NANOlab Center of Excellence literature database -- Query Results

“TEM investigation of SCC crack tips in high Si stainless steel tapered specimens”. Penders A, Konstantinovic MJ, Van Renterghem W, Bosch RW, Schryvers D, Corrosion Engineering Science And Technology (2021). http://doi.org/10.1080/1478422X.2021.1961665 Abstract: The stress corrosion cracking (SCC) mechanism is investigated in high Si duplex stainless steel in a simulated PWR environment based on TEM analysis of FIB-extracted SCC crack tips. The microstructural investigation in the near vicinity of SCC crack tips illustrates a strain-rate dependence in SCC mechanisms. Detailed analysis of the crack tip morphology, that includes crack tip oxidation and surrounding deformation field, indicates the existence of an interplay between corrosion- and deformation-driven failure as a function of the strain rate. Slow strain-rate crack tips exhibit a narrow cleavage failure which can be linked to the film-induced failure mechanism, while rounded shaped crack tips for faster strain rates could be related to the strain-induced failure. As a result, two nominal strain-rate-dependent failure regimes dominated either by corrosion or deformation-driven cracking mechanisms can be distinguished. Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT) Impact Factor: 0.879 DOI: 10.1080/1478422X.2021.1961665 Additional Links: UA library record; WoS full record; WoS citing articles show.php?record=6892
“Crack initiation in tapered high Si stainless steel specimens : stress threshold analyses”. Penders A, Konstantinovic MJ, Bosch RW, Schryvers D, Corrosion Engineering Science And Technology , 1 (2020). http://doi.org/10.1080/1478422X.2020.1785651 Abstract: Tapered specimens were used for an accelerated test technique to study the crack initiation of high Si stainless steel by means of constant elongation rate tensile testing in a simulated pressurised water reactor environment. Detailed crack density distributions were obtained by applying an advanced crack detection algorithm on iteratively displaced scanning electron microscopy pictures featuring stress corrosion cracks along the specimen's gauge length. By means of finite-element analysis, prominent peaks in the crack density graphs are demonstrated to be related to stress relief and stress build-up during the crack initiation phase. Intrinsic scatter related to the crack detection suggests that stress corrosion cracking is independent of the strain-rate for strain-rates lower than 10(-6 )s(-1). Based on the extrapolation to constant load conditions, the critical threshold value for the duplex high Si stainless steel is estimated to be around 580 MPa. Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT) Impact Factor: 1.8 Times cited: 1 DOI: 10.1080/1478422X.2020.1785651 Additional Links: UA library record; WoS full record; WoS citing articles show.php?record=6478

Abstract: The stress corrosion cracking (SCC) mechanism is investigated in high Si duplex stainless steel in a simulated PWR environment based on TEM analysis of FIB-extracted SCC crack tips. The microstructural investigation in the near vicinity of SCC crack tips illustrates a strain-rate dependence in SCC mechanisms. Detailed analysis of the crack tip morphology, that includes crack tip oxidation and surrounding deformation field, indicates the existence of an interplay between corrosion- and deformation-driven failure as a function of the strain rate. Slow strain-rate crack tips exhibit a narrow cleavage failure which can be linked to the film-induced failure mechanism, while rounded shaped crack tips for faster strain rates could be related to the strain-induced failure. As a result, two nominal strain-rate-dependent failure regimes dominated either by corrosion or deformation-driven cracking mechanisms can be distinguished.

Abstract: Tapered specimens were used for an accelerated test technique to study the crack initiation of high Si stainless steel by means of constant elongation rate tensile testing in a simulated pressurised water reactor environment. Detailed crack density distributions were obtained by applying an advanced crack detection algorithm on iteratively displaced scanning electron microscopy pictures featuring stress corrosion cracks along the specimen's gauge length. By means of finite-element analysis, prominent peaks in the crack density graphs are demonstrated to be related to stress relief and stress build-up during the crack initiation phase. Intrinsic scatter related to the crack detection suggests that stress corrosion cracking is independent of the strain-rate for strain-rates lower than 10(-6 )s(-1). Based on the extrapolation to constant load conditions, the critical threshold value for the duplex high Si stainless steel is estimated to be around 580 MPa.

Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)

Impact Factor: 1.8

Times cited: 1

DOI: 10.1080/1478422X.2020.1785651

Additional Links: UA library record; WoS full record; WoS citing articles

show.php?record=6478