“Transport, magnetic, and structural properties of La0.7Ce0.3MnO3 thin films: evidence for hole-doping”. Werner R, Raisch C, Leca V, Ion V, Bals S, Van Tendeloo G, Chasse T, Kleiner R, Koelle D, Physical review : B : solid state 79, 054416 (2009). http://doi.org/10.1103/PhysRevB.79.054416
Abstract: Cerium-doped manganite thin films were grown epitaxially by pulsed laser deposition at 720 °C and oxygen pressure pO2=125 Pa and were subjected to different annealing steps. According to x-ray diffraction (XRD) data, the formation of CeO2 as a secondary phase could be avoided for pO28 Pa. However, transmission electron microscopy shows the presence of CeO2 nanoclusters even in those films which appear to be single phase in XRD. With O2 annealing, the metal-to-insulator transition temperature increases, while the saturation magnetization decreases and stays well below the theoretical value for electron-doped La0.7Ce0.3MnO3 with mixed Mn3+/Mn2+ valences. The same trend is observed with decreasing film thickness from 100 to 20 nm, indicating a higher oxygen content for thinner films. Hall measurements on a film which shows a metal-to-insulator transition clearly reveal holes as dominating charge carriers. Combining data from x-ray photoemission spectroscopy, for determination of the oxygen content, and x-ray absorption spectroscopy (XAS), for determination of the hole concentration and cation valences, we find that with increasing oxygen content the hole concentration increases and Mn valences are shifted from 2+ to 4+. The dominating Mn valences in the films are Mn3+ and Mn4+, and only a small amount of Mn2+ ions can be observed by XAS. Mn2+ and Ce4+ XAS signals obtained in surface-sensitive total electron yield mode are strongly reduced in the bulk-sensitive fluorescence mode, which indicates hole-doping in the bulk for those films which do show a metal-to-insulator transition.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 3.836
Times cited: 25
DOI: 10.1103/PhysRevB.79.054416
|
|
|
|
“Tuning the superconducting properties of nanomaterials”. Croitoru MD, Shanenko AA, Peeters FM Springer, Dordrecht, page 1 (2009).
Abstract: Electron continement and its effect on the superconducting-to-normal phase transition driven by a magentic field and/or a current is studied in nanowires. Our investigation is based on a self-consistent numerical solution of the Bogoliubov-de Gennes equations. We find that in a parallel magneitc field and/or in the presence of a supercurrent the transition from the superconducting to the normal phase occurs as a cascade of discontinuous jumps in the superconducting order parameter for diameters D < 10 divided by 15 nm at T = 0. The critical magentic field exhibits quantum-size oscillations with pronounced resonant enhancements as a function of the wire radius.
Keywords: H1 Book chapter; Condensed Matter Theory (CMT); Electron microscopy for materials research (EMAT)
DOI: 10.1007/978-90-481-3120-4_1
|
|
|
|
“Two variants of the 1/2[110]p(203)p crystallographic shear structures: the phasoid Sr0.61Pb0.18(Fe0.75Mn0.25)O2.29”. Lepoittevin C, Hadermann J, Malo S, Pérez O, Van Tendeloo G, Hervieu M, Inorganic chemistry 48, 8257 (2009). http://doi.org/10.1021/ic900762s
Abstract: For the composition (Sr0.61Pb0.18)(Fe0.75Mn0.25)O2.29, a new modulated crystallographic shear structure, related to perovskite, has been synthesized and structurally characterized by transmission electron microscopy. The structure can be described using a monoclinic supercell with cell parameters am = 27.595(2) Å, bm = 3.8786(2) Å, cm = 13.3453(9) Å, and βm = 100.126(5)°, refined from powder X-ray diffraction data. The incommensurate crystallographic shear phases require an alternative approach using the superspace formalism. This allows a unified description of the incommensurate phases from a monoclinically distorted perovskite unit cell and a modulation wave vector. The structure deduced from the high-resolution transmission electron microscopy and high-angle annular dark-field−scanning transmission electron microscopy images is that of a 1/2[110]p(203)p crystallographic shear structure. The structure follows the concept of a phasoid, with two coexisting variants with the same unit cell. The difference is situated at the translational interface, with the local formation of double (phase 2) or single (phase 1) tunnels, where the Pb cations are likely located.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 4.857
