Kurttepeli M (2015) Carbon based materials and hybrid nanostructures investigated by advanced transmission electron microscopy. Antwerpen
Keywords: Doctoral thesis; Electron microscopy for materials research (EMAT)
|
|
|
“Catalyst design by NH4OH treatment of USY zeolite”. Van Aelst J, Verboekend D, Philippaerts A, Nuttens N, Kurttepeli M, Gobechiya E, Haouas M, Sree SP, Denayer JFM, Martens JA, Kirschhock CEA, Taulelle F, Bals S, Baron GV, Jacobs PA, Sels BF, Advanced functional materials 25, 7130 (2015). http://doi.org/10.1002/adfm.201502772
Abstract: Hierarchical zeolites are a class of superior catalysts which couples the intrinsic zeolitic properties to enhanced accessibility and intracrystalline mass transport to and from the active sites. The design of hierarchical USY (Ultra-Stable Y) catalysts is achieved using a sustainable postsynthetic room temperature treatment with mildly alkaline NH4OH ( 0.02(M)) solutions. Starting from a commercial dealuminated USY zeolite (Si/Al = 47), a hierarchical material is obtained by selective and tuneable creation of interconnected and accessible small mesopores (2- 6 nm). In addition, the treatment immediately yields the NH4+ form without the need for additional ion exchange. After NH4OH modification, the crystal morphology is retained, whereas the microporosity and relative crystallinity are decreased. The gradual formation of dense amorphous phases throughout the crystal without significant framework atom leaching rationalizes the very high material yields (>90%). The superior catalytic performance of the developed hierarchical zeolites is demonstrated in the acid-catalyzed isomerization of alpha-pinene and the metal-catalyzed conjugation of safflower oil. Significant improvements in activity and selectivity are attained, as well as a lowered susceptibility to deactivation. The catalytic performance is intimately related to the introduced mesopores, hence enhanced mass transport capacity, and the retained intrinsic zeolitic properties.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 12.124
Times cited: 64
DOI: 10.1002/adfm.201502772
|
|
|
“Combined macroscopic, nanoscopic, and atomic-scale characterization of gold-ruthenium bimetallic catalysts for octanol oxidation”. Chinchilla LE, Olmos C, Kurttepeli M, Bals S, Van Tendeloo G, Villa A, Prati L, Blanco G, Calvino JJ, Chen X, Hungría AB, Particle and particle systems characterization 33, 419 (2016). http://doi.org/10.1002/ppsc.201600057
Abstract: A series of gold-ruthenium bimetallic catalysts of increasing Au:Ru molar ratios supported on a Ce0.62Zr0.38O2 mixed oxide are prepared and their structural and chemical features characterized by a combination of macroscopic and atomic-scale techniques based on scanning transmission electron microscopy. The influence of the temperature of the final reduction treatment used as activation step (350-700 degrees C range) is also investigated. The preparation method used allows catalysts to be successfully prepared where a major fraction of the metal nanoparticles is in the size range below 5 nm. The structural complexities characteristic of this type of catalysts are evidenced, as well as the capabilities and limitations of both the macroscopic and microscopic techniques in the characterization of the system of metal nanoparticles. A positive influence of the addition of Ru on both the resistance against sintering and the catalytic performance of the starting supported Au catalyst is evidenced.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 4.474
Times cited: 7
DOI: 10.1002/ppsc.201600057
|
|
|
“Core-shell-corona doxorubicin-loaded superparamagnetic Fe3O4 nanoparticles for cancer theranostics”. Semkina A, Abakumov M, Grinenko N, Abakumov A, Skorikov A, Mironova E, Davydova G, Majouga AG, Nukolova N, Kabanov A, Chekhonin V;, Colloids and surfaces: B : biointerfaces 136, 1073 (2015). http://doi.org/10.1016/j.colsurfb.2015.11.009
