“Novel method to synthesize highly ordered ethane-bridged PMOs under mild acidic conditions : taking advantages of phosphoric acid”. Lin F, Meng X, Kukueva E, Kus M, Mertens M, Bals S, Van Doorslaer S, Cool P, Microporous and mesoporous materials: zeolites, clays, carbons and related materials 207, 61 (2015). http://doi.org/10.1016/j.micromeso.2014.12.029
Abstract: Highly ordered SBA-15-type ethane-bridged PMOs have been obtained by employing H3PO4 as acid to tune the pH in the presence of copolymer surfactant P123. The effects of the acidity and the addition of inorganic salt on the formation of the mesostructure are investigated. It is found that, compared with HCl, the polyprotic weak acid H3PO4 is preferable for the synthesis of highly ordered SBA-15-type ethane-bridged PMOs with larger pore size and surface areas under mild acidic conditions. Moreover, taking the advantages of the mild acidic condition, vanadium-containing SBA-15-type ethane-bridged PMOs were successfully prepared through a direct synthesis approach. The XRD, N2-sorption, UVVis and CW-EPR studies of the V-PMO show that part of the vanadium species are present in polymeric (VOV)n clusters, while part of the vanadium centers are well-dispersed and immobilized on the inner surface of the mesopores.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT); Laboratory of adsorption and catalysis (LADCA)
Impact Factor: 3.615
Times cited: 5
DOI: 10.1016/j.micromeso.2014.12.029
|
|
|
“Improvement in the coating homogeneity in electrosynthesized Rh structured catalysts for the partial oxidation of methane”. Benito P, Monti M, de Nolf W, Nuyts G, Janssens K, et al, Catalysis today 246, 154 (2015). http://doi.org/10.1016/J.CATTOD.2014.10.003
Abstract: The precipitation of Rh/Mg/Al and Rh/Al hydroxides on the surface of FeCrAlloy foams by a base electrogeneration method was investigated to improve the properties of the deposited film (homogeneity and composition) and therefore the performances of the structured catalysts, obtained by calcination, in the Catalytic Partial Oxidation of CH4 to syngas. The work focussed on decreasing current gradients within open-cell foam cylinders by increasing the number of electrical contacts from 1 to 3 points to promote a more homogeneous precipitation of the hydroxides. Electrochemical and catalytic tests as well as SEM/EDS and mu-XRFIXRD analyses allowed to correlate the effect of the number of electrical contact points with materials properties. Lastly, syntheses were performed on Pt plates to study the effect of the electrical behaviour and shape of the support on the composition of the film. A more homogeneous coating of the foam surface was achieved by adopting a configuration with 3 contact points since the reduction of nitrates and water molecules that generates the basic media in the vicinity of the support was enhanced. Layer thicknesses up to 5-15 mu m were deposited; however, the sequential precipitation of a film with composition closer to the expected one and a layer enriched in Al and Rh (outer layer) was not avoided. The improvement in the coating gave rise to enhanced performances for a sample prepared at -1.1 V for 3000 s. Contrarily, the low adherence of the outer layer in a sample prepared at -1.2 V for 2000 s during both calcination and catalytic tests may be responsible of the unexpected decrease in catalytic performances. The same sequential precipitation was observed by performing the syntheses on Pt plates, showing that the electrical nature the support did not play a key role on this phenomenon. (C) 2014 Elsevier B.V. All rights reserved.
Keywords: A1 Journal article; AXES (Antwerp X-ray Analysis, Electrochemistry and Speciation)
Impact Factor: 4.636
Times cited: 14
DOI: 10.1016/J.CATTOD.2014.10.003
|
|
|
“Enhanced stability of hydrogen atoms at the graphene/graphane interface of nanoribbons”. Ao ZM, Hernández-Nieves AD, Peeters FM, Li S, Applied physics letters 97, 233109 (2010). http://doi.org/10.1063/1.3525377
Abstract: The thermal stability of graphene/graphane nanoribbons (GGNRs) is investigated using density functional theory. It is found that the energy barriers for the diffusion of hydrogen atoms on the zigzag and armchair interfaces of GGNRs are 2.86 and 3.17 eV, respectively, while the diffusion barrier of an isolated H atom on pristine graphene was only ∼ 0.3 eV. These results unambiguously demonstrate that the thermal stability of GGNRs can be enhanced significantly by increasing the hydrogen diffusion barriers through graphene/graphane interface engineering. This may provide new insights for viable applications of GGNRs.
