“Direct observation of laser-induced crystallization of a-C : H films”. Nistor LC, van Landuyt J, Ralchenko VG, Kononenko TV, Obraztsova ED, Strelnitsky VE, Applied physics A : materials science &, processing 58, 137 (1994). http://doi.org/10.1007/BF00332170
Abstract: The post-growth modification of diamond-like amorphous hydrogenated carbon a-C:H films by laser treatment has been studied by transmission electron microscopy and Raman spectroscopy. a-C:H films grown on Si substrates by benzene decomposition in a rf glow discharge were irradiated with 15 ns pulses of a KrF-excimer laser with fluences in the ran e of E = 50-700 mJ/cm(2). At fluences below 100 mJ/cm(2) an increase in the number of graphitic clusters and in their ordering was evidenced from Raman spectra, while the film structure remained amorphous according to electron microscopy and electron diffraction observations. At higher fluences the appearance of diamond particles of 2-7 nm size, embedded into the lower crystallized graphitic matrix, was observed and simultaneously a progressive growth of graphite nanocrystals with dimensions from 2 nm to 4 nm was deduced from Raman measurements. The maximum thickness of the crystallized surface layer (approximate to 400 nm) and the degree of laser annealing are limited by the film ablation which starts at E > 250 mJ/cm(2). The laser-treated areas lose their chemical inertness. In particular, chemical etching in chromium acid becomes possible, which may be used for patterning the highly inert carbon films.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Times cited: 73
DOI: 10.1007/BF00332170
|
|
|
“Superstructure and structural variants in Sr2CuO2(CO3)”. Milat O, Van Tendeloo G, Amelinckx S, Babu TGN, Greaves C, Journal of solid state chemistry 109, 5 (1994). http://doi.org/10.1006/jssc.1994.1063
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.133
Times cited: 11
DOI: 10.1006/jssc.1994.1063
|
|
|
“Defects and phase transformation in monclinic natural hollandite: BaxMn8O16”. Nistor LC, Van Tendeloo G, Amelinckx S, Journal of solid state chemistry 109, 152 (1994)
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.133
Times cited: 13
|
|
|
“Defects and phase transition in monoclinic natural hollandite : BaxMn8O16”. Nistor LC, Van Tendeloo G, Amelinckx S, Journal of solid state chemistry 109, 152 (1994). http://doi.org/10.1006/jssc.1994.1085
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.133
Times cited: 13
DOI: 10.1006/jssc.1994.1085
|
|
|
“Lead-mercury based superconductors: the 1212 cuprate Pb0.7Hg0.3Sr2+xCa0.7Nd0.3-xCu2O7-\delta and the new oxycarbonate Pb0.7Hg0.3Sr4Cu2CO3O7”. Martin C, Hervieu M, Huvé, M, Michel C, Maignan A, Van Tendeloo G, Raveau B, Physica C-Superconductivity And Its Applications 222, 19 (1994)
Keywords: A1 Journal article; Electron Microscopy for Materials Science (EMAT);
Impact Factor: 0.942
Times cited: 49
|
|
|
“Lead-mercury-based superconductors –, the 1212-cuprate Pb0.7Hg0.3Sr2+xCa0.7Nd0.3-xCu2O7-\delta and the new oxycarbonate Pb0.7Hg0.3Sr4Cu2CO3O7”. Martin C, Hervieu M, Huvé, M, Michel C, Maignan A, Van Tendeloo G, Raveau B, Physica: C : superconductivity 222, 19 (1994). http://doi.org/10.1016/0921-4534(94)90109-0
Abstract: A new superconducting mercury oxycarbonate, Pb0.7Hg0.3Sr4Cu2CO3O7, has been synthesized. This tetragonal phase (a = 3.824 angstrom, c= 16.468 angstrom) consists of an intergrowth of two nonsuperconducting compounds, Sr2CuO2CO3 and Pb0.7Hg0.3Sr2CuO5. It exhibits after optimization a critical temperature of 70 K, with a sharp transition and a superconducting volume fraction of 50%. Its behavior can be compared to that of thallium oxycarbonates previously isolated. This study is completed by a reinvestigation of the 1212 cuprate of the system Hg-Pb-Sr-Ca-Nd-Cu. A superconducting phase with the 1212 structure, similar to that previously obtained but with a significantly different composition, Pb0.7Hg0.3Sr2+xCa0.7Nd0.3-xCu2O7, has been obtained, with a T(c onset) of 100 K. The behavior of the latter is compared with other lead-based 1212 cuprates.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 0.942
