“Electrodeposition of Ag nanoparticles onto carbon coated TEM grids : a direct approach to study early stages of nucleation”. Ustarroz J, Gupta U, Hubin A, Bals S, Terryn H, Electrochemistry communications 12, 1706 (2010). http://doi.org/10.1016/j.elecom.2010.10.002
Abstract: An innovative experimental approach to study the electrodeposition of small nanoparticles and the early stages of electrochemical nucleation and growth is presented. Carbon coated gold TEM grids are used as substrates for the electrodeposition of silver nanoparticles so that electrochemical data, FESEM, HAADFSTEM and HRTEM data can be acquired from the same sample without the need to remove the particles from the substrate. It is shown that the real distribution of nanoparticles cannot be resolved by FESEM whereas HAADFSTEM analysis confirms that a distribution of small nanoparticles (d ≈ 12 nm) coexist with large nanoparticles corresponding to a bimodal size distribution. Besides, particles grown under the same conditions have been found to present different structures such as monocrystals, polycrystals or aggregates of smaller particles.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 4.396
Times cited: 52
DOI: 10.1016/j.elecom.2010.10.002
|
|
“Effect of the substitution Ba\leftrightarrow Sr on the Ga-1222 superstructure : an electron diffraction study”. Milat O, Van Tendeloo G, Amelinckx S, Wright AJ, Greaves C, Chemistry of materials 7, 1709 (1995). http://doi.org/10.1021/cm00057a021
Abstract: The superstructure of the RE(2)(Sr0.85-xBaxNd0.15)(2)GaCU2O9 compound is found to change significantly with increasing substitution of Ba for Sr. Most of the changes take place in the (Sr0.85-xBaxNd0.15)O-GaO-(Sr0.85-xBaxNd0.15)O lamella, the rest of the basic structure being hardly affected. The structural changes for O less than or equal to x less than or equal to 0.65 are studied by electron diffraction. The arrangement of the chains of GaO4 tetrahedra in the Ba-free compound becomes disordered at x > 0.25. At x similar to 0.65 a rearrangement of the chains in the GaO layers takes place; they form a meandering arrangement, which can be described on a 4a(p) x 2a(p) x c(p) superlattice. This rearrangement is accompanied by ordering of Ba and Sr atoms in the adjacent (ST0.85-xBaxNd0.15)O layers. A simple scheme is proposed to explain the influence of the substitution of Ba for Sr on the linking of the GaO4 tetrahedra and on the geometry of the ''chains'' in the GaO layer.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 8.354
DOI: 10.1021/cm00057a021
|
|
“Novel, oxygen-deficient n=3 RP-member Sr3NdFe3O9-\delta and its topotactic derivatives”. Pelloquin D, Hadermann J, Giot M, Caignaert V, Michel C, Hervieu M, Raveau B, Chemistry of materials 16, 1715 (2004). http://doi.org/10.1021/cm030351n
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 9.466
Times cited: 24
DOI: 10.1021/cm030351n
|
|
“Crystal structure and properties of the Na1-xRu2O4 phase”. Panin RV, Khasanova NR, Abakumov AM, Schnelle W, Hadermann J, Antipov EV, Russian chemical bulletin 55, 1717 (2006). http://doi.org/10.1007/s11172-006-0478-6
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 0.529
Times cited: 5
DOI: 10.1007/s11172-006-0478-6
|
|
“NOxproduction in a rotating gliding arc plasma: potential avenue for sustainable nitrogen fixation”. Jardali F, Van Alphen S, Creel J, Ahmadi Eshtehardi H, Axelsson M, Ingels R, Snyders R, Bogaerts A, Green Chemistry 23, 1748 (2021). http://doi.org/10.1039/D0GC03521A
Abstract: The fast growing world population demands food to survive, and nitrogen-based fertilizers are essential to ensure sufficient food production. Today, fertilizers are mainly produced from non-sustainable fossil fuels<italic>via</italic>the Haber–Bosch process, leading to serious environmental problems. We propose here a novel rotating gliding arc plasma, operating in air, for direct NO<sub>x</sub>production, which can yield high nitrogen content organic fertilizers without pollution associated with ammonia emission. We explored the efficiency of NO<sub>x</sub>production in a wide range of feed gas ratios, and for two arc modes: rotating and steady. When the arc is in steady mode, record-value NO<sub>x</sub>concentrations up to 5.5% are achieved which are 1.7 times higher than the maximum concentration obtained by the rotating arc mode, and with an energy consumption of 2.5 MJ mol<sup>−1</sup>(or<italic>ca.</italic>50 kW h kN<sup>−1</sup>);<italic>i.e.</italic>the lowest value so far achieved by atmospheric pressure plasma reactors. Computer modelling, using a combination of five different complementary approaches, provides a comprehensive picture of NO<sub>x</sub>formation in both arc modes; in particular, the higher NO<sub>x</sub>production in the steady arc mode is due to the combined thermal and vibrationally-promoted Zeldovich mechanisms.
