Abstract: The patterns of Ni release from Nitinol vary depending on the type of material (NiTi alloys with low or no processing versus commercial wires or sheets). A thick TiO2 layer generated on the wire surface during processing is often considered as a reliable barrier against Ni release. The present study of Nitinol wires with surface oxides resulting from production was conducted to identify the sources of Ni release and its distribution in the surface sublayers. The chemistry and topography of the surfaces of Nitinol wires drawn using different techniques were studied with XPS and SEM. The distribution of Ni into surface depth and the surface oxide thickness were evaluated using Auger spectroscopy, TEM with FIB and ELNES. Ni release was estimated using either ICPA or AAS. Potentiodynamic potential polarization of selected wires was performed in as-received state with no strain and in treated strained samples. Wire samples in the as-received state showed low breakdown potentials (200 mV); the improved corrosion resistance of these wires after treatment was not affected by strain. It is shown how processing techniques affect surface topography, chemistry and also Ni release. Nitinol wires with the thickest surface oxide TiO2 (up to 720 nm) showed the highest Ni release, attributed to the presence of particles of essentially pure Ni whose number and size increased while approaching the interface between the surface and the bulk. The biological implications of high and lasting Ni release are also discussed.

Abstract: A single crystal of Cu74.08Al23.13Be2.79 undergoes a martensitic phase transition at 246 and 232 K under heating and cooling, respectively. The phase fronts between the austenite and martensite regions of the sample are weakly mobile with a power-law resonance under external stress fields. Surprisingly, the martensite phase is elastically much harder than the austenite phase showing that interfaces between various crystallographic variants are strongly pinned and cannot be moved by external stress while the phase boundary between the austenite and martensite regions in the sample remains mobile. This unusual behavior was studied by dynamical mechanical analysis (DMA) and resonant ultrasound spectroscopy. The remnant strain, storage modulus, and internal friction were recorded simultaneously for different applied forces in DMA. With increasing forces, the remnant strain increases monotonously while the internal friction peak height shows a minimum at 300 mN. Transmission electron microscopy shows that the pinning is generated by dislocations which are inherited from the austenite phase.

Abstract: Molecular dynamics simulations were used to investigate the size-dependent melting mechanism of nickel nanoclusters of various sizes. The melting process was monitored by the caloric curve, the overall cluster Lindemann index, and the atomic Lindemann index. Size-dependent melting temperatures were determined, and the correct linear dependence on inverse diameter was recovered. We found that the melting mechanism gradually changes from dynamic coexistence melting to surface melting with increasing cluster size. These findings are of importance in better understanding carbon nanotube growth by catalytic chemical vapor deposition as the phase state of the catalyst nanoparticle codetermines the growth mechanism.

Abstract: ZSM-48 and related zeolites are considered to be highly disordered structures. Different polytypes can be clearly distinguished by simulation of high-resolution electron microscopy images. Synthesis of phase-pure polytypes was attempted. One of the investigated samples crystallized via seeding designated as COK-8 consisted of nanoscopic, needlelike crystals with a very large length/width ratio, growing along the pore direction. These specimens are phase-pure polytype 6 (PT6, numbering according to Lobo and van Koningsveld). Aggregates of these nanoneedles occasionally contained a second polytype: PT1. The latter polytype occurred more abundantly in larger crystal rods in an IZM-1 sample crystallized in ethylene glycol. Here too, the isolated crystallites mainly consist of large, defect-free regions of PT6. A simulation of polytype lattice energies offers a rational explanation for the observed polytypical intergrowth formation.

Abstract: Following extended use in organic chemistry, microwave-assisted synthesis is gaining more importance in the field of inorganic chemistry, especially for the synthesis of nanoporous materials. It offers some major advantages such as a significant shortening of the synthesis time and an improved promotion of nucleation. In the research here reported, microwave technology is applied for the synthesis of benzene bridged PMOs (periodic mesoporous organosilicas). PMOs are one of the latest innovations in the field of hybrid ordered mesoporous materials and have attracted much attention because of their feasibility in electronics, catalysis, separation and sorption applications. The different synthesis steps (stirring, aging and extraction) of the classical PMO synthesis are replaced by microwave-assisted synthesis steps. The characteristics of the as-synthesized materials are evaluated by X-ray diffraction, N2-sorption, thermogravimetric analysis, scanning- and transmission electron microscopy. The microwave-assisted synthesis drastically reduces the synthesis time by more than 40 hours without any loss in structural properties, such as mesoscale and molecular ordering. The porosity of the PMO materials has even been improved by more than 25%. Moreover, the number of handling/transfer steps and amounts of chemicals and waste are drastically reduced. The study also shows that there is a clear time (1 to 3 hours) and temperature frame (373 K to 403 K) wherein synthesis of benzene bridged PMO is optimal. In conclusion, the microwave-assisted synthesis pathway allows an improved material to be obtained in a more economical way i.e. a much shorter time with fewer chemicals and less waste.