Times cited: 11
DOI: 10.1021/ic900762s
|
|
|
|
“3D reconstruction of Ni4Ti3 precipitates in a Ni51Ti49 alloy in a FIB/SEM dual-beam system”. Cao S, Tirry W, van den Broek W, Schryvers D, Materials science forum 583, 277 (2008). http://doi.org/10.4028/www.scientific.net/MSF.583.277
Abstract: Ni4Ti3 precipitates play an important role in the shape memory and superelastic behaviour of thermo-mechanically treated Ni-Ti material. The 3D morphology and distribution of such precipitates with lenticular shape and rhombohedral atomic structure in the austenitic B2 matrix of a binary Ni-rich Ni-Ti alloy has been elucidated via a slice view procedure in a Dual-Beam FIB/SEM system. With the sequence of cross-section SE images obtained from the SEM, a 3D reconstruction has been achieved after proper alignment and image processing, from which both qualitative and quantitative analysis can be performed. Careful imaging is needed to ensure that all variants of the precipitates are observed with equal probability, regardless sample orientation. Moreover, due to the weak contrast of the precipitates, proper imaging conditions need to be selected to allow for semi-automated image treatment. Finally, a volume ratio of 10.2% for the Ni4Ti3 precipitates could be calculated, summed over all variants, which yields a net composition of Ni50.36Ti49.64 for the matrix, leading to an increase of 113 degrees for the martensitic start temperature Ms. Also, the expected relative orientation of the different variants of the precipitates could be confirmed. In the near future, other quantitative measures on the distribution of the precipitates can be expected.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT); Vision lab
DOI: 10.4028/www.scientific.net/MSF.583.277
|
|
|
|
“A-site ordering and stripe phases in manganite films”. Sudheendra L, Moshnyaga V, Lebedev OI, Gehrke K, Belenciuc A, Shapoval O, Van Tendeloo G, Samwer K, Physica: B : condensed matter
T2 –, International Conference on Strongly Correlated Electron Systems (SCES, 2007), MAY 13-18, 2007, Houston, TX 403, 1645 (2008). http://doi.org/10.1016/j.physb.2007.10.332
Abstract: Insulating and metallic stripes above and below the Curie temperature, T-C, respectively, were observed by a high-resolution scanning tunneling microscopy (STM) and/or spectroscopy (STS) in A-site ordered and macroscopically strain free epitaxial La0.75Ca0.25MnO3 film grown on MgO substrate. The “insulating” stripes were found to be incommensurable to the lattice and aligned along (110) direction. Metallic stripes were commensurable with periodicity 2a(p)similar to 0.8 nm and aligned parallel to the crystallographic a/b-axis. Formation of these stripes involves competing charge, orbital, and lattice orders and is an outcome of an overlapping of electron wave functions mediated by the local lattice-strain distribution, existed even in A-site ordered film due to the difference in cation radii of La and Ca. (C) 2007 Elsevier B.V. All rights reserved.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 1.386
DOI: 10.1016/j.physb.2007.10.332
|
|
|
|
“Accuracy and precision in model based EELS quantification”. Bertoni G, Verbeeck J, Ultramicroscopy 108, 782 (2008). http://doi.org/10.1016/j.ultramic.2008.01.004