Keywords: A1 Journal article; Engineering sciences. Technology; Plasma Lab for Applications in Sustainability and Medicine – Antwerp (PLASMANT)
Impact Factor: 9.125
DOI: 10.1039/D0GC03521A
|
|
“Power Pulsing To Maximize Vibrational Excitation Efficiency in N2Microwave Plasma: A Combined Experimental and Computational Study”. Van Alphen S, Vermeiren V, Butterworth T, van den Bekerom DCM, van Rooij GJ, Bogaerts A, Journal Of Physical Chemistry C 124, 1765 (2020). http://doi.org/10.1021/acs.jpcc.9b06053
Abstract: Plasma is gaining increasing interest for N2 fixation, being a flexible, electricity-driven alternative for the current conventional fossil fuel-based N2 fixation processes. As the vibrational-induced dissociation of N2 is found to be an energy-efficient pathway to acquire atomic N for the fixation processes, plasmas that are in vibrational nonequilibrium seem promising for this application. However, an important challenge in using nonequilibrium plasmas lies in preventing vibrational−translational (VT) relaxation processes, in which vibrational energy crucial for N2 dissociation is lost to gas heating. We present here both experimental and modeling results for the vibrational and gas temperature in a microsecond-pulsed microwave (MW) N2 plasma, showing how power pulsing can suppress this unfavorable VT relaxation and achieve a maximal vibrational nonequilibrium. By means of our kinetic model, we demonstrate that pulsed plasmas take advantage of the long time scale on which VT processes occur, yielding a very pronounced nonequilibrium over the whole N2 vibrational ladder. Additionally, the effect of pulse parameters like the pulse frequency and pulse width are investigated, demonstrating that the advantage of pulsing to inhibit VT relaxation diminishes for high pulse frequencies (around 7000 kHz) and long power pulses (above 400 μs). Nevertheless, all regimes studied here demonstrate a clear vibrational nonequilibrium while only requiring a limited power-on time, and thus, we may conclude that a pulsed plasma seems very interesting for energyefficient vibrational excitation.
Keywords: A1 Journal article; Engineering sciences. Technology; Plasma Lab for Applications in Sustainability and Medicine – Antwerp (PLASMANT)
Impact Factor: 3.7
DOI: 10.1021/acs.jpcc.9b06053
|
|
“Incommensurate crystallographic shear structures and magnetic properties of the cation deficient perovskite (Sr0.61Pb0.18)(Fe0.75Mn0.25)O2.29”. Malo S, Lepoittevin C, Pérez O, Hébert S, Van Tendeloo G, Hervieu M, Chemistry of materials 22, 1788 (2010). http://doi.org/10.1021/cm903288s
Abstract: The origin of the incommensurability in the crystallographic shear (CS) structure of the ferri-Manganite (Sr0.61Pb0.18)(Fe0.75Mn0.25)O2.29, related to the cation deficient perovskite, has been determined by careful analysis of the boundaries between the two variants constituting the phasoid. High Resolution Electron Microscopy/HAADF-STEM images allow the structural mechanisms to be understood through the presence of structural units common to both phases, responsible of the incommensurate character observed in the electron diffraction patterns. The structural analysis allows for identifying different types of CS phases in the Pb−Sr−Fe(Mn)−O diagram and shows that the stabilization of the six-sided tunnels requires a higher A/B cationic ratio. A description of these phases is proposed through simple structural building units (SBU), based on chains of octahedra bordered by two pyramids. The (Sr0.61Pb0.18)(Fe0.75Mn0.25)O2.29 CS compound exhibits a strong antiferromagnetic and insulating behavior, similar to the Fe-2201 and terrace ferrites but differs by the presence of a hysteresis, with a small coercive field.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 9.466
Times cited: 6
DOI: 10.1021/cm903288s
|
|
“The synthesis and complex anion-vacancy ordered structure of La0.33Sr0.67MnO2.42”. Dixon E, Hadermann J, Hayward MA, Journal of solid state chemistry 184, 1791 (2011). http://doi.org/10.1016/j.jssc.2011.05.026
Abstract: The low-temperature topotactic reduction of La0.33Sr0.67MnO3 with NaH results in the formation of La0.33Sr0.67MnO2.42. A combination of neutron powder and electron diffraction data show that La0.33Sr0.67MnO2.42 adopts a novel anion-vacancy ordered structure with a 6-layer OOTOOT' stacking sequence of the octahedral and tetrahedral layers (Pcmb, a=5.5804(1) Å, b=23.4104(7) Å, c=11.2441(3) Å). A significant concentration of anion vacancies at the anion site, which links neighbouring octahedral layers means that only 25% of the octahedral manganese coordination sites actually have 6-fold MnO6 coordination, the remainder being MnO5 square-based pyramidal sites. The chains of cooperatively twisted apex-linked MnO4 tetrahedra adopt an ordered -LRLR- arrangement within each tetrahedral layer. This is the first published example of a fully refined structure of this type which exhibits such intralayer ordering of the twisted tetrahedral chains. The rationale behind the contrasting structures of La0.33Sr0.67MnO2.42 and other previously reported reduced La1−xSrxMnO3−y phases is discussed.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.299