Keywords: A1 Journal article; Condensed Matter Theory (CMT)
Impact Factor: 3.411
Times cited: 43
DOI: 10.1063/1.3525377
|
|
|
“Structure solution and refinement of metal-ion battery cathode materials using electron diffraction tomography”. Hadermann J, Abakumov AM, And Materials 75, 485 (2019). http://doi.org/10.1107/S2052520619008291
Abstract: The applicability of electron diffraction tomography to the structure solution and refinement of charged, discharged or cycled metal-ion battery positive electrode (cathode) materials is discussed in detail. As these materials are often only available in very small amounts as powders, the possibility of obtaining single-crystal data using electron diffraction tomography (EDT) provides unique access to crucial information complementary to X-ray diffraction, neutron diffraction and high-resolution transmission electron microscopy techniques. Using several examples, the ability of EDT to be used to detect lithium and refine its atomic position and occupancy, to solve the structure of materials ex situ at different states of charge and to obtain in situ data on structural changes occurring upon electrochemical cycling in liquid electrolyte is discussed.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Times cited: 2
DOI: 10.1107/S2052520619008291
|
|
|
“High temperature rise dominated cracking mechanisms in ultra-ductile and tough titanium alloy”. Choisez L, Ding L, Marteleur M, Idrissi H, Pardoen T, Jacques PJ, Nature Communications 11, 2110 (2020). http://doi.org/10.1038/S41467-020-15772-1
Abstract: Extensive use of titanium alloys is partly hindered by a lack of ductility, strain hardening, and fracture toughness. Recently, several beta -metastable titanium alloys were designed to simultaneously activate both transformation-induced plasticity and twinning-induced plasticity effects, resulting in significant improvements to their strain hardening capacity and resistance to plastic localization. Here, we report an ultra-large fracture resistance in a Ti-12Mo alloy (wt.%), that results from a high resistance to damage nucleation, with an unexpected fracture phenomenology under quasi-static loading. Necking develops at a large uniform true strain of 0.3 while fracture initiates at a true fracture strain of 1.0 by intense through-thickness shear within a thin localized shear band. Transmission electron microscopy reveals that dynamic recrystallization occurs in this band, while local partial melting is observed on the fracture surface. Shear band temperatures of 1250-2450 degrees C are estimated by the fusible coating method. The reported high ductility combined to the unconventional fracture process opens alternative avenues toward Ti alloys toughening. Specific titanium alloys combine transformation-induced plasticity and twinning-induced plasticity for improved work hardening. Here, the authors show that these alloys also have an ultra-large fracture resistance and an unexpected fracture mechanism via dynamic recrystallization and local melting in a deformation band.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 16.6
Times cited: 1
DOI: 10.1038/S41467-020-15772-1
|
|
|
“Synthesis &ndash, properties correlation and the unexpected role of the titania support on the Grignard surface modification”. Van Dijck JG, Mampuys P, Ching HYV, Krishnan D, Baert K, Hauffman T, Verbeeck J, Van Doorslaer S, Maes BUW, Dorbec M, Buekenhoudt A, Meynen V, Applied Surface Science 527, 146851 (2020). http://doi.org/10.1016/J.APSUSC.2020.146851
Abstract: While the impact of reaction conditions on surface modification with Grignard reactants has been studied for silica supports, such information is absent for metal oxides like titania. Differences between modified titania and silica are observed, making it paramount to explore the reaction mechanism. A detailed study on the impact of the reaction conditions is reported, with a focus on the chain length of the alkyl Grignard reactant, its concentration, the reaction time and temperature, and the type of titania support. While the increase in the chain length reduces the amount of organic groups on the surface, the concentration, time and temperature show little/no influence on the modification degree. However, the type of titania support used and the percentage of amorphous phase present has a significant impact on the amount of grafted groups. Even though the temperature and concentration show no clear impact on the modification degree, they can cause changes in the surface hydroxyl population, which are thus not linked to the modification degree. Furthermore, the titania support is reduced during functionalization. This reduction dependents on the reaction temperature, the titania support and the chain length of the Grignard reactant. Similarly, this reduction is not linked to the modification degree.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT); Laboratory of adsorption and catalysis (LADCA); Organic synthesis (ORSY); Applied Electrochemistry & Catalysis (ELCAT)
Impact Factor: 6.7
Times cited: 5
DOI: 10.1016/J.APSUSC.2020.146851
|
|
|
“Simplex Volume Maximization (SiVM): a matrix factorization algorithm with non-negative constrains and low computing demands for the interpretation of full spectral X-ray fluorescence imaging data”. Alfeld M, Wahabzada M, Bauckhage C, Kersting K, van der Snickt G, Noble P, Janssens K, Wellenreuther G, Falkenberg G, Microchemical journal 132, 179 (2017). http://doi.org/10.1016/J.MICROC.2017.02.001
Abstract: Technological progress allows for an ever-faster acquisition of hyperspectral data, challenging the users to keep up with interpreting the recorded data. Matrix factorization, the representation of data sets by bases (or loads) and coefficient (or score) images is long used to support the interpretation of complex data sets. We propose in this publication Simplex Volume Maximization (SiVM) for the analysis of X-ray fluorescence (XRF) imaging data sets. SiVM selects archetypical data points that represents the data set and thus provides easily understandable bases, preserves the non-negative character of XRF data sets and has low demands concerning computing resources. We apply SiVM on an XRF data set of Hans Memling's Portrait of a man from the Lespinette family from the collection of the Mauritshuis (The Hague, NL) and discuss capabilities and shortcomings of SiVM. (C) 2017 Elsevier B.V. All rights reserved.
Keywords: A1 Journal article; AXES (Antwerp X-ray Analysis, Electrochemistry and Speciation)
Impact Factor: 3.034
Times cited: 8
DOI: 10.1016/J.MICROC.2017.02.001
|
|
|
“Source/drain materials for Ge nMOS devices: phosphorus activation in epitaxial Si, Ge, Ge1-xSnx and SiyGe1-x-ySnx”. Vohra A, Makkonen I, Pourtois G, Slotte J, Porret C, Rosseel E, Khanam A, Tirrito M, Douhard B, Loo R, Vandervorst W, Ecs Journal Of Solid State Science And Technology 9, 044010 (2020). http://doi.org/10.1149/2162-8777/AB8D91
Abstract: This paper benchmarks various epitaxial growth schemes based on n-type group-IV materials as viable source/drain candidates for Ge nMOS devices. Si:P grown at low temperature on Ge, gives an active carrier concentration as high as 3.5 x 10(20) cm(-3) and a contact resistivity down to 7.5 x 10(-9) Omega.cm(2). However, Si:P growth is highly defective due to large lattice mismatch between Si and Ge. Within the material stacks assessed, one option for Ge nMOS source/drain stressors would be to stack Si:P, deposited at contact level, on top of a selectively grown n-SiyGe1-x-ySnx at source/drain level, in line with the concept of Si passivation of n-Ge surfaces to achieve low contact resistivities as reported in literature (Martens et al. 2011 Appl. Phys. Lett., 98, 013 504). The saturation in active carrier concentration with increasing P (or As)-doping is the major bottleneck in achieving low contact resistivities for as-grown Ge or SiyGe1-x-ySnx. We focus on understanding various dopant deactivation mechanisms in P-doped Ge and Ge1-xSnx alloys. First principles simulation results suggest that P deactivation in Ge and Ge1-xSnx can be explained both by P-clustering and donor-vacancy complexes. Positron annihilation spectroscopy analysis, suggests that dopant deactivation in P-doped Ge and Ge1-xSnx is primarily due to the formation of P-n-V and SnmPn-V clusters. (C) 2020 The Author(s). Published on behalf of The Electrochemical Society by IOP Publishing Limited.