Abstract: The synthesis, electron diffraction (ED), synchrotron X-ray and neutron structure, X-ray absorption spectroscopy (XAS) and magnetic property studies of La2MnVO6 double perovskite are described. Analysis of the synchrotron powder X-ray diffraction data for La2MnVO6 indicates a disordered arrangement of Mn and V at the B-site of the perovskite structure. Absence of super-lattice reflections in the ED patterns for La2MnVO6 supports the disordered cation arrangement. Room temperature time-of-flight (TOF) neutron powder diffraction (NPD) data show no evidence of cation ordering, in corroboration with the ED and synchrotron studies (orthorhombic Pnma, a = 5.6097(3), b = 7.8837(5) and c = 5.5668(3) ; 295 K, NPD). A comparison of XAS analyses of La2TVO6 with T = Ni and Co shows T2+ formal oxidation state while the T = Mn material evidences a Mn3+ admixture into a dominantly Mn2+ ground state. V-K edge measurements manifest a mirror image behavior with a V4+ state for T = Ni and Co with a V3+ admixture arising in the T = Mn material. The magnetic susceptibility data for La2MnVO6 show ferromagnetic correlations; the observed effective moment, µeff (5.72 µB) is much smaller than the calculated moment (6.16 µB) based on the spin-only formula for Mn2+ (d5, HS) /V4+ (d1), supportive of the partly oxidized Mn and reduced V scenario (Mn3+/V3+).

Abstract: The activity concentration of 226Ra, 232Th and 40K in gas concrete samples collected from different suppliers and some provinces in Turkey were measured using gamma-ray spectrometry. Knowledge of radioactivity in gas concrete used in building materials enables one to assess any possible radiological risks to human health. The mean activity concentrations observed in the gas concrete samples were 82.0, 28.2 and 383.9 Bq kg−1 for 226Ra, 232Th and 40K, respectively. The radium equivalent activity, external and internal hazard indices as well as terrestrial absorbed dose and annual effective dose rate was calculated. The results indicate that the radium equivalent activity values of gas concrete samples are lower than the limit of 370 Bq kg−1, equivalent to a gamma-dose of 1.5 mSv y−1. Moreover, mass attenuation coefficients were measured in some gas concrete samples. It was found that the mass attenuation coefficients decreased with increasing photon energies. Also, chemical compositions and structural analysis (XRD and SEM) of the gas concrete samples were investigated.

Abstract: Black corals (Cnidaria, Antipatharia) from three different sources were investigated with the aim of detecting inorganic components and their morphology. In general, the skeleton of black corals was composed of the chitin fibrils admixed with peptides and the chitin presence was confirmed by the X-ray diffraction (XRD), Fourier Transformed Infrared Spectrometry (FTIR) and microRaman Microscopy, the latter giving the opportunity of tracing single fibrils and their location. The composition and concentrations of the inorganic components of the black corals were measured, using a scanning electron microprobe and micro-Particle Induced X-ray Emission (µ-PIXE). The application of such instruments enabled the estimation of the constituent distributions in a microscale. The mapping option was the most useful technique of making analyses in these studies, just to reveal the composition of chamber-like cells. Analysis of the morphology and microstructure showed that there were three distinct regions within the coral: a core and the cells encircled with adjacent interface gluing strips. The majority of the elements analyzed were selectively distributed and segregated in a striking way in mentioned distinctive zones of the skeleton and it was detected for the first time. The core area was characterized by the relatively elevated concentrations of Ca. The measurements gave extremely clear images of the distribution of particular elements in the skeletal tissue, with I, Ca, K and Fe much more concentrated in the gluing zones, while C, N, Na and Mg present in the interiors of particular skeletal cells. The distribution of some elements (Mg, Fe) and some compounds (chitin) and functional groups (SS, CI) allows differentiating the biological and mechanical functions of particular fragments of the rods. The kinds of elements and their concentrations measured were essentially in compliance with rare data available in the literature. The Raman technique gave the additional qualitative information about the structure of gluing zone and the chitin fibrils and surrounding matrix inside the cell interior.

Abstract: Ni4Ti3 precipitates play an important role in the shape memory and superelastic behaviour of thermo-mechanically treated Ni-Ti material. The 3D morphology and distribution of such precipitates with lenticular shape and rhombohedral atomic structure in the austenitic B2 matrix of a binary Ni-rich Ni-Ti alloy has been elucidated via a slice view procedure in a Dual-Beam FIB/SEM system. With the sequence of cross-section SE images obtained from the SEM, a 3D reconstruction has been achieved after proper alignment and image processing, from which both qualitative and quantitative analysis can be performed. Careful imaging is needed to ensure that all variants of the precipitates are observed with equal probability, regardless sample orientation. Moreover, due to the weak contrast of the precipitates, proper imaging conditions need to be selected to allow for semi-automated image treatment. Finally, a volume ratio of 10.2% for the Ni4Ti3 precipitates could be calculated, summed over all variants, which yields a net composition of Ni50.36Ti49.64 for the matrix, leading to an increase of 113 degrees for the martensitic start temperature Ms. Also, the expected relative orientation of the different variants of the precipitates could be confirmed. In the near future, other quantitative measures on the distribution of the precipitates can be expected.