Times cited: 8
DOI: 10.1016/j.jssc.2011.05.026
|
|
“The role of oxygen at the interface between titanium and carbon nanotubes”. Felten A, Suarez-Martinez I, Ke X, Van Tendeloo G, Ghijsen J, Pireaux J-J, Drube W, Bittencourt C, Ewels CP, ChemPhysChem : a European journal of chemical physics and physical chemistry 10, 1799 (2009). http://doi.org/10.1002/cphc.200900193
Abstract: We study the interface between carbon nanotubes (CNTs) and surface-deposited titanium using electron microscopy and photoemission spectroscopy, supported by density functional calculations. Charge transfer from the Ti atoms to the nanotube and carbide formation is observed at the interface which indicates strong interaction. Nevertheless, the presence of oxygen between the Ti and the CNTs significantly weakens the Ti-CNT interaction. Ti atoms at the surface will preferentially bond to oxygenated sites. Potential sources of oxygen impurities are examined, namely oxygen from any residual atmosphere and pre-existing oxygen impurities on the nanotube surface, which we enhance through oxygen plasma surface pre-treatment. Variation in literature data concerning Ohmic contacts between Ti and carbon nanotubes is explained via sample pre-treatment and differing vacuum levels, and we suggest improved treatment routes for reliable Schottky barrier-free Ti-nanotube contact formation.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 3.075
Times cited: 38
DOI: 10.1002/cphc.200900193
|
|
“Selective nickel-catalyzed conversion of model and lignin-derived phenolic compounds to cyclohexanone-based polymer building blocks”. Schutyser W, Van den Bosch S, Dijkmans J, Turner S, Meledina M, Van Tendeloo G, Debecker DP, Sels BF, Chemsuschem 8, 1805 (2015). http://doi.org/10.1002/cssc.201403375
Abstract: Valorization of lignin is essential for the economics of future lignocellulosic biorefineries. Lignin is converted into novel polymer building blocks through four steps: catalytic hydroprocessing of softwood to form 4-alkylguaiacols, their conversion into 4-alkylcyclohexanols, followed by dehydrogenation to form cyclohexanones, and Baeyer-Villiger oxidation to give caprolactones. The formation of alkylated cyclohexanols is one of the most difficult steps in the series. A liquid-phase process in the presence of nickel on CeO2 or ZrO2 catalysts is demonstrated herein to give the highest cyclohexanol yields. The catalytic reaction with 4-alkylguaiacols follows two parallel pathways with comparable rates: 1) ring hydrogenation with the formation of the corresponding alkylated 2-methoxycyclohexanol, and 2) demethoxylation to form 4-alkylphenol. Although subsequent phenol to cyclohexanol conversion is fast, the rate is limited for the removal of the methoxy group from 2-methoxycyclohexanol. Overall, this last reaction is the rate-limiting step and requires a sufficient temperature (> 250 degrees C) to overcome the energy barrier. Substrate reactivity (with respect to the type of alkyl chain) and details of the catalyst properties (nickel loading and nickel particle size) on the reaction rates are reported in detail for the Ni/CeO2 catalyst. The best Ni/CeO2 catalyst reaches 4-alkylcyclohexanol yields over 80 %, is even able to convert real softwood-derived guaiacol mixtures and can be reused in subsequent experiments. A proof of principle of the projected cascade conversion of lignocellulose feedstock entirely into caprolactone is demonstrated by using Cu/ZrO2 for the dehydrogenation step to produce the resultant cyclohexanones (approximate to 80%) and tin-containing beta zeolite to form 4-alkyl-e-caprolactones in high yields, according to a Baeyer-Villiger-type oxidation with H2O2.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 7.226
Times cited: 71
DOI: 10.1002/cssc.201403375
|
|
“Electron microscopy of carbon nanotubes and related structures”. Bernaerts D, Amelinckx S, Van Tendeloo G, van Landuyt J, The journal of physics and chemistry of solids 58, 1807 (1997). http://doi.org/10.1016/S0022-3697(98)80003-6
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.059
Times cited: 12
DOI: 10.1016/S0022-3697(98)80003-6
|
|
“The electrochemistry of a gelatin modified gold electrode”. De Wael K, Verstraete A, van Vlierberghe S, Dejonghe W, Dubruel P, Adriaens A, International journal of electrochemical science 6, 1810 (2011)
Abstract: This paper discusses the electrochemical behaviour of gelatin coated gold electrodes in physiological pH conditions in a potential window −1.5 till 1.0 V vs SCE by performing cyclic voltammetry. A comparison is made between gelatin A and gelatin B, which have respectively a positive and a negative net charge at physiological pH. The deposition of gelatin onto the gold surface is confirmed by means of attenuated total reflection-infrared (ATR-IR) spectroscopic analyses.
