“Structural properties of Zn-substituted epitaxial YBa2Cu3O7-\delta thin films”. Ye M, Schroeder J, Mehbod M, Deltour R, Naessens G, Duvigneaud PH, Verbist K, Van Tendeloo G, Superconductor science and technology 9, 543 (1996). http://doi.org/10.1088/0953-2048/9/7/006
Abstract: We optimized the deposition of YBa2(Cu1-xZnx)(3)O-7-delta thin-films using inverted cylindrical magnetron sputtering and report here a detailed structural study, especially in relation to crystal growth, associated surface morphology, Y2O3 precipitation and other secondary phases important for flux pinning. We find that the epitaxial quality of the Zn-substituted YBa2Cu3O7-delta films is decreased compared with high-quality pure YBa2Cu3O7-delta films prepared under identical conditions. The pure films have smoother surfaces, while those of Zn-substituted films contain pinholes and outgrowths. Secondary phases and a-axis grains were observed in the Zn-substituted films. Y2O3 precipitates with typical dimensions of 50-100 Angstrom have been found in both pure and Zn-substituted samples. However, their density of about 10(23) m(-3), observed in the pure films, is significantly reduced in the Zn-substituted films when increasing the Zn concentration up to 4%.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.325
Times cited: 7
DOI: 10.1088/0953-2048/9/7/006
|
|
|
“Structural requirements in lithium cobalt oxides for the catalytic oxidation of water”. Gardner GP, Go YB, Robinson DM, Smith PF, Hadermann J, Abakumov A, Greenblatt M, Dismukes GC, Angewandte Chemie: international edition in English 51, 1616 (2012). http://doi.org/10.1002/anie.201107625
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 11.994
Times cited: 119
DOI: 10.1002/anie.201107625
|
|
|
“Structural studies of diamond thin films grown from the arc plasma”. Nistor LC, van Landuyt J, Journal of materials research 12, 2533 (1998)
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 1.673
Times cited: 13
|
|
|
“Structural studies of nanocrystalline diamond thin films”. Nistor LC, van Landuyt J, Ralchenko VG, Obratzova ED, Korothushenko KG, Smolin AA, Materials science forum 239-241, 115 (1997)
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
|
|
|
“Structural studies on new ternary oxides Ba8Ta4Ti3O24 and Ba10Ta7.04Ti1.2O30”. Shpanchenko RV, Nistor L, Van Tendeloo G, van Landuyt J, Amelinckx S, Journal of solid state chemistry 114, 560 (1995). http://doi.org/10.1006/jssc.1995.1086
Abstract: The ternary oxides Ba8Ta4Ti3O24 and Ba10Ta7.04Ti1.2O30 were synthesized and their crystal structures and defects were studied by means of X-ray powder diffraction, electron diffraction, and high resolution electron microscopy. The crystal structure of Ba8Ta4Ti3O24 is based on the 8H (cchc)(2) close-packed stacking (a 10.0314 Angstrom, c = 18.869 Angstrom, SG P6(3)/mcm, Z = 3) and that of Ba10Ta7.04Ti1.2O30 and on the 10H (cchcc)(2) close-packed stacking (a = 5.7981 Angstrom, c = 23.755 Angstrom, SG P6(3)/mmc, Z = 1) of BaO3 layers. The structural refinements gave the following values for the R factors for Ba8Ta4Ti3O24 (Ba10Ta7.04Ti1.2O30) R(I) = 0.041 (0.039), R(P) = 0.108 (0.118), and R(wP) = 0.094 (0.099). The main feature of both structures is the presence of two types of face-sharing octahedra (FSO) with different occupancies by Ta atoms, Ti atoms, and vacancies, which results in the formation of a superstructure. It was shown that in the Ba8Ta4Ti3O24 structure these pairs of FSO occur in an ordered fashion and in the Ba10Ta7.04Ti1.2O30 structure in a disordered fashion. The existence of the wide range of solid solutions was shown to be also a consequence of the presence of one of the two types of face-sharing octahedra. (C) 1995 Academic Press, Inc,
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.133
Times cited: 23
DOI: 10.1006/jssc.1995.1086
|
|
|
“Structural studies on superconducting materials and fullerites by electron microscopy”. Van Tendeloo G, Amelinckx S, Advanced materials 5, 620 (1993). http://doi.org/10.1002/adma.19930050904
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 17.493
Times cited: 2
DOI: 10.1002/adma.19930050904
|
|
|
“Structural study of the new complex oxides Ba5-ySryR2-xAl2Zr1+xO13+x/2 (R=Gd-Lu, Y, Sc)”. Shpanchenko RV, Abakumov AM, Antipov EV, Nistor L, Van Tendeloo G, Amelinckx S, Journal of solid state chemistry 118, 180 (1995). http://doi.org/10.1006/jssc.1995.1329
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.133
Times cited: 8
DOI: 10.1006/jssc.1995.1329
|
|
|
