Abstract: Oxygen deficient perovskites Sr0.75Y0.25Co1-xMnxO3-y, x=0.5 and 0.75, were prepared by using the citrate route at 1373-1573 K for 48 h. The cubic Pm-3m perovskite structure for x=0.5 was confirmed by electron diffraction study and refined using neutron powder diffraction (NPD) data. For x=0.75, the superstructure corresponding to a=root 2 x a(per), b=2 x a(per), c=root 2 x a(per) (a(0)b(-)b(-) tilt system, space group Imma) was revealed by electron diffraction. The solid solution Sr0.75-xCaxY0.25Co0.25Mn0.75O3-y, 0.1 <= x <= 0.6 and compound Ca0.75Y0.25Mn0.85Co0.15O2.92 were prepared in air at 1573 K for 48 h. The crystal structure of Ca0.75Y0.25Mn0.85Co0.15O2.92 was refined using NPD data (S.G. Pnma, a=5.36595(4), b=7.5091(6), c=5.2992(4) angstrom, R-p=0.057, R-wp=0.056, chi(2)=4.26). High-temperature thermal expansion properties of the prepared compounds were studied in air using both dilatometry and high-temperature X-ray powder diffraction data (HTXRPD). They expanding non-linearly at 298-1073 K due to the loss of oxygen at high temperatures. Calculated average thermal expansion coefficients (TECs) for Sr0.75Y0.25Co1-xMnxO3-y, x=0.5, 0.75 and Ca0.75Y0.25Mn0.85Co0.15O2.92(1) are 15.5, 15.1, and 13.8 ppm K-1, respectively. Anisotropy of the thermal expansion along different unit cell axes was observed for Sr0.15Ca0.6Y0.25Co0.25Mn0.75O3-y, and Ca0.75Y0.25Mn0.85Co0.15O2.92. Conductivity of Sr0.75Y0.25Co1-xMnxO3-y, x=0.5 and 0.75 increases with the temperature reaching 110 S/cm for x=0.5 and 44 S/cm for x=0.75 at 1173 K. Samples of Sr0.75-xCaxY0.25Co0.25Mn0.75O3-y, 0.1 <= y <= 0.6 were found to be n-type conductors at room temperature with the similar temperature dependence of the conductivity and demonstrated the increase of the sigma value from similar to 1 to similar to 50 S/cm as the temperature increases from 300 to 1173 K. Their conductivity is described in terms of the small polaron charge transport with the activation energy (E-p) increasing from 340 to 430 meV with an increase of the calcium content from x=0 to x=0.6. (C) 2012 Elsevier Inc. All rights reserved.

Abstract: Porous solids with organized multiple porosity are of scientific and technological importance for broadening the application range from traditional areas of catalysis and adsorption/separation to drug release and biomedical imaging. Synthesis of crystalline porous materials offering a network of uniform micro- and mesopores remains a major scientific challenge. One strategy is based on variation of synthesis parameters of microporous networks, such as, for example, zeolites or metal organic frameworks (MOFs). Here, we show the rational development of an hierarchical variant of the microporous cubic Cu-3(BTC)(2) (BTC = 1,3,5-benzenetricarboxylate) HKUST-1 MOF having strictly repetitive S inn wide mesopores separated by uniform microporous walls in a single crystal structure. This new material coined COK-15 (COK = Centrum voor Oppervlaktechemie en Katalyse) was synthesized via a dual-templating approach. Stability was enhanced by Keggin type phosphotungstate (HPW) systematically occluded in the cavities constituting the walls between the mesopores.

Abstract: Pb cations in PbS quantum rods made from CdS quantum rods by successive complete cationic exchange reactions are partially re-exchanged for Cd cations. Using STEM-HAADF, we show that this leads to the formation of unique multiple dot-in-rod PbS/CdS heteronanostructures, with a photoluminescence quantum yield of 4555%. We argue that the formation of multiple dot-in-rods is related to the initial polycrystallinity of the PbS quantum rods, where each PbS crystallite transforms in a separate PbS/CdS dot-in-dot. Effective mass modeling indicates that electronic coupling between the different PbS conduction band states is feasible for the multiple dot-in-rod geometries obtained, while the hole states remain largely uncoupled.

Abstract: We report the direct formation of multiwalled carbon nanotubes (MWNT) by ultrasonication of graphite in dimethylformamide (DMF) upon addition of ferrocene aldehyde (Fc-CHO). The tubular structures appear exclusively at the edges of graphene layers and contain Fe clusters. Pc in conjunction with benzyl aldehyde, or other Fc derivatives, does not induce formation of NT. Higher amounts of Fc-CHO added to the dispersion do not increase significantly MWNT formation. Increasing the temperature reduces the amount of formation of MWNTs and shows the key role of ultrasound-induced cavitation energy. It is concluded that Fc-CHO first reduces the concentration of radical reactive species that slice graphene into small moieties, localizes itself at the edges of graphene, templates the rolling up of a sheet to form a nanoscroll, where it remains trapped, and finally accepts and donates unpaired electron to the graphene edges and converts the less stable scroll into a MWNT. This new methodology matches the long held notion that CNTs are rolled up graphene layers. The proposed mechanism is general and will lead to control the production of carbon nanostructures by simple ultrasonication treatments.