Abstract: Superparamagnetic iron oxide magnetic nanoparticles (MNPs) are successfully used as contrast agents in magnetic-resonance imaging. They can be easily functionalized for drug delivery functions, demonstrating great potential for both imaging and therapeutic applications. Here we developed new pH-responsive theranostic core-shell-corona nanoparticles consisting of superparamagentic Fe3O4 core that displays high T2 relaxivity, bovine serum albumin (BSA) shell that binds anticancer drug, doxorubicin (Dox) and poly(ethylene glycol) (PEG) corona that increases stability and biocompatibility. The nanoparticles were produced by adsorption of the BSA shell onto the Fe3O4 core followed by crosslinking of the protein layer and subsequent grafting of the PEG corona using monoamino-terminated PEG via carbodiimide chemistry. The hydrodynamic diameter, zeta-potential, composition and T2 relaxivity of the resulting nanoparticles were characterized using transmission electron microscopy, dynamic light scattering, thermogravimetric analysis and T2-relaxometry. Nanoparticles were shown to absorb Dox molecules, possibly through a combination of electrostatic and hydrophobic interactions. The loading capacity (LC) of the nanoparticles was 8 wt.%. The Dox loaded nanoparticles release the drug at a higher rate at pH 5.5 compared to pH 7.4 and display similar cytotoxicity against C6 and HEK293 cells as the free Dox. (C) 2015 Elsevier B.V. All rights reserved.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 3.887
Times cited: 37
DOI: 10.1016/j.colsurfb.2015.11.009
|
|
|
“Deactivation study of Fe2O3-CeO2 during redox cycles for CO production from CO2”. Dharanipragada NVRA, Meledina M, Galvita VV, Poelman H, Turner S, Van Tendeloo G, Detavernier C, Marin GB, Industrial and engineering chemistry research 55, 5911 (2016). http://doi.org/10.1021/acs.iecr.6b00963
Abstract: Deactivation was investigated in Fe2O3-CeO2 oxygen storage materials during repeated H-2-reduction and CO2-reoxidation. In situ XRD, XAS, and TEM were used to identify phases, crystallite sizes, and morphological changes upon cycling operation. The effect of redox cycling was investigated both in Fe-rich (80 wt % Fe2O3-CeO2) and Ce-rich (10 wt %Fe2O3-CeO2) materials. The former consisted of 100 nm Fe2O3 particles decorated with 5-10 nm Ce1-xFexO2-x. The latter presented CeO2 with incorporated Fe, i.e. a solid solution of Ce1-xFexO2-x, as the main oxygen carrier. By modeling the EXAFS Ce-K signal for as-prepared 10 wt %Fe2O3-CeO2, the amount of Fe in CeO2 was determined as 21 mol %, corresponding to 86% of the total iron content. Sintering and solid solid transformations, the latter including both new phase formation and element segregation, were identified as deactivation pathways upon redox cycling. In Ce-rich material, perovskite (CeFeO3) was identified by XRD. This phase remained inert during reduction and reoxidation, resulting in an overall lower oxygen storage capacity. Further, Fe segregated from the solid solution, thereby decreasing its reducibility. In addition, an increase in crystallite size occurred for all phases. In Fe-rich material, sintering is the main deactivation pathway, although Fe segregation from the solid solution and perovskite formation cannot be excluded.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.843
Times cited: 26
DOI: 10.1021/acs.iecr.6b00963
|
|
|
“Dislocation and back stress dominated viscoplasticity in freestanding sub-micron Pd films”. Lemoine G, Delannay L, Idrissi H, Colla M-S, Pardoen T, Acta materialia 111, 10 (2016). http://doi.org/10.1016/j.actamat.2016.03.038
Abstract: A dislocation-based crystal plasticity model is developed in order to study the mechanical and creep/ relaxation behaviour of polycrystalline metallic thin films. The model accounts for the confinement of plasticity due to grain boundaries and for the anisotropy of individual grains, as well as for the significant viscoplastic effects associated to dislocation dominated thermally activated mechanisms. Numerical predictions are assessed based on experimental tensile test followed by relaxation on freestanding Pd films, based on an on-chip test technique. The dislocation-based mechanism assumption captures all the experimental trends, including the stress strain response, the relaxation behaviour and the dislocation density evolution, confirming the dominance of a dislocation driven deformation mechanism for the present Pd films with high defects density. The model has also been used to address some original experimental evidences involving back stresses, Bauschinger effect, backward creep and strain recovery. (C) 2016 Acta Materialia Inc. Published by Elsevier Ltd. All rights reserved.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 5.301
Times cited: 6
DOI: 10.1016/j.actamat.2016.03.038
|
|
|
“Thickness dependence of scattering cross-sections in quantitative scanning transmission electron microscopy”. Martinez GT, van den Bos KHW, Alania M, Nellist PD, Van Aert S, Ultramicroscopy 187, 84 (2018). http://doi.org/10.1016/j.ultramic.2018.01.005
