Abstract: Results of dielectric and resonance frequency (f(r)) measurements below room temperature are presented for Pb(ZrxTi1-x)O-3, x = 0.515 and 0.520. It is shown that the temperature coefficient of f(r) changes sign from negative to positive around 210 and 265 K for x = 0.520 and 200 and 260 K for x = 0.515. Anomalies in the real part of the dielectric constant (epsilon') are observed around the same temperatures at which the temperature coefficient of f(r) changes sign because of the electrostrictive coupling between the elastic and dielectric responses. Low-temperature powder x-ray-diffraction (XRD) data, however, reveal only one transition from the tetragonal to monoclinic phase similar to that reported by Noheda et al. [Phys. Rev. B, 61, 8687 (2000)]. Electron-diffraction data, on the other hand, reveal yet another structural transition at lower temperatures corresponding to the second anomaly in the epsilon' vs T and f(r) vs T curves. This second transition is shown to be a cell-doubling transition not observed by Noheda et al. in their XRD studies. The observation of superlattice reflections raises doubts about the correctness of the Cm space group proposed by Noheda et al. for the monoclinic phase of Pb(ZrxTi(1-x))O-3 below the second transition temperature.

Abstract: A positron lifetime experiment is performed on samples produced by the compaction of nanocrystalline Ni3Al powder synthesized by the inert-gas condensation technique. In the lifetime spectrum we observe two components corresponding to defects. Computer (virtual) samples of n-Ni3Al are obtained using molecular dynamics combined with the Metropolis Monte Carlo technique. Positron lifetime calculations are then performed on selected regions of simulated samples. For this purpose, a new computational technique based on a generalization of the atomic superposition method for non-periodic systems was developed. Lifetimes calculated in this way are compared to experiment.

Abstract: Yittria-stabilized zirconia (YSZ) films doped with 3 and 9 vol%. Y(2)O(3), respectively, are epitaxially deposited on (0 0 1) silicon substrates by means of pulsed laser deposition (PLD) technique. Transmission electron microscopy (TEM) and X-ray diffraction are mainly combined to study the film microstructure. It is: found that the film structure strongly depends on the amount of Y(2)O(3) dopant. 99/0 Y(2)O(3)-doped films display a near cubic structure; 45 degrees 1/2(1 1 0) dislocations are the main defects in the film and thermal cracks are formed during cooling. The 3% Y(2)O(3)-doped films are dominated by {1 1 0} twin-related tetragonal domains in which monoclinic phase is found. The films are free of thermal cracks even for films thicker than 2 mum. (C) 2001 Elsevier Science B.V. All rights reserved.

Abstract: We report on the preparation of CuBa(2)(Sr(x)Ca(1-x))(n)Cu(n-1)O(y) compounds by fabrication of (Ba,Sr,Ca)CuO(2) superlattices with pulsed laser deposition (PLD). A technique called interval deposition is used to suppress multi-level or island growth resulting in high-quality superlattice structures. Both, the applicability of PLD to atomic engineering as well as the fabrication of artificial superconductors is demonstrated. The (Sr,Ca)CuO(2)-BaCuO(2) superlattices are characterized by X-ray diffraction, high-resolution electron microscopy (HREM) and selected area electron diffraction. The superlattice period has been deduced from electron diffraction patterns and XRD measurements. For Sr containing films, the best growth behavior is observed and films with the highest degree of crystallinity are obtained, whereas superconductivity is only found in less crystalline, Ca containing films. Under some deposition conditions and depending on the amount of Ba containing layers in the superlattice, it was observed that the BaCuO(2) material is converted to Ba(2)CuO(4-delta). Image simulations to interpret the HREM contrast are performed. (C) 2001 Elsevier Science B.V. All rights reserved.

Abstract: YCuO2 delafossite crystallizes into two stacking variants; hexagonal 2H or rhombohedral 3R, depending on the preparation conditions. The structure of the fully oxygenated material YCuO2.50 has been determined as orthorhombic (a(O) = 6.1961 Angstrom; b(O) = 11.2158 Angstrom; c(O) = 7.1505 Angstrom; space group Pnma). The structure is based on the hexagonal 2H structure (a(O) = a(H)root3; b(O) = c(H); c(O) = 2a(H)). Upon incomplete oxidation, a different YCuOZ phase with ideal composition YCuO2.33 and lattice parameters a(H root)3, a(H)root3, c(H) is also formed. Diffraction patterns are often very complex because of the presence of planar defects and intergrowth of both phases. Under electron beam irradiation, oxygen is released from the structure and one phase gradually transforms into the other. (C) 2001 Academic Press.

Abstract: The microstructure of (Bi,Pb)2Sr2Ca2Cu3Ox (Bi-2223) tapes has been investigated by means of transmission electron microscopy (TEM) and high-resolution TEM. The emphasis has been placed on: (1) an examination of the grain morphology and size, (2) grain and colony boundary angles, which are formed during the tape processing, (3) a study of the grain boundaries on an atomic scale, including intergrowth investigations. Tapes with different process parameters have been compared with respect to the microstructure. A fully processed tape has on the average 50% thicker Bi-2223 grains than a tape after the first annealing. The angles of c-axis tilt grain boundaries are on average 14° and 26° for the fully processed tape and the tape after the first annealing, respectively. The intergrowth content (15%) and distribution are similar in these two tapes.