Times cited: 49
DOI: 10.1016/0921-4534(94)90109-0
|
|
|
““Harmless&rdquo, carbon tubes around “dangerous&rdquo, asbestos fibres”. Zhang XF, Zhang XB, Van Tendeloo G, Meijer G, Carbon 32, 363 (1994). http://doi.org/10.1016/0008-6223(94)90206-2
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 6.196
Times cited: 2
DOI: 10.1016/0008-6223(94)90206-2
|
|
|
“A mercury-based “1201-0201&rdquo, intergrowth HgBa2La2Cu2O8+x: a 53K superconductor”. Huvé, M, Martin C, Van Tendeloo G, Maignan A, Michel C, Hervieu M, Raveau B, Solid state communications 90, 37 (1994)
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 1.897
Times cited: 7
|
|
|
“Substitution of mercury for thallium in the 2223 cuprate: the 130K superconductor Tl1.6Hg0.4Ba2Cu3O10-x”. Goutenoire F, Maignan A, Van Tendeloo G, Martin C, Michel C, Hervieu M, Raveau B, Solid state communications 90, 47 (1994)
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 1.897
Times cited: 16
|
|
|
“The domain configuration of the Au11In3 phase”. Kifune K, Yamamoto K, Maruyama S, Van Tendeloo G, Philosophical magazine letters 69, 211 (1994). http://doi.org/10.1080/09500839408241594
Abstract: The crystal structure of Au11In3 thin film alloys have been analysed by means of electron diffraction and high-resolution electron microscopy. The electron diffraction pattern and the high-resolution electron microscopy revealed that this structure was incommensurate and had a domain structure consisting of three kinds of structural unit. The approximant structural model, which is based on a h.c.p. stacking of the layers, is hexagonal with lattice parameters a = 7.612 nm and c = 0-478 nm.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 1.087
Times cited: 2
DOI: 10.1080/09500839408241594
|
|
|
“Electron microscopy and energy-loss spectroscopy of voidites in pure IaB diamonds”. Luyten W, Van Tendeloo G, Fallon PJ, Woods GS, Philosophical magazine: A: physics of condensed matter: defects and mechanical properties 69, 767 (1994). http://doi.org/10.1080/01418619408242517
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Times cited: 7
DOI: 10.1080/01418619408242517
|
|
|
“Atomic structure and defect structure of the superconducting HgBa2Can-1CunO2n+2+\delta homologous series”. Van Tendeloo G, Chaillout C, Capponi JJ, Marezio M, Antipov EV, Physica: C : superconductivity 223, 219 (1994). http://doi.org/10.1016/0921-4534(94)91264-5
Abstract: The perfect as well as the defect structure of several members of the superconducting family HgBa2Can-1CunO2n+2+delta have been studied in detail by electron diffraction and high-resolution electron microscopy Identification of the cation configuration is possible, even in the defect regions, with the help of computer simulations. The fine structure of several defects is analyzed in detail, the most common defect being the intergrowth of slabs corresponding to different n values in the title formula. In general, however, the crystals are of a high perfection, particularly for the lower n members. The occurrence of double (HgO)delta layers is seen occasionally, indicating the possible existence of a material with a double mercury layer. Some of these defects are possibly related to recently discovered anomalies at 250 K in these compounds.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 0.942
Times cited: 30
DOI: 10.1016/0921-4534(94)91264-5
|
|
|
“Copper oxycarbonates and mercury-based cuprates: promising high Tc superconductors”. Raveau B, Michel C, Hervieu M, Van Tendeloo G, Martin C, Maignan A, Journal of superconductivity 7, 9 (1994). http://doi.org/10.1007/BF00730359
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Times cited: 6
DOI: 10.1007/BF00730359
|
|
|
“Mixed valent iron oxides with the 0201-1201 intergrowth structure: (Pb1-xTlx)Sr4Fe2O9 (0≤x≤1)”. Daniel P, Barbey L, Groult D, Nguyen N, Van Tendeloo G, Raveau B, European journal of solid state and inorganic chemistry 31, 235 (1994)