“Structural, textural, and electronic properties of a nanosized mesoporous ZnxTi1-xO2-x solid solution prepared by a supercritical drying route”. Kolen'ko YV, Kovnir KA, Gavrilov AI, Garshev AV, Meskin PE, Churagulov BR, Bouchard M, Colbeau-Justin C, Lebedev OI, Van Tendeloo G, Yoshimura M, Journal of physical chemistry B 109, 20303 (2005). http://doi.org/10.1021/jp0535341
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 3.177
Times cited: 34
DOI: 10.1021/jp0535341
|
|
|
“Structural transformation in fluorinated LaACuGaO5 (A=Ca, Sr) brownmillerites”. Hadermann J, Van Tendeloo G, Abakumov AM, Pavlyuk BP, Rozova MG, Antipov EV, International journal of inorganic materials 2, 493 (2000). http://doi.org/10.1016/S1466-6049(00)00072-6
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Times cited: 13
DOI: 10.1016/S1466-6049(00)00072-6
|
|
|
“Structural transformations in the fluorinated T* phase”. Hadermann J, Abakumov AM, Lebedev OI, Van Tendeloo G, Rozova MG, Shpanchenko RV, Pavljuk BP, Kopnin EM, Antipov EV, Journal of solid state chemistry 147, 647 (1999). http://doi.org/10.1006/jssc.1999.8438
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.299
Times cited: 8
DOI: 10.1006/jssc.1999.8438
|
|
|
“Structural transitions in a classical two-dimensional molecule system”. Ferreira WP, Farias GA, Carmona HA, Peeters FM, Solid state communications 122, 665 (2002). http://doi.org/10.1016/S0038-1098(02)00157-6
Abstract: The ground state of a classical two-dimensional (2D) system with a finite number of charge particles, trapped by two positive impurity charges localized at a distance (z(0)) from the. 2D plane and separated from each other by a distance chi(p) are obtained. The impurities are allowed to carry more than one positive charge. This classical system can form a 2D-like classical molecule that exhibits structural transitions and spontaneous symmetry breaking as function of the separation between the positive charges before it transforms into two 2D-like classical atoms. We also observe structural transitions as a function of the dielectric constant of the substrate which supports the charged particles, in addition to broken symmetry states and unbinding of particles. (C) 2002 Elsevier Science Ltd. All rights reserved.
Keywords: A1 Journal article; Condensed Matter Theory (CMT)
Impact Factor: 1.554
Times cited: 3
DOI: 10.1016/S0038-1098(02)00157-6
|
|
|
“Structural transitions in a finite classical two-dimensional system”. Farias GA, Peeters FM, Solid state communications 100, 711 (1996). http://doi.org/10.1016/0038-1098(96)00438-3
Keywords: A1 Journal article; Condensed Matter Theory (CMT)
Impact Factor: 1.897
Times cited: 25
DOI: 10.1016/0038-1098(96)00438-3
|
|
|
“Structural variants of Ca0.85CuO2(Ca5+xCu6O12)”. Milat O, Van Tendeloo G, Amelinckx S, Babu TGN, Greaves C, Journal of solid state chemistry 101, 92 (1992). http://doi.org/10.1016/0022-4596(92)90205-A
Abstract: The structure of Ca0.85CuO2 was reexamined by means of electron diffraction and electron microscopy using the newly developed method of selective imaging in intergrowth structures in which the two substructures are based on different sublattices. The results of previous work are confirmed. Moreover, it is shown that two stacking variants and their twin related structures occur in the calcium substructure. The copper-oxygen substructure occurs in one variant only; it is often modulated by the various calcium arrangements, leading to phase disorder in its modulation pattern. It is shown that the ribbons of CuO4 clusters are presumably tilted with respect to the (010) plane.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.133
Times cited: 10
DOI: 10.1016/0022-4596(92)90205-A
|
|
|
“Structure and correlations in two-dimensional classical artificial atoms confined by a Coulomb potential”. Ferreira WP, Matulis A, Farias GA, Peeters FM, Physical review : E : statistical, nonlinear, and soft matter physics 67, 046601 (2003). http://doi.org/10.1103/PhysRevE.67.046601
Abstract: The ordering of N equally charged particles (-e) moving in two dimensions and confined by a Coulomb potential, resulting from a displaced positive charge Ze is discussed. This is a classical model system for atoms. We obtain the configurations of charged particles which, depending on the value of N and Z, may result in ring structures, hexagonal-type configurations, and for N/Z approximate to 1 in an inner structure of particles which is separated by an outer ring of particles. For N/Z << 1, the Hamiltonian of the parabolic confinement case is recovered. For N/Z approximate to 1, the configurations are very different from those found in the case of a parabolic confinement potential. A hydrodynamic analysis is presented in order to highlight the correlations effects.