Abstract: In quantitative scanning transmission electron microscopy (STEM), scattering cross-sections have been shown to be very sensitive to the number of atoms in a column and its composition. They correspond to the integrated intensity over the atomic column and they outperform other measures. As compared to atomic column peak intensities, which saturate at a given thickness, scattering cross-sections increase monotonically. A study of the electron wave propagation is presented to explain the sensitivity of the scattering cross-sections. Based on the multislice algorithm, we analyse the wave propagation inside the crystal and its link to the scattered signal for the different probe positions contained in the scattering cross-section for detector collection in the low-, middle- and high-angle regimes. The influence to the signal from scattering of neighbouring columns is also discussed.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.843
Times cited: 4
DOI: 10.1016/j.ultramic.2018.01.005
|
|
|
Van Boxem R (2015) Electron vortex beams : an in-depth theoretical study. Antwerpen
Keywords: Doctoral thesis; Electron microscopy for materials research (EMAT)
|
|
|
“Engineering properties by long range symmetry propagation initiated at perovskite heterostructure interface”. Liao ZL, Green RJ, Gauquelin N, Gonnissen J, Van Aert S, Verbeeck J, et al, Advanced functional materials , 1 (2016)
Abstract: In epitaxial thin film systems, the crystal structure and its symmetry deviate from the bulk counterpart due to various mechanisms such as epitaxial strain and interfacial structural coupling, which induce an accompanying change in their properties. In perovskite materials, the crystal symmetry can be described by rotations of 6-fold coordinated transition metal oxygen octahedra, which are found to be altered at interfaces. Here, we unravel how the local oxygen octahedral coupling (OOC) at perovskite heterostructural interfaces initiates a different symmetry in epitaxial films and provide design rules to induce various symmetries in thin films by careful selecting appropriate combinations of substrate/buffer/film. Very interestingly we discovered that these combinations lead to symmetry changes throughout the full thickness of the film. Our results provide a deep insight into understanding the origin of induced crystal symmetry in a perovskite heterostructure and an intelligent route to achieve unique functional properties.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 12.124
|
|
|
“Exceptional layered ordering of cobalt and iron in perovskites”. Lebedev OI, Turner S, Caignaert V, Cherepanov VA, Raveau B, Chemistry of materials 28, 2907 (2016). http://doi.org/10.1021/acs.chemmater.6b01046
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 9.466
Times cited: 4
DOI: 10.1021/acs.chemmater.6b01046
|
|
|
Guzzinati G (2015) Exploring electron beam shaping in transmission electron microscopy. Antwerpen
Keywords: Doctoral thesis; Electron microscopy for materials research (EMAT)
|
|
|
“Gas-phase synthesis of Mg-Ti nanoparticles for solid-state hydrogen storage”. Calizzi M, Venturi F, Ponthieu M, Cuevas F, Morandi V, Perkisas T, Bals S, Pasquini L, Physical chemistry, chemical physics 18, 141 (2016). http://doi.org/10.1039/c5cp03092g
Abstract: Mg-Ti nanostructured samples with different Ti contents were prepared via compaction of nanoparticles grown by inert gas condensation with independent Mg and Ti vapour sources. The growth set-up offered the option to perform in situ hydrogen absorption before compaction. Structural and morphological characterisation was carried out by X-ray diffraction, energy dispersive spectroscopy and electron microscopy. The formation of an extended metastable solid solution of Ti in hcp Mg was detected up to 15 at% Ti in the as-grown nanoparticles, while after in situ hydrogen absorption, phase separation between MgH2 and TiH2 was observed. At a Ti content of 22 at%, a metastable Mg-Ti-H fcc phase was observed after in situ hydrogen absorption. The co-evaporation of Mg and Ti inhibited nanoparticle coalescence and crystallite growth in comparison with the evaporation of Mg only. In situ hydrogen absorption was beneficial to subsequent hydrogen behaviour, studied by high pressure differential scanning calorimetry and isothermal kinetics. A transformed fraction of 90% was reached within 100 s at 300 degrees C during both hydrogen absorption and desorption. The enthalpy of hydride formation was not observed to differ from bulk MgH2.