Abstract: We present results on model based quantification of electron energy loss spectra (EELS), focusing on the factors that influence accuracy and precision in determining chemical concentrations. Several sources of systematical errors are investigated. The spectrometer entrance aperture determines the collection angle, and the effects of its position with respect to the transmitted beam are investigated, taking into account the diffraction by the crystal structure. The effect of the orientation of the sample is tested experimentally and theoretically on SrTiO3, and finally, a simulated experiment on c-BN at different thicknesses confirms the superior results of the model based method with respect to the conventional method. A test on a set of experimental reference compounds is presented, showing that remarkably good accuracy can be obtained. Recommendations are given to achieve high accuracy and precision in practice. (C) 2008 Elsevier B.V. All rights reserved.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.843
Times cited: 44
DOI: 10.1016/j.ultramic.2008.01.004
|
|
|
|
“Acoustic vibration modes and electron-lattice coupling in self-assembled silver nanocolumns”. Burgin J, Langot P, Arbouet A, Margueritat J, Gonzalo J, Afonso CN, Vallee F, Mlayah A, Rossell MD, Van Tendeloo G, Nano letters 8, 1296 (2008). http://doi.org/10.1021/nl073123r
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 12.712
Times cited: 30
DOI: 10.1021/nl073123r
|
|
|
|
“Andreev-type states induced by quantum confinement”. Shanenko AA, Croitoru MD, Mints RG, Peeters FM, Journal of Surface Investigation. X-ray, Synchrotron and Neutron Techniques 2, 611 (2008). http://doi.org/10.1134/S1027451008040216
Abstract: The properties of a clean superconductor with nanoscale dimensions are governed by quantum confinement of the electrons. This results in a spatially inhomogeneous superconducting condensate and in the formation of new Andreev-type quasiparticle states. These states are mainly located beyond regions where the superconducting condensate is enhanced. A numerical self-consistent solution of the Bogoliubov-de Gennes equations for a cylindrical metallic nanowire shows that these new Andreev-type states decrease the ratio of the energy gap to the critical temperature.
Keywords: A1 Journal article; Condensed Matter Theory (CMT); Electron microscopy for materials research (EMAT)
Times cited: 1
DOI: 10.1134/S1027451008040216
|
|
|
|
“Calculation of Debye-Waller temperature factors for GaAs”. Schowalter M, Rosenauer A, Titantah JT, Lamoen D, Springer proceedings in physics 120, 195 (2008)
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
|
|
|
|
“Carbon nanotube TiO2 hybrid films for detecting traces of O2”. Llobet E, Espinosa EH, Sotter E, Ionescu R, Vilanova X, Torres J, Felten A, Pireaux JJ, Ke X, Van Tendeloo G, Renaux F, Paint Y, Hecq M, Bittencourt C;, Nanotechnology 19, 375501 (2008). http://doi.org/10.1088/0957-4484/19/37/375501
Abstract: Hybrid titania films have been prepared using an adapted sol-gel method for obtaining well-dispersed hydrogen plasma-treated multiwall carbon nanotubes in either pure titania or Nb-doped titania. The drop-coating method has been used to fabricate resistive oxygen sensors based on titania or on titania and carbon nanotube hybrids. Morphology and composition studies have revealed that the dispersion of low amounts of carbon nanotubes within the titania matrix does not significantly alter its crystallization behaviour. The gas sensitivity studies performed on the different samples have shown that the hybrid layers based on titania and carbon nanotubes possess an unprecedented responsiveness towards oxygen (i.e. more than four times higher than that shown by optimized Nb-doped TiO(2) films). Furthermore, hybrid sensors containing carbon nanotubes respond at significantly lower operating temperatures than their non-hybrid counterparts. These new hybrid sensors show a strong potential for monitoring traces of oxygen (i.e. <= 10 ppm) in a flow of CO(2), which is of interest for the beverage industry.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 3.44
Times cited: 48
DOI: 10.1088/0957-4484/19/37/375501
|
|
|
|
“Chemistry and structure of anion-deficient perovskites with translational interfaces”. Abakumov AM, Hadermann J, Van Tendeloo G, Antipov EV, Journal of the American Ceramic Society 91, 1807 (2008). http://doi.org/10.1111/j.1551-2916.2008.02351.x
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.841
Times cited: 39
DOI: 10.1111/j.1551-2916.2008.02351.x
|
|
|
|