Keywords: A1 Journal article; Plasma Lab for Applications in Sustainability and Medicine – Antwerp (PLASMANT)
Impact Factor: 2.2
DOI: 10.1149/2162-8777/AB8D91
|
|
|
“Optimization of mobile scanning macro-XRF systems for the in situ investigation of historical paintings”. Alfeld M, Janssens K, Dik J, de Nolf W, van der Snickt G, Journal of analytical atomic spectrometry 26, 899 (2011). http://doi.org/10.1039/C0JA00257G
Abstract: Elemental distribution maps are of great interest in the study of historical paintings, as they allow to investigate the pigment use of the artist, to image changes made in the painting during or after its creation and in some cases to reveal discarded paintings that were later over painted. Yet a method that allows to record such maps of a broad range of elements in a fast, non-destructive and in situ manner is not yet commonly available; a dedicated mobile scanning XRF instrument might fill this gap. In this paper we present three self-built scanning macro-XRF instruments, each based on the experience gained with its precursor. These instruments are compared in terms of sensitivity and limits of detection, which includes a discussion of the use of polycapillary optics and pinhole collimators as beam defining devices. Furthermore, the imaging capabilities of the instruments are demonstrated in three exemplary cases: (parts of) historical paintings from the 15th to the 19th century are examined. These cases illustrate the value of element specific distribution maps in the study of historical paintings and allow in the case of Vincent van Gogh's Patch of Grass a direct comparison between in situ and synchrotron based scanning macro-XRF.
Keywords: A1 Journal article; AXES (Antwerp X-ray Analysis, Electrochemistry and Speciation)
Impact Factor: 3.379
Times cited: 107
DOI: 10.1039/C0JA00257G
|
|
|
“Seasonality of ship emission related atmospheric pollution over coastal and open waters of the North Sea”. Bencs L, Horemans B, Buczyńska AJ, Deutsch F, Degraeuwe B, Van Poppel M, Van Grieken R, Atmospheric Environment: X 7, 100077 (2020). http://doi.org/10.1016/J.AEAOA.2020.100077
Abstract: The seasonal changes of a large set of atmospheric pollutants (i.e., gases, water-soluble aerosols, metallic/elemental components and black carbon (BC) content) have been studied over the southern bight of the North Sea (the Belgian Continental Shelf) and the English Channel during several marine sampling campaigns, carried out in 2010-2011. A coastal research station at De Haan, Belgium was concurrently used as a background air monitoring site. Size-segregated aerosols (PM1, PM2.5-1, PM10-2.5) were analyzed for particulate mass, elemental content and water-soluble (ionic) compounds, while the equivalent BC content in PM10 was monitored with an Aethalometer. The results clearly demonstrated that the aerosols originating from ship exhaust emissions contributed mostly to fine fraction (PM1), and to a lesser extent to medium-sized fraction (PM2.5-1), whereas components of sea spray and of mineral/soil origin were dominating in the medium-size and coarse aerosol fractions. Looking at seasonal differences, more ship emission related components occurred in the fine and medium-sized PM during winter. Mineral aerosol components were more apparent in coarse PM and especially during the cold season, increased levels were noted. Similarly, higher concentrations of marine fine PM were found during winter, likely due to more extensive ship emissions and/or calm weather conditions. Gaseous pollutants (e.g., HNO2, HNO3, HCl, SO2, NH3) originating from exhaust fumes of ocean-going ships mostly reached the maximum levels in the cold season as well, thus supporting the more intense formation of secondary aerosols. The seasonal trends of total (inorganic) ionic species sampled on the open sea and at the coastal station were usually similar to those of the corresponding PM masses, peaking in the cold season. Sea salt bound fine sulfate and nitrate peaked in spring or the cold season for marine areas, whereas for the coastal site they clearly reached the maximum in the cold season. Ammonium-bound nitrates and sulfates in each PM fraction reached their peak air levels in the cold season over marine sites. Similar seasonal trends could be observed for the coastal station. The general tendency of aerosol distribution over the study areas was independent of the sampling site: the higher the aerosol mass on the open sea with ship traffic, the higher the suspended particulate mass sampled at the coast.