Keywords: A1 Journal article; Engineering Management (ENM); Electron microscopy for materials research (EMAT)
Impact Factor: 4.123
Times cited: 31
DOI: 10.1039/c5cp03092g
|
|
|
“Giant magnetoresistance in the half-metallic double-perovskite ferrimagnet Mn2FeReO6”. Li MR, Retuerto M, Deng Z, Stephens PW, Croft M, Huang Q, Wu H, Deng X, Kotliar G, Sánchez-Benítez J, Hadermann J, Walker D, Greenblatt M;, Angewandte Chemie: international edition in English 54, 12069 (2015). http://doi.org/10.1002/anie.201506456
Abstract: The first transition-metal-only double perovskite compound, Mn2+ Fe-2(3+) Re5+ O-6, with 17 unpaired d electrons displays ferrimagnetic ordering up to 520K and a giant positive magnetoresistance of up to 220% at 5K and 8 T. These properties result from the ferrimagnetically coupled Fe and Re sublattice and are affected by a two-to-one magnetic-structure transition of the Mn sublattice when a magnetic field is applied. Theoretical calculations indicate that the half-metallic state can be mainly attributed to the spin polarization of the Fe and Re sites.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 11.994
DOI: 10.1002/anie.201506456
|
|
|
“Highly efficient rutile TiO2 photocatalysts with single Cu(II) and Fe(III) surface catalytic sites”. Neubert S, Mitoraj D, Shevlin SA, Pulisova P, Heimann M, Du Y, Goh GKL, Pacia M, Kruczała K, Turner S, Macyk W, Guo ZX, Hocking RK, Beranek R;, Journal of materials chemistry A : materials for energy and sustainability 4, 3127 (2016). http://doi.org/10.1039/c5ta07036h
Abstract: Highly active photocatalysts were obtained by impregnation of nanocrystalline rutile TiO2 powders with small amounts of Cu(II) and Fe(III) ions, resulting in the enhancement of initial rates of photocatalytic degradation of 4-chlorophenol in water by factors of 7 and 4, compared to pristine rutile, respectively. Detailed structural analysis by EPR and X-ray absorption spectroscopy (EXAFS) revealed that Cu(II) and Fe(III) are present as single species on the rutile surface. The mechanism of the photoactivity enhancement was elucidated by a combination of DFT calculations and detailed experimental mechanistic studies including photoluminescence measurements, photocatalytic experiments using scavengers, OH radical detection, and photopotential transient measurements. The results demonstrate that the single Cu(II) and Fe(III) ions act as effective cocatalytic sites, enhancing the charge separation, catalyzing “dark” redox reactions at the interface, thus improving the normally very low quantum yields of UV light-activated TiO2 photocatalysts. The exact mechanism of the photoactivity enhancement differs depending on the nature of the cocatalyst. Cu(II)-decorated samples exhibit fast transfer of photogenerated electrons to Cu(II/I) sites, followed by enhanced catalysis of dioxygen reduction, resulting in improved charge separation and higher photocatalytic degradation rates. At Fe(III)-modified rutile the rate of dioxygen reduction is not improved and the photocatalytic enhancement is attributed to higher production of highly oxidizing hydroxyl radicals produced by alternative oxygen reduction pathways opened by the presence of catalytic Fe(III/II) sites. Importantly, it was demonstrated that excessive heat treatment (at 450 degrees C) of photocatalysts leads to loss of activity due to migration of Cu(II) and Fe(III) ions from TiO2 surface to the bulk, accompanied by formation of oxygen vacancies. The demonstrated variety of mechanisms of photoactivity enhancement at single site catalyst-modified photocatalysts holds promise for developing further tailored photocatalysts for various applications.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 8.867
Times cited: 44
DOI: 10.1039/c5ta07036h
|
|
|
“Hollow Zn/Co Zeolitic Imidazolate Framework (ZIF) and Yolk-Shell Metal@Zn/Co ZIF nanostructures”. Roesler C, Aijaz A, Turner S, Filippousi M, Shahabi A, Xia W, Van Tendeloo G, Muhler M, Fischer RA, Chemistry: a European journal 22, 3304 (2016). http://doi.org/10.1002/chem.201503619
Abstract: Metal-organic frameworks (MOFs) feature a great possibility for a broad spectrum of applications. Hollow MOF structures with tunable porosity and multifunctionality at the nanoscale with beneficial properties are desired as hosts for catalytically active species. Herein, we demonstrate the formation of well-defined hollow Zn/Co-based zeolitic imidazolate frameworks (ZIFs) by use of epitaxial growth of Zn-MOF (ZIF-8) on preformed Co-MOF (ZIF-67) nanocrystals that involve in situ self-sacrifice/excavation of the Co-MOF. Moreover, any type of metal nanoparticles can be accommodated in Zn/Co-ZIF shells to generate yolk-shell metal@ZIF structures. Transmission electron microscopy and tomography studies revealed the inclusion of these nanoparticles within hollow Zn/Co-ZIF with dominance of the Zn-MOF as shell. Our findings lead to a generalization of such hollow systems that are working effectively to other types of ZIFs.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 5.317