Keywords: A1 Journal article; Condensed Matter Theory (CMT)
Impact Factor: 2.366
Times cited: 14
DOI: 10.1103/PhysRevE.67.046601
|
|
|
“The structure and energetics of B3N2, B2N3, and BN4: symmetry breaking effects in B3N2”. Martin JML, El-Yazal J, François JP, Gijbels R, Molecular physics 85, 527 (1995). http://doi.org/10.1080/00268979500101281
Keywords: A1 Journal article; Plasma Lab for Applications in Sustainability and Medicine – Antwerp (PLASMANT)
Impact Factor: 1.72
Times cited: 19
DOI: 10.1080/00268979500101281
|
|
|
“Structure and function of p53-DNA complexes with inactivation and rescue mutations : a molecular dynamics simulation study”. Kamaraj B, Bogaerts A, PLoS ONE 10, e0134638 (2015). http://doi.org/10.1371/journal.pone.0134638
Abstract: The tumor suppressor protein p53 can lose its function upon DNA-contact mutations (R273C and R273H) in the core DNA-binding domain. The activity can be restored by second-site suppressor or rescue mutations (R273CT284R, R273HT284R, and R273HS240R). In this paper, we elucidate the structural and functional consequence of p53 proteins upon DNA-contact mutations and rescue mutations and the underlying mechanisms at the atomic level by means of molecular dynamics simulations. Furthermore, we also apply the docking approach to investigate the binding phenomena between the p53 protein and DNA upon DNA-contact mutations and rescue mutations. This study clearly illustrates that, due to DNA-contact mutants, the p53 structure loses its stability and becomes more rigid than the native protein. This structural loss might affect the p53-DNA interaction and leads to inhibition of the cancer suppression. Rescue mutants (R273CT284R, R273HT284R and R273HS240R) can restore the functional activity of the p53 protein upon DNA-contact mutations and show a good interaction between the p53 protein and a DNA molecule, which may lead to reactivate the cancer suppression function. Understanding the effects of p53 cancer and rescue mutations at the molecular level will be helpful for designing drugs for p53 associated cancer diseases. These drugs should be designed so that they can help to inhibit the abnormal function of the p53 protein and to reactivate the p53 function (cell apoptosis) to treat human cancer.
Keywords: A1 Journal article; Engineering sciences. Technology; Plasma Lab for Applications in Sustainability and Medicine – Antwerp (PLASMANT)
Impact Factor: 2.806
DOI: 10.1371/journal.pone.0134638
|
|
|
“Structure and high-temperature properties of the (Sr,Ca,Y)(Co,Mn)O3-y perovskites –, perspective cathode materials for IT-SOFC”. Napolsky PS, Drozhzhin OA, Istomin SY, Kazakov SM, Antipov EV, Galeeva AV, Gippius AA, Svensson G, Abakumov AM, Van Tendeloo G, Journal of solid state chemistry 192, 186 (2012). http://doi.org/10.1016/j.jssc.2012.03.056
Abstract: Oxygen deficient perovskites Sr0.75Y0.25Co1-xMnxO3-y, x=0.5 and 0.75, were prepared by using the citrate route at 1373-1573 K for 48 h. The cubic Pm-3m perovskite structure for x=0.5 was confirmed by electron diffraction study and refined using neutron powder diffraction (NPD) data. For x=0.75, the superstructure corresponding to a=root 2 x a(per), b=2 x a(per), c=root 2 x a(per) (a(0)b(-)b(-) tilt system, space group Imma) was revealed by electron diffraction. The solid solution Sr0.75-xCaxY0.25Co0.25Mn0.75O3-y, 0.1 <= x <= 0.6 and compound Ca0.75Y0.25Mn0.85Co0.15O2.92 were prepared in air at 1573 K for 48 h. The crystal structure of Ca0.75Y0.25Mn0.85Co0.15O2.92 was refined using NPD data (S.G. Pnma, a=5.36595(4), b=7.5091(6), c=5.2992(4) angstrom, R-p=0.057, R-wp=0.056, chi(2)=4.26). High-temperature thermal expansion properties of the prepared compounds were studied in air using both dilatometry and high-temperature X-ray powder diffraction data (HTXRPD). They expanding non-linearly at 298-1073 K due to the loss of oxygen at high temperatures. Calculated average thermal expansion coefficients (TECs) for Sr0.75Y0.25Co1-xMnxO3-y, x=0.5, 0.75 and