Keywords: A1 Journal article; AXES (Antwerp X-ray Analysis, Electrochemistry and Speciation)
Impact Factor: 1.469
|
|
“The local structure and composition of Ba4Nb2O9-based oxycarbonates”. Bezjak J, Abakumov AM, Recnik A, Krzmanc MM, Jancar B, Suvorov D, Journal of solid state chemistry 183, 1823 (2010). http://doi.org/10.1016/j.jssc.2010.06.003
Abstract: X-ray powder-diffraction(XRD),high-resolutiontransmissionelectronmicroscopy(HRTEM),electron diffraction(ED),infraredspectroscopy(IR),thermogravimetry(TG)andmassspectroscopy(MS)were performedtoinvestigatethecompositionandthecrystalstructureoftetra-bariumdi-niobate(V) Ba4Nb2O9. TheTG,MSandIRstudiesrevealedthatthecompoundisahydratedoxycarbonate.Assuming that thecarbonatestoichiometricallyreplacesoxygen,thecompositionofthelow-temperature a-modification,obtainedbyslowcoolingfrom1100 1C, correspondstoBa4Nb2O8.8(CO3)0.2 0.1H2O, while thequenchedhigh-temperature g-modificationhastheBa4Nb2O8.42(CO3)0.58 0.38H2O composi- tion. The a-phase hasacompositeincommensuratelymodulatedstructureconsistingoftwomutually interacting[Ba]N and the[(Nb,)O3]N subsystems.Thecompositemodulatedcrystalstructureofthe a-phase canbedescribedwiththelatticeparameters a¼10.2688(1) A˚ , c¼2.82426(8) A˚ , q¼0.66774(2)c* and asuperspacegroup R3m(00g)0s. TheHRTEManalysisdemonstratesthenanoscale twinningofthetrigonaldomainsparalleltothe{100}crystallographicplanes.Thetwinningintroduces a one-dimensionaldisorderintothe[(Nb,)O3]N subsystem,whichresultsinanaverage P62c crystal structureofthe a-phase. Possibleplacesforthecarbonategroupinthestructurearediscussedusinga comparisonwithotherhexagonalperovskite-basedoxycarbonates.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.299
Times cited: 10
DOI: 10.1016/j.jssc.2010.06.003
|
|
“A new Bi4Mn1/3W2/3O8Cl Sillén-Aurivillius intergrowth: synthesis and structural characterisation by quantitative transmission electron microscopy”. Avila-Brande D, Otero-Díaz LC, Landa-Cánovas AR, Bals S, Van Tendeloo G, European journal of inorganic chemistry , 1853 (2006). http://doi.org/10.1002/ejic.200501021
Abstract: The synthesis and structural characterisation of a new phase with nominal composition Bi4Mn1/3W2/3O8Cl is presented. Conventional and analytical transmission electron microscopy are used to determine the composition, unit-cell symmetry and space group of the compound, whereas a structural model is deducted by exit-wave reconstruction in the transmission electron microscope. This technique allows the microscope information limit of 1.1 angstrom to be reached and the (light) oxygen atoms in the presence of heavier atoms (Bi, W, Mn) to be imaged. The average structure is refined from Xray powder diffraction data using the Rietveld method yielding an orthorhombic unit cell with lattice parameters a 5.467(4) angstrom, b = 5.466(7) angstrom and c = 14.159(3) angstrom and space group Cm2m, which could be described as a Sillen-Aurivillius intergrowth. ((c) Wiley-VCH Verlag GmbH & Co. KGaA, 69451 Weinheim, Germany, 2006)
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.444
Times cited: 12
DOI: 10.1002/ejic.200501021
|
|
“Influence of axial and radial diffusion processes on the analytical performance of a glow discharge cell”. van Straaten M, Gijbels R, Vertes A, Analytical chemistry 64, 1855 (1992). http://doi.org/10.1021/ac00041a021
Keywords: A1 Journal article; Plasma Lab for Applications in Sustainability and Medicine – Antwerp (PLASMANT)
Impact Factor: 5.636
Times cited: 43
DOI: 10.1021/ac00041a021
|
|
“Establishing uniform acceptance in force biased Monte Carlo simulations”. Neyts EC, Thijsse BJ, Mees MJ, Bal KM, Pourtois G, Journal of chemical theory and computation 8, 1865 (2012). http://doi.org/10.1021/ct2008268
Abstract: Uniform acceptance force biased Monte Carlo (UFMC) simulations have previously been shown to be a powerful tool to simulate atomic scale processes, enabling one to follow the dynamical path during the simulation. In this contribution, we present a simple proof to demonstrate that this uniform acceptance still complies with the condition of detailed balance, on the condition that the characteristic parameter lambda = 1/2 and that the maximum allowed step size is chosen to be sufficiently small. Furthermore, the relation to Metropolis Monte Carlo (MMC) is also established, and it is shown that UFMC reduces to MMC by choosing the characteristic parameter lambda = 0 [Rao, M. et al. Mol. Phys. 1979, 37, 1773]. Finally, a simple example compares the UFMC and MMC methods.