Times cited: 43
DOI: 10.1002/chem.201503619
|
|
|
“Incorporation and study of SiV centers in diamond nanopillars”. Felgen N, Naydenov B, Turner S, Jelezko F, Reithmaier JP, Popov C, Diamond and related materials 64, 64 (2016). http://doi.org/10.1016/j.diamond.2016.01.011
Abstract: We report on the incorporation of SiV centers during hot filament chemical vapor deposition of diamond on top of diamond nanopillars with diameters down to 100 nm. The nanopillars themselves were prepared from nano crystalline diamond films by applying electron beam lithography and inductively coupled plasma reactive ion etching. The optical investigations revealed the presence of ensembles of SiV color centers incorporated during the overgrowth step. (C) 2016 Elsevier B.V. All rights reserved.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.561
Times cited: 14
DOI: 10.1016/j.diamond.2016.01.011
|
|
|
“The incorporation of nanoparticles into conventional glass-ionomer dental restorative cements”. Gjorgievska E, Van Tendeloo G, Nicholson JW, Coleman NJ, Slipper IJ, Booth S, Microscopy and microanalysis 21, 392 (2015). http://doi.org/10.1017/S1431927615000057
Abstract: Conventional glass-ionomer cements (GICs) are popular restorative materials, but their use is limited by their relatively low mechanical strength. This paper reports an attempt to improve these materials by incorporation of 10 wt% of three different types of nanoparticles, aluminum oxide, zirconium oxide, and titanium dioxide, into two commercial GICs (ChemFil((R)) Rock and EQUIA (TM) Fil). The results indicate that the nanoparticles readily dispersed into the cement matrix by hand mixing and reduced the porosity of set cements by filling the empty spaces between the glass particles. Both cements showed no significant difference in compressive strength with added alumina, and ChemFil((R)) Rock also showed no significant difference with zirconia. By contrast, ChemFil((R)) Rock showed significantly higher compressive strength with added titania, and EQUIA (TM) Fil showed significantly higher compressive strength with both zirconia and titania. Fewer air voids were observed in all nanoparticle-containing cements and this, in turn, reduced the development of cracks within the matrix of the cements. These changes in microstructure provide a likely reason for the observed increases in compressive strength, and overall the addition of nanoparticles appears to be a promising strategy for improving the physical properties of GICs.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 1.891
Times cited: 15
DOI: 10.1017/S1431927615000057
|
|
|
Van Havenbergh K (2015) Influence of silicon nanoparticle coating on the electrolyte decomposition in Li-ion batteries. Antwerpen
Keywords: Doctoral thesis; Electron microscopy for materials research (EMAT)
|
|
|
“Insertion compounds and composites made by ball milling for advanced sodium-ion batteries”. Zhang B, Dugas R, Rousse G, Rozier P, Abakumov AM, Tarascon J-M, Nature communications 7, 10308 (2016). http://doi.org/10.1038/ncomms10308
Abstract: Sodium-ion batteries have been considered as potential candidates for stationary energy storage because of the low cost and wide availability of Na sources. However, their future commercialization depends critically on control over the solid electrolyte interface formation, as well as the degree of sodiation at the positive electrode. Here we report an easily scalable ball milling approach, which relies on the use of metallic sodium, to prepare a variety of sodium-based alloys, insertion layered oxides and polyanionic compounds having sodium in excess such as the Na4V2(PO4)(2)F-3 phase. The practical benefits of preparing sodium-enriched positive electrodes as reservoirs to compensate for sodium loss during solid electrolyte interphase formation are demonstrated by assembling full C/P'2-Na-1[Fe0.5Mn0.5]O-2 and C/'Na3+xV2(PO4)(2)F-3' sodium-ion cells that show substantial increases (>10%) in energy storage density. Our findings may offer electrode design principles for accelerating the development of the sodium-ion technology.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 12.124
Times cited: 104
DOI: 10.1038/ncomms10308
|
|
|
“Interface control by chemical and dimensional matching in an oxide heterostructure”. O'Sullivan M, Hadermann J, Dyer MS, Turner S, Alaria J, Manning TD, Abakumov AM, Claridge JB, Rosseinsky MJ, Nature chemistry 8, 347 (2016). http://doi.org/10.1038/NCHEM.2441
Abstract: Interfaces between different materials underpin both new scientific phenomena, such as the emergent behaviour at oxide interfaces, and key technologies, such as that of the transistor. Control of the interfaces between materials with the same crystal structures but different chemical compositions is possible in many materials classes, but less progress has been made for oxide materials with different crystal structures. We show that dynamical self-organization during growth can create a coherent interface between the perovskite and fluorite oxide structures, which are based on different structural motifs, if an appropriate choice of cations is made to enable this restructuring. The integration of calculation with experimental observation reveals that the interface differs from both the bulk components and identifies the chemical bonding requirements to connect distinct oxide structures.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 25.87