Ca0.75Y0.25Mn0.85Co0.15O2.92(1) are 15.5, 15.1, and 13.8 ppm K-1, respectively. Anisotropy of the thermal expansion along different unit cell axes was observed for Sr0.15Ca0.6Y0.25Co0.25Mn0.75O3-y, and Ca0.75Y0.25Mn0.85Co0.15O2.92. Conductivity of Sr0.75Y0.25Co1-xMnxO3-y, x=0.5 and 0.75 increases with the temperature reaching 110 S/cm for x=0.5 and 44 S/cm for x=0.75 at 1173 K. Samples of Sr0.75-xCaxY0.25Co0.25Mn0.75O3-y, 0.1 <= y <= 0.6 were found to be n-type conductors at room temperature with the similar temperature dependence of the conductivity and demonstrated the increase of the sigma value from similar to 1 to similar to 50 S/cm as the temperature increases from 300 to 1173 K. Their conductivity is described in terms of the small polaron charge transport with the activation energy (E-p) increasing from 340 to 430 meV with an increase of the calcium content from x=0 to x=0.6. (C) 2012 Elsevier Inc. All rights reserved.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.299
Times cited: 5
DOI: 10.1016/j.jssc.2012.03.056
|
|
|
Martin JML, Franç,ois JP, Gijbels R, Almlö,f J (1991) Structure and infrared spectroscopy of the C11 molecule. University of Minnesota, Minneapolis, Minn
Keywords: MA3 Book as author; Plasma Lab for Applications in Sustainability and Medicine – Antwerp (PLASMANT)
|
|
|
“Structure and infrared spectroscopy of the C11 molecule”. Martin JML, François JP, Gijbels R, Almlöf J, Chemical physics letters 187, 367 (1991). http://doi.org/10.1016/0009-2614(91)80267-2
Keywords: A1 Journal article; Plasma Lab for Applications in Sustainability and Medicine – Antwerp (PLASMANT)
Impact Factor: 1.897
Times cited: 42
DOI: 10.1016/0009-2614(91)80267-2
|
|
|
“Structure and magnetic properties of a new anion-deficient perovskite Pb2Ba2BiFe4ScO13 with crystallographic shear structure”. Batuk M, Tyablikov OA, Tsirlin AA, Kazakov SM, Rozova MG, Pokholok KV, Filimonov DS, Antipov EV, Abakumov AM, Hadermann J, Materials research bulletin 48, 3459 (2013). http://doi.org/10.1016/j.materresbull.2013.05.028
Abstract: Pb2Ba2BiFe4ScO13, a new n = 5 member of the oxygen-deficient perovskite-based A(n)B(n)O(3n-2) homologous series, was synthesized using a solid-state method. The crystal structure of Pb2Ba2BiFe4ScO13 was investigated by a combination of synchrotron X-ray powder diffraction, electron diffraction, high-angle annular dark-field scanning transmission electron microscopy and Mossbauer spectroscopy. At 900 K, it crystallizes in the Ammm space group with the unit cell parameters a = 5.8459(1) angstrom, b = 4.0426(1) angstrom, and c=27.3435(1) angstrom. In the Pb2Ba2BiFe4ScO13 structure, quasi-two-dimensional perovskite blocks are periodically interleaved with 1/2[1 1 0] ((1) over bar 0 1)(p) crystallographic shear (CS) planes. At the CS planes, the corner-sharing FeO6 octahedra are transformed into chains of edge-sharing FeO5 distorted tetragonal pyramids. B-positions of the perovskite blocks between the CS planes are jointly occupied by Fe3+ and Sc3+. The chains of the FeO5 pyramids and (Fe,Sc)O-6 octahedra delimit six-sided tunnels that are occupied by double columns of cations with a lone electron pair (Pb2+). The remaining A-cations (Bi3+, Ba2+) occupy positions in the perovskite block. According to the magnetic susceptibility measurements, Pb2Ba2BiFe4ScO13 is antiferromagnetically ordered below T-N approximate to 350 K. (C) 2013 Elsevier Ltd. All rights reserved.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.446
Times cited: 2
DOI: 10.1016/j.materresbull.2013.05.028
|
|
|
“Structure and magnetotransport properties of La2/3Ca1/3MnO3 thin films prepared by pulsed laser deposition”. Lebedev OI, Van Tendeloo G, Amelinckx S, Leibold B, Habermeier HU, Phillipp F, Materials Research Society symposium proceedings
T2 –, Symposium on Advances in Laser Ablation of Materials at the 1998 MRS, Spring Meeting, April 13-16, 1998, San Francisco, Calif. , 219 (1998). http://doi.org/10.1557/PROC-526-219