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Times cited: 12
|
|
|
“The study of carbon nanotubes produced by catalytic method”. Ivanov V, Nagy JB, Lambin P, Lucas A, Zhang XB, Zhang XF, Bernaerts D, Van Tendeloo G, Amelinckx S, van Landuyt J, Chemical physics letters 223, 329 (1994)
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 1.897
Times cited: 405
|
|
|
“The study of carbon nanotubules produced by catalytic method”. Ivanov V, Nagy JB, Lambin P, Lucas A, Zhang XB, Zhang XF, Bernaerts D, Van Tendeloo G, Amelinckx S, van Landuyt J, Chemical physics letters 223, 329 (1994). http://doi.org/10.1016/0009-2614(94)00467-6
Abstract: Catalytic methods for the production of carbon nanotubules have been developed based on the decomposition of acetylene on well-dispersed metal particles strongly adsorbed on a support. Cobalt on silica was found to be the best catalyst-support combination for the production of graphitic tubules. The method for the catalyst preparation and the reaction conditions were optimized. Straight and coiled carbon tubules were obtained with inner and outer diameter of 3-7 and 15-20 nm, respectively, and up to 30 mum in length. These nanotubules were not coated by amorphous carbon. Traces of amorphous carbon could be removed by hydrogen. High resolution electron microscopy images and electron diffraction patterns of the straight nanotubules were similar to those obtained by the arc-discharge method. Coiled nanotubules were revealed by TEM to be regular polygonized helices where the bends are caused by pairs of pentagon-heptagon carbon rings among the hexagonal network.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 1.897
Times cited: 405
DOI: 10.1016/0009-2614(94)00467-6
|
|
|
“Laser induced phase transition in iron thin films”. Teodorescu VS, Mihailescu IN, Dinescu M, Chitica N, Nistor LC, van Landuyt J, Barborica A, Journal de physique: 3: applied physics, materials science, fluids, plasma and instrumentation 4, 127 (1994). http://doi.org/10.1051/jp4:1994427
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Times cited: 2
DOI: 10.1051/jp4:1994427
|
|
|
“Electron-diffraction evidence for ordering of interstitial silver ions in silver bromide microcrystals”. Goessens C, Schryvers D, van Dyck D, van Landuyt J, de Keyzer R, Physica status solidi: A 143, 277 (1994). http://doi.org/10.1002/pssa.2211430211
Abstract: The occurrence and origin of diffuse intensity contours in electron micrographs of AgBr crystals are investigated. The observations are interpreted in terms of a model, which attributes diffuse scattering to the presence of predominant atom or vacancy clusters of a particular polyhedral type. It is shown that irrespective of the crystal morphology, interstitial Ag ions order in AgBr material in clusters of finite size along 001 type planes. A different geometry of the diffuse intensity locus observed for triangular and hexagonal tabular grains is explained in terms of the different twin plane morphology of these grains.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT); Vision lab
Times cited: 7
DOI: 10.1002/pssa.2211430211
|
|
|
“The texture of catalytically grown coil-shaped carbon nanotubes”. Zhang XB, Zhang XF, Bernaerts D, Van Tendeloo G, Amelinckx S, van Landuyt J, Ivanov V, Nagy JB, Lambin P, Lucas AA, Europhysics letters 27, 141 (1994). http://doi.org/10.1209/0295-5075/27/2/011
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.095
Times cited: 168
DOI: 10.1209/0295-5075/27/2/011
|
|
|
“The reciprocal space of carbon tubes: a detailed interpretation of the electron diffraction effects”. Zhang XB, Zhang XF, Amelinckx S, Van Tendeloo G, van Landuyt J, Ultramicroscopy 54, 237 (1994). http://doi.org/10.1016/0304-3991(94)90123-6
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.436
Times cited: 59
DOI: 10.1016/0304-3991(94)90123-6
|
|
|
“Electron microscopy and X-ray diffraction studies of rapidly quenched Zr-Ni an Hf-Ni ribbons with about 90 at.% Ni”. Cziraki A, Fogarassy F, Van Tendeloo G, Lamparter P, Tegze M, Bakonyi I, Journal of alloys and compounds 210, 135 (1994). http://doi.org/10.1016/0925-8388(94)90128-7