Times cited: 28
DOI: 10.1038/NCHEM.2441
|
|
|
“Low-temperature plasticity of olivine revisited with in situ TEM nanomechanical testing”. Idrissi H, Bollinger C, Boioli F, Schryvers D, Cordier P, Science Advances 2, e1501671 (2016). http://doi.org/10.1126/sciadv.1501671
Abstract: The rheology of the lithospheric mantle is fundamental to understanding how mantle convection couples with plate tectonics. However, olivine rheology at lithospheric conditions is still poorly understood because experiments are difficult in this temperature range where rocks and mineral become very brittle. We combine techniques of quantitative in situ tensile testing in a transmission electron microscope and numerical modeling of dislocation dynamics to constrain the low-temperature rheology of olivine. We find that the intrinsic ductility of olivine at low temperature is significantly lower than previously reported values, which were obtained under strain-hardened conditions. Using this method, we can anchor rheological laws determined at higher temperature and can provide a better constraint on intermediate temperatures relevant for the lithosphere. More generally, we demonstrate the possibility of characterizing the mechanical properties of specimens, which can be available in the form of submillimeter-sized particles only.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Times cited: 32
DOI: 10.1126/sciadv.1501671
|
|
|
“MULTEM : a new multislice program to perform accurate and fast electron diffraction and imaging simulations using graphics processing units with CUDA”. Lobato I, Van Dyck D, Ultramicroscopy 156, 9 (2015). http://doi.org/10.1016/j.ultramic.2015.04.016
Abstract: The main features and the GPU implementation of the MULTEM program are presented and described. This new program performs accurate and fast multislice simulations by including higher order expansion of the multislice solution of the high energy Schrodinger equation, the correct subslicing of the three-dimensional potential and top-bottom surfaces. The program implements different kinds of simulation for CTEM, STEM, ED, PED, CBED, ADF-TEM and ABF-HC with proper treatment of the spatial and temporal incoherences. The multislice approach described here treats the specimen as amorphous material which allows a straightforward implementation of the frozen phonon approximation. The generalized transmission function for each slice is calculated when is needed and then discarded. This allows us to perform large simulations that can include millions of atoms and keep the computer memory requirements to a reasonable level. (C) 2015 Elsevier B.V. All rights reserved.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT); Vision lab
Impact Factor: 2.843
Times cited: 32
DOI: 10.1016/j.ultramic.2015.04.016
|
|
|
“Structure-property relations of methylamine vapor treated hybrid perovskite CH3NH3PbI3 films and solar cells”. Conings B, Bretschneider SA, Babayigit A, Gauquelin N, Cardinaletti I, Manca JV, Verbeeck J, Snaith HJ, Boyen H-G, ACS applied materials and interfaces 9, 8092 (2017). http://doi.org/10.1021/acsami.6b15175
Abstract: The power conversion efficiency of halide perovskite solar cells is heavily dependent on the perovskite layer being sufficiently smooth and pinhole-free. It has been shown that these features can be obtained even when starting out from rough and discontinuous perovskite film, by briefly exposing it to methylamine (MA) vapor. The exact underlying physical mechanisms of this phenomenon are, however, still unclear. By investigating smooth, MA treated films, based on very rough and discontinuous reference films of methylammonium triiode (MAPbI3), considering their morphology, crystalline features, local conductive properties, and charge carrier lifetime, we unravel the relation between their characteristic physical qualities and their performance in corresponding solar cells. We discover that the extensive improvement in photovoltaic performance upon MA treatment is a consequence of the induced morphological enhancement of the perovskite layer, together with improved electron injection into TiO2, which in fact compensates for an otherwise compromised bulk electronic quality, simultaneously caused by the MA treatment.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 7.504
Times cited: 43
DOI: 10.1021/acsami.6b15175
|
|
|
“A novel red Ca8.5Pb0.5Eu(PO4)7 phosphor for light emitting diodes application”. Deyneko DV, Morozov VA, Hadermann J, Savon AE, Spassky DA, Stefanovich SY, Belik AA, Lazoryak BI, Journal of alloys and compounds 647, 965 (2015). http://doi.org/10.1016/j.jallcom.2015.06.123