“Classification and control of the origin of photoluminescence from Si nanocrystals”. Godefroo S, Hayne M, Jivanescu M, Stesmans A, Zacharias M, Lebedev OI, Van Tendeloo G, Moshchalkov VV, Nature nanotechnology 3, 174 (2008). http://doi.org/10.1038/nnano.2008.7
Abstract: Silicon dominates the electronics industry, but its poor optical properties mean that III-V compound semiconductors are preferred for photonics applications. Photoluminescence at visible wavelengths was observed from porous Si at room temperature in 1990, but the origin of these photons (do they arise from highly localized defect states or quantum confinement effects?) has been the subject of intense debate ever since. Attention has subsequently shifted from porous Si to Si nanocrystals, but the same fundamental question about the origin of the photoluminescence has remained. Here we show, based on measurements in high magnetic fields, that defects are the dominant source of light from Si nanocrystals. Moreover, we show that it is possible to control the origin of the photoluminescence in a single sample: passivation with hydrogen removes the defects, resulting in photoluminescence from quantum-confined states, but subsequent ultraviolet illumination reintroduces the defects, making them the origin of the light again.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 38.986
Times cited: 426
DOI: 10.1038/nnano.2008.7
|
|
|
|
“Conformational analysis of TMC114, a novel HIV-1 protease inhibitor”. Nivesanond K, Peeters A, Lamoen D, van Alsenoy C, Journal of Chemical Information and Modeling 48, 99 (2008). http://doi.org/10.1021/ci7001318
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 3.76
Times cited: 13
DOI: 10.1021/ci7001318
|
|
|
|
“Control of surface plasmon localization via self-assembly of silver nanoparticles along silver nanowires”. Tran ML, Centeno SP, Hutchison JA, Engelkamp H, Liang D, Van Tendeloo G, Sels BF, Hofkens J, Uji-i H, Journal of the American Chemical Society 130, 17240 (2008). http://doi.org/10.1021/ja807218e
Abstract: A simple and low-cost method to create metal−metal hybrid nanostructures possessing fairly regularly spaced hot-spots of surface plasmon resonances is proposed. The nanohybrid structure was prepared via self-assembly during a simple drop-casting procedure, using chemically synthesized silver nanowires and silver nanoparticles prepared in a single batch of a polyol process. Wide field illumination of these nanohybrids produced hot-spots with spacings of around 500 nm to 1 ìm. The intensity of the emission/scattering from the hot-spots fluctuates over time. The proposed structure can be useful for the development of molecular-sensors or as a substrate for surface enhanced Raman/fluorescence spectroscopy.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 13.858
Times cited: 51
DOI: 10.1021/ja807218e
|
|
|
|
“Crosshatching on La0.5Ca0.5MnO3 ultrathin films epitaxially grown on SrTiO3(100)”. Wang Z-H, Lebedev OI, Van Tendeloo G, Cristiani G, Habermeier H-U, Physical review : B : condensed matter and materials physics 77, 1 (2008). http://doi.org/10.1103/PhysRevB.77.115330
Abstract: The morphological evolution in La(0.5)Ca(0.5)MnO(3)/SrTiO(3)(100) ultrathin films has been revealed by atomic force microscopy. It was found that ordered linear defects, which are in 1-2 unit cells high and oriented along the cubic [110] and [100] directions, first appear on the smooth surface of films with a thickness of 10 nm. As the epitaxial growth proceeds, these lines on surface develop into a crosshatch pattern for films with a thickness of 25 nm. Using the results of transmission electron microscopy and electrical measurements, we discuss the interplay between the surface pattern formation, the internal dislocation structure, and the variations in the electrical properties.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 3.836
Times cited: 8
DOI: 10.1103/PhysRevB.77.115330
|
|
|
|
“Crystal structure, phase transition, and magnetic ordering in perovskitelike Pb2-xBaxFe2O5 solid solutions”. Nikolaev IV, d' Hondt H, Abakumov AM, Hadermann J, Balagurov AM, Bobrikov IA, Sheptyakov DV, Pomjakushin VY, Pokholok KV, Filimonov DS, Van Tendeloo G, Antipov EV, Physical review : B : condensed matter and materials physics 78, 024426 (2008). http://doi.org/10.1103/PhysRevB.78.024426