Keywords: A1 Journal article; AXES (Antwerp X-ray Analysis, Electrochemistry and Speciation)
DOI: 10.1016/J.AEAOA.2020.100077
|
|
|
“Fast pixelated detectors in scanning transmission electron microscopy. Part I: data acquisition, live processing, and storage”. Nord M, Webster RWH, Paton KA, McVitie S, McGrouther D, MacLaren I, Paterson GW, Microscopy And Microanalysis 26, Pii S1431927620001713 (2020). http://doi.org/10.1017/S1431927620001713
Abstract: The use of fast pixelated detectors and direct electron detection technology is revolutionizing many aspects of scanning transmission electron microscopy (STEM). The widespread adoption of these new technologies is impeded by the technical challenges associated with them. These include issues related to hardware control, and the acquisition, real-time processing and visualization, and storage of data from such detectors. We discuss these problems and present software solutions for them, with a view to making the benefits of new detectors in the context of STEM more accessible. Throughout, we provide examples of the application of the technologies presented, using data from a Medipix3 direct electron detector. Most of our software are available under an open source licence, permitting transparency of the implemented algorithms, and allowing the community to freely use and further improve upon them.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.8
Times cited: 4
DOI: 10.1017/S1431927620001713
|
|
|
“Critical behavior of the ferromagnets CrI₃, CrBr₃, and CrGeTe₃, and the antiferromagnet FeCl₂, : a detailed first-principles study”. Tiwari S, Van de Put ML, Sorée B, Vandenberghe WG, Physical Review B 103, 014432 (2021). http://doi.org/10.1103/PHYSREVB.103.014432
Abstract: We calculate the Curie temperature of layered ferromagnets, chromium tri-iodide (CrI3), chromium tri-bromide (CrBr3), chromium germanium tri-telluride (CrGeTe3), and the Ned temperature of a layered antiferromagnet iron di-chloride (FeCl2), using first-principles density functional theory calculations and Monte Carlo simulations. We develop a computational method to model the magnetic interactions in layered magnetic materials and calculate their critical temperature. We provide a unified method to obtain the magnetic exchange parameters (J) for an effective Heisenberg Hamiltonian from first principles, taking into account both the magnetic ansiotropy as well as the out-of-plane interactions. We obtain the magnetic phase change behavior, in particular the critical temperature, from the susceptibility and the specific-heat, calculated using the three-dimensional Monte Carlo (METROPOLIS) algorithm. The calculated Curie temperatures for ferromagnetic materials (CrI3, CrBr3, and CrGeTe3), match well with experimental values. We show that the interlayer interaction in bulk CrI3 with R (3) over bar stacking is significantly stronger than the C2/m stacking, in line with experimental observations. We show that the strong interlayer interaction in R (3) over bar CrI3 results in a competition between the in-plane and the out-of-plane magnetic easy axes. Finally, we calculate the Ned temperature of FeCl2 to be 47 +/- 8 K and show that the magnetic phase transition in FeCl2 occurs in two steps with a high-temperature intralayer ferromagnetic phase transition and a low-temperature interlayer antiferromagnetic phase transition.
Keywords: A1 Journal article; Condensed Matter Theory (CMT)
Impact Factor: 3.836
DOI: 10.1103/PHYSREVB.103.014432
|
|
|
“Magnetic properties and critical behavior of magnetically intercalated WSe₂, : a theoretical study”. Reyntjens PD, Tiwari S, van de Put ML, Sorée B, Vandenberghe WG, 2d Materials 8, 025009 (2021). http://doi.org/10.1088/2053-1583/ABD1CC
Abstract: Transition metal dichalcogenides, intercalated with transition metals, are studied for their potential applications as dilute magnetic semiconductors. We investigate the magnetic properties of WSe2 doped with third-row transition metals (Co, Cr, Fe, Mn, Ti and V). Using density functional theory in combination with Monte Carlo simulations, we obtain an estimate of the Curie or Neel temperature. We find that the magnetic ordering is highly dependent on the dopant type. While Ti and Cr-doped WSe2 have a ferromagnetic ground state, V, Mn, Fe and Co-doped WSe2 are antiferromagnetic in their ground state. For Fe doped WSe2, we find a high Curie-temperature of 327 K. In the case of V-doped WSe2, we find that there are two distinct magnetic phase transitions, originating from a frustrated in-plane antiferromagnetic exchange interaction and a ferromagnetic out-of-plane interaction. We calculate the formation energy and reveal that, in contrast to earlier reports, the formation energy is positive for the intercalated systems studied here. We also show that in the presence of W-vacancies, it becomes favorable for Ti, Fe, and Co to intercalate in WSe2.
Keywords: A1 Journal article; Condensed Matter Theory (CMT)
Impact Factor: 6.937
Times cited: 1
DOI: 10.1088/2053-1583/ABD1CC
|
|
|
“The use of lead dodecanoate as an environmentally friendly coating to inhibit the corrosion of lead objects : comparison of three different deposition methods”. De Keersmaecker M, De Wael K, Adriaens A, Progress in organic coatings 74, 1 (2012). http://doi.org/10.1016/J.PORGCOAT.2012.01.014
Abstract: An aqueous sodium dodecanoate solution has been used for the formation of a protective coating for lead. Three deposition methods have been compared: immobilization using cyclic voltammetry, immersion and amperometry. Apart from this, we tested a reduction pretreatment of the lead surface (−1.5 V during 600 s) in order to obtain a more reproducible coating, resulting in a better corrosion protection behavior. The corrosion inhibition properties were examined using potentiodynamic polarization curves and electrochemical impedance measurements in a standard corrosive environment.
Keywords: A1 Journal article; AXES (Antwerp X-ray Analysis, Electrochemistry and Speciation)
Impact Factor: 2.858
Times cited: 8
DOI: 10.1016/J.PORGCOAT.2012.01.014
|
|
|
“On the Origin of Diamond Plates Deposited at Low Temperature”. Drijkoningen S, Pobedinskas P, Korneychuk S, Momot A, Balasubramaniam Y, Van Bael MK, Turner S, Verbeeck J, Nesladekt M, Haenen K, Crystal growth &, design 17, 4306 (2017). http://doi.org/10.1021/ACS.CGD.7B00623
Abstract: The crucial requirement for diamond growth at low temperatures, enabling a wide range of new applications, is a high plasma density at a low gas pressure, which leads to a low thermal load onto sensitive substrate materials. While these conditions are not within reach for resonance cavity plasma systems, linear antenna microwave delivery systems allow the deposition of high quality diamond films at temperatures around 400 degrees C and at pressures below 1 mbar. In this work the codeposition of high quality plates and octahedral diamond grains in nanocrystalline films is reported. In contrast to previous reports claiming the need for high temperatures (T >= 850 degrees C), low temperatures (320 degrees C <= T <= 410 degrees C) were sufficient to deposit diamond plate structures. Cross-sectional high resolution transmission electron microscopy studies show that these plates are faulty cubic diamond terminated by large {111} surface facets with very little sp(2) bonded carbon in the grain boundaries. Raman and electron energy loss spectroscopy studies confirm a high diamond quality, above 93% sp(3) carbon content. Three potential mechanisms, that can account for the initial development of the observed plates rich with stacking faults, and are based on the presence of impurities, are proposed.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 4.055
Times cited: 23
DOI: 10.1021/ACS.CGD.7B00623
|
|
|
“Influence of the deposition method, temperature and deposition time on the corrosion inhibition of lead dodecanoate coatings deposited on lead surfaces”. De Keersmaecker M, De Wael K, Adriaens A, Journal of solid state electrochemistry 17, 1259 (2013). http://doi.org/10.1007/S10008-012-1964-4
Abstract: Electrochemical impedance measurements have been used to investigate the influence of the deposition method, including time and temperature, upon the corrosion inhibition characteristics of lead dodecanoate coatings on lead electrodes. The results were analysed using multivariate statistics and show that, in general, these easily prepared coatings are very protective against corrosion. The temperature proves to be an important parameter for the quality and the corrosion inhibition efficiency of the coating. A comparison between two different electrochemically assisted deposition methods, immersion using a reduction pretreatment and cyclic voltammetry, does not show significant differences. Using the immersion technique at room temperature, the deposition time was tested as the third influencing parameter for the corrosion inhibition efficiency of the deposited lead dodecanoate coatings. A longer deposition time of the lead into the sodium dodecanoate solution provides a layer with a somewhat higher corrosion resistance.