Abstract: Ca9-xPbxEu(PO4)(7) (0 <= x <= 1) solid solutions with a whitlockite-type (or beta-Ca-3(PO4)(2)-type) structure (sp.gr. R3c) were prepared by a standard solid-state method in air. Their luminescent properties under near-ultraviolet (n-UV) light were investigated. Excitation spectra of Ca9-xPbxEu(PO4)(7) showed the strongest absorption at about 395 nm, which matches well with commercially available n-UV-emitting GaN-based LED chips. Emission spectra indicated an intense red emission due to the D-5(0) -> F-7(2) transition of Eu3+, with a maximum in the intensity for Ca8.5Pb0.5Eu(PO4)(7). The emission intensity of Ca8.5Pb0.5Eu(PO4)(7) was about 1.8 times higher than that of a Ca9Eu(PO4)(7) phosphor. We suggest that the introduction of Pb2+ is an efficient approach to enhance luminescence properties of such phosphors. We clarified the influence of the Ca2+/Pb2+ substitution on intensities of three bands for the D-5(0) -> F-7(0) transition in excitation spectra of Ca9-xPbxEu(PO4)(7). In addition, we found a reversible first-order phase transition from R3c to R (3) over barc symmetry by second-harmonic generation in the range from 753 K (x = 1) to 846 K (x = 0). (C) 2015 Elsevier B.V. All rights reserved.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 3.133
Times cited: 18
DOI: 10.1016/j.jallcom.2015.06.123
|
|
|
“One-pot synthesis of carbon-coated nanostructured iron oxide on few-layer graphene for lithium-ion batteries”. Sun Z, Madej E, Wiktor, Sinev I, Fischer RA, Van Tendeloo G, Muhler M, Schuhmann W, Ventosa E, Chemistry: a European journal 21, 16154 (2015). http://doi.org/10.1002/chem.201501935
Abstract: Nanostructure engineering has been demonstrated to improve the electrochemical performance of iron oxide based electrodes in Li-ion batteries (LIBs). However, the synthesis of advanced functional materials often requires multiple steps. Herein, we present a facile one-pot synthesis of carbon-coated nanostructured iron oxide on few-layer graphene through high-pressure pyrolysis of ferrocene in the presence of pristine graphene. The ferrocene precursor supplies both iron and carbon to form the carbon-coated iron oxide, while the graphene acts as a high-surface-area anchor to achieve small metal oxide nanoparticles. When evaluated as a negative-electrode material for LIBs, our composite showed improved electrochemical performance compared to commercial iron oxide nanopowders, especially at fast charge/discharge rates.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 5.317
Times cited: 8
DOI: 10.1002/chem.201501935
|
|
|
“Optical and photoelectrical properties of nanocrystalline indium oxide with small grains”. Forsh EA, Abakumov AM, Zaytsev VB, Konstantinova EA, Forsh PA, Rumyantseva MN, Gaskov AM, Kashkarov PK, Thin solid films : an international journal on the science and technology of thin and thick films 595, 25 (2015). http://doi.org/10.1016/j.tsf.2015.10.053
Abstract: Optical properties, spectral dependence of photoconductivity and photoconductivity decay in nanocrystalline indium oxide In2O3 are studied. A number of nanostructured In2O3 samples with various nanocrystals size are prepared by sol-gel method and characterized using various techniques. The mean nanocrystals size varies from 7 to 8 nm to 39-41 nm depending on the preparation conditions. Structural characterization of the In2O3 samples is performed by means of transmission electron microscopy and X-ray powder diffraction. The combined analysis of ultraviolet-visible absorption spectroscopy and diffuse reflectance spectroscopy shows that nanostructuring leads to the change in optical band gap: optical band gap of the In2O3 samples (with an average nanocrystal size from 7 to 41 nm) is equal to 2.8 eV. We find out the correlation between spectral dependence of photoconductivity and optical properties of nanocrystalline In2O3: sharp increase in photoconductivity was observed to begin at 2.8 eV that is equal to the optical bandgap in the In2O3 samples, and reached its maximum at 3.2-3.3 eV. The combined analysis of the slow photoconductivity decay in air, vacuum and argon, that was accurately fitted by a stretched-exponential function, and electron paramagnetic resonance (EPR) measurements shows that the kinetics of photoconductivity decay is strongly depended on the presence of oxygen molecules in the ambient of In2O3 nanocrystals. There is the quantitative correlation between EPR and photoconductivity data. Based on the obtained data we propose the model clearing up the phenomenon of permanent photoconductivity decay in nanocrystalline In2O3. (C) 2015 Elsevier B.V. All rights reserved.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 1.879
Times cited: 18
DOI: 10.1016/j.tsf.2015.10.053
|
|
|
“Post-synthesis bromination of benzene bridged PMO as a way to create a high potential hybrid material”. Huybrechts W, Mali G, Kuśtrowski P, Willhammar T, Mertens M, Bals S, Van Der Voort P, Cool P, Microporous and mesoporous materials: zeolites, clays, carbons and related materials 236, 244 (2016). http://doi.org/10.1016/j.micromeso.2016.09.003