Keywords: A1 Journal article; Plasma Lab for Applications in Sustainability and Medicine – Antwerp (PLASMANT)
Impact Factor: 5.245
Times cited: 20
DOI: 10.1021/ct2008268
|
|
“Crystal structure of Bi6Sr8-xCa3+xO22(-0.5\leq x\leq1.7): a mixed valence bismuth oxide related to perovskite”. Luhrs CC, Molins E, Van Tendeloo G, Beltran-Porter D, Fuertes A, Chemistry of materials 10, 1875 (1998). http://doi.org/10.1021/cm9800377
Abstract: The crystal structure of BiSr8-xCa3+xO22 has been determined by single-crystal X-ray diffraction. This phase is the same as Bi9Sr11Ca5Oy that was previously studied by several authors as a secondary phase in the Bi-Sr-Ca-Cu-O system and coexists in thermodynamic equilibrium with the superconductors Bi2Sr2CuO6 and Bi2Sr2CaCu2O8 It crystallizes in the monoclinic space group P2(1)/c, with cell parameters a 11.037(3) Angstrom, b = 5.971(2) Angstrom, c = 19.703(7) Angstrom, beta = 101.46(3)degrees Z = 2. The structure was solved by direct methods and full-matrix least-squares refinement. It is built up by perovskite-related blocks of composition [Sr8-xBi2Ca3+xO16] that intergrow with double rows [Bi4O6] running along b. The perovskite blocks are formed by groups of five octahedra that are shifted from each other 3/2 root 2a(p) along [110](p) (a(p) being the parameter of the cubic perovskite subcell) in a zigzag configuration and are aligned with this direction parallel to the one forming an angle of 25" with the c axis. In turn, the perovskite blocks [Sr8-xBi2Ca3+xO16] are shifted from each other 1/2 of both a(p) and root 2a(p) along [100](p) and [110](p), respectively. In the double rows, two trivalent bismuth atoms are placed, forming dimeric anion complexes [Bi2O6].(6-).6- The oxygen atoms around bismuth in these dimers are placed in the vertexes of a distorted trigonal bipyramid, with one vacant position that would be occupied by the lone pairs characteristic for the electronic configuration of Bi(III). The B sites in the perovskite blocks are occupied by pentavalent bismuth atoms and calcium atoms; the remaining Sr and Ca ions occupy the A sites of the perovskite blocks with coordination numbers with oxygen ranging from 10 to 12. The mean valence for Bi is +3.67 [33.3% of Bi(V) and 66.7% of Bi(III)]. The oxygen vacancies are located in the boundaries between domains having the two possible configurations of the perovskite subcell as in the anionic superconductor Bi3BaO5.5. The oxidation of Bi6Sr8-xCa3+xO22 at 650 degrees C allows the complete filling of the oxygen vacancies to form the double perovskite (Sr2-xCax)Bi1.4Ca0.6O6 that shows 92.5% of bismuth in +5 oxidation state. The experimental high-resolution electon microscopy image and the electron diffraction pattern of powder samples along the [010]* zone axis are in good agreement with those calculated from the structural model obtained by single-crystal X-ray diffraction. The material is almost free of defects and the occurrence of planar defects is very exceptional.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 9.466
Times cited: 6
DOI: 10.1021/cm9800377
|
|
“Au@MOF-5 and Au/Mox@MOF-5 (M = Zn, Ti, x = 1, 2) : preparation and microstructural characterisation”. Müller M, Turner S, Lebedev OI, Wang Y, Van Tendeloo G, Fischer RA, European journal of inorganic chemistry , 1876 (2011). http://doi.org/10.1002/ejic.201001297
Abstract: The Zn-carboxylate-based porous coordination polymer MOF-5 [Zn4O(bdc)3] and the metal oxide loaded materials ZnO@MOF-5 and TiO2@MOF-5 were loaded in a second step with the precursor [ClAuCO] to yield intermediate materials denoted as [ClAuCO]@MOF-5, [ClAuCO]/ZnO@MOF-5 and [ClAuCO]/TiO2@MOF-5. These composites were decomposed to Au@MOF-5, Au/ZnO@MOF-5 and Au/TiO2@MOF-5 under hydrogen at 100 °C. The nanoparticle-loaded hybrid materials were characterised by powder X-ray diffraction (PXRD), IR spectroscopy, X-ray photoelectron spectroscopy (XPS) and N2 sorption measurements, which reveal an intact MOF-5 structure that maintains a high specific surface area. For Au@MOF-5, crystalline Au nanoparticles were distributed over the MOF matrix in a homogeneous fashion with a size of ca. 13 nm, evidenced by high resolution transmission electron microscopy. In the case of Au/ZnO@MOF-5, the Au and metal oxide particles of a few nm in size were coexistent in a given volume of the MOF-5 matrix and were not separated in different crystalline MOF particles. For the TiO2 loaded materials the oxide is preferentially located near the outer surface of the MOF particles, leading to an increase of larger exterior Au particles in comparison to very small interior Au particles as observed for the other materials. Au@MOF-5, Au/ZnO@MOF-5 and Au/TiO2@MOF-5 were tested in liquid-phase oxidation of alcohols. Preliminary results show a high activity for the Au loaded materials in this reaction. This observation is attributed to the microstructure of the composites with very small Au particles distributed homogeneously over the MOF matrix.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.444