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 3.836
Times cited: 29
DOI: 10.1103/PhysRevB.78.024426
|
|
|
|
“Crystalline and amorphous frameworks with giant pores: what information ca we expect from advanced TEM?”.Lebedev OI, Van Tendeloo G, Electron microscopy and multiscale modeling: proceedings of the AIP conference proceedings 999, 245 (2008)
Keywords: P1 Proceeding; Electron microscopy for materials research (EMAT)
|
|
|
|
“DART explained: how to carry out a discrete tomography reconstruction”. Batenburg KJ, Bals S, Sijbers J, Van Tendeloo G, , 295 (2008)
Keywords: P1 Proceeding; Electron microscopy for materials research (EMAT); Vision lab
|
|
|
|
“Development of photocatalytic efficient Ti-based nanotubes and nanoribbons by conventional and microwave assisted synthesis strategies”. Ribbens S, Meynen V, Van Tendeloo G, Ke X, Mertens M, Maes BUW, Cool P, Vansant EF, Microporous and mesoporous materials: zeolites, clays, carbons and related materials 114, 401 (2008). http://doi.org/10.1016/j.micromeso.2008.01.028
Abstract: Titanate nanotubes were prepared via a hydrothermal treatment of TiO2 powders (Riedel De Haen) in a basic solution. Morphology and structure of the prepared samples were characterized by high resolution transmission electron microscopy (HRTEM), selected area electron diffraction (SAED), XRD, FT-Raman spectroscopy, nitrogen sorption and DSC. The photocatalytic activity was evaluated by photocatalytic oxidation of rhodamine 6G. Trititanate nanotubes (TTNT) with inner pore diameters between 4 and 4.2 nm and surface areas up till 360 m(2)/g could be synthesized. The synthesis route was modified by introduction of a calcination step, by applying a lower hydrothermal temperature and microwave irradiation in order to increase the photocatalytic activity of the porous photoactive nanotubular materials. Calcination and a softer hydrothermal treatment led to the formation of anatase without affecting the surface area and nanotubular shape of the samples. In this way, the photocatalytic activity of the original trititanate nanotubes could be significantly increased. By making use of microwave assisted synthesis, the photocatalytic activity call also be increased due to the presence of anatase. However, by applying microwave synthesis, a different structure was obtained, nanoribbons (NR) instead of nanotubcs, resulting in a decrease in surface area and porosity.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT); Laboratory of adsorption and catalysis (LADCA); Organic synthesis (ORSY)
Impact Factor: 3.615
Times cited: 47
DOI: 10.1016/j.micromeso.2008.01.028
|
|
|
|
“Direct imaging of loaded metal-organic framework materials (metal@MOF-5)”. Turner S, Lebedev OI, Schroeder F, Fischer RA, Van Tendeloo G, Chemistry of materials 20, 5622 (2008). http://doi.org/10.1021/cm801165s
Abstract: We illustrate the potential of advanced transmission electron microscopy for the characterization of a new class of soft porous materials: metal@Zn4O(bdc)3 (metal@MOF-5; bdc = 1,4-benzenedicarboxylate). By combining several electron microscopy techniques (transmission electron microscopy (TEM), high-resolution transmission electron microscopy (HRTEM), electron diffraction (ED), high-angle annular dark-field scanning transmission electron microscopy (HAADF-STEM), and electron tomography) and by carefully reducing the electron dose to avoid beam damage, it is possible to simultaneously characterize the MOF-5 framework material and the loaded metal nanoparticles. We also demonstrate that electron tomography can be used to accurately determine the position and distribution of the particles within the MOF-5 framework. To demonstrate the implementation of these microscopy techniques and what kind of results can be expected, measurements on gas-phase-loaded metal−organic framework materials Ru@MOF-5 and Pd@MOF-5 are presented.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 9.466
Times cited: 112
DOI: 10.1021/cm801165s
|