Abstract: La1-xCaxMnO3-delta (LCMO) thin films are grown by pulsed laser deposition on a (100) SrTiO3 substrate at temperatures between 530 degrees C and 890 degrees C. The magnetotransport properties show a high negative magnetoresistance and a shift of the maximum of the R(T) curve as function of temperature. The Curie temperature changes with deposition temperature and film quality in the range of 100-220K. The film quality is characterised by X-ray diffraction and transmission electron microscopy (TEM); film and target compositions were verified by atomic emission spectroscopy. The local structure of the film depends on the growth conditions and substrate temperature. TEM reveals a slight distortion of the film leading to a breakdown of the symmetry from orthorhombic to monoclinic. At the highest growth temperatures, a well defined interface is observed within the LCMO film, parallel to the substrate surface; this interface divides the film into two lamellae with a different microstructure. The lamella close to the substrate is perfectly coherent with the substrate, suggesting that it is strained as a result of the lattice parameter mismatch; the upper lamella shows a typical domain structure with unusual translation interfaces characterised by a displacement vector of the type 1/2[010](m) and 1/2[001](m) when referred ten the monoclinic lattice.
Keywords: P1 Proceeding; Electron microscopy for materials research (EMAT)
DOI: 10.1557/PROC-526-219
|
|
|
“The structure and manipulation of vortex states in a superconducting square with 2 ×, 2 blind holes”. Berdiyorov GR, Milošević, MV, Peeters FM, Journal of low temperature physics 139, 229 (2005). http://doi.org/10.1007/s10909-005-3926-z
Keywords: A1 Journal article; Condensed Matter Theory (CMT)
Impact Factor: 1.3
Times cited: 4
DOI: 10.1007/s10909-005-3926-z
|
|
|
“Structure and microstructure of epitaxial Sr4Fe6O13-\delta films on SrTiO3”. Rossell MD, Abakumov AM, Van Tendeloo G, Pardo JA, Santiso J, Chemistry and materials 16, 2578 (2004). http://doi.org/10.1021/cm0498234
Abstract: The crystal structure and the microstructure of epitaxial Sr4Fe6O13+/-delta thin films grown on a single-crystal SrTiO3 substrate by PLD have been investigated. A combination of electron diffraction and high-resolution microscopy allows us to refine the structure and to identify an incommensurate modulation in the Sr4Fe6O13+/-delta films. The incommensurate structure (q = alphaa(m)* approximate to 0.39alpha(m)*, superspace group Xmmm(alpha00)0s0) can be interpreted as an oxygen-deficient modification in the Fe2O2.5 double layers. Moreover, it is shown that the experimentally determined a component of the modulation can be used consistently to estimate the local oxygen content in the Sr4Fe6O13+/-delta films. The compound composition can therefore be described as Sr4Fe6O12+2alpha and the value alpha = 0.39 corresponds to a Sr4Fe6O12.78 composition. The misfit stress along the Sr4Fe6O13+/-delta/SrTiO3 interface is accommodated via both elastic deformation and inelastic mechanisms (misfit dislocations and 90degrees rotation twins). The present results also suggest the existence of SrFeO3 perovskite in the Sr4Fe6O13+/-delta films.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 9.466
Times cited: 26
DOI: 10.1021/cm0498234
|
|
|
“Structure and microstructure of La1-xCaxMnO3- thin films prepared by pulsed layer deposition”. Lebedev OI, Van Tendeloo G, Amelinckx S, Leibold B, Habermeier H-U, Physical review : B : condensed matter and materials physics 58, 8065 (1998). http://doi.org/10.1103/PhysRevB.58.8065
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 3.836
Times cited: 131
DOI: 10.1103/PhysRevB.58.8065
|
|
|
“Structure and phase transitions in C60 and C70 fullerites”. Van Tendeloo G, Muto S, van Heurck C, Amelinckx S, , 476 (1992)
Keywords: P3 Proceeding; Electron microscopy for materials research (EMAT)
Times cited: 1
|
|
|
“Structure and properties of (Sr,Ca)CuO2-BaCuO2 superlattices grown by pulsed laser interval deposition”. Koster G, Verbist K, Rijnders G, Rogalla H, Van Tendeloo G, Blank DHA, Physica: C : superconductivity 353, 167 (2001). http://doi.org/10.1016/S0921-4534(00)01763-9
