NANOlab Center of Excellence literature database -- Query Results

“Origin of different deactivation of Pd/SnO₂ and Pd/GeO₂ catalysts in methanol dehydrogenation and reforming: a comparative study”. Lorenz H, Zhao Q, Turner S, Lebedev OI, Van Tendeloo G, Kloetzer B, Rameshan C, Pfaller K, Applied catalysis : A : general 381, 242 (2010). http://doi.org/10.1016/j.apcata.2010.04.015 Abstract: Pd particles supported on SnO2 and GeO2 have been structurally investigated by X-ray diffraction, (High-Resolution) transmission and scanning electron microscopy after different reductive treatments to monitor the eventual formation of bimetallic phases and catalytically tested in methanol dehydrogenation/ reforming. For both oxides this included a thin film sample with well-defined Pd particles and a powder catalyst prepared by incipient wetness impregnation. The hexagonal and the tetragonal polymorph were studied for powder GeO2. Pd2Ge formation was observed on all GeO2-supported catalysts, strongly depending on the specific sample used. Reduction of the thin film at 573K resulted in full transformation into the bimetallic state. The partial solubility of hexagonal GeO2 in water and its thermal structural instability yielded Pd2Ge formation at 473 K, at the cost of a structurally inhomogeneous support and Ge metal formation at higher reduction temperatures. Pd on tetragonal GeO2 entered a state of strong metalsupport interaction after reduction at 573673 K, resulting in coalescing Pd2Ge particles on a sintered and re-crystallized support, apparently partially covering the bimetallic particles and decreasing the catalytic activity. Pd2Ge on amorphous thin film and hexagonal GeO2 converted methanol primarily via dehydrogenation to CO and H2. At 573 K, formation of Pd2Sn and also PdSn occurred on the Pd/SnO2 thin film. Pd3Sn2 (and to some extent Pd2Sn) were predominantly obtained on the respective powder catalyst. Strong deactivation with increasing reduction temperature was observed, likely not based on the classical strong metalsupport interaction effect, but rather on a combination of missing active structural ensembles on Sn-enriched bimetallic phases and the formation of metallic -Sn. Correlations to Pd and its bimetallics supported on ZnO, Ga2O3 and In2O3 were also discussed. Keywords: A1 Journal article; Electron microscopy for materials research (EMAT) Impact Factor: 4.339 Times cited: 14 DOI: 10.1016/j.apcata.2010.04.015 Additional Links: UA library record; WoS full record; WoS citing articles show.php?record=2522
“Pd-In₂O₃ interaction due to reduction in hydrogen: consequences for methanol steam reforming”. Lorenz H, Turner S, Lebedev OI, Van Tendeloo G, Klötzer B, Rameshan C, Pfaller K, Penner S, Applied catalysis : A : general 374, 180 (2010). http://doi.org/10.1016/j.apcata.2009.12.007 Abstract: Two different Pd/In2O3 samples including a thin film model catalyst with well-defined Pd particles grown on NaCl(0 0 1) supports and a powder catalyst prepared by an impregnation technique are examined by electron microscopy, X-ray diffraction and catalytic measurements in methanol steam reforming in order to correlate the formation of different oxide-supported bimetallic PdIn phases with catalytic activity and selectivity. A PdIn shell around the Pd particles is observed on the thin film catalyst after embedding the Pd particles in In2O3 at 300 K, likely because alloying to PdIn and oxidation to In2O3 are competing processes. Increased PdIn bimetallic formation is observed up to 573 K reduction temperature until at 623 K the film stability limit in hydrogen is reached. Oxidative treatments at 573 K lead to decomposition of PdIn and to the formation of an In2O3 shell covering the Pd particles, which irreversibly changes the activity and selectivity pattern to clean In2O3. PdIn and Pd2In3 phases are obtained on the powder catalyst after reduction at 573 K and 673 K, respectively. Only CO2-selective methanol steam reforming is observed in the reduction temperature range between 473 K and 573 K. After reduction at 673 K encapsulation of the bimetallic particles by crystalline In2O3 suppresses CO2 formation and only activity and selectivity of clean In2O3 are measured. Keywords: A1 Journal article; Electron microscopy for materials research (EMAT) Impact Factor: 4.339 Times cited: 55 DOI: 10.1016/j.apcata.2009.12.007 Additional Links: UA library record; WoS full record; WoS citing articles show.php?record=3553

Abstract: Pd particles supported on SnO2 and GeO2 have been structurally investigated by X-ray diffraction, (High-Resolution) transmission and scanning electron microscopy after different reductive treatments to monitor the eventual formation of bimetallic phases and catalytically tested in methanol dehydrogenation/ reforming. For both oxides this included a thin film sample with well-defined Pd particles and a powder catalyst prepared by incipient wetness impregnation. The hexagonal and the tetragonal polymorph were studied for powder GeO2. Pd2Ge formation was observed on all GeO2-supported catalysts, strongly depending on the specific sample used. Reduction of the thin film at 573K resulted in full transformation into the bimetallic state. The partial solubility of hexagonal GeO2 in water and its thermal structural instability yielded Pd2Ge formation at 473 K, at the cost of a structurally inhomogeneous support and Ge metal formation at higher reduction temperatures. Pd on tetragonal GeO2 entered a state of strong metalsupport interaction after reduction at 573673 K, resulting in coalescing Pd2Ge particles on a sintered and re-crystallized support, apparently partially covering the bimetallic particles and decreasing the catalytic activity. Pd2Ge on amorphous thin film and hexagonal GeO2 converted methanol primarily via dehydrogenation to CO and H2. At 573 K, formation of Pd2Sn and also PdSn occurred on the Pd/SnO2 thin film. Pd3Sn2 (and to some extent Pd2Sn) were predominantly obtained on the respective powder catalyst. Strong deactivation with increasing reduction temperature was observed, likely not based on the classical strong metalsupport interaction effect, but rather on a combination of missing active structural ensembles on Sn-enriched bimetallic phases and the formation of metallic -Sn. Correlations to Pd and its bimetallics supported on ZnO, Ga2O3 and In2O3 were also discussed.

Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)

Impact Factor: 4.339

Times cited: 14

DOI: 10.1016/j.apcata.2010.04.015

Additional Links: UA library record; WoS full record; WoS citing articles

show.php?record=2522

Abstract: Two different Pd/In2O3 samples including a thin film model catalyst with well-defined Pd particles grown on NaCl(0 0 1) supports and a powder catalyst prepared by an impregnation technique are examined by electron microscopy, X-ray diffraction and catalytic measurements in methanol steam reforming in order to correlate the formation of different oxide-supported bimetallic PdIn phases with catalytic activity and selectivity. A PdIn shell around the Pd particles is observed on the thin film catalyst after embedding the Pd particles in In2O3 at 300 K, likely because alloying to PdIn and oxidation to In2O3 are competing processes. Increased PdIn bimetallic formation is observed up to 573 K reduction temperature until at 623 K the film stability limit in hydrogen is reached. Oxidative treatments at 573 K lead to decomposition of PdIn and to the formation of an In2O3 shell covering the Pd particles, which irreversibly changes the activity and selectivity pattern to clean In2O3. PdIn and Pd2In3 phases are obtained on the powder catalyst after reduction at 573 K and 673 K, respectively. Only CO2-selective methanol steam reforming is observed in the reduction temperature range between 473 K and 573 K. After reduction at 673 K encapsulation of the bimetallic particles by crystalline In2O3 suppresses CO2 formation and only activity and selectivity of clean In2O3 are measured.