Keywords: A1 Journal article; AXES (Antwerp X-ray Analysis, Electrochemistry and Speciation)
Impact Factor: 2.316
Times cited: 4
DOI: 10.1007/S10008-012-1964-4
|
|
|
“Low-field switching of noncollinear spin texture at La0.7Sr0.3MnO3-SrRuO3interfaces”. Das S, Rata AD, Maznichenko I V, Agrestini IS, Pippel E, Gauquelin N, Verbeeck J, Chen K, Valvidares SM, Vasili HB, Herrero-Martin J, Pellegrin E, Nenkov K, Herklotz A, Ernst A, Mertig I, Hu Z, Doerr K, Physical review B 99, 024416 (2019). http://doi.org/10.1103/PHYSREVB.99.024416
Abstract: Interfaces of ferroic oxides can show complex magnetic textures which have strong impact on spintronics devices. This has been demonstrated recently for interfaces with insulating antiferromagnets such as BiFeO3. Here, noncollinear spin textures which can be switched in very low magnetic field are reported for conducting ferromagnetic bilayers of La0.7Sr0.3MnO3-SrRuO3 (LSMO-SRO). The magnetic order and switching are fundamentally different for bilayers coherently grown in reversed stacking sequence. The SRO top layer forms a persistent exchange spring which is antiferromagnetically coupled to LSMO and drives switching in low fields of a few milliteslas. Density functional theory reveals the crucial impact of the interface termination on the strength of Mn-Ru exchange coupling across the interface. The observation of an exchange spring agrees with ultrastrong coupling for the MnO2/SrO termination. Our results demonstrate low-field switching of noncollinear spin textures at an interface between conducting oxides, opening a pathway for manipulating and utilizing electron transport phenomena in controlled spin textures at oxide interfaces.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 3.836
Times cited: 19
DOI: 10.1103/PHYSREVB.99.024416
|
|
|
“S,O-functionalized metal-organic frameworks as heterogeneous single-site catalysts for the oxidative alkenylation of arenes via C- H activation”. Van Velthoven N, Henrion M, Dallenes J, Krajnc A, Bugaev AL, Liu P, Bals S, Soldatov A, Mali G, De Vos DE, Acs Catalysis 10, 5077 (2020). http://doi.org/10.1021/ACSCATAL.0C00801
Abstract: Heterogeneous single-site catalysts can combine the R precise active site design of organometallic complexes with the efficient recovery of solid catalysts. Based on recent progress on homogeneous thioether ligands for Pd-catalyzed C-H activation reactions, we here develop a scalable metal-organic framework-based heterogeneous single-site catalyst containing S,O-moieties that increase the catalytic activity of Pd(II) for the oxidative alkenylation of arenes. The structure of the Pd@MOF-808-L1 catalyst was characterized in detail via solid-state nuclear magnetic resonance spectroscopy, N-2 physisorption, and high-angle annular dark field scanning transmission electron microscopy, and the structure of the isolated palladium active sites could be identified by X-ray absorption spectroscopy. A turnover frequency (TOF) of 8.4 h(-1) was reached after 1 h of reaction time, which was 3 times higher than the TOF of standard Pd(OAc)(2), ranking Pd@MOF-808-L1 among the most active heterogeneous catalysts ever reported for the nondirected oxidative alkenylation of arenes. Finally, we showed that the single-site catalyst promotes the oxidative alkenylation of a broad range of electron-rich arenes, and the applicability of this heterogeneous system was demonstrated by the gram-scale synthesis of industrially relevant products.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 12.9
Times cited: 37
DOI: 10.1021/ACSCATAL.0C00801
|
|
|
“Single-site metal-organic framework catalysts for the oxidative coupling of arenes via C-H/C-H activation”. Van Velthoven N, Waitschat S, Chavan SM, Liu P, Smolders S, Vercammen J, Bueken B, Bals S, Lillerud KP, Stock N, De Vos DE, Chemical science 10, 3616 (2019). http://doi.org/10.1039/C8SC05510F
Abstract: C-H activation reactions are generally associated with relatively low turnover numbers (TONs) and high catalyst concentrations due to a combination of low catalyst stability and activity, highlighting the need for recyclable heterogeneous catalysts with stable single-atom active sites. In this work, several palladium loaded metal-organic frameworks (MOFs) were tested as single-site catalysts for the oxidative coupling of arenes (e.g. o-xylene) via C-H/C-H activation. Isolation of the palladium active sites on the MOF supports reduced Pd(0) aggregate formation and thus catalyst deactivation, resulting in higher turnover numbers (TONs) compared to the homogeneous benchmark reaction. Notably, a threefold higher TON could be achieved for palladium loaded MOF-808 due to increased catalyst stability and the heterogeneous catalyst could efficiently be reused, resulting in a cumulative TON of 1218 after three runs. Additionally, the palladium single-atom active sites on MOF-808 were successfully identified by Fourier transform infrared (FTIR) and extended X-ray absorption fine structure (EXAFS) spectroscopy.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 8.668
Times cited: 68
DOI: 10.1039/C8SC05510F
|
|
|
“Role of the relative humidity and the Cd/Zn stoichiometry in the photooxidation process of cadmium yellows (CdS/Cd1-xZnxS) in oil paintings”. Monico L, Chieli A, De Meyer S, Cotte M, de Nolf W, Falkenberg G, Janssens K, Romani A, Miliani C, Chemistry: a European journal 24, 11584 (2018). http://doi.org/10.1002/CHEM.201801503