|
|
|
“Direct observation of nanometer-scale pinning sites in (Nd0.33Eu0.20Gd0.47)Ba2Cu3O7-\delta single crystals”. Das P, Koblischka MR, Turner S, Van Tendeloo G, Wolf T, Jirsa M, Hartmann U, Europhysics letters 83, 37005 (2008). http://doi.org/10.1209/0295-5075/83/37005
Abstract: We report on the observation of self-organized stripe-like structures on the as-grown surface and in the bulk of (Nd,Eu,Gd)Ba2Cu3Oy single crystals. The periodicity of the stripes on the surface lies between 500800 nm. These are possibly the growth steps of the crystal. Transmission electron microscopy investigations revealed stripes of periodicity in the range of 2040 nm in the bulk. From electron back scattered diffraction investigations, no crystallographic misorientation due to the nanostripes has been found. Scanning tunneling spectroscopic experiments revealed nonsuperconducting regions, running along twin directions, which presumably constitute strong pinning sites.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 1.957
Times cited: 5
DOI: 10.1209/0295-5075/83/37005
|
|
|
|
“Dislocations and plasticity of experimentally deformed coesite”. Idrissi H, Cordier P, Jacob D, Walte N, European journal of mineralogy 20, 665 (2008). http://doi.org/10.1127/0935-1221/2008/0020-1849
Abstract: Dislocation microstructures have been characterized by transmission electron microscopy in polycrystalline coesite deformed experimentally at 4 GPa, 1200 degrees C. Burgers vectors have been determined by large-angle convergent-beam electron diffraction. Sample orientation was assisted by precession electron diffraction to overcome difficulties arising from pseudo-hexagonal symmetry. The results are explained by using a pseudo-hexagonal setting. We found that most dislocations observed are of the 1/3 < 2 (1) over bar(1) over bar0 > type. No clear glide plane was identified, suggesting that climb is activated under these conditions. This conclusion is supported by the observation of numerous subgrain boundaries. We have also observed some [00011 dislocations. Finally, the C12/cl space group to which coesite belongs being centred, an additional slip system is observed: 1/6[(1) over bar2 (1) over bar3](01 (1) over bar1) (1/2[(1) over bar 10](110) in the monoclinic setting).
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 1.362
Times cited: 5
DOI: 10.1127/0935-1221/2008/0020-1849
|
|
|
|
“Dynamics of nanoclustering in Te+ implanted Si after application of high frequency electromagnetic field and thermal annealing”. Kalitzova M, Lebedev OI, Zollo G, Gesheva K, Vlakhov E, Marinov Y, Ivanova T;, Applied physics A : materials science &, processing 91, 515 (2008). http://doi.org/10.1007/s00339-008-4441-2
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 1.455
DOI: 10.1007/s00339-008-4441-2
|
|
|
|
“Effect of annealing on cold-rolled Ni-Ti alloys”. Srivastava AK, Yang Z, Schryvers D, van Hurnbeeck J, Materials science and engineering: part A: structural materials: properties, microstructure and processing 481, 594 (2008). http://doi.org/10.1016/j.msea.2006.12.216
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 3.094
Times cited: 8
DOI: 10.1016/j.msea.2006.12.216
|
|
|
|
“Effect of temperature on the 002 electron structure factor and its consequence for the quantification of ternary and quaternary III-V crystals”. Titantah JT, Lamoen D, Schowalter M, Rosenauer A, Springer proceedings in physics 120, 189 (2008)
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
|
|
|
|
“The effect of temperature on the structural, electronic and optical properties of sp3-rich amorphous carbon”. Titantah JT, Lamoen D, Journal of physics : condensed matter 20, 035216 (2008). http://doi.org/10.1088/0953-8984/20/03/035216
