Abstract: Insulating and metallic stripes above and below the Curie temperature, T-C, respectively, were observed by a high-resolution scanning tunneling microscopy (STM) and/or spectroscopy (STS) in A-site ordered and macroscopically strain free epitaxial La0.75Ca0.25MnO3 film grown on MgO substrate. The “insulating” stripes were found to be incommensurable to the lattice and aligned along (110) direction. Metallic stripes were commensurable with periodicity 2a(p)similar to 0.8 nm and aligned parallel to the crystallographic a/b-axis. Formation of these stripes involves competing charge, orbital, and lattice orders and is an outcome of an overlapping of electron wave functions mediated by the local lattice-strain distribution, existed even in A-site ordered film due to the difference in cation radii of La and Ca. (C) 2007 Elsevier B.V. All rights reserved.

Abstract: Hollow silica spheres were quickly synthesized by an octylamine (OA) templating method using tetraethyl orthosilicate (TEOS) as the silica source. N2-sorption results indicate that the hollow spheres have high surface areas and pore volumes. XRD and TEM measurements reveal that the structure of the hollow spheres depends on the amount of TEOS used in the synthesis. When low amount of TEOS is added, the template-containing precursor spheres depict an XRD pattern with two peaks, which can be indexed to a lamellar phase. After the removal of the template, the obtained hollow spheres show no diffraction peaks in the XRD pattern, suggesting that the nanopores in the silica shells are disordered. If increasing the amount of TEOS, either the uncalcined or the calcined sample gives an XRD pattern with a single diffraction peak. The mesostructure of these hollow silica spheres is typically as HMS materials. TGA analyses suggest that the interaction between the silica species and surfactant is stronger in the latter case.

Abstract: ITEM specimens of a LaAlO3/SrTiO3 multilayer are prepared by FIB with internal lift out. Using a Ga+1 beam of 5 kV, a final cleaning step yielding top, top-angle, side, and bottom-angle cleaning is performed. Different cleaning procedures, which can be easily implemented in a dual beam FIB system, are described and compared; all cleaning types produce thin lamellae, useful for HRTEM and HAADF-STEM work up to atomic resolution. However, the top cleaned lamellae are strongly affected by the curtain effect. Top-angle cleaned specimens show an amorphous layer of around 5 nm at the specimen surfaces, due to damage and redeposition. Furthermore, it is observed that the LaAlO3 layers are preferentially destroyed and transformed into amorphous material, during the thinning process.

Abstract: Single crystals with two different morphologies, black and brown, of C60 with about 12% C70 have been studied by synchrotron X-ray diffraction. Integrated intensities from 8 reflections show that the charge distribution of the C60 cluster is shell-like giving rise to an oscillatory behaviour in the diffracted intensities. From the intensities, the distance between diametrically opposite carbon atoms has been determined to be (7.24 +/- 0.22) angstrom. The thickness of the charge distribution of the shell can be estimated as 3.06 angstrom and the cavity within a C60 cluster to have a diameter of about 4.18 angstrom. The finite longitudinal width of the diffraction peaks from black crystals indicates a lack of long-range crystalline order. The rocking curves are about 7-degrees broad and depict an unusually smooth behaviour. This may be indicative of a glassy or hexatic phase. High-resolution electron microscopy allows small crystallites with a relatively well-defined orientation relationship to be identified. In contrast, brown crystals have long-range order.