Abstract: Cadmium yellows (CdYs) refer to a family of cadmium sulfide pigments, which have been widely used by artists since the late 19th century. Despite being considered stable, they are suffering from discoloration in iconic paintings, such as Joy of Life by Matisse, Flowers in a blue vase by Van Gogh, and The Scream by Munch, most likely due to the formation of CdSO4 center dot nH(2)O. The driving factors of the CdYs degradation and how these affect the overall process are still unknown. Here, we study a series of oil mock-up paints made of CdYs of different stoichiometry (CdS/Cd0.76Zn0.24S) and crystalline structure (hexagonal/ cubic) before and after aging at variable relative humidity under exposure to light and in darkness. Synchrotron radiation-based X-ray methods combined with UV-Vis and FTIR spectroscopy show that: 1) Cd0.76Zn0.24S is more susceptible to photooxidation than CdS; both compounds can act as photocatalysts for the oil oxidation. 2) The photooxidation of CdS/Cd0.76Zn0.24S to CdSO4 center dot nH(2)O is triggered by moisture. 3) The nature of alteration products depends on the aging conditions and the Cd/Zn stoichiometry. Based on our findings, we propose a scheme for the mechanism of the photocorrosion process and the photocatalytic activity of CdY pigments in the oil binder. Overall, our results form a reliable basis for understanding the degradation of CdS-based paints in artworks and contribute towards developing better ways of preserving them for future generations.
Keywords: A1 Journal article; AXES (Antwerp X-ray Analysis, Electrochemistry and Speciation)
Impact Factor: 5.317
Times cited: 5
DOI: 10.1002/CHEM.201801503
|
|
|
“Disclosing the binding medium effects and the pigment solubility in the (photo)reduction process of chrome yellows (PbCrO4/PbCr1-xSxO4)”. Monico L, Sorace L, Cotte M, de Nolf W, Janssens K, Romani A, Miliani C, ACS Omega 4, 6607 (2019). http://doi.org/10.1021/ACSOMEGA.8B03669
Abstract: The darkening due to chemical alteration of chrome yellows (PbCrO4/PbCr1-xSxO4) is a phenomenon threatening a large number of 19th-20th century paintings, including the Amsterdam Sunflowers by Vincent van Gogh. Our earlier studies have proven that the alteration is due to a Cr(VI) -> Cr(III) reduction with Cr(V)-species that are formed as long-lived intermediates and that bCr(1-x)S(x)O(4) (0 < x <= 0.8) types undergo reduction more readily than monoclinic, S-free, PbCrO4. In this context, there is still lack of knowledge about the effects of the chemical properties of the binding medium (i.e., chemical composition and drying process) and the solubility of chrome yellows on the overall reduction pathways. Here, we study a series of naturally and photochemically aged mock-up paints prepared by mixing chrome yellow powders (PbCrO4/PbCr0.2S0.8O4) with either linseed oil or a water-based acrylic emulsion as the binding medium. Equivalent paints made up of the highly soluble K2CrO4 were also investigated and used as benchmarks to provide a more in-depth understanding of the influence of the solubility on the chromate reduction pathways in the two different binders. A combination of synchrotron radiation-based Cr K-edge X-ray absorption near edge structure (XANES), electron paramagnetic resonance (EPR), and UV-Visible spectroscopy measurements shows that: (1) the Cr(VI) reduction results from the interaction between the pigment and the binder; (2) the process is more significant in oil, giving rise to Cr(V)- and Cr(III)-species as well as oxidized organic compounds; (3) the lightfastness of the chrome yellow pigment is enhanced in the acrylic binder; and (4) the tendency toward chromium reduction increases with increasing solubility of the pigment. Based on our findings, we propose a scheme for the mechanism of the (photo)reduction process of chrome yellows in the oil and acrylic binder. Overall, our results provide new insights into the factors driving the degradation of lead chromate-based paints in artworks and contribute to the development of strategies for preserving them over time.
Keywords: A1 Journal article; AXES (Antwerp X-ray Analysis, Electrochemistry and Speciation)
Times cited: 4
DOI: 10.1021/ACSOMEGA.8B03669
|
|
|
“Probing the chemistry of CdS paints in The Scream by in situ noninvasive spectroscopies and synchrotron radiation x-ray techniques”. Monico L, Cartechini L, Rosi F, Chieli A, Grazia C, De Meyer S, Nuyts G, Vanmeert F, Janssens K, Cotte M, De Nolf W, Falkenberg G, Sandu ICA, Tveit ES, Mass J, De Freitas RP, Romani A, Miliani C, Science Advances 6, eaay3514 (2020). http://doi.org/10.1126/SCIADV.AAY3514
Abstract: The degradation of cadmium sulfide (CdS)-based oil paints is a phenomenon potentially threatening the iconic painting The Scream (ca. 1910) by Edvard Munch (Munch Museum, Oslo) that is still poorly understood. Here, we provide evidence for the presence of cadmium sulfate and sulfites as alteration products of the original CdS-based paint and explore the external circumstances and internal factors causing this transformation. Macroscale in situ noninvasive spectroscopy studies of the painting in combination with synchrotron-radiation x-ray microspectroscopy investigations of a microsample and artificially aged mock-ups show that moisture and mobile chlorine compounds are key factors for promoting the oxidation of CdS, while light (photodegradation) plays a less important role. Furthermore, under exposure to humidity, parallel/secondary reactions involving dissolution, migration through the paint, and recrystallization of water-soluble phases of the paint are associated with the formation of cadmium sulfates.