Abstract: We report on the preparation of CuBa(2)(Sr(x)Ca(1-x))(n)Cu(n-1)O(y) compounds by fabrication of (Ba,Sr,Ca)CuO(2) superlattices with pulsed laser deposition (PLD). A technique called interval deposition is used to suppress multi-level or island growth resulting in high-quality superlattice structures. Both, the applicability of PLD to atomic engineering as well as the fabrication of artificial superconductors is demonstrated. The (Sr,Ca)CuO(2)-BaCuO(2) superlattices are characterized by X-ray diffraction, high-resolution electron microscopy (HREM) and selected area electron diffraction. The superlattice period has been deduced from electron diffraction patterns and XRD measurements. For Sr containing films, the best growth behavior is observed and films with the highest degree of crystallinity are obtained, whereas superconductivity is only found in less crystalline, Ca containing films. Under some deposition conditions and depending on the amount of Ba containing layers in the superlattice, it was observed that the BaCuO(2) material is converted to Ba(2)CuO(4-delta). Image simulations to interpret the HREM contrast are performed. (C) 2001 Elsevier Science B.V. All rights reserved.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 1.404
Times cited: 8
DOI: 10.1016/S0921-4534(00)01763-9
|
|
|
“Structure and properties of the YBa2Cu3O7-x/LaAlO3 superlattices”. Lebedev OI, Hamet JF, Van Tendeloo G, Beaumont V, Raveau B, Journal of applied physics 90, 5261 (2001). http://doi.org/10.1063/1.1406963
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.068
Times cited: 13
DOI: 10.1063/1.1406963
|
|
|
“Structure and spectrum of anisotropically confined two-dimensional clusters with logarithmic interaction”. Apolinario SWS, Partoens B, Peeters FM, Physical review : E : statistical physics, plasmas, fluids, and related interdisciplinary topics 72, 046122 (2005). http://doi.org/10.1103/PhysRevE.72.046122
Abstract: We studied the structural and spectral properties of a classical system consisting of a finite number of particles, moving in two dimensions, and interacting through a repulsive logarithmic potential and held together by an anisotropic harmonic potential. Increasing the anisotropy of the confinement potential can drive the system from a two-dimensional (2D) to a one-dimensional (1D) configuration. This change occurs through a sequence of structural transitions of first and second order which are reflected in the normal mode frequencies. Our results of the ground state configurations are compared with recent experiments and we obtained a satisfactory agreement. The transition from the 1D line structure to the 2D structure occurs through a zigzag transition which is of second order. We found analytical expressions for the eigenfrequencies before the zigzag transition, which allowed us to obtain an analytical expression for the anisotropy parameter at which the zigzag transition occurs as a function of the number of particles in the system.
Keywords: A1 Journal article; Condensed Matter Theory (CMT)
Impact Factor: 2.366
Times cited: 22
DOI: 10.1103/PhysRevE.72.046122
|
|
|
“Structure and spectrum of classical two-dimensional clusters with a logarithmic interaction potential”. Partoens B, Deo PS, Physical review : B : condensed matter and materials physics 69, 245415 (2004). http://doi.org/10.1103/PhysRevB.69.245415
Keywords: A1 Journal article; Condensed Matter Theory (CMT)
Impact Factor: 3.836
Times cited: 12
DOI: 10.1103/PhysRevB.69.245415
|
|
|
“Structure and spectrum of the anisotropically confined two-dimensional Yukawa system”. Cândido L, Rino J-P, Studart N, Peeters FM, Journal of physics : condensed matter 10, 11627 (1998). http://doi.org/10.1088/0953-8984/10/50/004
Keywords: A1 Journal article; Condensed Matter Theory (CMT)
Impact Factor: 2.649
Times cited: 69
DOI: 10.1088/0953-8984/10/50/004
|
|