Abstract: Periodic mesoporous organosilicas provide the best of two worlds: the strength and porosity of an inorganic framework combined with the infinite possibilities created by the organic bridging unit. In this work we focus on post-synthetical modification of benzene bridged PMO, in order to create bromobenzene PMO. In the past, this proved to be very challenging due to unwanted structural deterioration. However, now we have found a way to brominate this material whilst keeping the structure intact. In-depth structural analysis by solid state NMR and XPS shows both vast progress over previous attempts as well as potential for improvement.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT); Laboratory of adsorption and catalysis (LADCA)
Impact Factor: 3.615
Times cited: 7
DOI: 10.1016/j.micromeso.2016.09.003
|
|
|
“Process variability in Cu2ZnSnSe4 solar cell devices: Electrical and structural investigations”. Brammertz G, Buffiere M, Verbist C, Bekaert J, Batuk M, Hadermann J, et al, The conference record of the IEEE Photovoltaic Specialists Conference
T2 –, IEEE 42nd Photovoltaic Specialist Conference (PVSC), JUN 14-19, 2015, New Orleans, LA (2015)
Abstract: We have fabricated 9.7% efficient Cu2ZnSnSe4/CdS/ZnO solar cells by H2Se selenization of sequentially sputtered metal layers. Despite the good efficiency obtained, process control appears to be difficult. In the present contribution we compare the electrical and physical properties of two devices with nominal same fabrication procedure, but 1% and 9.7% power conversion efficiency respectively. We identify the problem of the lower performing device to be the segregation of ZnSe phases at the backside of the sample. This ZnSe seems to be the reason for the strong bias dependent photocurrent observed in the lower performing devices, as it adds a potential barrier for carrier collection. The reason for the different behavior of the two nominally same devices is not fully understood, but speculated to be related to sputtering variability.
Keywords: P1 Proceeding; Engineering sciences. Technology; Electron microscopy for materials research (EMAT); Condensed Matter Theory (CMT)
|
|
|
“Quantifying inflow and RANS turbulence model form uncertainties for wind engineering flows”. Gorle C, Garcia Sánchez C, Iaccarino G, Journal of wind engineering and industrial aerodynamics
T2 –, 6th International Symposium on Computational Wind Engineering (CWE), JUN 08-12, 2014, Hamburg, GERMANY 144, 202 (2015). http://doi.org/10.1016/j.jweia.2015.03.025
Abstract: Reynolds-averaged Navier-Stokes (RANS) simulations are often used in the wind engineering practice for the analysis of turbulent bluff body flows. An approach that allows identifying the uncertainty related to the use of reduced-order turbulence models in RANS simulations would significantly increase the confidence in the use of simulation results as a basis for design decisions. In the present study we apply a strategy that enables quantifying these uncertainties by introducing perturbations in the Reynolds stress tensor to simulations of the flow in downtown Oklahoma City. The method is combined with a framework to quantify uncertainties in the inflow wind direction and intensity, and the final result of the UQ approach is compared to field measurement data for the velocity at 13 locations in the downtown area. (C) 2015 Elsevier Ltd. All rights reserved.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.049
Times cited: 22
DOI: 10.1016/j.jweia.2015.03.025
|
|
|
“Doping anatase TiO2with group V-b and VI-b transition metal atoms: a hybrid functional first-principles study”. Matsubara M, Saniz R, Partoens B, Lamoen D, Physical chemistry, chemical physics 19, 1945 (2017). http://doi.org/10.1039/C6CP06882K
Abstract: We investigate the role of transition metal atoms of group V-b (V, Nb, Ta) and VI-b (Cr, Mo, W) as n- or p-type dopants in anatase TiO$_2$ using thermodynamic
principles and density functional theory with the Heyd-Scuseria-Ernzerhof HSE06 hybrid functional. The HSE06 functional provides a realistic value for the band gap, which ensures a correct classification of dopants as shallow or deep donors or acceptors. Defect formation energies and thermodynamic transition levels are calculated taking into account the constraints imposed by the stability of TiO$_2$ and the solubility limit of the impurities.
Nb, Ta, W and Mo are identified as shallow donors. Although W provides two electrons, Nb and Ta show a considerable lower formation energy, in particular under O-poor conditions. Mo donates in principle one electron, but under specific conditions can turn into a double donor. V impurities are deep donors and Cr
shows up as an amphoteric defect, thereby acting as an electron trapping center in n-type TiO$_2$ especially under O-rich conditions. A comparison with the available experimental data yields excellent agreement.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT); Condensed Matter Theory (CMT)
Impact Factor: 4.123
Times cited: 19
DOI: 10.1039/C6CP06882K
|
|