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.999
Times cited: 26
DOI: 10.1016/0925-8388(94)90128-7
|
|
|
“A simple preparation method for air-sensitive specimens for transmission electron microscopy demonstrated by Rb6C60”. Zhang XF, Zhang XB, Bernaerts D, Van Tendeloo G, Amelinckx S, van Landuyt J, Werner H, Ultramicroscopy 55, 25 (1994). http://doi.org/10.1016/0304-3991(94)90077-9
Abstract: In this paper a particularly simple but efficient method is presented by which samples of alkali-doped C-60 materials or other air-sensitive materials can be prepared and transferred into a transmission electron microscope for direct observations and investigations. Flexible, transparent glove bags are used which are filled to a slight overpressure with dry nitrogen. Under this protective atmosphere, the air-sensitive sample is mounted in the specimen holder and inserted in the vacuum of the electron microscope. Rb6C60 which is prepared and transferred into the microscope in this way has been investigated by transmission electron microscopy (TEM). The results confirm the bcc structure and especially the location of the rubidium atoms.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.436
Times cited: 2
DOI: 10.1016/0304-3991(94)90077-9
|
|
|
“Structural evolution of Bi2Sr2CaCu2O8+\delta single crystals studies by “in situ&rdquo, heating electron microscopy”. Zhang XF, Van Tendeloo G, Philosophical magazine: A: physics of condensed matter: defects and mechanical properties 70, 549 (1994)
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Times cited: 5
|
|
|
“Structural characteristics of the 40K superconductor Bi2Sr5Cu3(CO3)2O10: a HREM study”. Hervieu M, Pelloquin D, Michel C, Van Tendeloo G, Raveau B, Journal of solid state chemistry 112, 139 (1994)
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.133
Times cited: 5
|
|
|
“Structural aspects of Li-doped tubular bismuth cuprates (Bi2Sr3Cu2-xLixOy): an electron microscopy study”. Van Tendeloo G, Domengès B, Caldes MT, Hervieu M, Raveau B, Journal of solid state chemistry 112, 161 (1994)
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.133
|
|
|
“Up close: Center for Electron Microscopy of Materials Science at the University of Antwerp”. Van Tendeloo G, Schryvers D, van Dyck D, van Landuyt J, Amelinckx S, MRS bulletin , 57 (1994)
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT); Vision lab
Impact Factor: 5.667
|
|
|
“Structural and physical properties of the new superconductor Hg0.5Pb0.5Sr4-xBaxCu2(CO3)O7-\delta”. Huvé, M, Van Tendeloo G, Hervieu M, Maignan A, Raveau B, Physica: C : superconductivity 231, 15 (1994). http://doi.org/10.1016/0921-4534(94)90138-4
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 0.942
Times cited: 14
DOI: 10.1016/0921-4534(94)90138-4
|
|
|
“Molecular orientation and conductivity in highly oriented poly(p-phenylene vinylene)”. Briers J, Eevers W, Cos P, Geise HJ, Mertens R, Nagels P, Zhang XB, Van Tendeloo G, Herrebout W, van der Veken B, Polymer 35, 4569 (1994). http://doi.org/10.1016/0032-3861(94)90804-4
Keywords: A1 Journal article; Molecular Spectroscopy (MolSpec); Electron microscopy for materials research (EMAT)
Impact Factor: 3.562
Times cited: 16
DOI: 10.1016/0032-3861(94)90804-4
|
|
|
“Structural aspects and antiferromagnetic ordering in the “123&rdquo, derivative LnSr2Cu2Ga1-xFexO7-\delta (Ln = Y, Ho)”. Rykov A, Caignaert V, Van Tendeloo G, Greneche JM, Studer F, Nguyen N, Ducouret A, Bonville P, Raveau B, Journal of solid state chemistry 113, 94 (1994)
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.133
Times cited: 9
|
|
|
“High resolution electron microscopic study of Ba7Sc6Al2O19 and related phases”. Shpanchenko RV, Nistor L, Van Tendeloo G, Amelinckx S, Antipov EV, Kovba LM, Journal of solid state chemistry 113, 193 (1994). http://doi.org/10.1006/jssc.1994.1359
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.133
Times cited: 3
DOI: 10.1006/jssc.1994.1359
|
|