Times cited: 75
DOI: 10.1002/ejic.201001297
|
|
“The design of magneto-plasmonic nanostructures formed by magnetic Prussian Blue-type nanocrystals decorated with Au nanoparticles”. Sanchis-Gual R, Susic I, Torres-Cavanillas R, Arenas-Esteban D, Bals S, Mallah T, Coronado-Puchau M, Coronado E, Chemical Communications 57, 1903 (2021). http://doi.org/10.1039/D0CC08034A
Abstract: We have developed a general protocol for the preparation of hybrid nanostructures formed by nanoparticles (NPs) of molecule-based magnets based on Prussian Blue Analogues (PBAs) decorated with plasmonic Au NPs of different shapes. By adjusting the pH, Au NPs can be attached preferentially along the edges of the PBA or randomly on the surface. The protocol allows tuning the plasmonic properties of the hybrids in the whole visible spectrum.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 6.319
Times cited: 5
DOI: 10.1039/D0CC08034A
|
|
“Atomic resolution coordination mapping in Ca2FeCoO5 brownmillerite by spatially resolved electron energy-loss spectroscopy”. Turner S, Verbeeck J, Ramezanipour F, Greedan JE, Van Tendeloo G, Botton GA, Chemistry of materials 24, 1904 (2012). http://doi.org/10.1021/cm300640g
Abstract: Using a combination of high-angle annular dark field scanning transmission electron microscopy and atomically resolved electron energy-loss spectroscopy at high energy resolution in an aberration-corrected electron microscope, we demonstrate the capability of coordination mapping in complex oxides. Brownmillerite compound Ca2FeCoO5, consisting of repetitive octahedral and tetrahedral coordination layers with Fe and Co in a fixed 3+ valency, is selected to demonstrate the principle of atomic resolution coordination mapping. Analysis of the Co-L2,3 and the Fe-L2,3 edges shows small variations in the fine structure that can be specifically attributed to Co/Fe in tetrahedral or in octahedral coordination. Using internal reference spectra, we show that the coordination of the Fe and Co atoms in the compound can be mapped at atomic resolution.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 9.466
Times cited: 33
DOI: 10.1021/cm300640g
|
|
“Monitoring the laccase reaction of vanillin and poplar hydrolysate”. Sóti V, Jacquet N, Apers S, Richel A, Lenaerts S, Cornet I, Journal of chemical technology and biotechnology 91, 1914 (2016). http://doi.org/10.1002/JCTB.4789
Abstract: BACKGROUND Laccase is an intensively researched enzyme for industrial use. Except for decolorisation measurements, HPLC analysis is the conventional method for monitoring the phenolic removal during laccase enzyme reaction. This paper reports an investigation of the continuous UV absorbance follow-up of the laccase reaction with steam pretreated poplar hydrolysate. RESULTS Vanillin was used as a model substrate and lignocellulose xylose rich fraction (XRF) as a biologically complex substrate for laccase detoxification. The reaction was followed by HPLC-UV as well as by UV spectrometric measurements. Results suggest that the reaction can be successfully monitored by measuring the change of UV absorbance at 280 nm, without previous compound separation. In case of XRF experiments the spectrophotometric follow-up is especially useful, as HPLC analysis takes a long time and provides less information than in case of single substrates. The method seems to be suitable for optimization and process control. CONCLUSION The obtained results can help to construct a fast, easy and straightforward monitoring system for laccase-phenolic substrate reactions.
Keywords: A1 Journal article; Engineering sciences. Technology; Sustainable Energy, Air and Water Technology (DuEL); Biochemical Wastewater Valorization & Engineering (BioWaVE)
Impact Factor: 3.135
Times cited: 3
DOI: 10.1002/JCTB.4789
|
|
“Doping anatase TiO2with group V-b and VI-b transition metal atoms: a hybrid functional first-principles study”. Matsubara M, Saniz R, Partoens B, Lamoen D, Physical chemistry, chemical physics 19, 1945 (2017). http://doi.org/10.1039/C6CP06882K
Abstract: We investigate the role of transition metal atoms of group V-b (V, Nb, Ta) and VI-b (Cr, Mo, W) as n- or p-type dopants in anatase TiO$_2$ using thermodynamic
principles and density functional theory with the Heyd-Scuseria-Ernzerhof HSE06 hybrid functional. The HSE06 functional provides a realistic value for the band gap, which ensures a correct classification of dopants as shallow or deep donors or acceptors. Defect formation energies and thermodynamic transition levels are calculated taking into account the constraints imposed by the stability of TiO$_2$ and the solubility limit of the impurities.
