefore consistent with a differentiation of glassmaking recipes, detectable in glass composition, occurring in the period around ad 150.
Keywords: A1 Journal article; History; AXES (Antwerp X-ray Analysis, Electrochemistry and Speciation)
Impact Factor: 1.47
Times cited: 39
DOI: 10.1111/J.1475-4754.2008.00434.X
|
“Fluorite-like phases in the BaF2-BiF3-Bi2O3 system-synthesis, conductivity and defect clustering”. Serov TV, Dombrovski EN, Ardashnikova EI, Dolgikh VA, el Omari M, el Omari M, Abaouz A, Senegas J, Chaban NG, Abakumov AM, Van Tendeloo G, Materials research bulletin 40, 821 (2005). http://doi.org/10.1016/j.materresbull.2005.02.007
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.446
Times cited: 4
DOI: 10.1016/j.materresbull.2005.02.007
|