Keywords: A1 Journal article; Engineering sciences. Technology; AXES (Antwerp X-ray Analysis, Electrochemistry and Speciation)
Impact Factor: 13.6
Times cited: 4
DOI: 10.1126/SCIADV.AAY3514
|
|
|
“Growth mechanism of epitaxial SrTiO3 on a (1 x 2) + (2 x 1) reconstructed Sr(1/2 ML)/Si(001) surface”. Spreitzer M, Klement D, Egoavil R, Verbeeck J, Kovac J, Zaloznik A, Koster G, Van Tendeloo G, Suvorov D, Rijnders G, Journal Of Materials Chemistry C 8, 518 (2020). http://doi.org/10.1039/C9TC04092G
Abstract: Sub-monolayer control over the growth at silicon-oxide interfaces is a prerequisite for epitaxial integration of complex oxides with the Si platform, enriching it with a variety of functionalities. However, the control over this integration is hindered by the intense reaction of the constituents. The most suitable buffer material for Si passivation is metallic strontium. When it is overgrown with a layer of SrTiO3 (STO) it can serve as a pseudo-substrate for the integration with functional oxides. In our study we determined a mechanism for epitaxial integration of STO with a (1 x 2) + (2 x 1) reconstructed Sr(1/2 ML)/Si(001) surface using all-pulsed laser deposition (PLD) technology. A detailed analysis of the initial deposition parameters was performed, which enabled us to develop a complete protocol for integration, taking into account the peculiarities of the PLD growth, STO critical thickness, and process thermal budget, in order to kinetically trap the reaction between STO and Si and thus to minimize the thickness of the interface layer. The as-prepared oxide layer exhibits STO(001)8Si(001) out-of-plane and STO[110]8Si[100] in-plane orientation and together with recent advances in large-scale PLD tools these results represent a new technological solution for the implementation of oxide electronics on demand.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 6.4
Times cited: 12
DOI: 10.1039/C9TC04092G
|
|
|
“New solid electrolyte Na9Al(MoO4)6 : structure and Na+ ion conductivity”. Savina AA, Morozov VA, Buzlukov AL, Arapova IY, Stefanovich SY, Baklanova YV, Denisova TA, Medvedeva NI, Bardet M, Hadermann J, Lazoryak BI, Khaikina EG, Chemistry of materials 29, 8901 (2017). http://doi.org/10.1021/ACS.CHEMMATER.7B03989
Abstract: <script type='text/javascript'>document.write(unpmarked('Solid electrolytes are important materials with a wide range of technological applications. This work reports the crystal structure and electrical properties of a new solid electrolyte Na9Al(MoO4)(6). The monoclinic Na9Al(MoO4)(6) consists of isolated polyhedral, [Al(MoO4)(6)](9-) clusters composed of a central AlO6 octahedron sharing vertices with six MoO4 tetrahedra to form a three-dimensional framework. The AlO6 octahedron also shares edges with one NalO(6) octahedron and two Na2O(6) octahedra. Na3-Na5 atoms are located in the framework cavities. The structure is related to that of sodium ion conductor II-Na3Fe2(AsO4)(3). High-temperature conductivity measurements revealed that the conductivity (sigma) of Na9Al(MoO4)(6) at 803 K equals 1.63 X 10(-2) S cm(-1). The temperature behavior of the Na-23 and Al-27 nuclear magnetic resonance spectra and the spin-lattice relaxation rates of the Na-23 nuclei indicate the presence of fast Na+ ion diffusion in the studied compound. At T\u003C490 K, diffusion occurs by means of Na+ ion jumps exclusively through the sublattice of Na3-Na5 positions, whereas Na1 and Na2 become involved in the diffusion processes (through chemical exchange with the Na3-Na5 sublattice) only at higher temperatures.'));
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 9.466
Times cited: 13
DOI: 10.1021/ACS.CHEMMATER.7B03989
|
|
|
“Laser synthesis of hard carbon for anodes in Na-ion battery”. Zhang B, Deschamps M, Ammar M-R, Raymundo-Pinero E, Hennet L, Batuk D, Tarascon J-M, Advanced Materials Technologies 2, 1600227 (2017). http://doi.org/10.1002/ADMT.201600227
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Times cited: 10
DOI: 10.1002/ADMT.201600227
|
|
|
“Chemical imaging of stained-glass windows by means of macro X-ray fluorescence (MA-XRF) scanning”. van der Snickt G, Legrand S, Caen J, Vanmeert F, Alfeld M, Janssens K, Microchemical journal 124, 615 (2016). http://doi.org/10.1016/J.MICROC.2015.10.010
Abstract: Since the recent development of a mobile setup, MA-XRF scanning proved a valuable tool for the non-invasive, technical study of paintings. In this work, the applicability of MA-XRF scanning for investigating stained-glass windows inside a conservation studio is assessed by analysis of a high-profile, well-studied late-mediaeval panel. Although accurate quantification of components is not feasible with this analytical imaging technique, plotting the detected intensities of K versus Ca in a scatter plot allowed distinguishing glass fragments of different compositional types within the same panel. In particular, clusters in the Ca/K correlation plot revealed the presence of two subtypes of potash glass and three subtypes of high lime low alkali glass. MA-XRF results proved consistent with previous quantitative SEM-EDX analysis on two samples and analytical-based theories on glass production in the Low Countries formulated in literature. A bi-plot of the intensities of the more energetic Rb-K versus Sr-K emission lines yielded a similar glass type differentiation and is here presented as suitable alternative in case the Ca/K signal ratio is affected by superimposed weathering crusts. Apart from identification of the chromophores responsible for the green, blue and red glass colors, contrasting the associated elemental distribution maps obtained on the exterior and interior side of the glass permitted discriminating between colored pot metal glass and multi-layered flashed glass as well. Finally, the benefit of obtaining compositional information from the entire surface, as opposed to point analysis, was illustrated by the discovery of what appears to be a green cobalt glass a feature that was previously missed on this well-studied stained-glass window, both by connoisseurs and spectroscopic sample analysis. (C) 2015 Elsevier B.V. All rights reserved.