Abstract: In this work, we have studied the TMA/H(2)O (TMA Al(CH(3))(3)) atomic layer deposition (ALD) of Al(2)O(3) on hydroxyl (OH) and thiol (SH) terminated semiconductor substrates. Total reflection x-ray fluorescence reveals a complex growth-per-cycle evolution during the early ALD reaction cycles. OH and SH terminated surfaces demonstrate growth inhibition from the second reaction cycle on. Theoretical calculations, based on density functional theory, are performed on cluster models to investigate the first TMA/H(2)O reaction cycle. Based on the theoretical results, we discuss possible mechanisms for the growth inhibition from the second reaction cycle on. In addition, our calculations show that AlCH(3) groups are hydrolyzed by a H(2)O molecule adsorbed on a neighboring Al atom, independent of the type of backbonds (Si-O, Ge-O, or Ge-S) of AlCH(3). The coordination of Al remains four-fold after the first TMA/H(2)O reaction cycle. (C) 2012 American Vacuum Society. [DOI: 10.1116/1.3664090]

Abstract: It is demonstrated that glycogen as a biodegradable and inexpensive material coming from renewable resources can be used as a carrier for the construction of in vivo imaging nanoagents. The model system considered is composed of glycogen modified with gadolinium and fluorescent labels. Systematic studies of properties of these nanocarriers by a variety of physical methods and results of in vivo tests of biodegradability are reported. This represents, to the authors' best knowledge, the first such use of glycogen.

Abstract: We have prepared tungsten oxide films decorated with gold particles on Si substrates by aerosol assisted chemical vapor deposition (AACVD) and characterized them using scanning electron microscopy (SEM), transmission electron microscopy (TEM) and X-ray photoelectron spectroscopy (XPS). SEM shows that the films are composed of needle-like structures and TEM shows that both the needles and the gold particles are crystalline. XPS indicates the presence of oxygen vacancies, i.e. the films are WO3−x, and hence the deposited material is composed of semiconducting nanostructures and that the interaction between the gold particles and the WO3 needles surface is weak. The synthesis of semiconducting tungsten oxide nanostructures decorated with metal particles represents an important step towards the development of sensing devices with optimal properties.

Abstract: The aim of this paper is to gain understanding of the quasi-static, large strain deformation behavior at room-temperature of high-purity alpha-Ti with an initial split-basal texture. Simple shear tests were conducted along different directions in order to quantify the material's anisotropy and hardening evolution for different strain paths such as monotonic, Bauschinger, and cyclic loadings. The stress-strain curves indicate that the material displays strong anisotropy in the flow behavior. In order to capture the link between microstructure evolution (occurrence of twinning, grain size evolution, etc.) and the macroscopic response, a thoroughly detailed multi-scale characterization using scanning electron microscope (SEM) observations and electron backscattered diffraction (EBSD) analysis was also conducted. Specifically, EBSD analyses indicate that the twin activity and grain fragmentation are responsible for the observed difference between the macroscopic hardening rates corresponding to different directions and loading paths. (C) 2011 Elsevier B.V. All rights reserved.

Abstract: The Plantin-Moretus Museum/Print Room in Antwerp, Belgium, gathers one of the most precious collections of typographical material and old printed books in the world. Rich decorations of this former printing-house and the history of the building itself underline its uniqueness. The cultural heritage (CH) objects collected in the museum, in particular books and manuscripts are vulnerable to the atmospheric pollution and can be irreversibly damaged. To assess the air quality inside the museum, four consecutive sampling campaigns were performed in each season of the year. The gas monitoring of nitrogen dioxide (NO2), sulphur dioxide (SO2) and ozone (O3) was carried out outside the building, in galleries and in showcases by means of using diffusive samplers. The particulate matter (PM) was collected in bulk form and as single particles and then analysed with use of energy dispersive X-ray fluorescence (EDXRF) and electron probe micro-analyser (EPMA), respectively. The museum complex turned out to show good protection against gaseous pollutants, especially SO2 and O3. The concentrations of these pollutants were significantly reduced inside the building in comparison to the outdoor ones. Similar protective character of the museum complex was established in case of the coarse fraction of PM; however with some limitations. Single particle analysis showed that the relative abundance of carbon-rich particles inside the museum was greater than outside. Moreover, these particles contributed more to the fine fraction of PM than to the coarse fraction. Therefore, for better preservation of cultural heritage, special attention should be paid to the small particles and their distribution within the museum.