Nb, Ta, W and Mo are identified as shallow donors. Although W provides two electrons, Nb and Ta show a considerable lower formation energy, in particular under O-poor conditions. Mo donates in principle one electron, but under specific conditions can turn into a double donor. V impurities are deep donors and Cr
shows up as an amphoteric defect, thereby acting as an electron trapping center in n-type TiO$_2$ especially under O-rich conditions. A comparison with the available experimental data yields excellent agreement.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT); Condensed Matter Theory (CMT)
Impact Factor: 4.123
Times cited: 19
DOI: 10.1039/C6CP06882K
|
|
“Study on the impregnation of archaeological waterlogged wood with consolidation treatments using synchrotron radiation microtomography”. Bugani S, Modugno F, Lucejko JJ, Giachi G, Cagno S, Cloetens P, Janssens K, Morselli L, Analytical and bioanalytical chemistry 395, 1977 (2009). http://doi.org/10.1007/S00216-009-3101-5
Abstract: In favourable conditions of low temperature and low oxygen concentration, archaeological waterlogged wooden artefacts, such as shipwrecks, can survive with a good state of preservation. Nevertheless, anaerobic bacteria can considerably degrade waterlogged wooden objects with a significant loss in polysaccharidic components. Due to these decay processes, wood porosity and water content increase under ageing. In such conditions, the conservation treatments of archaeological wooden artefacts often involve the replacement of water with substances which fill the cavities and help to prevent collapse and stress during drying. The treatments are very often expensive and technically difficult, and their effectiveness very much depends on the chemical and physical characteristics of the substances used for impregnation. Also important are the degree of cavity-filling, penetration depth and distribution in the structure of the wood. In this study, the distribution in wood cavities of some mixtures based on polyethylene glycols and colophony, used for the conservation of waterlogged archaeological wood, was investigated using synchrotron radiation X-ray computed microtomography (SR-A mu CT). This non-destructive imaging technique was useful for the study of the degraded waterlogged wood and enabled us to visualise the morphology of the wood and the distribution of the materials used in the wood treatments. The study has shown how deposition is strictly related to the dimension of the wooden cavities. The work is currently proceeding with the comparison of synchrotron observations with the data of the solutions viscosity and with those of the properties imparted to the wood by the treatments.
Keywords: A1 Journal article; AXES (Antwerp X-ray Analysis, Electrochemistry and Speciation)
Impact Factor: 3.431
Times cited: 30
DOI: 10.1007/S00216-009-3101-5
|
|
“Tetragonal Cs1.17In0.81Cl3 : a charge-ordered indium halide perovskite derivative”. Tan X, Stephens PW, Hendrickx M, Hadermann J, Segre CU, Croft M, Kang C-J, Deng Z, Lapidus SH, Kim SW, Jin C, Kotliar G, Greenblatt M, Chemistry of materials 31, 1981 (2019). http://doi.org/10.1021/ACS.CHEMMATER.8B04771
Abstract: Polycrystalline samples of Cs1.17In0.81Cl3 were prepared by annealing a mixture of CsCl, InCl, and InCl3, stoichiometric for the targeted CsInCl3. Synchrotron powder X-ray diffraction refinement and chemical analysis by energy dispersive X-ray indicated that Cs1.17In0.81Cl3, a tetragonal distorted perovskite derivative (I4/m), is the thermodynamically stable product. The refined unit cell parameters and space group were confirmed by electron diffraction. In the tetragonal structure, In+ and In3+ are located in four different crystallographic sites, consistent with their corresponding bond lengths. In1, In2, and In3 are octahedrally coordinated, whereas In4 is at the center of a pentagonal bipyramid of Cl because of the noncooperative octahedral tilting of In4Cl6. The charged-ordered In+ and In3+ were also confirmed by X-ray absorption and Raman spectroscopy. Cs1.17In0.81Cl3 is the first example of an inorganic halide double perovskite derivative with charged-ordered In+ and In3+. Band structure and optical conductivity calculations were carried out with both generalized gradient approximation (GGA) and modified Becke-Johnson (mBJ) approach; the GGA calculations estimated the band gap and optical band gap to be 2.27 eV and 2.4 eV, respectively. The large and indirect band gap suggests that Cs1.17In0.81Cl3 is not a good candidate for photovoltaic application.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 9.466
Times cited: 6
DOI: 10.1021/ACS.CHEMMATER.8B04771
|
|
“Tuning the pore size of ink-bottle mesopores by atomic layer deposition”. Dendooven J, Goris B, Devloo-Casier K, Levrau E, Biermans E, Baklanov MR, Ludwig KF, van der Voort P, Bals S, Detavernier C, Chemistry of materials 24, 1992 (2012). http://doi.org/10.1021/cm203754a
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 9.466
Times cited: 52
DOI: 10.1021/cm203754a
|
|
“Comment on ALaMn2O6-y (A = K, Rb): novel ferromagnetic manganites exhibiting negative giant magnetoresistance”. Hadermann J, Abakumov AM, Van Rompaey S, Mankevich AS, Korsakov IE, Chemistry of materials 21, 2000 (2009). http://doi.org/10.1021/cm900298a
Keywords: Editorial; Electron microscopy for materials research (EMAT)
Impact Factor: 9.466
Times cited: 4
DOI: 10.1021/cm900298a
|
|
“Synthesis, structure, and electrochemical properties of k-based sulfates K2M2(SO4)3) with M = Fe and Cu”. Lander L, Rousse G, Batuk D, Colin CV, Dalla Corte DA, Tarascon J-M, Inorganic chemistry 56, 2013 (2017). http://doi.org/10.1021/ACS.INORGCHEM.6B02526
