Abstract: Carbon nitride nanospheres have been synthesized into copper by simultaneous high fluence (10(18) at. cm(-2)) implantations of C-12 and N-15 ions. The composition of the implanted region has been measured using C-12(d,p(0))C-13 and N-15(d,alpha(0))C-13 nuclear reactions induced by a 1.05 MeV deuteron beam. The C-12 and N-15 depth profiles are very close and the retained doses into copper are relatively high, which indicates that carbon and nitrogen diffusion processes are likely limited during implantation. High resolution transmission electron microscopy (HRTEM) observations and electron diffraction (ED) analyses have been carried out to determine the structure of the nanospheres formed during implantation. Some consist in small hollow amorphous nanocapsules with sizes ranging from 30 to 100 nm. Large gas bubbles with diameters up to 300 mn have also been observed in the copper matrix. Electron energy-loss spectroscopy (EELS) measurements performed on the small nanocapsules indicate that their shells are composed of carbon and nitrogen. (c) 2007 Elsevier B.V. All rights reserved.

Abstract: In this work, GaN growth on porous Si(111) will be reported. The porosity of the substrates was 30% or 50%. In the latter case, various thicknesses, from 0.6 mu m to 10 mu m, were investigated. The morphology of the GaN surfaces was analyzed by optical interference microscopy. The crystalline quality of the epitaxial layers was characterized by High Resolution X-Ray Diffraction (HR-XRD) and cross-sectional Transmission Electron Microscopy (TEM). A Full Width at Half Maximum (FWHM) of the X-ray symmetric rocking curve (0002) 2 theta – omega scan of 290 arc see was obtained for a 1 mu m thick GaN layer, which is comparable with that of GaN grown on bulk Si(111) substrates. (c) 2007 WILEY-VCH Verlag GmbH Co. KGaA, Weinheim.

Abstract: We compare the magnetic properties of pure and oxidized Co nanoparticles embedded in an amorphous Al2O3 matrix. Nanoparticles with diameters of 2 or 3 nm were prepared by alternate pulsed laser deposition in high vacuum conditions, and some of them were exposed to O-2 after production and before being embedded. The nanoparticles are organized in layers, the effective edge-to-edge in-depth separation being 5 or 10 nm. The lower saturation magnetizations per Co atom for the samples containing oxidized nanoparticles provide evidence for the formation of antiferromagnetic CoO shells in the nanoparticles. None of the samples with Co/CoO nanoparticles show exchange bias, while vertical hysteresis loop shifts and enhanced coercivities (as compared to samples with pure Co nanoparticles) are observed. This constitutes evidence for the nanoparticles size being in all cases smaller than the critical size for exchange bias. The difference in coercivity versus temperature dependences for the samples with pure and oxidized Co nanoparticles shows that the exchange anisotropy in Co/CoO nanoparticles appears at temperatures lower than 50 K. (c) 2007 American Institute of Physics.

Abstract: Focused ion beam specimen preparation has been used for NiTi samples and SrTiO(3)/SrRuO(3) multilayers with prevention of surface amorphization and Ga implantation by a 2-kV cleaning procedure. Transmission electron microscopy techniques show that the samples are of high quality with a controlled thickness over large scales. Furthermore, preferential thinning effects in multicompounds are avoided, which is important when analytical transmission electron microscopy measurements need to be interpreted in a quantitative manner. The results are compared to similar measurements acquired for samples obtained using conventional preparation techniques such as electropolishing for alloys and ion milling for oxides.