Abstract: The effect of temperature on the structural, electronic and optical properties of dense tetrahedral amorphous carbon made of similar to 80% sp(3)-bonded atoms is investigated using a combination of the classical Monte Carlo technique and density functional theory. A structural transformation accompanied by a slight decrease of the sp(3) fraction is evidenced above a temperature of about 600 degrees C. A structural analysis in combination with energy-loss near-edge structure calculations shows that beyond this temperature, the sp(2)-bonded C sites arrange themselves so as to enhance the conjugation of the p electrons. The Tauc optical band gap deduced from the calculated dielectric function shows major changes beyond this temperature in accordance with experimental results. Energy-loss near-edge structure and band gap calculations additionally reveal a massive destabilization of the of sp(3) bonding phase in favour of sp(2) bonding at a temperature of about 1300 degrees C which agrees very well with the reported value of 1100 degrees C.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.649
Times cited: 11
DOI: 10.1088/0953-8984/20/03/035216
|
|
|
|
“Electrical switching in Fe/Cr/MgO/Fe magnetic tunnel junctions”. Halley D, Majjad H, Bowen M, Najjari N, Henry Y, Ulhaq-Bouillet C, Weber W, Bertoni G, Verbeeck J, Van Tendeloo G, Applied physics letters 92, 212115 (2008). http://doi.org/10.1063/1.2938696
Abstract: Hysteretic resistance switching is observed in epitaxial Fe/Cr/MgO/Fe magnetic tunnel junctions under bias voltage cycling between negative and positive values of about 1 V. The junctions switch back and forth between high- and low-resistance states, both of which depend on the device bias history. A linear dependence is found between the magnitude of the tunnel magnetoresistance and the crafted resistance of the junctions. To explain these results, a model is proposed that considers electron transport both by elastic tunneling and by defect-assisted transmission. (c) 2008 American Institute of Physics.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 3.411
Times cited: 33
DOI: 10.1063/1.2938696
|
|
|
|
“Electrochemical growth and characterization of nanostructured ZnO thin films”. Ghica C, Enculescu I, Nistor LC, Matei E, Van Tendeloo G, Journal of optoelectronics and advanced materials 10, 3237 (2008)
Abstract: ZnO is a wide band-gap (ca. 3.4 eV) semiconductor, piezoelectric, pyroelectric, biocompatible, transparent in the visible spectrum and UV light emitting material. The fabrication in 2001 of the first nanobelts of semiconductor oxide materials lead to a rapid expansion of researches concerning one dimensional nanostructures (nanotubes, nanowires, nanobelts), given their possible application in optics, optoelectronics, piezoelectricity, catalysis. Researches carried on up to date evidenced the possibility to obtain an extraordinary variety of ZnO nanostructures, in function of the experimental parameters and the used growth methods. In this work we present morphostructural results on nanostructured ZnO layers obtained by electrochemical deposition. The films have been grown on gold covered glass plates and Si wafers, in various experimental conditions such as: nature of the wetting agents, electrical polarization of the substrate (continuous, pulsed). The influence of the growth conditions on the crystalline structure and morphology of the films is revealed by scanning and transmission electron microscopy studies. The films show a variety of growth morphologies, from entangled-wires-like to honeycomb-like layers. These large-specific-surface layers will be tested as nanostructured substrates for photovoltaic cells with improved efficiency.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 0.449
|
|
|
|
“Electron energy-loss spectroscopy and first-principles calculation studies on a Ni-Ti shape memory alloy”. Yang Z, Tirry W, Lamoen D, Kulkova S, Schryvers D, Acta materialia 56, 395 (2008). http://doi.org/10.1016/j.actamat.2007.10.001
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 5.301
Times cited: 20
DOI: 10.1016/j.actamat.2007.10.001
|
|
|
|
“Electron energy-loss spectroscopy study of NiTi shape memory alloys”. Yang ZQ, Schryvers D, Materials science and engineering: part A: structural materials: properties, microstructure and processing 481, 214 (2008). http://doi.org/10.1016/j.msea.2006.12.227
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 3.094
Times cited: 7
DOI: 10.1016/j.msea.2006.12.227
|
|