Abstract: Statistical parameter estimation theory is proposed as a method to quantify electron microscopy images. It aims at obtaining precise and accurate values for the unknown structure parameters including, for example, atomic column positions and types. In this theory, observations are purely considered as data planes, from which structure parameters have to be determined using a parametric model describing the images. The method enables us to measure positions of atomic columns with a precision of the order of a few picometers even though the resolution of the electron microscope is one or two orders of magnitude larger. Moreover, small differences in averaged atomic number, which cannot be distinguished visually, can be quantified using high-angle annular dark field scanning transmission electron microscopy images. Finally, it is shown how to optimize the experimental design so as to attain the highest precision. As an example, the optimization of the probe size for nanoparticle radius measurements is considered. It is also shown how to quantitatively balance signal-to-noise ratio and resolution by adjusting the probe size.

Abstract: The effect of thermal treatment and mechanical stress on the structural and photocatalytic properties of eight different (synthetic and commercial) photocatalysts has been thoroughly investigated. Different mesoporous Ti-based materials were prepared via surfactant based synthesis routes (e.g. Pluronic 123, CTMABr = Cetyltrimethylammonium bromide) or via template-free synthesis routes (e.g. trititanate nanotubes). Also, the stabilizing effect of the NaOH/NH4OH post-treatment on the templated mesoporous materials and their photocatalytic activity was investigated. Furthermore, the thermal and mechanical properties of commercially available titanium dioxides such as P25 Evonik® and Millenium PC500® were studied. The various photocatalysts were analyzed with N2-sorption, X-ray diffraction (XRD), high resolution transmission electron microscopy (HR-TEM), differential scanning calorimetry (DSC) and thermal gravimetric analysis (TGA) to obtain information concerning the specific surface area, pore volume, crystal structure, morphology, phase transitions, etc. In general, results show that the NaOH post-treatment leads to an increased control of the crystallization process during calcination resulting in a higher thermal stability, but at the same time diminishes the photocatalytic activity. Mesoporous materials in which pre-synthesized nanoparticles are used as titania source have the best mechanical stability whereas the mechanical stability of the nanotubes is the most limited. At increased temperatures and pressures, the tested commercial titanium dioxides lose their superior photocatalytic activity caused by a decreased accessibility of the active sites. The observed changes in adsorption capacities and photocatalytic activities cannot be assigned to one single phenomenon. In this respect, it shows the need to define a general/standard method to compare different photocatalysts. Furthermore, it is shown that the photocatalytic properties do not necessarily deteriorate under thermal stress, but can be improved due to crystallization, even though the initial material is (partially) destroyed. It is shown that the usefulness of a specific type of photocatalyst strongly depends on the application and the temperature/pressure to which it needs to resist.

Abstract: Rational synthesis of nanowires via the vaporliquidsolid (VLS) mechanism with compositional and structural controls is vitally important for fabricating functional nanodevices from bottom up. Here, we show that branched indium tin oxide nanowires can be in situ seeded in vapor transport growth using tailored AuCu alloys as catalyst. Furthermore, we demonstrate that VLS synthesis gives unprecedented freedom to navigate the ternary InSnO phase diagram, and a rare and bulk-unstable cubic phase can be selectively stabilized in nanowires. The stabilized cubic fluorite phase possesses an unusual almost equimolar concentration of In and Sn, forming a defect-free epitaxial interface with the conventional bixbyite phase of tin-doped indium oxide that is the most employed transparent conducting oxide. This rational methodology of selecting phases and making abrupt axial heterojunctions in nanowires presents advantages over the conventional synthesis routes, promising novel composition-modulated nanomaterials.

Abstract: The electronic properties of two-dimensional honeycomb structures of molybdenum disulfide (MoS(2)) subjected to biaxial strain have been investigated using first-principles calculations based on density functional theory. On applying compressive or tensile bi-axial strain on bi-layer and mono-layer MoS(2), the electronic properties are predicted to change from semiconducting to metallic. These changes present very interesting possibilities for engineering the electronic properties of two-dimensional structures of MoS(2).

Abstract: Using template-containing silica microspheres as a precursor, novel ordered mesoporous silica nanoparticles with a narrow pore size distribution and high crystallinity have been synthesized by various hydrothermal merging processes. Several architectures like chains, dumbbells, triangles, squares and flowers have been discovered. The linking mechanisms of these interacting silica spheres leading to the formation of ordered nano-structures are studied by HRTEM, HAADF-STEM and electron tomography and a plausible model is presented for several merging processes.

Abstract: The fabrication and integration of low-resistance carbon nanotubes (CNTs) for interconnects in future integrated circuits requires characterization techniques providing structural and electrical information at the nanometer scale. In this paper we present a slice-and-view approach based on electrical atomic force microscopy. Material removal achieved by successive scanning using doped ultra-sharp full-diamond probes, manufactured in-house, enables us to acquire two-dimensional (2D) resistance maps originating from different depths (equivalently different CNT lengths) on CNT-based interconnects. Stacking and interpolating these 2D resistance maps results in a three-dimensional (3D) representation (tomogram). This allows insight from a structural (e.g. size, density, distribution, straightness) and electrical point of view simultaneously. By extracting the resistance evolution over the length of an individual CNT we derive quantitative information about the resistivity and the contact resistance between the CNT and bottom electrode.