Abstract: Stabilizing new host structures through potassium extraction from K-based polyanionic materials has been proven to be an interesting approach to develop new Li+/Na+ insertion materials. Pursuing the same trend, we here report the feasibility of preparing langbeinite “Fe-2(SO4)(3)” via electrochemical and chemical oxidation of K2Fe2(SO4)(3). Additionally, we succeeded in stabilizing a new K2Cu2(SO4)(3) phase via a solid-state synthesis approach. This novel compound crystallizes in a complex orthorhombic structure that differs from that of langbeinite as deduced from synchrotron X-ray and neutron powder diffraction. Electrochemically, the performance of this new phase is limited, which we explain in terms of sluggish diffusion kinetics. We further show that K2Cu2(SO4)(3) decomposes into K2Cu3O(SO4)(3) on heating, and we report for the first time the synthesis of fedotovite K2Cu3O(SO4)(3). Finally, the fundamental attractiveness of these S = 1/2 systems for physicists is examined by neutron magnetic diffraction, which reveals the absence of a long-range ordering of Cu2+ magnetic moments down to 1.5 K.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 4.857
Times cited: 13
DOI: 10.1021/ACS.INORGCHEM.6B02526
|
|
“Tuning electronic and magnetic properties of monolayer \alpha-RuCl3 by in-plane strain”. Iyikanat F, Yagmurcukardes M, Senger RT, Sahin H, Journal of materials chemistry C : materials for optical and electronic devices 6, 2019 (2018). http://doi.org/10.1039/C7TC05266A
Abstract: By employing density functional theory-based methods, the structural, vibrational, electronic, and magnetic properties of monolayer -RuCl3 were investigated. It was demonstrated that ferromagnetic (FM) and zigzag-antiferromagnetic (ZZ-AFM) spin orders in the material have very close total energies with the latter being the ground state. We found that each Ru atom possesses a magnetic moment of 0.9 (B) and the material exhibits strong magnetic anisotropy. While both phases exhibit indirect gaps, the FM phase is a magnetic semiconductor and the ZZ-AFM phase is a non-magnetic semiconductor. The structural stability of the material was confirmed by phonon calculations. Moreover, dynamical analysis revealed that the magnetic order in the material can be monitored via Raman measurements of the crystal structure. In addition, the magnetic ground state of the material changes from ZZ-AFM to FM upon certain applied strains. Valence and conduction band-edges of the material vary considerably under in-plane strains. Owing to the stable lattice structure and unique and controllable magnetic properties, monolayer -RuCl3 is a promising material in nanoscale device applications.
Keywords: A1 Journal article; Condensed Matter Theory (CMT)
Impact Factor: 5.256
Times cited: 16
DOI: 10.1039/C7TC05266A
|
|
“ELNES study of carbon K-edge spectra of plasma deposited carbon films”. Hamon A-L, Verbeeck J, Schryvers D, Benedikt J, van den Sanden RMCM, Journal of materials chemistry 14, 2030 (2004). http://doi.org/10.1039/b406468m
Abstract: Electron energy loss spectroscopy was used to investigate the bonding of plasma deposited carbon films. The experimental conditions include the use of a specific collection angle for which the shape of the spectra is free of the orientation dependency usually encountered in graphite due to its anisotropic structure. The first quantification process of the energy loss near-edge structure was performed by a standard fit of the collected spectrum, corrected for background and multiple scattering, with three Gaussian functions followed by a comparison with the graphite spectrum obtained under equivalent experimental conditions. In a second approach a fitting model directly incorporating the background subtraction and multiple scattering removal was applied. The final numerical results are interpreted in view of the deposition conditions of the films and the actual fitting procedure with the related choice of parameters.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 6.626
Times cited: 61
DOI: 10.1039/b406468m
|
|
“The synthesis and thermodynamic properties of strontium fluoromanganite Sr2.5Mn6O12.5-\deltaF2”. Kovba ML, Skolis YY, Abakumov AM, Hadermann J, Sukhushina IS, Russian journal of physical chemistry A 84, 2033 (2010). http://doi.org/10.1134/S0036024410120046
Abstract: The existence of the [SrF(0.8)O(0.1)](2.5)[Mn(6)O(12)] = Sr(2.5)Mn(6)O(12.5 – delta)F(2) compound was established in the SrO-Mn(2)O(3)-SrF(2) system at 900A degrees C and p(O(2)) = 1 atm. The crystal structure of strontium fluoromanganite was determined from the X-ray powder diffraction data, electron diffraction, and high-resolution electron microscopy. It can be described in the monoclynic system with four Miller hklm indices: hklm: H = h a* + k b* + l c (1) (*) + m q (1), q (1), q (1) = c (2) (*) = gamma c (1) (*) , gamma a parts per thousand 0.632, a a parts per thousand a a parts per thousand 9.72 , b a parts per thousand 9.55 , c (1) a parts per thousand 2.84 , c (2) a parts per thousand 4.49 , monoclinic angle gamma a parts per thousand 95.6A degrees. The electromotive force method with a solid fluorine ion electrolyte was used to refine the composition of fluoromanganite and determine the thermodynamic functions of its formation from phases neighboring in the phase diagram (SrMn(3)O(6), Mn(2)O(3), SrF(2), and oxygen), Delta GA degrees, kJ/mol = -(111.7 +/- 1.9) + (89.5 +/- 1.5) x 10(-3) T.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 0.581
Times cited: 1
DOI: 10.1134/S0036024410120046
|