Abstract: The post-growth modification of diamond-like amorphous hydrogenated carbon a-C:H films by laser treatment has been studied by transmission electron microscopy and Raman spectroscopy. a-C:H films grown on Si substrates by benzene decomposition in a rf glow discharge were irradiated with 15 ns pulses of a KrF-excimer laser with fluences in the ran e of E = 50-700 mJ/cm(2). At fluences below 100 mJ/cm(2) an increase in the number of graphitic clusters and in their ordering was evidenced from Raman spectra, while the film structure remained amorphous according to electron microscopy and electron diffraction observations. At higher fluences the appearance of diamond particles of 2-7 nm size, embedded into the lower crystallized graphitic matrix, was observed and simultaneously a progressive growth of graphite nanocrystals with dimensions from 2 nm to 4 nm was deduced from Raman measurements. The maximum thickness of the crystallized surface layer (approximate to 400 nm) and the degree of laser annealing are limited by the film ablation which starts at E > 250 mJ/cm(2). The laser-treated areas lose their chemical inertness. In particular, chemical etching in chromium acid becomes possible, which may be used for patterning the highly inert carbon films.

Abstract: The occurrence and origin of diffuse intensity contours in electron micrographs of AgBr crystals are investigated. The observations are interpreted in terms of a model, which attributes diffuse scattering to the presence of predominant atom or vacancy clusters of a particular polyhedral type. It is shown that irrespective of the crystal morphology, interstitial Ag ions order in AgBr material in clusters of finite size along 001 type planes. A different geometry of the diffuse intensity locus observed for triangular and hexagonal tabular grains is explained in terms of the different twin plane morphology of these grains.

Abstract: Twin-domains of a b.c.c. crystalline phase with a = 0.29 nm have been found in a surface layer on surfaces of Al-Co decagonal quasicrystals and the coexisting tau(2)-Al13Co4 crystalline approximant. These surface layer domains are introduced during the preparation of electron microscopy thin films by ion milling.

Abstract: For column structures, such as fee-based alloys viewed along the cube direction, the concept of electron channelling through the atom columns is more and more used to interpret the corresponding HREM images. In the case of(partially) disordered columns, the projected potential approach which is used in the channelling description must be questioned since the arrangement of the atoms along the beam direction might affect the exit wave of the electrons. In this paper, we critically inspect this top-bottom effect using multi-slice calculations. A modified channelling theory is introduced which turns out to be very appropriate for the interpretation of these results. For substitutionally disordered column structures, it is also discussed how to link the chemical composition of the material to statistical data of the HREM image. This results in a convenient tool to discern images taken at different thicknesses and focus values.