Keywords: A1 Journal article; AXES (Antwerp X-ray Analysis, Electrochemistry and Speciation); Antwerp Cultural Heritage Sciences (ARCHES)
Impact Factor: 3.034
Times cited: 22
DOI: 10.1016/J.MICROC.2015.10.010
|
|
|
“Vortex patterns in a mesoscopic superconducting rod with a magnetic dot”. Doria MM, Romaguera AR de C, Peeters FM, Physical review : B : condensed matter and materials physics 81, 104529 (2010). http://doi.org/10.1103/PhysRevB.81.104529
Abstract: We study a mesoscopic superconducting rod with a magnetic dot on its top having its moment oriented along the axis of symmetry. We study the dependence of the vortex pattern with the height and find that for very short and very long rods, the vortex pattern acquires a simple structure, consisting of giant and of multivortex states, respectively. In the long limit, the most stable configuration consists of two vortices, that reach the lateral surface of the rod diametrically opposed. The long rod shows reentrant behavior within some range of its radius and of the dots magnetic moment. Our results are obtained within the Ginzburg-Landau approach in the limit of no magnetic shielding.
Keywords: A1 Journal article; Condensed Matter Theory (CMT)
Impact Factor: 3.836
Times cited: 5
DOI: 10.1103/PhysRevB.81.104529
|
|
|
“Doping of Bi4Fe5O13F with pentagonal Cairo lattice with Cr and Mn: Synthesis, structure and magnetic properties”. Rozova MG, Grigoriev VV, Tyablikov OA, Filimonov DS, Zakharov KV, Volkova OS, Vasiliev AN, Antipov EV, Abakumov AM, Materials research bulletin 87, 54 (2017). http://doi.org/10.1016/J.MATERRESBULL.2016.11.018
Abstract: The substitution of Cr3+ and Mn3+ for Fe3+ in the Bi4Fe6O13F oxyfluoride featuring the magnetically frustrated pentagonal Cairo lattice is reported. Bi4Fe4.1Cr0.9O13F and BiFe4.2Mn0.8O13F have been prepared using a solid state reaction in inert atmosphere. Their crystal structures were studied with transmission electron microscopy, powder X-ray diffraction and Fe-57 Mossbauer spectroscopy (S.G. P4(2)/mbc, a = 8.27836(2)angstrom, c = 18.00330(9) angstrom, R-F = 0.031 (Bi4Fe4.1Cr0.9O13F)), a= 8.29535(3)angstrom, c= 18.0060(1)angstrom, R-F = 0.027 (Bi4Fe4.1Cr0.9O13F)). The structures are formed by infinite rutile-like chains of the edge sharing BO6 octahedra (B transition metal cations) linked by the Fe2O7 groups of two corner-sharing tetrahedra. The"voids in thus formed framework are occupied by the Bi4F tetrahedra. The Fe-57 Mossbauer spectroscopy reveals that Cr3+ and Mn3+ replace Fe3+. exclusively at the octahedral positions. The Mn- and Cr-doped compounds demonstrate antiferromagnetic ordering below T-N =165 K and 120 K, respectively. (C) 2016 Elsevier Ltd. All rights reserved.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.446
Times cited: 1
DOI: 10.1016/J.MATERRESBULL.2016.11.018
|
|
|
“Negative magnetoresistance in thin superconducting films with parallel orientation of current and magnetic field”. Vodolazov DY, Berdiyorov G, Peeters FM, Physica: C : superconductivity 552, 64 (2018). http://doi.org/10.1016/J.PHYSC.2018.07.002
Abstract: Thin superconducting films can exhibit negative magnetoresistance when an in-plane external magnetic field is aligned parallel with the transport current. We explain this effect as due to appearance of parallel vortices in the plain of the film at the first critical magnetic field H-c1 which leads to an enhancement of the superconducting properties and impedes the motion of the current induced perpendicular vortices. Our theoretical results are based on a numerical solution of the time-dependent and stationary 3D Ginzburg-Landau equations.
Keywords: A1 Journal article; Condensed Matter Theory (CMT)
Impact Factor: 1.404
Times cited: 6
DOI: 10.1016/J.PHYSC.2018.07.002
|
|
|
“Surface passivation of CIGS solar cells using gallium oxide”. Garud S, Gampa N, Allen TG, Kotipalli R, Flandre D, Batuk M, Hadermann J, Meuris M, Poortmans J, Smets A, Vermang B, Physica status solidi : A : applications and materials science 215, 1700826 (2018). http://doi.org/10.1002/PSSA.201700826
Abstract: This work proposes gallium oxide grown by plasma-enhanced atomic layer deposition, as a surface passivation material at the CdS buffer interface of Cu(In,Ga)Se-2 (CIGS) solar cells. In preliminary experiments, a metal-insulator-semiconductor (MIS) structure is used to compare aluminium oxide, gallium oxide, and hafnium oxide as passivation layers at the CIGS-CdS interface. The findings suggest that gallium oxide on CIGS may show a density of positive charges and qualitatively, the least interface trap density. Subsequent solar cell results with an estimated 0.5nm passivation layer show an substantial absolute improvement of 56mV in open-circuit voltage (V-OC), 1mAcm(-2) in short-circuit current density (J(SC)), and 2.6% in overall efficiency as compared to a reference (with the reference showing 8.5% under AM 1.5G).
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 1.775
Times cited: 8
DOI: 10.1002/PSSA.201700826
|
|